CN102978899A - 一种油蜡布用防水剂 - Google Patents
一种油蜡布用防水剂 Download PDFInfo
- Publication number
- CN102978899A CN102978899A CN2012105053985A CN201210505398A CN102978899A CN 102978899 A CN102978899 A CN 102978899A CN 2012105053985 A CN2012105053985 A CN 2012105053985A CN 201210505398 A CN201210505398 A CN 201210505398A CN 102978899 A CN102978899 A CN 102978899A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- proofing agent
- cerecloth
- oily
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种油蜡布用防水剂,由以下重量份的各成分组成:氢氧化钠0.3~1份;石蜡13~18份;聚乙烯醇22~25份;磷酸三甲苯酯3~9份;聚乙烯乙酸酯2~7份;松香5~10份;丙烯酸树脂3~6份;石粉35~45份。上述油蜡布用防水剂,由于有氢氧化钠的存在,可减少气味污染,同时,用本发明的油蜡布用防水剂制作的油蜡布,使用范围广,寒冷气候不脆硬,高温天气不软化,其手感始终保持稳定状态,因此产品具有良好的经济效益和社会效益。
Description
技术领域
本发明涉及纺织品领域,特别是涉及一种油蜡布用防水剂。
背景技术
目前随着油蜡布行业的迅速发展,市场对于油蜡布的质量要求越来越高,由于油蜡布的使用一般用于户外居多,因此对油蜡布的防水性能有着更为严格的要求,从而对于用于生产防水油蜡布的防水剂也有特殊的要求。但是目前用于油蜡布的防水剂防水效果不理想,且生产及使用过程中气味较重从而对环境造成污染。同时存在防水剂所生产的油蜡布使用范围窄,寒冷气候易脆硬,高温天气易软化,其手感不稳定,因此产品的经济效益和社会效益不理想。
发明内容
基于此,有必要针对现有技术中的不足,提供一种气味轻、环保的油蜡布用防水剂。
一种油蜡布用防水剂,由以下重量份的各成分组成:
氢氧化钠 0.3~1份;
石蜡 13~18份;
聚乙烯醇 22~25份;
磷酸三甲苯酯 3~9份;
聚乙烯乙酸酯 2~7份;
松香 5~10份;
丙烯酸树脂 3~6份;
石粉 35~45份。
在本发明优选的实施例中,一种油蜡布用防水剂,由以下重量份的各成分组成:
氢氧化钠 0.3份;
石蜡 13份;
聚乙烯醇 22份;
磷酸三甲苯酯 9份;
聚乙烯乙酸酯 7份;
松香 10份;
丙烯酸树脂 3份;
石粉 35份。
在本发明优选的实施例中,一种油蜡布用防水剂,由以下重量份的各成分组成:
氢氧化钠 1份;
石蜡 18份;
聚乙烯醇 25份;
磷酸三甲苯酯 3份;
聚乙烯乙酸酯 7份;
松香 5份;
丙烯酸树脂 3份;
石粉 45份。
上述油蜡布用防水剂,由于有氢氧化钠的存在,可减少气味污染,同时,用本发明的油蜡布用防水剂制作的油蜡布,使用范围广,寒冷气候不脆硬,高温天气不软化,其手感始终保持稳定状态,因此产品具有良好的经济效益和社会效益。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施方式,进一步阐述本发明。
实施例1
一种油蜡布用防水剂,由以下重量份的各成分组成:
氢氧化钠 0.6份;
石蜡 15份;
聚乙烯醇 25份;
磷酸三甲苯酯 7份;
聚乙烯乙酸酯 5份;
松香 8份;
丙烯酸树脂 5份;
石粉 42份。
本实施例的油蜡布用防水剂,具有价格低、环保、无毒、无害、无强烈刺激气味等优点,同时,使得制备得到的油蜡布的拉伸强度有所提高,扩大了使用范围。
实施例2
一种油蜡布用防水剂,由以下重量份的各成分组成:
氢氧化钠 0.3份;
石蜡 13份;
聚乙烯醇 22份;
磷酸三甲苯酯 9份;
聚乙烯乙酸酯 7份;
松香 10份;
丙烯酸树脂 3份;
石粉 35份。
实施例3
一种油蜡布用防水剂,由以下重量份的各成分组成:
氢氧化钠 1份;
石蜡 18份;
聚乙烯醇 25份;
磷酸三甲苯酯 3份;
聚乙烯乙酸酯 7份;
松香 5份;
丙烯酸树脂 3份;
石粉 45份。
上述油蜡布用防水剂,由于有氢氧化钠的存在,可减少气味污染,同时,用本发明的油蜡布用防水剂制作的油蜡布,使用范围广,寒冷气候不脆硬,高温天气不软化,其手感始终保持稳定状态,因此产品具有良好的经济效益和社会效益。
以上所述实施例仅表达了本发明的几种实施方式,其描述较为具体和详细,但并不能因此而理解为对本发明专利范围的限制。应当指出的是,对于本领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干变形和改进,这些都属于本发明的保护范围。因此,本发明专利的保护范围应以所附权利要求为准。
Claims (3)
1.一种油蜡布用防水剂,其特征在于,由以下重量份的各成分组成:
氢氧化钠 0.3~1份;
石蜡 13~18份;
聚乙烯醇 22~25份;
磷酸三甲苯酯 3~9份;
聚乙烯乙酸酯 2~7份;
松香 5~10份;
丙烯酸树脂 3~6份;
石粉 35~45份。
2.根据权利要求1所述的油蜡布用防水剂,其特征在于,由以下重量份的各成分组成:
氢氧化钠 0.3份;
石蜡 13份;
聚乙烯醇 22份;
磷酸三甲苯酯 9份;
聚乙烯乙酸酯 7份;
松香 10份;
丙烯酸树脂 3份;
石粉 35份。
3.根据权利要求1所述的油蜡布用防水剂,其特征在于,由以下重量份的各成分组成:
氢氧化钠 1份;
石蜡 18份;
聚乙烯醇 25份;
磷酸三甲苯酯 3份;
聚乙烯乙酸酯 7份;
松香 5份;
丙烯酸树脂 3份;
石粉 45份。