CN103013266A - Reflection heat insulating coating for building - Google Patents
Reflection heat insulating coating for building Download PDFInfo
- Publication number
- CN103013266A CN103013266A CN2012104204121A CN201210420412A CN103013266A CN 103013266 A CN103013266 A CN 103013266A CN 2012104204121 A CN2012104204121 A CN 2012104204121A CN 201210420412 A CN201210420412 A CN 201210420412A CN 103013266 A CN103013266 A CN 103013266A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- thickening material
- insulation paint
- reflective heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a reflection heat insulating coating for a building. The reflection heat insulating coating comprises the following components in parts by weight: 9.5 to 23 parts of water, 0.44 to 1.08 parts of thickener, 0.45 to 0.55 part of dispersing agent, 0.1 to 0.2 part of wetting agent, 0.4 to 0.8 part of defoaming agent, 0.05 to 0.25 part of multifunctional auxiliary agent, 0.05 to 0.15 part of preservative, 0.05 to 0.25 part of mildew preventive, 15 to 25 parts of titanium dioxide, 0 to 22.5 parts of nano heat insulating powder slurry, 2 to 6.5 parts of filling, 1 to 2 parts of anti-freezing agent, 1.25 to 2 parts of coalescing agent, 0.01 to 0.02 part of emulsifying agent, 25 to 40 parts of emulsion, 2.5 to 5 parts of hydrophobing agent, 0.05 to 0.15 part of pH value adjustment agent and 0.02 to 0.07 part of tributyl phosphate. After the coating is formed into a film, the surface of the coating is high in hydrophobicity; the coating has hydrophobic, water-proof and self-cleaning functions; and the heat insulating performance of the coating film can be improved.
Description
Technical field
The present invention relates to a kind of reflective heat-insulation paint for building, belong to building material technical field.
Background technology
In recent years, along with the attention of country to building energy conservation, the external wall outer insulation market development is swift and violent.Although the various forms of external thermal insulation systems such as rock cotton board, styrofoam, extruded sheet and heat-insulating granules mortar have played certain effect for the energy-saving and emission-reduction of building field, but also expose gradually the some shortcomings part, such as engineering method is complicated, long in time limit, cost is high, quality control is difficult etc.
In view of this, recent research to reflective heat-insulation paint for building has had considerable progress.Different with traditional external wall outer insulation, reflective heat-insulation paint is based on diverse mentality of designing.Traditional external wall outer insulation adopts the thinking of " block up ", with the heat in the external world every saving in thermal insulation layer in the outside of building basic unit.Reflective heat-insulation paint then adopts the design concept of " dredging ", with instant the reflecting away of the energy of sunlight, and will build in good time the accumulation heat discharge in infrared mode.
Reflective heat-insulation paint for building in the market mainly with glass microballon, hollow glass micropearl, hollow ceramic microspheres as functional filler, to reach the purpose of reflective insulation.But this kind reflective heat-insulation paint exists the following problem that can't avoid: owing to the shielding effect of other fillers, the reflex action of functional filler is affected (1); (2) because the particle diameter of functional filler is generally larger, there is the occasion of requirement not meet the demands in some coating fineness; (3) because the crisp brittle nature of matter of functional filler, can not produce according to traditional building coating technique fully, thereby present most producer adopts to roll the altar method and produce, and this production technique inefficiency, production time prolong, the equipment washing difficulty, and facility investment is very large.
Therefore, existing reflective heat-insulation paint for building is restricting it in the development and application of building energy saving field.
Summary of the invention
The object of the invention provides a kind of reflective heat-insulation paint for building.
For achieving the above object, the technical solution used in the present invention is: a kind of reflective heat-insulation paint for building in weight part, comprises following component:
9.5 ~ 23 parts in water
0.44 ~ 1.08 part of thickening material
0.45 ~ 0.55 part of dispersion agent
0.1 ~ 0.2 part of wetting agent
0.4 ~ 0.8 part of defoamer
0.05 ~ 0.25 part of multifunctional assistant
0.05 ~ 0.15 part of sanitas
0.05 ~ 0.25 part of mould inhibitor
15 ~ 25 parts of titanium dioxides
10 ~ 22.5 parts in nano heat-insulating powder slurry
2 ~ 6.5 parts of fillers
1 ~ 2 part of frostproofer
1.25 ~ 2 parts of film coalescence aid
0.01 ~ 0.02 part of emulsifying agent
25 ~ 40 parts of emulsions
2.5 ~ 5 parts of hydrophobizing agents
0.05 ~ 0.15 part of pH value conditioning agent
0.02 ~ 0.07 part of tributyl phosphate
Wherein, the solid content of described nano heat-insulating powder slurry is 40 ~ 60%, is the mixture of rutile type nano titanic oxide and metal oxide, and its particle diameter is 250 ~ 400 nanometers; Described metal oxide is selected from one or more in ferric oxide, Vanadium Pentoxide in FLAKES and the Manganse Dioxide;
Described hydrophobizing agent is polysiloxane emulsion.
Above, described hydrophobizing agent is the hydrophobizing agent of polysiloxane emulsion class, it also can be the hydrophobizing agent of the polysiloxane emulsion class of modification, it can select existing goods, as selects water nano hydrophobizing agent SS-1(Beijing Shouchuang Nano Techn Co., Ltd. to produce) or hydrophobizing agent LC-808(Shandong Lu worker's coatings additive(s) factory product).
The nano heat-insulating powder slurry that the present invention adopts is on the basis of Rutile type Titanium Dioxide, and particle diameter is less, disperses more even more stable, better surface reflection scattering power is arranged, and very high emittance is arranged, reflection that can be stronger and radiation sunlight reduce the absorption to solar energy.
It is the main function filler that the present invention adopts nano heat-insulating powder slurry, and modified titanium is the subsidiary function filler, is that coating has good reflectivity to sunlight, and heat is had good radiativity; Add simultaneously suitable hydrophobic material, so that film coated surface has larger contact angle to water, reduce rainwater and invade profit and permeate what film, the water ratio that reduces to film, not only give certain hydrophobic water-repellancy of filming, and reduced the thermal conductivity of filming, improve the thermal insulation of filming.
Adopt the made coating film forming rear surface of coating of the present invention that good hydrophobicity is arranged, this specific character not only makes to film has certain hydrophobic waterproof self-cleaning function, and because the surface tension decrease of filming, increase the contact angle of water, reduced the invade profit of rainwater to filming, stoped moisture to the internal penetration of filming, reduced the water ratio of filming, the thermal conductivity that reduces to film has finally reduced the specific absorption of filming to solar spectrum, has promoted the heat-proof quality of filming.
The hydrophobizing agent that the present invention adopts can reduce the surface tension of filming significantly; Hydrophobizing agent adds the surface that can form rapidly a kind of special construction in the coating at coating surface, and similar with the chessboard of chess, the black square of imaginary chessboard is hydrophobic surface, and white square is water-wetted surface, and namely hydrophobic surface and water-wetted surface are staggered.By adding the nano material of different-grain diameter and structure, the quantity and the power of hydrophobicity of control hydrophobic surface, its macro surface shows as both hydrophobicly at last, and certain wetting ability is arranged again, and the while does not affect ventilation property and the recoatability of filming.
In the technique scheme, described defoamer comprises the first defoamer and the second defoamer, and described the first defoamer is organosilicon and ester class compound defoamer, and described the second defoamer is the mixture of water drain silica and mineral oil.Add defoamer and can eliminate the foaming that produces in coating material production and the construction, the composite use of these two kinds of defoamers and tributyl phosphate can effectively reduce the generation of the defectives such as shrinkage cavity, cissing.
In the technique scheme, described sanitas is isothiazoline-3-ketone sanitas; Described mould inhibitor is the fused heterocycle type mould inhibitor.Sanitas and mould inhibitor can prevent from coating and film being subject to microorganism encroach and causing rotten risk.
In the technique scheme, described thickening material comprises the first thickening material, the second thickening material and the 3rd thickening material; Described the first thickening material is the ether of cellulose thickening material, and described the second thickening material is alkali swelling type thickening material, and described the 3rd thickening material is the polyurethanes thickening material.The reasonably combined use of all kinds of thickening materials can make coating that good rheological is arranged, and improves application property, reduces the possibility that minute water occurs.
In the technique scheme, described titanium dioxide is Rutile type Titanium Dioxide.Rutile type Titanium Dioxide is strong, weather-proof ageing-resistant to the specular scattering ability of sunlight, stable chemical performance.
In the technique scheme, described filler is selected from one or both in sericite in powder and the water-ground limestone.
Sericite in powder is flakey, and is full of elasticity, flexible, and resistance to abrasion and wear resistance are good, and high temperature insulation can increase in coating and is coated with film toughness and improves weathering resistance; The water-ground limestone Heat stability is good, whiteness is high, oil absorbency is low, is a kind of customary filler.
In the technique scheme, described frostproofer is ethylene glycol or propylene glycol; The effective constituent of described film coalescence aid is 2,2,4-neopentyl glycol-1,3 mono isobutyrate; Described emulsifying agent is polyoxyethylene sorbitan fatty acid ester emulsifying agent.
In the technique scheme, described emulsion is selected from one or more in pure-acrylic emulsion, organosilicon crylic acid latex and the fluorine carbon emulsion.
Emulsion is the basic substance of coating film forming, and the performance of emulsion is largely determining the quality of coating property.The emulsion that the application chooses has good weather-proof ageing resistance, water-fast contamination resistance and the good transparency.
In the technique scheme, described pH value conditioning agent is selected from 2-amino-2-methyl-1-propanol, ammoniacal liquor or sodium hydroxide solution.2-amino-2-methyl-1-propanol is called for short AMP-95.
In the technique scheme, described dispersion agent is water-based polycarboxylic acid salt dispersion agent; Described wetting agent is alkylphenol polyoxyethylene class wetting agent; The effective constituent of described multifunctional assistant is 2-amino-2-methyl-1-propanol.Its effect is to make the uniform filling dispersion and keep stable, makes coating to base material good wettability be arranged, and strengthens and films to the sticking power of base material.
Principle of work of the present invention is as follows: the sun at every moment huge energy to terrestrial radiation, the solar radiation spectrum in the earth atmosphere upper bound more than 99% between 0.15~4.0 micron of wavelength, about 50% solar radiation energy is (0.4~0.76 micron of wavelength) in the visible range, 7% in the UV spectrum district (wavelength<0.4 micron), 43% at infrared spectral region (wavelength〉0.76 micron), and beta maximum energy is at 0.475 micron place of wavelength; Solar radiation is by atmosphere, and a part arrives ground, is called direct solar radiation; Another part is absorption, scattering and the reflections such as the molecule, the micronic dust in the atmosphere, steam of atmosphere; A solar radiation part that is scattered is returned the outer space, and another part arrives ground, and this part of arrival ground is called diffusesolarradiation; The diffusesolarradiation and the direct solar radiation sum that arrive ground are called total radiation; Solar radiation is by behind the atmosphere, its intensity and spectral power distribution all change, and the solar radiation energy that arrives ground is more much smaller than aeropause, and energy distribution almost disappeares in the UV spectrum district on solar spectrum, be reduced to 40% in the visible range, and increase to 60% at infrared spectral region.Solar light irradiation all can produce reflection, absorption and transmission phenomenon on any object; Wherein, there is following relation: ρ+α+r=1 between its reflectivity ρ, specific absorption α and the transmissivity r.Because the following matrix of filming mostly is the materials such as opaque mortar, concrete, putty, thus can be similar to think transmittance r=0, following formula is reduced to ρ+α=1.Hence one can see that, improve the heat-proof quality of filming, and will reduce the specific absorption of filming, and will reduce the specific absorption of filming, and can adopt two kinds of measures: direct method and indirect method.Direct method adopts exactly gives the hydrophobicity of filming, and reduces the invade profit of rainwater to filming, and stops moisture to the internal penetration of filming, and reduces the water ratio of filming, and the thermal conductivity that reduces to film reduces specific absorption.Indirect method is exactly according to ρ+α=1, the specific absorption α that the reflectivity ρ that increase is filmed comes relative reduce to film.
The present invention utilizes direct method, in prescription, add hydrophobizing agent, hydrophobizing agent adds the surface that can form rapidly a kind of special construction in the coating at coating surface, similar with the chessboard of chess, the black square of imagination chessboard is hydrophobic surface, white square is water-wetted surface, be that hydrophobic surface and water-wetted surface are staggered, by adding the nano material of different-grain diameter and structure, the quantity of control hydrophobic surface and the power of hydrophobicity, last its macro surface shows as both hydrophobic, and certain wetting ability is arranged again, does not affect ventilation property and the recoatability of filming simultaneously.This shows, the adding of hydrophobizing agent, not only making films has certain hydrophobic waterproof self-cleaning function, and make the surface tension decrease of filming, and increased the contact angle of water, reduced the invade profit of rainwater to filming, stop moisture to the internal penetration of filming, reduced the water ratio of filming, the thermal conductivity that reduces to film has finally reduced the specific absorption of filming to solar spectrum.
The present invention has utilized indirect method simultaneously, adds nano heat-insulating powder slurry in prescription, and the good reflective heat-insulation paint of heat-proof quality is filmed and mainly is made of transmitance height macromolecule resin, the functional filler that plays reflected solar radiation and other necessary component.Wherein, selecting of functional filler is the key factor that affects heat-proof quality.The present invention has chosen the nano modification heat-insulating powder, and the main component of nano heat-insulating powder slurry is rutile type nano titanic oxide and metal oxide ir radiation powder.The refractive index of rutile titanium dioxide is 2.8, and reflection coefficient is 80%, and solar radiation is had good reflected refraction effect.It is titanium dioxide about 250 ~ 400 nanometers that nano heat-insulating powder slurry adopts particle diameter, and this size is about about half of the visible spectrum of concentration of energy and infrared spectra wavelength, and it is had best reflecting effect.And, use active organic group that processing is wrapped up on the surface of titanium dioxide, not only improve the reflectivity of titanium dioxide surface, and make it in the non-microbead type architectural reflective heat-insulation paint of hydrophobicity, reduce gathering, disperse more even, the raising reflection efficiency.
In addition, natural object when absorbing sunlight also constantly to extraneous irradiating infrared light and the longer hertzian wave of wavelength.This radiation is that the thermal motion by molecule, atom causes, the surface properties of the size of quantity of radiant energy and temperature and object has very close relationship, is commonly referred to as thermal radiation.The periphery of the earth is wrapped in thick atmospheric layer, the gas and the various suspended substances such as water vapour, dust that contain nitrogen, oxygen, carbonic acid gas, ozone in the atmospheric layer, reflection, sorption are played in the thermal radiation that these materials send ground object, hamper the object thermal radiation to the energy dispersal in outer space.But in 8 ~ 13.5 microns wavelength band, the materials such as water vapour, carbonic acid gas and ozone are very weak to thermal-radiating absorption and reflection potential, and the transparency of atmosphere in this wave band is high, is commonly referred to atmospheric window.The thermal radiation of ground object can be hanged down continually and directly be passed atmospheric window and reach the outer space, realizes diffusion and the release of energy.
Although distribute outside the external world through the reflection of film coated surface and the Multi reflection on the middle titanium dioxide heat-insulating powder surface of filming, still have the sunlight of small part to enter the inside of filming and be converted into heat.Metal oxide ir radiation powder in the nano heat-insulating powder slurry has higher emittance at 8 ~ 13.5 microns, and the heat in filming is transmitted into the external world in infrared mode by atmospheric window, further reduces and films to sun Optical Absorption.
Because technique scheme is used, the present invention compared with prior art has following advantages:
1. the present invention's design has obtained a kind of new reflective heat-insulation paint for building, adopt the nano modification heat-insulating powder, the main component of nano heat-insulating powder slurry is rutile type nano titanic oxide and metal oxide ir radiation powder, it has very high reflection, obstruct and radiance, good heat-insulation effect to solar spectrum.
2. the present invention has added suitable hydrophobizing agent in formulation for coating material, so that film coated surface has larger contact angle to water, reducing rainwater invades profit and permeates what film, the water ratio that reduces to film, not only give certain hydrophobic water-repellancy of filming, and reduced the thermal conductivity of filming, and finally reduced the specific absorption of filming to solar spectrum, improve the thermal insulation of filming.
The concise production process of coating of the present invention, low cost, construction is easy, the duration is short, aqueous, environmental protective, nontoxicly do not fire, and production technique is simply efficient, facility investment is little, can be widely used in the various smooth and special-shaped part of external surface of buildings.
Embodiment
The invention will be further described below in conjunction with embodiment:
Embodiment one
A kind of reflective heat-insulation paint for building in weight part, comprises following component and preparation method:
In disperseing cylinder, add 8.5 parts of water and 0.04 part of first thickening material (BERMOCOLL EHM300, a kind of compound non-ionic water-soluble ether of cellulose), start about dispersion machine speed governing to 800 rev/min, add successively 0.45 part of DA dispersion agent, 0.1 part PE100 wetting agent, 0.2 part the first defoamer (SPA202), 0.3 part the second defoamer (DFC17), 0.05 part multifunctional assistant (AMP95), 0.05 portion sanitas (DOA2w), 0.005 part mould inhibitor (H981), stir, continue to add 15 parts of titanium dioxides, 22.5 part nano heat-insulating powder slurry, 2.5 part 800 order sericites in powder, 4 part of 800 order water-ground limestone;
With 1 part of propylene glycol, 1.25 parts of film coalescence aid (CS-12), 0.01 part of emulsifying agent (T-80), 1 part of water pre-emulsification, add to disperse in the cylinder, improve rotating speed to 1200 rev/min, disperseed 30 minutes; Move in the paint mixing cylinder after will disperseing in the cylinder gained slurry by sand mill sand milling to 60 micron fineness, be under 800 rev/mins the rotating speed at dispersion machine, add successively 40 parts of pure-acrylic emulsions, 0.2 part of second thickening material (SJB-2), 0.2 part of the 3rd thickening material (RM-2020), 2.5 parts of SS-1 hydrophobizing agents, regulate pH value to 9.5 with ammoniacal liquor, add at last 0.05 part of tributyl phosphate, filter and package and get product.
Through test, reach over-all properties requirement, detected result such as the following table of premium grads among GB/T25261-2010 " reflective heat-insulation paint for building " and the GB/T9755-2001 " exterior wall coating material of synthetic resin emulsion " through end properties.
Annotate: 1 ~ 12 foundation is GB/T9755-2001 in the table, and 13,14 foundations are GB/T25261-2010.
For hydrophobic test, because not yet there are relevant criterion in present industry and country, so the present invention tests in accordance with the following methods:
One, contact angle method of testing
1, take a sample by the regulation of GB 3186, sampling amount is decided according to the check needs;
2, the humiture of the status adjustment of test plate (panel) and test should meet the regulation of GB 9278;
3, (increased pressure board, thickness are the eternit flat board of the technical requirements of 4mm ~ 6mm), and its surface treatment is undertaken by 7.3 regulation among the GB/T 9271-1988 in order to meet 1 class version in the JC/T 412-1991 table 2 with test plate (panel) in test;
4, coating thickness is 150 microns, and coating together; Make 3 test plate (panel)s;
5, curing time is 7 days;
6, take the good test plate (panel) film coated surface of maintenance as tested solid, take water as drop, as the contact angle of separating method test water to filming, the result gets the mean value that three test plate (panel)s record contact angle with outside view;
7, contact angle is qualified greater than 60 degree.
Two, trickle observation
1, requires according to the method described above to make 3 test plate (panel)s;
2, test plate (panel) being positioned over testing table is, long limit becomes 45 degree with sea line, and minor face is parallel with sea line;
3, with the common suction pipe water droplet that vertically drips in the upper end of test plate (panel), observe the operation form of water droplet on test plate (panel) and judged classification:
Poor: water droplet flows down on test plate (panel) naturally from water-drop point, forms a continuous washmarking;
Qualified: water droplet beading from the test plate (panel) tumbles, though washmarking is arranged, discontinuous;
Well: water droplet beading from the test plate (panel) tumbles, and seldom washmarking is arranged;
Outstanding: water droplet beading from the test plate (panel) tumbles, almost without washmarking;
The hydrophobicity of reflective heat-insulation paint require to reach simultaneously contact angle greater than 60 degree and trickle grade reach qualified more than.
According to above-described method, as shown in the table to the hydrophobicity test result of reflective heat-insulation paint:
Embodiment two
A kind of reflective heat-insulation paint for building in weight part, comprises following component and preparation method:
In disperseing cylinder, add 17.5 parts of water and 0.06 part of first thickening material (BERMOCOLL EHM300, it is a kind of compound non-ionic water-soluble ether of cellulose), start about dispersion machine speed governing to 800 rev/min, add successively 0.5 part of DA dispersion agent, 0.15 part PE100 wetting agent, 0.2 part the first defoamer (SPA202), 0.2 part the second defoamer (DFC17), 0.15 part multifunctional assistant (AMP95), 0.1 portion sanitas (DOA2w), 0.25 part mould inhibitor (H981), stir, continue to add 19 parts of titanium dioxides, 15 parts of nano heat-insulating powder slurries, 2.5 part 800 order sericites in powder, 4 part of 800 order water-ground limestone;
With 1.5 parts of ethylene glycol, 1.7 parts of film coalescence aid (CS-12), 0.015 part of emulsifying agent (T-80), 1.825 parts of water pre-emulsifications, add and disperse in the cylinder; Improve rotating speed to 1200 rev/min, disperseed 30 minutes; Move in the paint mixing cylinder after will disperseing in the cylinder gained slurry by sand mill sand milling to 60 micron fineness, be under 800 rev/mins the rotating speed at dispersion machine, add successively 31.5 parts of organosilicon crylic acid latexs, 0.25 part of second thickening material (SJB-2), 0.25 part of the 3rd thickening material (RM-2020), 3.7 parts of hydrophobizing agents (LC-808), regulate pH value to 9.5 with 30 sodium hydroxide solutions, add at last 0.05 part of tributyl phosphate, filter and package and get product.
Through test, reach the over-all properties requirement of premium grads among GB/T25261-2010 " reflective heat-insulation paint for building " and the GB/T9755-2001 " exterior wall coating material of synthetic resin emulsion ", detected result such as following table through end properties:
Annotate: 1 ~ 12 foundation is GB/T9755-2001 in the table, and 13,14 foundations are GB/T25261-2010.
Embodiment three
A kind of reflective heat-insulation paint for building in weight part, comprises following component and preparation method:
In disperseing cylinder, add 20 parts of water and 0.08 part of first thickening material (BERMOCOLL EHM300), start about dispersion machine speed governing to 800 rev/min, add successively 0.55 part of DA dispersion agent, 0.2 part PE100 wetting agent, 0.4 part the first defoamer (SPA202), 0.4 part the second defoamer (DFC17), 0.25 part multifunctional assistant (AMP95), 0. 15 portions of sanitass (DOA2w), 0.05 part mould inhibitor (H981), stir, continue to add 25 parts of titanium dioxides, 10 parts of nano heat-insulating powder slurries, 2.5 part 800 order sericites in powder, 4 part of 800 order water-ground limestone;
With 1.5 parts of ethylene glycol, 1.5 parts of film coalescence aid (CS-12), 0.02 part of emulsifying agent (T-80), 1.7 parts of water pre-emulsifications, add and disperse in the cylinder; Improve rotating speed to 1200 rev/min, disperseed 30 minutes; Move in the paint mixing cylinder after will disperseing in the cylinder gained slurry by sand mill sand milling to 60 micron fineness, be under 800 rev/mins the rotating speed at dispersion machine, add successively 25 parts of organosilicon crylic acid latexs, 0.5 part of second thickening material (SJB-2), 0.5 part of the 3rd thickening material (RM-2020), 5 parts of SS-1 hydrophobizing agents, regulate pH value to 9.5 with AMP95, add at last 0.05 part of tributyl phosphate, filter and package and get product.
Through test, reach the over-all properties requirement of premium grads among GB/T25261-2010 " reflective heat-insulation paint for building " and the GB/T9755-2001 " exterior wall coating material of synthetic resin emulsion ", detected result such as following table through end properties:
Annotate: 1 ~ 12 foundation is GB/T9755-2001 in the table, and 13,14 foundations are GB/T25261-2010.
From top three embodiment as seen, the properties of reflective heat-insulation paint for building of the present invention all can satisfy the requirement of premium grads and GB/T25261-2010 standard among the GB/T9755-2001, and has good hydrophobicity.The good hydrophobicity of having filmed, contact angle reach more than 100 degree, and this specific character can reduce the invade profit of rainwater to filming, and stop moisture to the internal penetration of filming, and reduce the water ratio of filming, and the thermal conductivity that reduces to film helps to promote the heat-proof quality of filming.
By the peripheral protective application reflective heat-insulation paint of the present invention at buildings, not only can have certain hydrophobic waterproof self-cleaning function, and can reflect the obstruct solar energy, and the heat energy of oneself accumulation is dispersed in the environment with the form of radiation goes.
Claims (10)
1. a reflective heat-insulation paint for building is characterized in that, in weight part, comprises following component:
9.5 ~ 23 parts in water
0.44 ~ 1.08 part of thickening material
0.45 ~ 0.55 part of dispersion agent
0.1 ~ 0.2 part of wetting agent
0.4 ~ 0.8 part of defoamer
0.05 ~ 0.25 part of multifunctional assistant
0.05 ~ 0.15 part of sanitas
0.05 ~ 0.25 part of mould inhibitor
15 ~ 25 parts of titanium dioxides
10 ~ 22.5 parts in nano heat-insulating powder slurry
2 ~ 6.5 parts of fillers
1 ~ 2 part of frostproofer
1.25 ~ 2 parts of film coalescence aid
0.01 ~ 0.02 part of emulsifying agent
25 ~ 40 parts of emulsions
2.5 ~ 5 parts of hydrophobizing agents
0.05 ~ 0.15 part of pH value conditioning agent
0.02 ~ 0.07 part of tributyl phosphate
Wherein, the solid content of described nano heat-insulating powder slurry is 40 ~ 60%, is the mixture of rutile type nano titanic oxide and metal oxide, and its particle diameter is 250 ~ 400 nanometers; Described metal oxide is selected from one or more in ferric oxide, Vanadium Pentoxide in FLAKES and the Manganse Dioxide;
Described hydrophobizing agent is polysiloxane emulsion.
2. reflective heat-insulation paint for building according to claim 1, it is characterized in that: described defoamer comprises the first defoamer and the second defoamer, described the first defoamer is organosilicon and ester class compound defoamer, and described the second defoamer is the mixture of water drain silica and mineral oil.
3. reflective heat-insulation paint for building according to claim 1, it is characterized in that: described sanitas is isothiazoline-3-ketone sanitas; Described mould inhibitor is the fused heterocycle type mould inhibitor.
4. reflective heat-insulation paint for building according to claim 1, it is characterized in that: described thickening material comprises the first thickening material, the second thickening material and the 3rd thickening material; Described the first thickening material is the ether of cellulose thickening material, and described the second thickening material is alkali swelling type thickening material, and described the 3rd thickening material is the polyurethanes thickening material.
5. reflective heat-insulation paint for building according to claim 1, it is characterized in that: described titanium dioxide is Rutile type Titanium Dioxide.
6. reflective heat-insulation paint for building according to claim 1, it is characterized in that: described filler is selected from one or both in sericite in powder and the water-ground limestone.
7. reflective heat-insulation paint for building according to claim 1, it is characterized in that: described frostproofer is ethylene glycol or propylene glycol; The effective constituent of described film coalescence aid is 2,2,4-neopentyl glycol-1,3 mono isobutyrate; Described emulsifying agent is polyoxyethylene sorbitan fatty acid ester emulsifying agent.
8. reflective heat-insulation paint for building according to claim 1, it is characterized in that: described emulsion is selected from one or more in pure-acrylic emulsion, organosilicon crylic acid latex and the fluorine carbon emulsion.
9. reflective heat-insulation paint for building according to claim 1, it is characterized in that: described pH value conditioning agent is selected from 2-amino-2-methyl-1-propanol, ammoniacal liquor or sodium hydroxide solution.
10. reflective heat-insulation paint for building according to claim 1, it is characterized in that: described dispersion agent is water-based polycarboxylic acid salt dispersion agent; Described wetting agent is alkylphenol polyoxyethylene class wetting agent; The effective constituent of described multifunctional assistant is 2-amino-2-methyl-1-propanol.