CN102989802A - Production technology for high-strength mesh-producing hardware wires - Google Patents
Production technology for high-strength mesh-producing hardware wires Download PDFInfo
- Publication number
- CN102989802A CN102989802A CN201210582261XA CN201210582261A CN102989802A CN 102989802 A CN102989802 A CN 102989802A CN 201210582261X A CN201210582261X A CN 201210582261XA CN 201210582261 A CN201210582261 A CN 201210582261A CN 102989802 A CN102989802 A CN 102989802A
- Authority
- CN
- China
- Prior art keywords
- steel wire
- wirerods
- high strength
- tricky
- strength according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the manufacturing process of wires, particularly to a production technology for high-strength mesh-producing hardware wires. The method includes die arrangement: selecting and subjecting a steel wire with a diameter of 6.5 to 11 passes of drawing which include phi5.90, phi5.10, phi4.40, phi3.80, phi3.30, phi2.85, phi2.50, phi2.20, phi1.95, phi1.75 and phi1.55, wherein cooling water is used for cooling during each pass of drawing; and stretching the steel wire: extracting the steel wire by 2-3m with a chain, then stopping a machine and taking down a thimble, checking the diameter of the steel wire, and then fixing the steel wire on a reel, bypassing the steel wire and fixing on a spool after the steel wire is accumulated by a certain amount on the reel, and then performing a next stretching. The wire prepared through the technology is high in surface finish, suitable for follow-up surface plating procedures and high in strength and hardness simultaneously so as to guarantee product safety.
Description
Technical field
The present invention relates to a kind of manufacturing process of wire rod, be specifically related to a kind of high strength net processed five metals production of wirerods.
Background technology
Woven wire is the traditional industrial goods of China, has widely purposes in many fields such as scientific research, production and lives.The wire rod that woven wire is used obtains by drawing process, drawing process is a kind of typical method for metal working, be under the drawing effect, reduce the sectional area of metal rapidoprint by the die hole core, to obtain high accuracy, the wire rod of best bright finish or a kind of plastic working technique of tubing.
And the wire surface fineness that prior art obtains is low, is not suitable for the electroplating technology on follow-up surface, and intensity and hardness are low, can't guarantee the security of product, is not suitable for net processed.
Summary of the invention
The objective of the invention is to overcome the deficiency that prior art exists, provide that a kind of energy consumption is low, the uniform high strength of wire rod performance net processed five metals production of wirerods.
Purpose of the present invention is achieved through the following technical solutions:
A kind of high strength net processed five metals production of wirerods, it comprises following technique:
Row's mold technique:
Choose diameter and be 6.5 steel wire through Φ 5.90, Φ 5.10, Φ 4.40, Φ 3.80, Φ 3.30, Φ 2.85, Φ 2.50, Φ 2.20, Φ 19.5, Φ 1.75, Φ 1.55 totally 11 passes of drawing, wherein cool off with cooling water during every time drawing;
The tricky head technique of steel wire:
With chain steel wire is extracted to stop after the 2-3 rice and take off thimble, check gauge of wire, again being fixed on the steel wire on the reel; Then steel wire is walked around steel wire and is fixed on the I-beam wheel after the certain amount of reel accumulation, then descend tricky head one.
Wherein, the material of described steel wire is Q195.
Wherein, it is that 1# wire drawing powder is lubricated that calcium is adopted in described front 9 procedure drawings, guarantees that its lubricity is good, and wire surface is difficult for garland, breaks, and rear 2 procedure drawings are adopted and taken out the line oil lubrication, guarantee that wire surface is highly polished, are silver bright color.
Wherein, describedly take out line oil the ratio take weight ratio as 10:1 is mixed to get by White Mineral Oil and soap silk.
Wherein, described drawing speed 10 meter per seconds.
Wherein, front 9 roads carry out the tricky head of pointing with the mode of pointing, and last 2 passages are carried out tricky head after using the moulding of abrasive machine sand milling.
Wherein, need steel wire fully to cool off during described steel wire drawing.
Wherein, guarantee that the trend of steel wire is consistent during tricky of described steel wire.
The present invention compared with prior art has following advantage and beneficial effect: the wire surface that the present invention makes is highly polished, is suitable for the electroplating technology on follow-up surface, has simultaneously higher intensity, hardness, can guarantee the security performance of product, is applicable to net processed.
The specific embodiment:
For the ease of those skilled in the art's understanding, the present invention is described in further detail below in conjunction with embodiment, but protection scope of the present invention is not limited to following embodiment.
A kind of high strength net processed five metals production of wirerods, it comprises following technique:
Row's mold technique:
Choosing material is Q195, diameter is 6.5 steel wire process Φ 5.90, Φ 5.10, Φ 4.40, Φ 3.80, Φ 3.30, Φ 2.85, Φ 2.50, Φ 2.20, Φ 19.5, Φ 1.75, Φ 1.55 is totally 11 passes of drawing, wherein, cool off with cooling water after every time drawing, it is that 1# wire drawing powder is lubricated that calcium is adopted in front 9 procedure drawings, guarantee that its lubricity is good, wire surface is difficult for garland, break, rear 2 procedure drawings are adopted and are taken out the line oil lubrication, the assurance wire surface is highly polished, be silver bright color, the ratio take weight ratio as 10:1 is mixed to get by White Mineral Oil and soap silk to take out line oil, and the speed of every time drawing is 10 meter per seconds.
The tricky head technique of steel wire:
With chain steel wire is extracted to stop after the 2-3 rice and take off thimble, check gauge of wire, again being fixed on the steel wire on the reel; Then steel wire is walked around steel wire and is fixed on the I-beam wheel after the certain amount of reel accumulation, then descend tricky head one.
Front 9 roads carry out the tricky head of pointing with the mode of pointing, and last 2 passages are carried out tricky head after using the moulding of abrasive machine sand milling.Need steel wire fully to cool off during steel wire drawing.The trend that guarantees steel wire during tricky of steel wire is consistent.
The wire surface that present embodiment makes is highly polished, is suitable for the electroplating technology on follow-up surface, has simultaneously higher intensity, and tensile strength can reach 1000-1200MPa, can guarantee the security performance of product, satisfies the requirement of system net fully.
Above-described embodiment is the better embodiment of the present invention, but embodiments of the present invention are not restricted to the described embodiments, and the equivalent variations of therefore doing according to the present patent application claim is included within protection scope of the present invention.
Claims (8)
1. high strength net processed five metals production of wirerods, it is characterized in that: it comprises identity technique and the tricky head technique of steel wire:
Identity technique:
Choose diameter and be 6.5 steel wire through Φ 5.90, Φ 5.10, Φ 4.40, Φ 3.80, Φ 3.30, Φ 2.85, Φ 2.50, Φ 2.20, Φ 19.5, Φ 1.75, Φ 1.55 totally 11 passes of drawing, wherein cool off with cooling water during every time drawing;
The tricky head technique of steel wire:
With chain steel wire is extracted to stop after the 2-3 rice and take off thimble, check gauge of wire, again being fixed on the steel wire on the reel; Then steel wire is walked around steel wire and is fixed on the I-beam wheel after the certain amount of reel accumulation, then descend tricky head one.
2. a kind of high strength according to claim 1 net processed five metals production of wirerods, it is characterized in that: the material of described steel wire is Q195.
3. a kind of high strength according to claim 1 net processed five metals production of wirerods is characterized in that: it is that 1# wire drawing powder is lubricated that calcium is adopted in described front 9 procedure drawings, and rear 2 procedure drawings are adopted and taken out the line oil lubrication.
4. a kind of high strength according to claim 3 net processed five metals production of wirerods is characterized in that: describedly take out line oil the ratio take weight ratio as 10:1 is mixed to get by White Mineral Oil and soap silk.
5. a kind of high strength according to claim 1 net processed five metals production of wirerods is characterized in that: described drawing speed 10 meter per seconds.
6. a kind of high strength according to claim 1 net processed five metals production of wirerods, it is characterized in that: front 9 roads carry out the tricky head of pointing with the mode of pointing, and last 2 passages are carried out tricky head after using the moulding of abrasive machine sand milling.
7. a kind of high strength according to claim 1 net processed five metals production of wirerods is characterized in that: need steel wire fully to cool off during described steel wire drawing.
8. a kind of high strength according to claim 1 net processed five metals production of wirerods is characterized in that: guarantee that the trend of steel wire is consistent during tricky of described steel wire.