CN102964929A - 饮用水池用喷涂速凝橡胶沥青防水材料 - Google Patents
饮用水池用喷涂速凝橡胶沥青防水材料 Download PDFInfo
- Publication number
- CN102964929A CN102964929A CN2012104999932A CN201210499993A CN102964929A CN 102964929 A CN102964929 A CN 102964929A CN 2012104999932 A CN2012104999932 A CN 2012104999932A CN 201210499993 A CN201210499993 A CN 201210499993A CN 102964929 A CN102964929 A CN 102964929A
- Authority
- CN
- China
- Prior art keywords
- rubber
- spraying
- solid content
- latex
- pond
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是一种饮用水池用的喷涂速凝橡胶沥青防水材料,其是采用最新工艺将乳化沥青与高分子聚合物橡胶胶乳按比例配制成液体橡胶沥青乳液组分,再与凝结剂按比例混合的一种水基喷涂料。处方中乳化沥青、胶乳、化学稳定剂等均是选择无挥发性有机化合物和有机溶剂。施工主要采用机械喷涂的方式,喷涂30秒成膜。所形成的弹性膜具有高伸长率(>1000%)和高弹性恢复率(>90%)的特点,因此拥有比传统材料更好的防水效果。本发明的饮用水池用喷涂速凝橡胶沥青防水材料在生产,施工和使用中,均不使用有机溶剂,无毒无味,无废料,无废气排放,无污染;在整个施工工程中,无需加热,常温施工,无明火,保证了材料的安全性和可靠性。
Description
技术领域
本发明涉及一种防水涂料,尤其是一种饮用水池用喷涂速凝橡胶沥青防水材料。
技术背景
现阶段大部分防水涂料都不能长期浸泡在水中,而且很多防水材料含有溶于水的有毒物质,加上使用寿命短的缺点,因此传统防水材料不能满足饮用水池对防水的要求。
发明内容
本发明为解决斜坡屋面的防水问题,提供了一种可用于饮用水池的防水,具有高粘结强度、高伸长率、环保对水质无影响、使用寿命长的饮用水池用喷涂速凝橡胶沥青防水材料。
本发明是通过如下技术方案实现的:
一种饮用水池用喷涂速凝橡胶沥青防水材料,其特征在:由固含量为55~70%的液体橡胶沥青胶乳液组分、浓度1~20%凝结剂组分分别按比例配制的水基喷涂料,凝结剂组分与液体橡胶沥青胶乳液组分的喷涂容量比为1/15~1/3.5; 所述液体橡胶沥青乳液组分的配方比例按重量百分比计为:固含量55~70%的橡胶胶乳53~79%、固含量45~50%的沥青乳液19~43%、炭黑0~6%、细粉料0~7%、阴离子分散剂0.02~3%、阴离子表面活性剂0.02~2.5%、稳定剂0.001~0.003%;其中所述的细粉料为瓷粉、重钙粉或轻钙粉;所述凝结剂组分的配方比例按重量百分比计为:氯化钙95~99.6%、氯化钠0.2~2%、复合铝铁聚合物0.2~3%或配方比例为:氯化钙92~99.9%、复合铝铁聚合物0.1~8%;按比例将上述的金属盐溶于水中,分别拌合均匀,配制为浓度1~20%。
所述橡胶胶乳是通过自由基乳液聚合法制备合成的橡胶胶乳或直接购买的商品;所述的沥青乳液是用沥青配制成的沥青乳液或直接购买的商品。
所述橡胶胶乳为天然橡胶胶乳或合成橡胶胶乳,合成橡胶胶乳为丁苯橡胶、顺丁橡胶、丁腈橡胶、乙丙橡胶、异戊橡胶、氯丁橡胶、氯丁二烯橡胶、丁二烯苯乙烯共聚物橡胶、丁二烯丙烯腈共聚物橡胶、异丁烯聚合物橡胶、异戊二烯聚合物橡胶或聚丁二烯橡胶的2~4种制成的胶乳。
所述天然橡胶胶乳和合成橡胶胶乳其含固量低于55~70%时,可通过低温提取法,温度控制在7~-4℃时,提取固含量达55~70%时,再将胶乳装入反应釜中升温到30~50℃时备用。
所述沥青乳液的配制方法为:在乳化沥青设备中加入重量份为100份的沥青并保持在120℃;加入重量份为100~122份浓度为0.5~1.5%的阴离子乳化剂水溶液,温度为40~80℃,进行高速剪切搅拌制得固含量为55~70%沥青乳液。
所述沥青为70-90#的石油沥青、煤焦沥青、天然沥青、页岩沥青或改制沥青。
所述液体橡胶沥青胶乳液组分的制备方法:当沥青乳液降至20~40℃时在搅拌下加入液体炭黑或炭黑粉、细粉料或液体细粉料、阴离子分散剂、阴离子表面活性剂、稳定剂,然后将橡胶胶乳徐徐加入,搅拌均匀,制得含固量55~70%的液体橡胶沥青乳液。
当制得沥青乳液固含量大于47%或橡胶胶乳固含量大于60%时,根据使用条件不同,也可以在橡胶沥青乳液合成中不加入液体炭黑或炭黑粉、细粉料或液体细粉料,只要将沥青乳液、橡胶胶乳在20~40℃温度范围加入阴离子分散剂、阴离子表面活性剂和稳定剂,搅拌均匀即可。
本发明的原料成分:乳化沥青,成分包括石油沥青(沥青质、油分、树脂质)、水、 乳化剂(羧酸盐型金属皂)。橡胶胶乳,成分包括橡胶、乳化剂、水等。活性剂,为脂肪酸盐。稳定剂,为液体钙锌稳定剂。所用原料均在常温下混合反应,喷涂成膜后经检测产品达到安全无毒级。本发明还做了小白鼠、金鱼试验。用本发明喷涂小型饮用水池并加满水,一段时间后用其中的水给小白鼠饮用并观察小白鼠身体的健康状况。试验结果小白鼠各项生理指标均正常。用内部已喷涂本发明的鱼缸放养金鱼,金鱼正常在水中生长,对鱼缸中的水进行检测未发现有毒物质。两项实验证明本发明的喷涂速凝橡胶沥青防水材料完全可以用于饮用水池的防水。
本发明的有益效果是:本发明的饮用水池用喷涂速凝橡胶沥青防水材料在生产,施工和使用中,均不使用有机溶剂,无毒无味,无废料,无废气排放,无污染;在整个施工工程中,无需加热,常温施工,无明火,保证了材料的安全性和可靠性。施工中乳化沥青、胶乳、化学稳定剂等均是选择无挥发性有机化合物和有机溶剂。施工主要采用机械喷涂的方式,喷涂过程中凝结剂组分与液体橡胶沥青胶乳液组分混合迅速固化30秒成膜。所形成的弹性膜具有高伸长率(>1000%)和高弹性恢复率(>90%)的特点,因此拥有比传统材料更好的防水效果。成膜过程主要是沥青分子与胶乳之间的物理交联因此不会在施工过程中产生污染。
具体实施方式
实施例1:凝结剂组分的制备
配方:氯化钙99.6%、氯化钠0.2%、复合铝铁聚合物0.2%。按比例将上述的金属盐溶于水中,分别拌合均匀,配制为浓度20%。
实施例2:凝结剂组分的制备
配方:氯化钙95%、氯化钠2%、复合铝铁聚合物3%。按比例将上述的金属盐溶于水中,分别拌合均匀,配制为浓度1%。
实施例3:凝结剂组分的制备
配方:氯化钙97%、氯化钠1%、复合铝铁聚合物2%。按比例将上述的金属盐溶于水中,分别拌合均匀,配制为浓度10%。
实施例4:凝结剂组分的制备
配方:氯化钙99.9%、复合铝铁聚合物0.1%。按比例将上述的金属盐溶于水中,分别拌合均匀,配制为浓度20%。
实施例5:凝结剂组分的制备
配方:氯化钙92%、复合铝铁聚合物8%。按比例将上述的金属盐溶于水中,分别拌合均匀,配制为浓度10%。
实施例6:凝结剂组分的制备
配方:氯化钙96%、复合铝铁聚合物4%。按比例将上述的金属盐溶于水中,分别拌合均匀,配制为浓度1%。
实施例7:橡胶胶乳的处理
天然橡胶胶乳和合成橡胶胶乳其含固量低于55~70%时,可通过低温提取法,温度控制在7~-4℃时,提取固含量达55~70%时,再将胶乳装入反应釜中升温到30~50℃时备用。
实施例8:沥青乳液的配制
在乳化沥青设备中加入重量份为100份的沥青并保持在120℃;加入重量份为122份的阴离子乳化剂水溶液(羧酸盐型金属皂,浓度为1%),温度为60~80℃,进行高速剪切搅拌制得固含量为45%沥青乳液。
实施例9:沥青乳液的配制
在乳化沥青设备中加入重量份为100份的90#的石油沥青并保持在120℃;加入重量份为110份的阴离子乳化剂水溶液(羧酸盐型金属皂,浓度为0.5%),温度为40~60℃,进行高速剪切搅拌制得固含量为50%沥青乳液。
实施例10:沥青乳液的配制
在乳化沥青设备中加入重量份为100份的70#的煤焦沥青并保持在120℃;加入重量份为108份的阴离子乳化剂水溶液(羧酸盐型金属皂,浓度为1.5%),温度为40~80℃,进行高速剪切搅拌制得固含量为48%沥青乳液。
实施例11:液体橡胶沥青胶乳液组分的制备
当实施例8沥青乳液降至20~40℃时在搅拌下加入液体炭黑或炭黑粉、瓷粉细粉料或液体细粉料,阴离子分散剂、阴离子表面活性剂、稳定剂,然后将固含量55%为合成橡胶胶乳徐徐加入,搅拌均匀制得含固量55%的液体橡胶沥青乳液。
具体配方比例按重量百分比计为:固含量45%的沥青乳液(实施例8)31%、固含量55%的橡胶胶乳53%、炭黑6%、细粉料7%、阴离子分散剂0.5%、阴离子表面活性剂2.498%、稳定剂0.002%。
实施例12:液体橡胶沥青胶乳液组分的制备
当实施例9中沥青乳液降至20~40℃时在搅拌下加入液体炭黑、重钙粉细粉料,阴离子分散剂、阴离子表面活性剂、稳定剂,然后将固含量60%为合成橡胶胶乳徐徐加入,搅拌均匀制得固含量60%的液体橡胶沥青乳液。
具体配方比例按重量百分比计为:固含量60%的沥青乳液(实施例9)19、固含量60%的橡胶胶乳79%、炭黑1%、细粉料1%、阴离子分散剂0.5%、阴离子表面活性剂0.02%、稳定剂0.001%。
实施例13:液体橡胶沥青胶乳液组分的制备
当实施例10中沥青乳液降至20~40℃时在搅拌下加入炭黑粉、瓷粉细粉料,阴离子分散剂、阴离子表面活性剂、稳定剂,然后将固含量70%为合成橡胶胶乳徐徐加入,搅拌均匀制得固含量75%的液体橡胶沥青乳液。
具体配方比例按重量百分比计为:固含量48%的沥青乳液(实施例10)19%、固含量70%的橡胶胶乳71%、炭黑6%、细粉料0.0977%、阴离子分散剂3%、阴离子表面活性剂0.02%、稳定剂0.003%。
实施例14:液体橡胶沥青胶乳液组分的制备
当制得沥青乳液固含量大于47%或橡胶胶乳固含量大于60%时,根据使用条件不同,也可以在橡胶沥青乳液合成中不加入液体炭黑或炭黑粉,瓷粉细粉料或液体细粉料,只要将沥青乳液,橡胶胶乳在温度20-40℃范围加入阴离子分散剂阴离子表面活性剂、稳定剂搅拌均匀即可。
具体配方比例:固含量47~50%的沥青乳液40.957%、固含量60~70%的橡胶胶乳59%、阴离子分散剂0.02%、阴离子表面活性剂0.02%、稳定剂0.003%。
Claims (8)
1.一种饮用水池用喷涂速凝橡胶沥青防水材料,其特征在:由固含量为55~75%的液体橡胶沥青胶乳液组分、浓度1~20%凝结剂组分分别按比例配制的水基喷涂料,凝结剂组分与液体橡胶沥青胶乳液组分的喷涂容量比为1/15~1/3.5;
所述液体橡胶沥青乳液组分的配方比例按重量百分比计为:固含量55~70%的橡胶胶乳53~79%、固含量45~50%的沥青乳液19~43%、炭黑0~6%、细粉料0~7%、阴离子分散剂0.02~3%、阴离子表面活性剂0.02~2.5%、稳定剂0.001~0.003%;其中所述的细粉料为瓷粉、重钙粉或轻钙粉;
所述凝结剂组分的配方比例按重量百分比计为:氯化钙95~99.6%、氯化钠0.2~2%、复合铝铁聚合物0.2~3%或配方比例为:氯化钙92~99.9%、复合铝铁聚合物0.1~8%;按比例将上述的金属盐溶于水中,分别拌合均匀,配制为浓度1~20%。
2.根据权利要求1所述的饮用水池用喷涂速凝橡胶沥青防水材料,其特征在于:所述橡胶胶乳是通过自由基乳液聚合法制备合成的橡胶胶乳或直接购买的商品;所述的沥青乳液是用沥青配制成的沥青乳液或直接购买的商品。
3.根据权利要求2所述的饮用水池用喷涂速凝橡胶沥青防水材料,其特征在于:所述橡胶胶乳为天然橡胶胶乳或合成橡胶胶乳,合成橡胶胶乳为丁苯橡胶、顺丁橡胶、丁腈橡胶、乙丙橡胶、异戊橡胶、氯丁橡胶、氯丁二烯橡胶、丁二烯苯乙烯共聚物橡胶、丁二烯丙烯腈共聚物橡胶、异丁烯聚合物橡胶、异戊二烯聚合物橡胶或聚丁二烯橡胶的2~4种制成的胶乳。
4.根据权利要求3所述的饮用水池用喷涂速凝橡胶沥青防水材料,其特征在于:所述天然橡胶胶乳和合成橡胶胶乳其含固量低于55~70%时,可通过低温提取法,温度控制在7~-4℃时,提取固含量达55~70%时,再将胶乳装入反应釜中升温到30~50℃时备用。
5.根据权利要求1所述的饮用水池用喷涂速凝橡胶沥青防水材料,其特征在于:所述沥青乳液的配制方法为:在乳化沥青设备中加入重量份为100份的沥青并保持在120℃;加入重量份为100~122份浓度为0.5~1.5%的阴离子乳化剂水溶液,温度为40~80℃,进行高速剪切搅拌制得固含量为55~70%沥青乳液。
6. 根据权利要求5所述的饮用水池用喷涂速凝橡胶沥青防水材料,其特征在于:所述沥青为70-90#的石油沥青、煤焦沥青、天然沥青、页岩沥青或改制沥青。
7.根据权利要求1所述的饮用水池用喷涂速凝橡胶沥青防水材料,其特征在于所述液体橡胶沥青胶乳液组分的制备方法:当沥青乳液降至20~40℃时在搅拌下加入液体炭黑或炭黑粉、细粉料或液体细粉料、阴离子分散剂、阴离子表面活性剂、稳定剂,然后将橡胶胶乳徐徐加入,搅拌均匀,制得含固量55~75%的液体橡胶沥青乳液。
8.根据权利要求7所述的饮用水池用喷涂速凝橡胶沥青防水材料,其特征在于:当制得沥青乳液固含量大于47%或橡胶胶乳固含量大于60%时,根据使用条件不同,也可以在橡胶沥青乳液合成中不加入液体炭黑或炭黑粉,细粉料或液体细粉料,只要将沥青乳液、橡胶胶乳在20~40℃温度范围加入阴离子分散剂、阴离子表面活性剂和稳定剂,搅拌均匀即可。