CN109355957A - Stainless steel producing technique of steel cable - Google Patents
Stainless steel producing technique of steel cable Download PDFInfo
- Publication number
- CN109355957A CN109355957A CN201811226636.2A CN201811226636A CN109355957A CN 109355957 A CN109355957 A CN 109355957A CN 201811226636 A CN201811226636 A CN 201811226636A CN 109355957 A CN109355957 A CN 109355957A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- wire rod
- finished product
- producing technique
- rope
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of production technologies, and the present invention relates to wirerope fields, and in particular to a kind of stainless steel producing technique of steel cable, the stainless steel producing technique of steel cable, comprising the following steps: step 1: pretreatment；Step 2: drawing；Step 3: heat treatment；Step 4: stock is twisted into rope；Step 5: quality inspection；The present invention has rational design, provides a kind of stainless steel producing technique of steel cable, and the stainless steel producing technique of steel cable is processed by raw material of stainless steel, and process is succinct, and low energy consumption, and wire broken rate is low, high production efficiency, function admirable after synthesis.
Description
Technical field
The present invention relates to wirerope fields, more particularly, to stainless steel producing technique of steel cable.
Background technique
Traditional wirerope is usually that raw material production and processing is made with high-carbon steel, the higher fracture of wire of intensity hardness of high-carbon steel
Rate is not easy control, and simultaneously, once compression ratio is higher in process for high-carbon steel, the toughness of material itself can decline, shadow
Ring subsequent use effect.
Summary of the invention
The present invention be solve the problems, such as it is set forth above to providing a kind of galvanized steel wire rope processing technology, the plating thus
The step of zinc wirerope processing technology includes:
Step 1；Pretreatment: stainless steel wire rod is placed on pay off rack, is carried out cleaning treatment with machinery, is entered after the completion of cleaning
It applies boron equipment to carry out applying boron processing, finally enters drying equipment drying, obtain pretreatment wire rod；
Step 2；Drawing: pretreatment wire rod is placed in drawbench and carries out multiple drawing, take-up obtains semi-finished product line after the completion of drawing
Material；
Step 3；Heat treatment: the semi-finished product wire rod after drawing process is put into heat-treatment furnace and is heated, after the completion of heating
It cleaned, cooled down；
Step 4；Stock is twisted into rope: half product wire rod after will be zinc-plated, which is put on stubborn stock machine, twist stock conjunction rope, obtains finished product wirerope；
Step 5；Quality inspection: after processing is completed testing to the quality of wirerope finished product, examines qualified vanning, examines
It is unqualified to re-start processing.
Preferably, the temperature of heat-treatment furnace described in the step 3 is within the scope of 700-800 DEG C.
The beneficial effects of the present invention are: the present invention has rational design, a kind of stainless steel producing technique of steel cable, institute are provided
Stainless steel producing technique of steel cable is stated, is processed by raw material of stainless steel, process is succinct, and low energy consumption, and wire broken rate is low, raw
Produce high-efficient, function admirable after synthesis.
Specific embodiment
All features disclosed in this specification or disclosed all methods or in the process the step of, in addition to mutually exclusive
Feature and/or step other than, can combine in any way.
Any feature of this specification, unless specifically stated, can be equivalent by other or substitution with similar purpose it is special
Sign is replaced.That is, unless specifically stated, each feature is an example in a series of equivalent or similar characteristics.
Step 1；Pretreatment: stainless steel wire rod is placed on pay off rack, cleaning treatment is carried out with machinery, after the completion of cleaning
It carries out applying boron processing into boron equipment is applied, finally enters drying equipment drying, obtain pretreatment wire rod；
Step 2；Drawing: pretreatment wire rod is placed in drawbench and carries out multiple drawing, take-up obtains semi-finished product line after the completion of drawing
Material；
Step 3；Heat treatment: the semi-finished product wire rod after drawing process is put into heat-treatment furnace and is heated, after the completion of heating
It cleaned, cooled down；
Step 4；Stock is twisted into rope: half product wire rod after will be zinc-plated, which is put on stubborn stock machine, twist stock conjunction rope, obtains finished product wirerope；
Step 5；Quality inspection: after processing is completed testing to the quality of wirerope finished product, examines qualified vanning, examines
It is unqualified to re-start processing.
The beneficial effects of the present invention are: the present invention has rational design, a kind of stainless steel producing technique of steel cable, institute are provided
Stainless steel producing technique of steel cable is stated, is processed by raw material of stainless steel, process is succinct, and low energy consumption, and wire broken rate is low, raw
Produce high-efficient, function admirable after synthesis.
The invention is not limited to specific embodiments above-mentioned.The present invention, which expands to, any in the present specification to be disclosed
New feature or any new combination, and disclose any new method or process the step of or any new combination.
Claims (2)
1. a kind of stainless steel producing technique of steel cable, which is characterized in that the galvanized steel wire rope processing technology makees stainless steel
Processed for raw material, it the following steps are included:
Step 1；Pretreatment: stainless steel wire rod is placed on pay off rack, is carried out cleaning treatment with machinery, is entered after the completion of cleaning
It applies boron equipment to carry out applying boron processing, finally enters drying equipment drying, obtain pretreatment wire rod；
Step 2；Drawing: pretreatment wire rod is placed in drawbench and carries out multiple drawing, take-up obtains semi-finished product line after the completion of drawing
Material；
Step 3；Heat treatment: the semi-finished product wire rod after drawing process is put into heat-treatment furnace and is heated, after the completion of heating
It cleaned, cooled down；
Step 4；Stock is twisted into rope: half product wire rod after will be zinc-plated, which is put on stubborn stock machine, twist stock conjunction rope, obtains finished product wirerope；
Step 5；Quality inspection: after processing is completed testing to the quality of wirerope finished product, examines qualified vanning, examines
It is unqualified to re-start processing.
2. galvanized steel wire rope processing technology according to claim 1, which is characterized in that heat-treatment furnace described in the step 3
Temperature within the scope of 700-800 DEG C.