CN102977651A - 一种墙面涂料 - Google Patents
一种墙面涂料 Download PDFInfo
- Publication number
- CN102977651A CN102977651A CN2012105540666A CN201210554066A CN102977651A CN 102977651 A CN102977651 A CN 102977651A CN 2012105540666 A CN2012105540666 A CN 2012105540666A CN 201210554066 A CN201210554066 A CN 201210554066A CN 102977651 A CN102977651 A CN 102977651A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- wall coating
- urea
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种墙面涂料，由以下重量份的组分组成，磷酸三丁酯20-45份、碳酸钙10-15份、钛白粉5-10份、硬脂酸锌2-5份、碳酸二甲酯11-18份、烧碱2-8份、尿素3-7份、六偏磷酸钠4-9份、甲基硅醇钠10-15份、立德粉7-19份、绒毛粉11-17份。本发明所述的环保墙面涂料的挥发性有机物含量少，环境污染较小，节能减排、低碳环保，可广泛用于墙面的涂装。
Description
技术领域
技术领域 本发明涉及一种内墙粉刷涂料，尤其是瓷质涂料，本发明还涉及该瓷质涂料的制备方法，属于化工领域。
背景技术
背景技术 近年来，建筑行业的内墙粉刷普遍采用腻子灰或水性腻子灰，但采用腻子灰粉刷还存在着容易起泡、脱粉，遇水发霉、疏松剥落等不足。因此，寻求一种坚硬、防水、防霉、环保的新颖内墙粉刷涂料，已成为广大用户的迫切需求和时代进步的发展趋势。
发明内容
发明内容 本发明的目的在于提供一种内墙粉刷瓷质涂料，该涂料洁白无瑕，坚固耐用，防水防霉，无味，无气，无毒，生产无燥音，无油烟，无废弃物排放，节能环保，生产成本较低。
为达到上述目的，本发明所解决的技术方案是，一种墙面涂料，由以下重量份的组分组成，磷酸三丁酯20-45份、碳酸钙10-15份、钛白粉5-10份、硬脂酸锌2-5份、碳酸二甲酯11-18份、烧碱2-8份、尿素3-7份、六偏磷酸钠4-9份、甲基硅醇钠10-15份、立德粉7-19份、绒毛粉11-17份。
本发明一种瓷质墙面涂料其制备方法是：
将原料放入搅拌桶，充分搅拌均匀，将其充分搅拌均匀后，即可装桶使用。
本发明一种瓷质墙面涂料施工使用方法是：
1、待刷墙面底子要求干燥、平实；
2、将本品均匀涂刮一次。干透后再刮第二次，厚度依质量需求而定。
3、待盖面基本干后抛光即可。
本发明的有益效果：本发明所述的环保墙面涂料的挥发性有机物含量少，环境污染较小，节能减排、低碳环保，可广泛用于墙面的涂装。
具体实施方式
实施例1
一种墙面涂料，由以下重量份的组分组成，磷酸三丁酯20-45份、碳酸钙10-15份、钛白粉5-10份、硬脂酸锌2-5份、碳酸二甲酯11-18份、烧碱2-8份、尿素3-7份、六偏磷酸钠4-9份、甲基硅醇钠10-15份、立德粉7-19份、绒毛粉11-17份。
实施例2
一种墙面涂料，由以下重量份的组分组成，磷酸三丁酯20-45份、碳酸钙10-15份、钛白粉5-10份、硬脂酸锌2-5份、碳酸二甲酯11-18份、烧碱2-8份、尿素3-7份、六偏磷酸钠4-9份、甲基硅醇钠10-15份、立德粉7-19份、绒毛粉11-17份。
实施例3
一种墙面涂料，由以下重量份的组分组成，磷酸三丁酯20-45份、碳酸钙10-15份、钛白粉5-10份、硬脂酸锌2-5份、碳酸二甲酯11-18份、烧碱2-8份、尿素3-7份、六偏磷酸钠4-9份、甲基硅醇钠10-15份、立德粉7-19份、绒毛粉11-17份。
Claims (1)
1.一种墙面涂料，其特征在于：由以下重量份的组分组成，磷酸三丁酯20-45份、碳酸钙10-15份、钛白粉5-10份、硬脂酸锌2-5份、碳酸二甲酯11-18份、烧碱2-8份、尿素3-7份、六偏磷酸钠4-9份、甲基硅醇钠10-15份、立德粉7-19份、绒毛粉11-17份。