CN102977683A - UV photoluminescence ink - Google Patents

UV photoluminescence ink Download PDF

Info

Publication number
CN102977683A
CN102977683A CN 201210332490 CN201210332490A CN102977683A CN 102977683 A CN102977683 A CN 102977683A CN 201210332490 CN201210332490 CN 201210332490 CN 201210332490 A CN201210332490 A CN 201210332490A CN 102977683 A CN102977683 A CN 102977683A
Authority
CN
China
Prior art keywords
photoluminescence
forgery ink
prepolymer
ink according
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201210332490
Other languages
Chinese (zh)
Inventor
颜爱国
刘浩梅
薛继武
石亮
张馨宇
武凡靖
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN CHANGDE JINPENG PRINTING CO Ltd
Hunan University of Technology
Original Assignee
HUNAN CHANGDE JINPENG PRINTING CO Ltd
Hunan University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN CHANGDE JINPENG PRINTING CO Ltd, Hunan University of Technology filed Critical HUNAN CHANGDE JINPENG PRINTING CO Ltd
Priority to CN 201210332490 priority Critical patent/CN102977683A/en
Publication of CN102977683A publication Critical patent/CN102977683A/en
Pending legal-status Critical Current

Abstract

The present invention discloses a UV photoluminescence ink, and belongs to the field of printing ink preparation. The UV photoluminescence ink is characterized in that modified ZnS:Cu is adopted as a luminescence material, a mixture of an epoxy acrylic acid resin and a polyester acrylate resin is adopted as a prepolymer, a mixture of trimethylolpropane triacrylate and tripropylene glycol diacrylate is adopted as a diluted monomer, a photoinitiator, an accelerator, an antifoaming agent and the like are matched, and uniform mixing is performed to obtain the finished product. The UV photoluminescence ink can be widely applicable for printing on securities, tax receipts, invoices, credit cards and other valuable bills.

Description

A kind of UV photoluminescence printing ink
Technical field
The present invention relates to a kind of printing UV printing ink, i.e. a kind of UV photoluminescence printing ink for fields such as commodity outer packaging, security, tax reciept, invoice, credits card.
Background technology
The photoluminescence anti-forgery ink has disguised better, in bright gay color, with low cost and anti-counterfeiting technology is implemented the characteristics such as convenient, demonstrates huge application potential in the fields such as valuable bills such as security, tax reciept, invoice, credits card.In recent years, developed multiple light photoluminescence anti-forgery ink both at home and abroad.Such as, Chinese patent CN1544545A discloses a kind of long persistence luminescent painting ink, Chinese patent CN1313364A discloses a kind of luminous ink paint, Chinese patent CN1143659A discloses a kind of universal colorful luminescent ink, Chinese patent CN1465631A discloses a kind of non-emissive property enviroment protective energy storage luminous ink, Chinese patent CN1059544A discloses a kind of permanent shining printing ink, Chinese patent CN1114967A discloses a kind of flash of light that has, the phosphorescent coating of luminescent properties, Chinese patent CN1125746A discloses a kind of luminous paint with ultra-long afterglow, Chinese patent CN1542060A discloses a kind of luminous paint etc.After the printing ink that above-mentioned patent relates to is subject to excited by visible light, all can continue at the dark place luminous, but not anti-solvent is arranged, hardness is low, crocking resistance is poor, contaminate environment, affect the shortcomings such as operator are healthy, its dried forms is high bake, energy consumption is large, and efficient is low.
UV curable ink, i.e. UV printing ink, be a kind of can be dry under UV-irradiation, the printing ink of film forming.Owing to do not use solvent, to the environment zero release, and need not high bake, be a kind of real environmental protection, energy-conservation printing ink.At present, Chinese patent CN1657575A discloses a kind of UV light solidified luminous printing ink, uses the alkaline earth aluminate of activated by rare earth elements, silicate to be luminescent material, successfully prepares a kind of excited by visible light UV light solidified luminous printing ink.But, because rare-earth substance is strategic material, itself also can cause considerable damage to environment the refinement of rare earth, country strictly controls the links of Rare Earth Production in recent years, and very worthy, therefore, have the defectives such as cost height, raw material sources be unstable based on the luminescent ink of the luminescent material of rare earth background preparation.
Summary of the invention
The excited by visible light, the green UV photoluminescence printing ink that the purpose of this invention is to provide a kind of preparation take ZnS:Cu as luminescent material, this printing ink has solved the not anti-solvent of existing printing ink, hardness is low, crocking resistance is poor, contaminate environment, affect the shortcomings such as operator are healthy, and raw materials enjoy stable sources, cheaply is easy to get.
Technical scheme of the present invention realizes that by following approach the implementation step is as follows:
(1) surface modification of luminescent powder
Because the ZnS:Cu luminescent powder is inorganic particle, have hydrophilic surface, and prepolymer is lyophobic dust such as epoxy acrylic resin and polyester acrylate resin etc., mixes in order to make both, must carry out surface modification to luminescent powder.Take by weighing 1 kilogram of ZnS:Cu luminescent powder and add in the high mixer, 80 ℃ of design temperatures mixed two hours; Take by weighing in the 25 gram silicone oil adding high mixers and mixed 10 minutes with luminescent powder, realize the surface modification to luminescent powder
(2) printing ink preparation
Described photoluminescence UV printing ink, the weight percent content of each raw material (wt%) is:
Prepolymer 30.0%-56.0%
Modification luminescent powder 30.0%-50.0%
Promotor 2.0%-5.0%
Diluting monomer 3.0%-6.0%
Light trigger 1.0%-5.0%
Defoamer 0.5%-5.0%.
After prepolymer, light trigger, diluting monomer, promotor weighed up by above-mentioned prescription, putting into successively black had lid to be in harmonious proportion bucket, and then stirring at low speed adds the modification luminescent powder to dissolving, and high-speed stirring is 30 minutes again.Defoamer divides two portions to add, and a part adds in whipping process, and another part adds when stirring is finished soon.Can obtain at last photoluminescence UV printing ink.
The invention has the beneficial effects as follows:
(1) the present invention utilizes high-performance ZnS:Cu luminescent powder to be raw material, raw materials usedly cheaply is easy to get, and is with low cost;
(2) the present invention has carried out surface modification to the ZnS:Cu luminescent powder, is conducive to it and fully is distributed in the prepolymer, has promoted the press quality of printing ink;
(3) the present invention uses epoxy acrylic resin and polyester acrylate resin compound to be prepolymer, can effectively regulate ink product curing speed, hardness and crocking resistance;
(4) the present invention uses Viscoat 295 and tripropylene glycol diacrylate to be diluting monomer, can effectively regulate solvability and the viscosity-reducing performance of printing ink, and snappiness and the water tolerance of solidifying rear product.
Embodiment
The present invention is further illustrated below in conjunction with specific examples:.
Embodiment 1
Epoxy acrylic resin 27.0 wt%
Polyester acrylate resin 27.0 wt%
Diethylamine 4.0 wt%
Viscoat 295 1.5 wt%
Tripropylene glycol diacrylate 1.5 wt%
1-hydroxyl-cyclohexyl-phenyl ketone 3.5 wt%
Modification yellow-green colour luminescent powder 33.0 wt%
Defoamer Foamex N 2.5 wt%.
At first 40.0 parts of weight epoxy acrylic resins and 40.0 parts of weight polyester acrylate resin agitatings are mixed, form prepolymer; 2.5 parts of weight Viscoat 295s and 2.5 parts of weight tripropylene glycol diacrylates are mixed the formation diluting monomer.Then 54.0 parts of weight prepolymers, 4.0 parts of weight diethylamine, 3.0 parts of weight diluting monomers and 3.5 parts of weight 1-hydroxyl-cyclohexyl-phenyl ketones are added in black tone with cover and the bucket stirring at low speed 20 minutes successively; The last modification yellow-green colour luminescent powder that under high-speed stirring, adds 33.0 parts of weight, 2.5 a part weight defoamer adds at twice, to add 1.5 parts of weight after 5 minutes in high-speed stirring for the first time, remain 1.0 parts of weight defoamers and stirring end adding in front 1 minute, after stirring, namely get photoluminescence UV printing ink.This printing ink is through silk screen printing and behind the UV photocuring, and trace after 10 minutes, can continue luminous 8 hours at excited by visible light in the dark.
Embodiment 2
Epoxy acrylic resin 20.0 wt%
Polyester acrylate resin 20.0 wt%
Diethylamine 4.0 wt%
Viscoat 295 1.5 wt%
Tripropylene glycol diacrylate 1.5 wt%
1-hydroxyl-cyclohexyl-phenyl ketone 3.5 wt%
Modification yellow-green colour luminescent powder 44.5 wt%
Defoamer Foamex N 5.0 wt%.
At first 30.0 parts of weight epoxy acrylic resins and 30.0 parts of weight polyester acrylate resin agitatings are mixed, form prepolymer; 2.5 parts of weight Viscoat 295s and 2.5 parts of weight tripropylene glycol diacrylates are mixed the formation diluting monomer.Then 40.0 parts of weight prepolymers, 4.0 parts of weight diethylamine, 3.0 parts of weight diluting monomers and 3.5 parts of weight 1-hydroxyl-cyclohexyl-phenyl ketones are added in black tone with cover and the bucket stirring at low speed 20 minutes successively; The last modification yellow-green colour luminescent powder that under high-speed stirring, adds 44.5 parts of weight, 5.0 a part weight defoamer adds at twice, to add 3.5 parts of weight after 5 minutes in high-speed stirring for the first time, remain 1.5 parts of weight defoamers and stirring end adding in front 1 minute, after stirring, namely get photoluminescence UV printing ink.This printing ink is through silk screen printing and behind the UV photocuring, and trace after 10 minutes, can continue luminous 10 hours at excited by visible light in the dark.
Embodiment 3
Epoxy acrylic resin 17.0 wt%
Polyester acrylate resin 17.0 wt%
Diethylamine 4.5 wt%
Viscoat 295 1.5 wt%
Tripropylene glycol diacrylate 1.5 wt%
1-hydroxyl-cyclohexyl-phenyl ketone 3.5 wt%
Modification yellow-green colour luminescent powder 50.0 wt%
Defoamer Foamex N 5.0 wt%.
At first 20.0 parts of weight epoxy acrylic resins and 20.0 parts of weight polyester acrylate resin agitatings are mixed, form prepolymer; 2.5 parts of weight Viscoat 295s and 2.5 parts of weight tripropylene glycol diacrylates are mixed the formation diluting monomer.Then 34.0 parts of weight prepolymers, 4.5 parts of weight diethylamine, 3.0 parts of weight diluting monomers and 3.5 parts of weight 1-hydroxyl-cyclohexyl-phenyl ketones are added in black tone with cover and the bucket stirring at low speed 20 minutes successively; The last modification yellow-green colour luminescent powder that under high-speed stirring, adds 50.0 parts of weight, 5.0 a part weight defoamer adds at twice, to add 3.5 parts of weight after 5 minutes in high-speed stirring for the first time, remain 1.5 parts of weight defoamers and stirring end adding in front 1 minute, after stirring, namely get photoluminescence UV printing ink.This printing ink is through silk screen printing and behind the UV photocuring, and trace after 10 minutes, can continue luminous 12 hours at excited by visible light in the dark.
The above is described in detail with reference to the preparation method who implements this UV photoluminescence anti-forgery ink, be intended to further specify know-why of the present invention, illustrative rather than determinate, anyly simply copying and applying according to what limited range was carried out, all is to enforcement of the present invention.

Claims (7)

1. UV photoluminescence anti-forgery ink, it is characterized in that: use the ZnS:Cu of modification to be luminescent material, take epoxy acrylic resin and polyester acrylate resin compound as prepolymer, take Viscoat 295 and tripropylene glycol diacrylate mixture as diluting monomer, be equipped with again light trigger, promotor and defoamer etc. and mix and form.
2. a kind of UV photoluminescence anti-forgery ink according to claim 1, it is characterized in that: described luminescent material is yellow-green colour ZnS:Cu luminescent powder.
3. a kind of UV photoluminescence anti-forgery ink according to claim 1 is characterized in that: one or more modifications in described ZnS:Cu luminescent powder use dimethyl silicone oil, methyl-silicone oil, ethyl silicon oil, phenyl silicone oil, the Methyl Hydrogen Polysiloxane Fluid.
4. a kind of UV photoluminescence anti-forgery ink according to claim 1, it is characterized in that: described prepolymer is epoxy acrylic resin and polyester acrylate resin compound, and its ratio is 10:1 ~ 1:10.
5. a kind of UV photoluminescence anti-forgery ink according to claim 1, it is characterized in that: described diluting monomer is Viscoat 295 and tripropylene glycol diacrylate mixture, and its ratio is 10:1 ~ 1:10.
6. a kind of UV photoluminescence anti-forgery ink according to claim 1 is characterized in that: described photoluminescence UV printing ink, and the weight percent content of each raw material (wt%) is:
Prepolymer 30.0%-56.0%
Modification luminescent powder 30.0%-50.0%
Promotor 2.0%-5.0%
Diluting monomer 3.0%-6.0%
Light trigger 1.0%-5.0%
Defoamer 0.5%-5.0%.
7. a kind of UV photoluminescence anti-forgery ink according to claim 1, it is characterized in that, the preparation method of described UV photoluminescence anti-forgery ink is, after prepolymer, light trigger, diluting monomer, promotor weighed up by above-mentioned prescription, put into successively black lid mediation bucket is arranged, then stirring at low speed adds the modification luminescent powder to dissolving, and high-speed stirring is 30 minutes again; Defoamer divides two portions to add, and a part adds in whipping process, and another part adds when stirring is finished soon; Can obtain at last photoluminescence UV printing ink.
CN 201210332490 2012-09-11 2012-09-11 UV photoluminescence ink Pending CN102977683A (en)