CN102943408B - 一种卷烟滤嘴棒用成型纸的制备方法 - Google Patents
一种卷烟滤嘴棒用成型纸的制备方法 Download PDFInfo
- Publication number
- CN102943408B CN102943408B CN201210387303.4A CN201210387303A CN102943408B CN 102943408 B CN102943408 B CN 102943408B CN 201210387303 A CN201210387303 A CN 201210387303A CN 102943408 B CN102943408 B CN 102943408B
- Authority
- CN
- China
- Prior art keywords
- paper
- wood chip
- pulp
- preparation
- cigarette filter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种防伪卷烟滤嘴棒用成型纸的制备方法。选择阔叶木片和针叶木片并按一定的比例混合均匀;经洗涤、汽蒸加热、压榨工序将混合均匀的木片充分软化并分离得到木浆纤维,对木浆纤维经过漂白、筛选和打浆制得纸浆原浆;在纸浆原浆中加入烟叶纤维后放入打浆机中进行打浆得到含有烟叶纤维的纸浆;然后分别以NaOH或KaOH作为添加剂、以CaCO3或CaSO4作为填充剂添加入纸浆,并流送至造纸机的头箱和网部,再经过压榨、干燥、卷取、分切、包装,即得本发明所述的防伪卷烟滤嘴棒用成型纸。本发明生产工艺简单,样式新颖,具有较强的防伪功能,可以有选择性地降低烟气中的有害物质。
Description
技术领域
本发明属于卷烟包装材料加工技术领域,具体来讲,涉及一种具有防伪功能的卷烟滤嘴棒用成型纸的制备方法。
背景技术
卷烟滤嘴棒用成型纸,属工业用薄型特种纸类,主要应用于烟草行业卷烟过滤嘴中包裹醋酸纤维丝束,因其能够有效降低吸烟对人体的危害而被广泛应用。现有技术中,普通成型纸以木浆、麻浆或者木浆和麻浆的混合浆为主要原料,经过一定的加工工序制备而成,且制备方法较为成熟,易于复制伪。目前,普通的消费者很难通过目测成型纸而辨别出真假卷烟烟支,卷烟制假贩假者正是利用了这一机会,将伪造的成型纸用于假烟生产,以假冒伪劣的卷烟产品以次充好,攫取高额利润,严重损害了广大消费者的利益。同时卷烟制假售假严重危害着卷烟工业的正常发展,假烟的制造和销售使得大量税款流失,国家利益蒙受巨大损失。
发明内容
本发明的目的在于针对现有技术中的不足,提供一种制备具有防伪效果的卷烟滤嘴棒用成型纸的方法,为辨别卷烟真假提供条件。
本发明的目的通过以下技术方案予以实现。
*除非另有说明,本发明所采用的百分数均为质量百分数。
一种卷烟滤嘴棒用成型纸的制备方法,包括以下步骤:
1、原料准备:根据成型纸所需透气度要求,选择阔叶木片和针叶木片作为原料,并按照8:2~3:7的比例将阔叶木片和针叶木片混合均匀,备用;
其中,所述的阔叶木片和所述的针叶木片的尺寸为5mm×10mm×25mm~10mm×20mm×50mm;
2、原浆制备:经洗涤、汽蒸加热、压榨工序将步骤(1)中的木片充分软化并分离得到木浆纤维,对木浆纤维经过漂白、筛选和打浆制得纸浆原浆,备用;
3、掺入纤维:将纸浆原浆加热到40~50℃后,加入3%~30%的烟叶纤维后放入打浆机中进行打浆,打浆比压为5~16Kg/m2,得到含有烟叶纤维的纸浆,备用;
4、在步骤(3)中得到的含有烟叶纤维的纸浆中加入1~2%的NaOH或KaOH作为添加剂,15~25%的CaCO3或CaSO4作为填充剂,再流送至造纸机的头箱和网部,经过压榨、干燥、卷取、分切、包装,即得本发明所述的防伪卷烟滤嘴棒用成型纸。
与现有技术相比,本发明具有如下有益效果:
1、本发明通过加入烟叶纤维,形成直观、明显的视觉效果,为真假烟鉴别提供评价依据和有效途径,使烟用成型纸能够有效地防止被仿造和伪造。
2、 本方法制备得到的成型纸能够选择性地降低烟气中的有害物质。某些组份如烟碱,在常温下与烟丝内部的其他成分结合得比较牢固。当卷烟燃烧时,在高温蒸馏作用下会被大量释放出来,并随着主流烟气带至过滤嘴处,然后进入人体成为了有害物质。由于烟叶纤维同样含有性质类似的物质,它们之间的热力学性质差异小,亲和力大,因此经过烟叶纤维时截留效率较高,可减少被人体吸食的数量,从而实现有选择性地降低主流烟气中的有害物质。
附图说明
图1为本发明制备方法得到的卷烟滤嘴棒用成型纸;
图2为普通卷烟滤嘴棒用成型纸;
图3为本发明应用于卷烟烟支制备的烟支结构示意图。
图中:1- 防伪卷烟滤嘴棒用成型纸,2-接装纸,3-烟支,4-丝束。
具体实施方式
下面结合附图及具体实施例对本发明加以说明,应当注意,具体实施例不以任何方式对本发明加以限制,依据本发明的教导所作得任何变更或替换,均属于本发明的保护范围。
实施例1
选择阔叶木片和针叶木片,所述的阔叶木片和所述的针叶木片的尺寸为5mm×10mm×25mm~10mm×20mm×50mm,并按照8:2的比例混合均匀;经洗涤、汽蒸加热、压榨工序,将混合均匀的木片充分软化并分离得到木浆纤维,对木浆纤维经过漂白、筛选和打浆制得纸浆原浆;将纸浆原浆加热到40~50℃后,加入3%的烟叶纤维后放入打浆机中进行打浆,打浆比压为5Kg/m2,得到含有烟叶纤维的纸浆;加入1%的NaOH作为添加剂, 15%的CaCO3作为填充剂后,流送至造纸机的头箱和网部,再经过压榨、干燥、卷取、分切、包装,即得本发明所述的防伪卷烟滤嘴棒用成型纸。
实施例2
选择阔叶木片和针叶木片,所述的阔叶木片和所述的针叶木片的尺寸为5mm×10mm×25mm~10mm×20mm×50mm,并按照7:3的比例混合均匀;经洗涤、汽蒸加热、压榨工序,将混合均匀的木片充分软化并分离得到木浆纤维,对木浆纤维经过漂白、筛选和打浆制得纸浆原浆;将纸浆原浆加热到40~50℃后,加入30%的烟叶纤维后放入打浆机中进行打浆,打浆比压为16Kg/m2,得到含有烟叶纤维的纸浆;加入1.5%的NaOH作为添加剂, 20%的CaCO3作为填充剂后,流送至造纸机的头箱和网部,再经过压榨、干燥、卷取、分切、包装,即得本发明所述的防伪卷烟滤嘴棒用成型纸。
实施例3
选择阔叶木片和针叶木片,所述的阔叶木片和所述的针叶木片的尺寸为5mm×10mm×25mm~10mm×20mm×50mm,并按照6:4的比例混合均匀;经洗涤、汽蒸加热、压榨工序,将混合均匀的木片充分软化并分离得到木浆纤维,对木浆纤维经过漂白、筛选和打浆制得纸浆原浆;将纸浆原浆加热到40~50℃后,加入10%的烟叶纤维后放入打浆机中进行打浆,打浆比压为8Kg/m2,得到含有烟叶纤维的纸浆;加入2%的NaOH作为添加剂, 25%的CaCO3作为填充剂后,流送至造纸机的头箱和网部,再经过压榨、干燥、卷取、分切、包装,即得本发明所述的防伪卷烟滤嘴棒用成型纸。
实施例4
选择阔叶木片和针叶木片,所述的阔叶木片和所述的针叶木片的尺寸为5mm×10mm×25mm~10mm×20mm×50mm,并按照5:5的比例混合均匀;经洗涤、汽蒸加热、压榨工序,将混合均匀的木片充分软化并分离得到木浆纤维,对木浆纤维经过漂白、筛选和打浆制得纸浆原浆;将纸浆原浆加热到40~50℃后,加入15%的烟叶纤维后放入打浆机中进行打浆,打浆比压为10Kg/m2,得到含有烟叶纤维的纸浆;加入1%的KaOH作为添加剂, 15%的CaSO4作为填充剂后,流送至造纸机的头箱和网部,再经过压榨、干燥、卷取、分切、包装,即得本发明所述的防伪卷烟滤嘴棒用成型纸。
实施例5
选择阔叶木片和针叶木片,所述的阔叶木片和所述的针叶木片的尺寸为5mm×10mm×25mm~10mm×20mm×50mm,并按照4:6的比例混合均匀;经洗涤、汽蒸加热、压榨工序,将混合均匀的木片充分软化并分离得到木浆纤维,对木浆纤维经过漂白、筛选和打浆制得纸浆原浆;将纸浆原浆加热到40~50℃后,加入15%的烟叶纤维后放入打浆机中进行打浆,打浆比压为10Kg/m2,得到含有烟叶纤维的纸浆,;加入1.5%的KaOH作为添加剂,20%的CaSO4作为填充剂后,流送至造纸机的头箱和网部,再经过压榨、干燥、卷取、分切、包装,即得本发明所述的防伪卷烟滤嘴棒用成型纸。
实施例6
选择阔叶木片和针叶木片,所述的阔叶木片和所述的针叶木片的尺寸为5mm×10mm×25mm~10mm×20mm×50mm,并按照3:7的比例混合均匀;经洗涤、汽蒸加热、压榨工序,将混合均匀的木片充分软化并分离得到木浆纤维,对木浆纤维经过漂白、筛选和打浆制得纸浆原浆;将纸浆原浆加热到40~50℃后,加入15%的烟叶纤维后放入打浆机中进行打浆,打浆比压为10Kg/m2,得到含有烟叶纤维的纸浆;加入2%的KaOH作为添加剂, 25%的CaSO4作为填充剂后,流送至造纸机的头箱和网部,再经过压榨、干燥、卷取、分切、包装,即得本发明所述的防伪卷烟滤嘴棒用成型纸。
本发明方法制备得到的卷烟滤棒用成型纸,通过在纸浆原浆中加入一定比例的烟叶纤维,形成直观、明显的视觉效果,为真假烟鉴别提供评价依据和有效途径,使烟用成型纸能够有效地防止被仿造和伪造。同时,能够选择性地降低烟气中的有害物质。例如烟碱,其在常温下与烟丝内部的其他成分结合得比较牢固。当卷烟燃烧时,在高温蒸馏作用下会被大量释放出来,并随着主流烟气带至过滤嘴处,然后进入人体成为了有害物质。由于烟叶纤维内含有与烟碱性质类似的物质,它们之间的热力学性质差异小,亲和力大,因此主流延期经过烟叶纤维时被烟叶纤维截留效率较高,可有效减少被人体吸食的数量,从而实现有选择性地降低主流烟气中的有害物质。
将本发明含有烟叶纤维的烟用成型纸1通过与接装纸2、丝束、烟丝4等原辅材料配合使用,组装成一支卷烟烟支4,如图3所示。
Claims (2)
1.一种防伪卷烟滤嘴棒用成型纸的制备方法,其特征在于,包括以下步骤:
(1)原料准备:选择阔叶木片和针叶木片作为原料,并按照8:2~3:7的比例将阔叶木片和针叶木片混合均匀,备用;
(2)原浆制备:经洗涤、汽蒸加热、压榨工序将步骤(1)中的木片充分软化并分离得到木浆纤维,对木浆纤维经过漂白、筛选和打浆制得纸浆原浆,备用;
(3)掺入纤维:将纸浆原浆加热到40~50℃后,加入3%~30%的烟叶纤维后放入打浆机中进行打浆,打浆比压为5~16Kg/m2,得到含有烟叶纤维的纸浆,备用;
(4)在步骤(3)中得到的含有烟叶纤维的纸浆中加入1~2%的NaOH或KaOH作为添加剂,15~25%的CaCO3或CaSO4作为填充剂,再流送至造纸机的头箱和网部,经过压榨、干燥、卷取、分切、包装,即得本发明所述的防伪卷烟滤嘴棒用成型纸。
2.根据权利要求1所述的卷烟滤嘴棒用成型纸的制备方法,其特征在于:所述步骤(1)中阔叶木片和所述的针叶木片的尺寸为5mm×10mm×25mm~10mm×20mm×50mm。