CN102993922A - Anti-sinking poly ethylene (PE) super-clear base coat - Google Patents
Anti-sinking poly ethylene (PE) super-clear base coat Download PDFInfo
- Publication number
- CN102993922A CN102993922A CN2012104884021A CN201210488402A CN102993922A CN 102993922 A CN102993922 A CN 102993922A CN 2012104884021 A CN2012104884021 A CN 2012104884021A CN 201210488402 A CN201210488402 A CN 201210488402A CN 102993922 A CN102993922 A CN 102993922A
- Authority
- CN
- China
- Prior art keywords
- group
- component
- butyl acetate
- sinking
- super
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an anti-sinking poly ethylene (PE) super-clear base coat. The anti-sinking PE super-clear base coat comprises a component A and a component B, wherein the component A is prepared from unsaturated polyester resin, a dispersing agent, a flatting agent, an antifoaming agent, hydroquinone, superfine silicon dioxide, pigment, nitrocotton, unsaturated quick-drying polyester resin and the like as well as an environment-friendly solvent; the component B is prepared from solvents such as n-butyl acetate, absolute ethyl alcohol and dimethyl carbonate. The anti-sinking PE super-clear base coat, which is good in anti-sinking property, high in transparency and easy to polish, is prepared by completely and uniformly stirring the component A and the component B with colorless and transparent cobalt water in a certain ratio, adding methyl ethyl ketone peroxide in a certain proportion to be stirred completely and uniformly. Detection and trial prove that all the performance indexes meet national standards and enterprise standards which are recorded nationally (standard number: Q/BDSH003-2008 and record number: QB/442000 87 259-2008); the base coat has good levelling, quick defoaming, low odor and quick drying velocity during the construction; and a coating layer has the characteristics, which are beyond the similar PED super clear bases, of good anti-sinking performance, high greening resistance, excellent transparency, thick coating capability and the like, and is easy to grind. The anti-sinking PE super-clear base coat disclosed by the invention is widely popular with costumers.
Description
Technical field
The present invention relates to a kind of lacquer, the special clear priming paint of especially a kind of anti-sag PE.
Background technology
Present prior art, the special clear priming paint of anti-sag PE is a kind of environment-friendly type coating of high comprehensive performance, has good, the characteristics such as transparency is high, easy polishing of anti-sag resistance, is widely used in the primer painting of high-grade suite solid wood furniture and high-grade office furniture.After the construction of commercial like product, drawbacks common shows as does the defectives such as speed is slow, anti-sag resistance is poor, sticking power is general, transparency is low, grinability is general, and this is a difficult problem that always perplexs coating industry.
Summary of the invention
The objective of the invention is: the special clear priming paint of a kind of anti-sag PE is provided, it have formed on the surface of office furniture or solid wood furniture that one deck does that speed is fast, anti-sag resistance is fabulous, transparency is high, the coating of easy polishing, environmental protection, and when being used with finish paint, transparency is high, fullness ratio is good, can prevent the sagging property because of generation of long duration.
The present invention is achieved in that the special clear priming paint of a kind of anti-sag PE, and first component, component B, Lan Shui, plain boiled water weight part ratio are 100:30:1.2～1.5:1.5～1.8 when paint;
The weight percent of first component prescription is:
The A group
Unsaturated polyester resin 40%～45%, dispersion agent 0.1%～0.2%,
Defoamer 0.1%～0.2%, flow agent 0.1%～0.3%,
Resorcinol 0.1%～0.3%, n-butyl acetate 1%～1.5%,
Dehydrated alcohol 2%～3%;
The B group
Superfine silicon dioxide 0.2%～0.4%;
The C combination
Zinic stearas 2%～4%, 400 order talcum powder 5%～7%,
Transparent powder 13%～15%;
The D group
N-butyl acetate 1%～1.5%;
The E group
Nitro-cotton liquid 4%～6%, unsaturated quick-drying vibrin 20%～25%,
N-butyl acetate 0.4%～0.6%;
The weight percent sum of each raw material is 100% in the first component.
The weight percent of component B prescription is as follows:
N-butyl acetate 40%～60%, dehydrated alcohol 10%～20%, methylcarbonate 30%～40%;
The preparation weight percent of nitro-cotton liquid is as follows:
N-butyl acetate 45%～55%, 1/4 nitro-cotton 45%～55%.
The preparation method of the special clear priming paint of a kind of anti-sag PE, comply with following step:
(1) selects clean standard compliant dispersion cylinder, drop into successively unsaturated polyester resin, dispersion agent, defoamer, flow agent, Resorcinol, n-butyl acetate, dehydrated alcohol in the A group, start dispersion machine, disperse; To disperse 5 minutes under the 600-800r/min rotating speed;
(2) under the 600-800r/min rotating speed, drop into superfine silicon dioxide in the B group, to being thoroughly dispersed in the lacquer, then with Zinic stearas in the C group, 400 order talcum powder, transparent powder after be thoroughly dispersed in the lacquer, to being thoroughly dispersed in the lacquer;
(3) with n-butyl acetate side washing in the D group, the powder on cylinder limit and the dispersion impeller is washed in the cylinder, disperse 10-15min to fineness≤50UM with 1000-1500r/min, guarantee not bound edge of powder, not conglomeration;
(4) nitro-cotton liquid, unsaturated quick-drying vibrin, the n-butyl acetate in the input E group under the 600-800r/min rotating speed disperses 5-8min, and viscosity controller is at 5000 ± 500CPS/30 ℃.
Embodiment
The invention will be further described below in conjunction with embodiment.
Embodiment 1
The special clear priming paint of a kind of anti-sag PE, first component, component B, Lan Shui, plain boiled water weight part ratio are 100:30:1.2～1.5:1.5～1.8 when paint;
The weight percent of first component prescription is:
The A group
Unsaturated polyester resin 45%, dispersion agent 0.1%,
Defoamer 0.1%, flow agent 0.1%,
Resorcinol 0.1%%, n-butyl acetate 1%,
Dehydrated alcohol 3%;
The B group
Superfine silicon dioxide 0.2%;
The C group
Zinic stearas 2%, 400 order talcum powder 5%,
Transparent powder 13%;
The D group
N-butyl acetate 1%;
The E group
Nitro-cotton liquid 4%, unsaturated quick-drying vibrin 25%,
N-butyl acetate 0.4%;
The weight percent of component B prescription is as follows:
N-butyl acetate 40%, dehydrated alcohol 20%, methylcarbonate 40%;
The preparation method of component B: add successively n-butyl acetate, dehydrated alcohol, methylcarbonate and stir 5-8min to full and uniform at 600-800r/min.
The preparation weight percent of nitro-cotton liquid is as follows:
N-butyl acetate 45%～55%, 1/4 nitro-cotton 45%～55%.
The preparation method of nitro-cotton liquid is: at first add n-butyl acetate, it is lower to slowly run at 600-800r/min, slowly throws in 1/4 nitro-cotton, then disperses 15-20min to dissolve fully to material with 800-1000r/min.
Bright Chemical Manufacture is opened in plain boiled water methylethyl ketone peroxide Shenyang;
Bright Chemical Manufacture is opened in the different Rinmann's green of Lan Shui Shenyang;
Unsaturated quick-drying vibrin 2307S Changxing chemistry;
Dispersion agent FEKA4010 EFKA;
Defoamer AC-300 Taiwan three is changed;
Flow agent FEKA3777 EFKA.
The preparation method of the special clear priming paint of a kind of anti-sag PE, comply with following step:
(1) selects clean standard compliant dispersion cylinder, drop into successively unsaturated polyester resin, dispersion agent, defoamer, flow agent, Resorcinol, n-butyl acetate, dehydrated alcohol in the A group, start dispersion machine, disperse; To disperse 5 minutes under the 600-800r/min rotating speed;
(2) under the 600-800r/min rotating speed, drop into superfine silicon dioxide in the B group, to being thoroughly dispersed in the lacquer, then with Zinic stearas in the C group, 400 order talcum powder, transparent powder after be thoroughly dispersed in the lacquer, to being thoroughly dispersed in the lacquer;
(3) with n-butyl acetate side washing in the D group, the powder on cylinder limit and the dispersion impeller is washed in the cylinder, disperse 10-15min to fineness≤50UM with 1000-1500r/min, guarantee not bound edge of powder, not conglomeration;
(4) nitro-cotton liquid, unsaturated quick-drying vibrin, the n-butyl acetate in the input E group under the 600-800r/min rotating speed disperses 5-8min, and viscosity controller is at 5000 ± 500CPS/30 ℃.
Embodiment 2
The weight percent of first component prescription is:
The A group
Unsaturated polyester resin 40%, dispersion agent 0.2%,
Defoamer 0.2%, flow agent 0.3%,
Resorcinol 0.3%, n-butyl acetate 1.5%,
Dehydrated alcohol 3%;
The B group
Superfine silicon dioxide 0.4%;
The C group
Zinic stearas 4%, 400 order talcum powder 7%, transparent powder 15%;
The D group
N-butyl acetate 1.5%;
The E group
Nitro-cotton liquid 6%, unsaturated quick-drying vibrin 20%, n-butyl acetate 0.6%;
The weight percent of component B prescription is as follows:
N-butyl acetate 60%, dehydrated alcohol 10%, methylcarbonate 30%;
Embodiment 3
The weight percent of first component prescription is:
The A group
Unsaturated polyester resin 42.4%, dispersion agent 0.2%,
Defoamer 0.2%, flow agent 0.2%,
Resorcinol 0.2%, n-butyl acetate 1.5%,
Dehydrated alcohol 2%;
The B group
Superfine silicon dioxide 0.3%;
The C group
Zinic stearas 3%, 400 order talcum powder 6%, transparent powder 14%;
The D group
N-butyl acetate 1.5%;
The E group
Nitro-cotton liquid 5%, unsaturated quick-drying vibrin 23%, n-butyl acetate 0.5%;
The weight percent sum of each raw material is 100% in the first component.
The weight percent of component B prescription is as follows:
N-butyl acetate 50%, dehydrated alcohol 15%, methylcarbonate 35%;
The present invention and commercially available prod be compared as follows table:
| Sequence number | Interventions Requested | The present invention | Commercially available prod 1 | Commercially available prod 2 |
| 1 | Surface drying (min) | 15 | 17 | 19 |
| 2 | Do solid work (min) | 12 | 20 | 24 |
| 3 | Transparency | Good | Generally | Generally |
| 4 | Fillibility | Good | Very | Generally |
| 5 | Anti-sag resistance | Without sinking | Sink | Excessive settlement |
| 6 | Sticking power | 1 grade | 2 grades | 2 grades |
| 7 | Grinability | Good | Very | Very |
| 8 | Stability in storage | 180 days | 90 days | 80 days |
The object of the invention is to control from the starting material of system lacquer usefulness, by selecting the starting material of excellent properties, formed on the surface of office furniture or solid wood furniture that one deck does that speed is fast, anti-sag resistance is fabulous, transparency is high, the coating of easy polishing, environmental protection, and when being used with finish paint, transparency is high, fullness ratio is good, can prevent the sagging property because of generation of long duration.Exotic materials on paint film property impact as: unsaturated polyester resin and unsaturated quick-drying vibrin possess anti-sag resistance, have improved greatly the anti-sag PE anti-sag resistance at the special clear end, easy grinability etc.; The starting material merchant that talcum powder and transparent powder have selected domestic state-of-the-art technology to produce, Effective Raise the transparency etc. of PE lacquer; Consider from the mechanics angle, select nitro-cotton as material, fully use mechanics principle and material principle of polarity, make the present invention possess the special mechanics effect that other similar paint can not be compared; Produce component B and take into full account environment friendly, take full advantage of the principle of polarity of material, adopt without benzene and hang down the contaminative solvent as material, the company standard that the every detection index of the product of producing is all put on record well below country; Select colourless blue water, avoided blue water on the impact of paint film greening, improved greatly the sharpness of paint film.
The special clear priming paint property indices of anti-sag PE of the present invention is as follows:
| Project | Index | The result |
| Paint film appearance | Smooth, smooth | Smooth, smooth |
The anti-sag senior thinner property indices of PE of the present invention is as follows:
| Test item | Index | The result |
| Color, (Fe-Co) number | ≤1 | 1 |
| Outward appearance and transparency | As clear as crystal, no suspended substance | As clear as crystal, no suspended substance |
| Moisture content | Not muddy | Not muddy |
The special clear priming paint of anti-sag PE of the present invention after testing and probationary certificate, this product property indices all meets national standard; During construction, levelling is good, and froth breaking is fast, and smell is low; Coating has that fullness ratio is good, anti-sag resistance is good, transparency is excellent, easy polishing, sprays the characteristics that other PE products such as effect of being equivalent to commercially available prod spraying 2 times for 1 time can not be compared.
Above-described only is preferential embodiment of the present invention.Should be pointed out that for the person of ordinary skill of the art in the situation that does not break away from the principle of the invention, can also make some improvement and modification, this also is considered as protection scope of the present invention.
Claims (2)
1. special clear priming paint of anti-sag PE, it is characterized in that: first component, component B, Lan Shui, plain boiled water weight part ratio are 100:30:1.2～1.5:1.5～1.8 during paint;
The weight percent of first component prescription is:
The A group
Unsaturated polyester resin 40%～45%, dispersion agent 0.1%～0.2%,
Defoamer 0.1%～0.2%, flow agent 0.1%～0.3%,
Resorcinol 0.1%～0.3%, n-butyl acetate 1%～1.5%,
Dehydrated alcohol 2%～3%;
The B group
Superfine silicon dioxide 0.2%～0.4%;
The C combination
Zinic stearas 2%～4%, 400 order talcum powder 5%～7%,
Transparent powder 13%～15%;
The D group
N-butyl acetate 1%～1.5%;
The E group
Nitro-cotton liquid 4%～6%, unsaturated quick-drying vibrin 20%～25%,
N-butyl acetate 0.4%～0.6%;
The weight percent of component B prescription is as follows:
N-butyl acetate 40%～60%, dehydrated alcohol 10%～20%, methylcarbonate 30%～40%;
The preparation weight percent of nitro-cotton liquid is as follows:
N-butyl acetate 45%～55%, 1/4 nitro-cotton 45%～55%.
2. the preparation method of the special clear priming paint of a kind of anti-sag PE as claimed in claim 1 is characterized in that according to following step:
(1) selects clean standard compliant dispersion cylinder, drop into successively unsaturated polyester resin, dispersion agent, defoamer, flow agent, Resorcinol, n-butyl acetate, dehydrated alcohol in the A group, start dispersion machine, disperse; To disperse 5 minutes under the 600-800r/min rotating speed;
(2) under the 600-800r/min rotating speed, drop into superfine silicon dioxide in the B group, to being thoroughly dispersed in the lacquer, then with Zinic stearas in the C group, 400 order talcum powder, transparent powder after be thoroughly dispersed in the lacquer, to being thoroughly dispersed in the lacquer;
(3) with n-butyl acetate side washing in the D group, the powder on cylinder limit and the dispersion impeller is washed in the cylinder, disperse 10-15min to fineness≤50UM with 1000-1500r/min, guarantee not bound edge of powder, not conglomeration;
(4) nitro-cotton liquid, unsaturated quick-drying vibrin, the n-butyl acetate in the input E group under the 600-800r/min rotating speed disperses 5-8min, and viscosity controller is at 5000 ± 500CPS/30 ℃.