CN102965047A - Double-sided all-purpose adhesive tape - Google Patents
Double-sided all-purpose adhesive tape Download PDFInfo
- Publication number
- CN102965047A CN102965047A CN2012105521824A CN201210552182A CN102965047A CN 102965047 A CN102965047 A CN 102965047A CN 2012105521824 A CN2012105521824 A CN 2012105521824A CN 201210552182 A CN201210552182 A CN 201210552182A CN 102965047 A CN102965047 A CN 102965047A
- Authority
- CN
- China
- Prior art keywords
- adhesive tape
- parts
- adhesive
- sided
- double
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a double-sided all-purpose adhesive tape. The adhesive tape is prepared by taking a fiber fabric as a base material, and respectively coating an adhesive layer on the upper and lower sides of the base material. The adhesive layer comprises the following materials in parts by weight: 30-50 parts of butyl rubber, 10-25 parts of polyisobutylene (middle molecular weight), 5-15 parts of polyisobutylene (low molecular weight), 0-10 parts of operating oil, 10-20 parts of modified terpene resin, 0.3-0.5 part of a colorant, 0-0.5 part of an antioxidant, and 0-15 parts of a filler. When the double-sided all-purpose adhesive tape is applied to construction, an adhesive is not required to be daubed on the scene, the double-sided all-purpose adhesive tape can be directly used just through uncovering release paper, and therefore, the adhesive tape is simple and convenient; the adhesive tape is good in weather resistance, aging resistance, water repellency, anti-skidding property, adsorbability, shock-absorbing property, explosion-proof property and heat insulation property, longer in application time and wider in application range; and the adhesive tape has an excellent bonding capacity to various sheet metals, plastic sheets, plastic films and various pipes, therefore, the adhesive tape is extensive in use.
Description
Technical field
The present invention relates to a kind of two-sided Universal adhesive adhesive tape.
Background technology
At present in building and decoration construction, often run into various sticking operations, as pasting wall tile with cement, stick with glue agent stickup automobile interior, pasting waterproof roll etc. with tackiness agent, these constructional methods will be carried out the multiple working procedure construction at the scene, complex procedures, use duration, execute-in-place does not often reach the technological standard requirement, affects duration and result of use.
Summary of the invention
Purpose of the present invention is exactly in order to overcome the above problems, and simply and easily two-sided Universal adhesive adhesive tape of a kind of construction is provided.
The two-sided Universal adhesive adhesive tape of the present invention is take cloth as base material, and upper and lower faces is coated with respectively adhesive layer.
Its mixing ratio by weight of the material of adhesive layer is as follows:
Production method: isoprene-isobutylene rubber, polyisobutene are rehearsed in 50-100 ℃ of adding milling machine, sizing material mixes rear adding resin, process oil, filler, tinting material, oxidation inhibitor, rehearsal 5-20min, then drop into and in the time of 160 ℃-180 ℃, play glue in the glue melting box, be applied to the base material two sides, it is curling to add separate-type paper, cuts to get final product.
The two-sided Universal adhesive adhesive tape of the present invention is by being coated on tackiness agent on the base material, form a kind of double sticky tape of three-decker, tackiness agent is smeared at the scene that need not during construction, can directly use, simple and convenient, adhesive layer is comprised of isoprene-isobutylene rubber and tackifying resin material, has good weathering resistance, ageing resistance, waterproof, anti-skidding, absorption, shock-absorbing, explosion-proof, thermal insulation, duration of service is more permanent, and range of application is wider, to various sheet metals, plastic plate, plastics film, various tubing have splendid viscosifying power, can be used for various vehicle interiors decorates, the Indoor environment finishing, pipeline corrosion protection is processed, the house mending-leakage, bonding nameplate label etc., of many uses.
Embodiment
Embodiment 1:
Get isoprene-isobutylene rubber 268 30kg, polyisobutene (middle molecular weight) 10kg, polyisobutene (lower molecular weight) 5kg, naphthenic oil 1kg, modified terpene resin 10kg, carbon black colorant 0.3kg, antioxidant 1010 0.1kg, light calcium carbonate filler 1kg.Preparation method: isoprene-isobutylene rubber, polyisobutene are rehearsed in 50-100 ℃ of adding milling machine, sizing material mixes rear adding resin, naphthenic oil, light calcium carbonate, carbon black colorant, oxidation inhibitor, rehearsal 5-20min, then drop into and in the time of 160 ℃-180 ℃, play glue in the glue melting box, be applied to the base material two sides, add separate-type paper curling, cut and get final product.
Embodiment 2:
Get isoprene-isobutylene rubber 301 50kg, polyisobutene (middle molecular weight) 25kg, polyisobutene (lower molecular weight) 15kg, naphthenic oil 10kg, modified terpene resin 20kg, carbon black colorant 0.5kg, talcum powder 15kg, isoprene-isobutylene rubber, polyisobutene are rehearsed in 50-100 ℃ of adding milling machine, sizing material mixes rear adding resin, naphthenic oil, talcum powder, carbon black colorant, rehearsal 5-20min, then drop into and in the time of 160 ℃-180 ℃, play glue in the glue melting box, be applied to the base material two sides, add separate-type paper curling, cut.
Embodiment 3:
Get isoprene-isobutylene rubber 1751 40kg, polyisobutene (middle molecular weight) 18kg, polyisobutene (lower molecular weight) 10kg, third fractional oil 5kg, modified terpene resin 15kg, iron oxide red tinting material 0.4kg, antioxidant 264 0.25kg, potter's clay filler 8kg, isoprene-isobutylene rubber, polyisobutene are rehearsed in 50-100 ℃ of adding milling machine, sizing material mixes rear adding resin, third fractional oil, potter's clay, iron oxide red tinting material, rehearsal 5-20min, then drop into and in the time of 160 ℃-180 ℃, play glue in the glue melting box, be applied to the base material two sides, add separate-type paper curling, cut.
Embodiment 4:
Get isoprene-isobutylene rubber 268 40kg, polyisobutene (middle molecular weight) 20kg, polyisobutene (lower molecular weight) 8kg, modified terpene resin 12kg, iron oxide red tinting material 0.35kg, antioxidant 264 0.4kg, isoprene-isobutylene rubber, polyisobutene are rehearsed in 50-100 ℃ of adding milling machine, sizing material mixes rear adding resin, iron oxide red tinting material, antioxidant 264, rehearsal 5-20min, then drop into and in the time of 160 ℃-180 ℃, play glue in the glue melting box, be applied to the base material two sides, add separate-type paper curling, cut.
Claims (6)
1. two-sided Universal adhesive adhesive tape, it is characterized in that: this adhesive tape is take cloth as base material, and upper and lower faces is coated with respectively adhesive layer.
2. two-sided Universal adhesive adhesive tape according to claim 1, it is characterized in that: its mixing ratio by weight of the material of described adhesive layer is as follows:
Isoprene-isobutylene rubber 30-50 part, polyisobutene (middle molecular weight) 10-25 part, polyisobutene (lower molecular weight) 5-15 part, process oil 0-10 part, modified terpene resin 10-20 part, tinting material 0.3-0.5 part, oxidation inhibitor 0-0.5 part, filler 0-15 part.
3. two-sided Universal adhesive adhesive tape according to claim 2 is characterized in that: described isoprene-isobutylene rubber is optional to be isoprene-isobutylene rubber 268,301 or 1751.
4. two-sided Universal adhesive adhesive tape according to claim 2, it is characterized in that: described process oil is naphthenic oil or third fractional oil.
5. two-sided Universal adhesive adhesive tape according to claim 2, it is characterized in that: described oxidation inhibitor is antioxidant 264 or 1010.
6. two-sided Universal adhesive adhesive tape according to claim 2, it is characterized in that: described filler is light calcium carbonate or talcum powder or potter's clay.