CN102936467A - 一种天然植物胶的制备方法 - Google Patents
一种天然植物胶的制备方法 Download PDFInfo
- Publication number
- CN102936467A CN102936467A CN2012104415122A CN201210441512A CN102936467A CN 102936467 A CN102936467 A CN 102936467A CN 2012104415122 A CN2012104415122 A CN 2012104415122A CN 201210441512 A CN201210441512 A CN 201210441512A CN 102936467 A CN102936467 A CN 102936467A
- Authority
- CN
- China
- Prior art keywords
- mixture
- preparation
- stirring
- flour
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种天然植物胶的制备工艺。其制备的主要过程是:将小麦粉和三甲胺加入到软水中,搅拌升温至90℃使其完全溶解,搅拌50min;待降温至60℃加入过硫酸铵,搅拌10-15min;再加入木薯淀粉粉和高岭土,搅拌均匀后加热升温,温度控制在75℃,保温30min;最后加入松香,搅拌均匀,降至室温即得产品。该工艺方法简单、耗能低,得出的产品经检测不含甲苯、二甲苯等有害物质,其胶液粘连性强、环保无污染。
Description
技术领域
本发明涉及一种胶的制备工艺,尤其涉及一种天然植物胶的制备方法。
背景技术
长时间以来,甲醛因其成本低廉而成为合成胶黏剂的重要原料,如聚乙烯醇缩甲醛胶、脲醛树脂胶、酚醛树脂胶等都含有一定量未反应完全的游离甲醛,在加压、使用过程中缓慢放出,引起环境污染,危害健康,普遍成为人们生活中的致病隐患。
随着环境保护意识和健康意识日益深入人心,天然无毒害的胶黏剂的出台成为一项重要课题。目前,我国胶黏剂的生产虽然已经有了很大发展,但是由于一些观念上的忽视和技术方面的限制,天然环保型胶黏剂的研发工作还没有实质性的突破,例如,许多淀粉类植物和高蛋白类植物来源广、产量高,又是可再生资源,经过加工作为胶黏剂的合成原料具有无可比拟的优越性,却长期得不到重视;技术上,植物淀粉、植物蛋白粉制作的胶黏剂粘结强度和抗水性较差,缺乏抗微生物的能力,以往的产品大多达不到工业的应用标准。
发明内容
本发明的目的是对植物淀粉、植物蛋白进行改性,制作出高粘度、高稳定性的的天然环保胶粘剂,使之符合多方面应用的要求。
本发明技术方案如下:
核心成分配比:木薯淀粉30-70%、小麦粉5-25%、三甲胺1.5%、高岭土8.8%、松香1.5%、过硫酸铵0.2%。
制备步骤:(1)将三甲胺和小麦粉加入到为核心成分质量3倍的软水中,搅拌升温至90℃使其完全溶解,搅拌50min;(2)降温至60℃加入过硫酸铵,搅拌10min;(3)加入木薯淀粉粉及高岭土,搅拌均匀后加热升温,温度控制在80℃左右,保温30min;(4)最后加入松香,搅拌均匀,降至室温即得产品。
所述三甲胺(分子式:C3H9N;分子量:59.11)具有叔胺的典型性质,包括成盐、氧化等。三甲胺可以使植物淀粉、植物蛋白粉改性和水解而获得良好的胶黏性。
所述松香的主要成分为树脂酸(分子式:C19H29COOH,分子量:302.46),占90%左右,使之具有增黏、乳化、软化、防潮、防腐、绝缘等优良性能。松香在热熔、压敏和溶剂型胶黏剂中常用作增黏树脂,增加初黏性,提高粘接强度。
所述过硫酸铵(化学式:(NH4)2S2O8;相对分子质量:228.20)主要用途是作为氧化剂、漂白剂和消毒剂,也可以用作淀粉胶黏剂的助氧化剂,与淀粉成分中的蛋白质反应提高粘接性。
所述高岭土具有白度高、质软、易分散悬浮于水中、良好的可塑性和高的粘结性、优良的电绝缘性能;具有良好的抗酸溶性、很低的阳离子交换量、较好的耐火性等理化性质,是一种制作天然植物黏胶的优良抗水剂。
本发明实施例的制备方法简单、耗能低,得出的产品经检测不含甲苯、二甲苯等有害物质,其胶液粘连性强、环保无污染。
附图说明
图1表示本发明实施例提供的天然植物胶制备方法的实现流程图。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白,以下结合附图及实施例,对本发明进行进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
图1示出了本发明实施例提供的天然植物胶制备方法的实现流程,详述如下:
在步骤S101中,将三甲胺和小麦粉加入到软水中,搅拌升温至90℃使其完全溶解,搅拌50min;
在本发明的实施例中,软水的用量是核心成分质量总和的3倍。
在本发明的实施例中,核心成分包括木薯淀粉30-70%、小麦粉5-25%、三甲胺1.5%、高岭土8.7%、松香1.5%及过硫酸铵0.3%。
在步骤S102中,降温至60℃加入过硫酸铵,搅拌10-15min;
在步骤S103中,加入木薯淀粉及高岭土,搅拌均匀后加热升温,温度控制在75℃左右,保温30min;
在步骤S104中,最后加入松香,搅拌均匀,降至室温即得产品。
实例一:将三甲胺1.5g和小麦粉20g加入到300g的软水中,搅拌升温至90℃使其完全溶解,搅拌50min;降温至60℃加入过硫酸铵0.2g,搅拌10min;加入68g木薯淀粉粉及8.8g高岭土,搅拌均匀后加热升温,温度控制在80℃左右,保温30min;(4)最后加入松香1.5g,搅拌均匀,降至室温即得产品。
经检测:胶液中不含甲苯、中苯、二甲苯、甲醛等芳烃,温度为25℃时,胶液粘度为40020mPas。
实例二:将小麦粉15g和三甲胺1.5g加入到300g的软水中,搅拌升温至90℃使其完全溶解,搅拌50min;降温至60℃加入过硫酸铵0.2g,搅拌10min;加入35g木薯淀粉粉及8.8g高岭土,搅拌均匀后加热升温,温度控制在80℃左右,保温30min;(4)最后加入松香1.5g,搅拌均匀,降至室温即得产品。
经检测:胶液中不含甲苯、中苯、二甲苯、甲醛等芳烃,温度为25℃时,胶液粘度为39960mPas。
实例三:将小麦粉10g和三甲胺1.5g加入到300g的软水中,搅拌升温至90℃使其完全溶解,搅拌50min;降温至60℃加入过硫酸铵0.2g,搅拌10min;加入58g木薯淀粉粉及8.8g高岭土,搅拌均匀后加热升温,温度控制在80℃左右,保温30min;(4)最后加入松香1.5g,搅拌均匀,降至室温即得产品。
经检测:胶液中不含甲苯、中苯、二甲苯、甲醛等芳烃,温度为25℃时,胶液粘度为41310mPas。
本发明实施例的制备方法简单、耗能低,得出的产品经检测不含甲苯、二甲苯等有害物质,其胶液粘连性强、环保无污染。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以作出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (3)
1.一种天然植物胶的制备方法,其特征在于,所述产品的核心成分是:木薯淀粉30-70%、小麦粉5-25%、三甲胺1.5%、高岭土8.7%、松香1.5%及过硫酸铵0.3%。
2.如权利要求1所述的制备方法,其特征在于,所述制备过程包括:
(1)将三甲胺和小麦粉加入到软水中,搅拌升温至90℃使其完全溶解,搅拌50min;
(2)降温至60℃加入过硫酸铵,搅拌10-15min;
(3)加入木薯淀粉及高岭土,搅拌均匀后加热升温,温度控制在75℃,保温30min;
(4)最后加入松香,搅拌均匀,降至室温即得产品。
3.根据权利要求2(1)所述的一种天然植物胶的制备方法,其特征在于,所述软水的用量是核心成分质量总和的3倍。