CN102925009B - A kind of single-component single coating PP metallic paint and preparation method thereof - Google Patents
A kind of single-component single coating PP metallic paint and preparation method thereof Download PDFInfo
- Publication number
- CN102925009B CN102925009B CN201210480397.XA CN201210480397A CN102925009B CN 102925009 B CN102925009 B CN 102925009B CN 201210480397 A CN201210480397 A CN 201210480397A CN 102925009 B CN102925009 B CN 102925009B
- Authority
- CN
- China
- Prior art keywords
- component
- metallic paint
- single coating
- coating
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of single-component single coating PP metallic paint and preparation method thereof, prepared by the component of following weight percent content: silver powder 7%-10%, solvent 20%-30%, chlorinatedpolyolefins 40%-50%, vinylchlorid terpolymer 10%-20%, anti-settling wax slurry 6%-8%, silver powder is immersed in the solvent of 40 ~ 60wt%, chlorinatedpolyolefins, vinylchlorid terpolymer, anti-settling wax slurry is put in remaining solvent, and both mix and namely prepare single-component single coating PP metallic paint.Compared with prior art, the present invention has higher sticking power, and coating process is simple, and does not need to add curing agent component.
Description
Technical field
The present invention relates to a kind of metallic paint and preparation method thereof, especially relate to a kind of single-component single coating PP metallic paint and preparation method thereof.
Background technology
In automotive industry paint field, at present for the metallic paint of PP ground. be generally two components. two coating application techniques, both first Primer was sprayed, the two component metallic paint of spraying again, this kind of paint and coating process, the too expensive but spray cycles of cost is long. and technique is loaded down with trivial details, therefore, exploitation single coating single-component PP metallic paint becomes present problem demanding prompt solution, and disclosed by the invention is exactly a kind of single coating single-component PP metal and preparation method thereof.This kind of single coating single-component PP metallic paint meets the trend of current automotive industry paint field paint development.
Summary of the invention
Object of the present invention be exactly in order to overcome above-mentioned prior art exist defect and provide one not need to add curing agent component, sticking power good single-component single coating PP metallic paint and preparation method thereof.
Object of the present invention can be achieved through the following technical solutions:
A kind of single-component single coating PP metallic paint, is prepared by the component of following weight percent content:
Silver powder 7%-10%, solvent 20%-30%, chlorinatedpolyolefins 40%-50%, vinylchlorid terpolymer 10%-20%, anti-settling wax slurry 6%-8%.
Described solvent be selected from N-BUTYL ACETATE, dimethylbenzene or toluene one or more.
Described chlorinatedpolyolefins comprises the product that the commercially available trade mark is eastman-cp343-3, eastman-cp343-1 or eastman-cp164-1.
Described vinylchlorid terpolymer comprises the product that the commercially available trade mark is WACKER, E15/45M, H15/45M or LL4320.
Described anti-settling wax slurry is the polyethylene wax slurry of dispersion.
The trade mark that described anti-settling wax slurry is produced for De Qian company is the product of DeuRheo201, DeuRheo211, DeuRheo211F or DeuRheo202.
Described silver powder comprises the product that the commercially available trade mark is Toyal, TCR3040,4690NS, 6340NS or V160.
A preparation method for single-component single coating PP metallic paint, comprises the following steps:
(1) silver powder is soaked 5min in the solvent of 40 ~ 60wt%, and then with dispersion machine stir, controls stirring velocity is 300r/min, churning time be 15min to uniformity, making become component A;
(2) successively by chlorinatedpolyolefins, vinylchlorid terpolymer, anti-settling wax slurry put in remaining solvent, dispersion machine stirs, and controls stirring velocity is 1500r/min, churning time be 15min to uniformity, making become B component;
(3) component A is joined in B component, with dispersion machine stir, control stirring velocity is 1200r/min, churning time be 15min to uniformity, namely prepare single-component single coating PP metallic paint.
Compared with prior art, the present invention has the following advantages:
(1) there is higher sticking power;
(2) coating process is simple;
(3) the present invention is single-component, and matrix resin is chlorinatedpolyolefins and vinylchlorid terpolymer, in atmosphere from dry, so without the need to solidifying agent, can be coated with ETL estimated time of loading without the need to considering.
(4) improve the quality of products, improve product competitiveness.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1.
A preparation method for single-component single coating PP metallic paint, the method comprises following processing step:
(1) first drop into 7%V160,12% N-BUTYL ACETATE, soak 5min.And then with dispersion machine stir, stirring velocity is 300r/min, churning time be 15min to uniformity, make become component A.
(2) drop into the eastman-cp343-3 (25%) of 50% more successively, 10%E15/45M, the DeuRheo201 of 8%, 13% dimethylbenzene, dispersion machine stirs, and stirring velocity is 1500r/min, and churning time is that 15min is to uniformity.Making becomes B component.
(3) component A is joined in B component.With dispersion machine stir, stirring velocity is 1200r/min, churning time be 15min to uniformity, single-component single coating PP metallic paint.
Embodiment 2
A preparation method for high-effect water tolerance PP priming paint, the method comprises following processing step:
(1) first drop into 8%TCR3040,11% N-BUTYL ACETATE, soak 5mmin.And then with dispersion machine stir, stirring velocity is 300r/min, churning time be 15min to uniformity, make become component A.
(2) drop into the eastman-cp343-1 (50%) of 45% more successively, 15%H15/45M, the DeuRheo211 of 7%, 14% dimethylbenzene, dispersion machine stirs, and stirring velocity is 1500r/min, and churning time is that 15min is to uniformity.Making becomes B component.
(3) component A is joined in B component.With dispersion machine stir, stirring velocity is 1200r/min, churning time be 15min to uniformity, single-component single coating PP metallic paint.
Embodiment 3
A preparation method for high-effect water tolerance PP priming paint, the method comprises following processing step:
(1) first drop into 9%6340NS, 10% N-BUTYL ACETATE, soak 5min.And then with dispersion machine stir, stirring velocity is 300r/min, churning time be 15min to uniformity, make become component A.
(2) drop into the eastman-cp164-1 (25%) of 48% more successively, 12%LL4320, the DeuRheo202 of 6%, 15% toluene, dispersion machine stirs, and stirring velocity is 1500r/min, and churning time is that 15min is to uniformity.Making becomes B component.
(3) component A is joined in B component.With dispersion machine stir, stirring velocity is 1200r/min, churning time be 15min to uniformity, single-component single coating PP metallic paint.
Embodiment 4
A preparation method for single-component single coating PP metallic paint, comprises the following steps:
(1) the Toyal silver powder of 10kg is soaked 5min in the dimethylbenzene of 12kg, and then with dispersion machine stir, controls stirring velocity is 300r/min, churning time be 15min to uniformity, making become component A;
(2) successively anti-settling to chlorinatedpolyolefins eastman-cp343-3,14kg vinylchlorid terpolymer E15/45M, 6kg of 40kg wax slurry DeuRheo201 is put in the dimethylbenzene of 18kg, dispersion machine stirs, control stirring velocity is 1500r/min, churning time be 15min to uniformity, make become B component;
(3) component A is joined in B component, with dispersion machine stir, control stirring velocity is 1200r/min, churning time be 15min to uniformity, namely prepare single-component single coating PP metallic paint.
Embodiment 5
A preparation method for single-component single coating PP metallic paint, comprises the following steps:
(1) the 6340NS silver powder of 8kg is soaked 5min in the toluene of 10kg, and then with dispersion machine stir, controls stirring velocity is 300r/min, churning time be 15min to uniformity, making become component A;
(2) successively anti-settling to chlorinatedpolyolefins eastman-cpi64-1,20kg vinylchlorid terpolymer LL4320,7kg of 45kg wax slurry DeuRheo202 is put in the dimethylbenzene of 10kg, dispersion machine stirs, control stirring velocity is 1500r/min, churning time be 15min to uniformity, make become B component;
(3) component A is joined in B component, with dispersion machine stir, control stirring velocity is 1200r/min, churning time be 15min to uniformity, namely prepare single-component single coating PP metallic paint.
Claims (6)
1. a single-component single coating PP metallic paint, is characterized in that, this metallic paint is prepared by the component of following weight percent content:
Silver powder 7%-10%, solvent 20%-30%, chlorinatedpolyolefins 40%-50%, vinylchlorid terpolymer 10%-20%, anti-settling wax slurry 6%-8%;
Described chlorinatedpolyolefins comprises the product that the commercially available trade mark is eastman-cp343-3 or eastman-cp343-1, and described vinylchlorid terpolymer comprises the product that the commercially available trade mark is WACKER, E15/45M or H15/45M.
2. a kind of single-component single coating PP metallic paint according to claim 1, is characterized in that, described solvent be selected from N-BUTYL ACETATE, dimethylbenzene or toluene one or more.
3. a kind of single-component single coating PP metallic paint according to claim 1, is characterized in that, described anti-settling wax slurry is the polyethylene wax slurry of dispersion.
4. a kind of single-component single coating PP metallic paint according to claim 1 or 3, is characterized in that, the trade mark that described anti-settling wax slurry is produced for De Qian company is the product of DeuRheo201, DeuRheo211, DeuRheo211F or DeuRheo202.
5. a kind of single-component single coating PP metallic paint according to claim 1, it is characterized in that, described silver powder comprises the product that the commercially available trade mark is Toyal or TCR3040.
6. a preparation method for single-component single coating PP metallic paint as claimed in claim 1, it is characterized in that, the method comprises the following steps:
(1) silver powder is soaked 5min in the solvent of 40 ~ 60wt%, and then with dispersion machine stir, controls stirring velocity is 300r/min, churning time be 15min to uniformity, making become component A;
(2) successively by chlorinatedpolyolefins, vinylchlorid terpolymer, anti-settling wax slurry put in remaining solvent, dispersion machine stirs, and controls stirring velocity is 1500r/min, churning time be 15min to uniformity, making become B component;
(3) component A is joined in B component, with dispersion machine stir, control stirring velocity is 1200r/min, churning time be 15min to uniformity, namely prepare single-component single coating PP metallic paint.