CN102936834A - Method for preparing far infrared textiles by using master batch process - Google Patents
Method for preparing far infrared textiles by using master batch process Download PDFInfo
- Publication number
- CN102936834A CN102936834A CN2012104763154A CN201210476315A CN102936834A CN 102936834 A CN102936834 A CN 102936834A CN 2012104763154 A CN2012104763154 A CN 2012104763154A CN 201210476315 A CN201210476315 A CN 201210476315A CN 102936834 A CN102936834 A CN 102936834A
- Authority
- CN
- China
- Prior art keywords
- far infrared
- far
- textiles
- infrared
- master batch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing far infrared textiles by using a master batch process. The method comprises the following steps of: preparing far infrared ceramic micro powder into far infrared master batches, mixing with polyacrylonitrile and then spinning to prepare far infrared fibers; preparing the far infrared fibers into far infrared flocculus; and finally, adding the far infrared flocculus in the textiles, wherein the addition of the far infrared flocculus is adjustable, and particularly is 1-45 percent. The method disclosed by the invention has the advantages of simple preparation process, simpleness in operation and higher yield; and the prepared far infrared radiated textiles are good in warm-keeping property.
Description
Technical field
The present invention relates to a kind of preparation method of far-infrared textiles, relate in particular to the method for the standby far-infrared textiles of a kind of master batch legal system.
Background technology
Common textiles is because heat insulation effect is limited, when weather is colder, can not satisfy well people to the requirement of textiles, common way is thickeied textiles exactly, warming effect is improved, but the increase of thickness increases manufacturing cost on the one hand, also be unfavorable on the other hand aesthetic, and the operation of product is more complicated, and yield rate is lower.
Summary of the invention
Main purpose of the present invention is, overcome the defective that existing textiles exists, and the method for the standby far-infrared textiles of a kind of master batch legal system is provided, technical problem to be solved is to improve the warmth retention property of existing textiles, improve yield rate, thereby more be suitable for practicality, and have the value on the industry.
The object of the invention to solve the technical problems realizes by the following technical solutions: the method for the standby far-infrared textiles of a kind of master batch legal system, the method comprises the steps: far infrared ceramic micro powder is made far-infrared matrix, spinning after mixing with polypropylene is fine again, be prepared into far IR fibre, again described far IR fibre is made the far infrared flocculus, at last described far infrared flocculus is added in the textiles.
Further, the addition of described far infrared flocculus is adjustable.
Again further, the addition of described far infrared flocculus is 1%~45%.
Compared with prior art, usefulness of the present invention is: the method for the standby far-infrared textiles of this master batch legal system, and preparation technology is simple, and is simple to operate, and yield rate is higher, and the infrared textiles warmth retention property that makes is good.
The specific embodiment
Reach technological means and the effect that predetermined goal of the invention is taked for further setting forth the present invention, its specific embodiment of preparation method, feature and the effect thereof of the far-infrared textiles that foundation the present invention is proposed are described in detail as follows.
The method of the standby far-infrared textiles of a kind of master batch legal system, at first far infrared ceramic micro powder is made the high concentration far-infrared matrix, concentration is about 85%, spinning after mixing with polypropylene is fine again, be prepared into far IR fibre, again far IR fibre is made the far infrared flocculus, at last 40% far infrared flocculus is added in the textiles.
The method of the standby far-infrared textiles of this master batch legal system, preparation technology is simple, and is simple to operate, and yield rate is higher, and the infrared textiles warmth retention property that makes is good.
The above, it only is preferred embodiment of the present invention, be not that the present invention is done any pro forma restriction, although the present invention discloses as above with preferred embodiment, yet be not to limit the present invention, any those skilled in the art, within not breaking away from the technical solution of the present invention scope, when the technology contents that can utilize above-mentioned announcement is made a little change or is modified to the equivalent embodiment of equivalent variations, in every case be the content that does not break away from technical solution of the present invention, any simple modification that foundation technical spirit of the present invention is done above embodiment, equivalent variations and modification all still belong in the scope of technical solution of the present invention.
Claims (3)
1. the method for the standby far-infrared textiles of a master batch legal system, it is characterized in that, the method comprises the steps: far infrared ceramic micro powder is made far-infrared matrix, spinning after mixing with polypropylene is fine again, be prepared into far IR fibre, again described far IR fibre is made the far infrared flocculus, at last described far infrared flocculus is added in the textiles.
2. the method for the standby far-infrared textiles of master batch legal system according to claim 1 is characterized in that, the addition of described far infrared flocculus is adjustable.
3. each described master batch legal system is characterized in that for the method for far-infrared textiles according to claim 1 and 2, and the addition of described far infrared flocculus is 1%~45%.