CN102925007B - Automobile bumper bar coating with reflection and dazzling effects - Google Patents
Automobile bumper bar coating with reflection and dazzling effects Download PDFInfo
- Publication number
- CN102925007B CN102925007B CN201210480218.2A CN201210480218A CN102925007B CN 102925007 B CN102925007 B CN 102925007B CN 201210480218 A CN201210480218 A CN 201210480218A CN 102925007 B CN102925007 B CN 102925007B
- Authority
- CN
- China
- Prior art keywords
- coating
- reflective
- percent
- bar coating
- coloured effect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to an automobile bumper bar coating with the reflection and dazzling effects. The coating comprises the following raw materials in weight percent: 2-8 percent of chameleon nacrolacquer, 6-10 percent of reflecting coating dedicated glass powder, 10-20 percent of dimethylbenzene, 0.1-1 percent of wetting agent, 10-30 percent of resin, 30-50 percent of cellulose acetate butyrate, and 10-20 percent of butyl acetate. Compared with the prior art, the coating is richer in color, and has the colorful dazzling effect, so that an automobile adopting the coating and driving at night has the reflection effect in case of light illumination and has the obvious safety alarming function, as a result, a driver can be reminded to avoid a traffic accident; the changing colors can improve the value of the automobile itself; and moreover, coatings with different colors and effects can be made as per different requirements.
Description
Technical field
The present invention relates to a kind of coating, especially relate to a kind of with nerf bar coating that is reflective and fantasy coloured effect.
Background technology
At present; market nerf bar color mostly is pure color and metallic color two class; attractive in appearance; protection; be worth upper obviously not enough with embodiment automobile itself, color is too single to the visual impact of people, is also only protect automobile itself in protection; the height that can not rise to the life safety of protection automotive vehicle owner comes up, for shortcomings such as the value promoting automobile itself are not enough.
Summary of the invention
Object of the present invention is exactly provide a kind of nerf bar coating with reflective and fantasy coloured effect and preparation method thereof to overcome defect that above-mentioned prior art exists.
Object of the present invention can be achieved through the following technical solutions:
With a nerf bar coating that is reflective and fantasy coloured effect, this coating is made up of the raw material of following weight percent:
This coating is made up of the raw material of following weight percent:
Described reflective coating special glass powder is the mixture of plumbous oxide, silicon-dioxide and titanium dioxide.
Described wetting agent is selected from commercially available BYK110 or BYK161.
Described resin is acrylic resin.
Described cellulose acetate butyrate is selected from one or more in commercially available CAB381-0.5 or CAB381-1.
With a preparation method for the nerf bar coating of reflective and fantasy coloured effect, this preparation method comprises the following steps:
(1) chameleon nacrolacquer, reflective coating special glass powder, dimethylbenzene and wetting agent are added in container successively, stir into pasty state, prepare the first component;
(2) resin, cellulose acetate butyrate and N-BUTYL ACETATE are added in the first component successively, under the stirring velocity of 1000-2000 rev/min, stir and obtain product.
Compared with prior art, the present invention has the following advantages:
One, color is abundanter, and with the fantasy coloured effect of seven color variable colors;
Two, automobile is when night running, has reflecting effect after irradiate light, with obvious safe warning function, reminds motorist in time, avoid traffic accident;
Three, seven color colors of change can promote the value of automobile itself;
Four, the coating of different color and effect can be made according to different requirement.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1
With a nerf bar coating that is reflective and fantasy coloured effect, this coating is made up of the raw material of following weight percent: chameleon nacrolacquer 4, reflective coating special glass powder 8, dimethylbenzene 17.6, BYK110 0.4, acrylic resin (Bayer450) 20, cellulose acetate butyrate (CAB381-0.5) 40, N-BUTYL ACETATE 10.
Wherein, reflective coating special glass powder is the mixture of plumbous oxide, silicon-dioxide and titanium dioxide.
With a preparation method for the nerf bar coating of reflective and fantasy coloured effect, this preparation method comprises the following steps:
(1) chameleon nacrolacquer, reflective coating special glass powder, dimethylbenzene and wetting agent are added in container successively, stir into pasty state, prepare the first component;
(2) resin, cellulose acetate butyrate and N-BUTYL ACETATE are added in the first component successively, under the stirring velocity of 1000 revs/min, stir and obtain product.
Embodiment 2
With a nerf bar coating that is reflective and fantasy coloured effect, this coating is made up of the raw material of following weight percent: chameleon nacrolacquer 3, reflective coating special glass powder 6, dimethylbenzene 10, wetting agent (BYK161) 1, acrylic resin (nuplex1385) 30, cellulose acetate butyrate (CAB381-1) 30, N-BUTYL ACETATE 20.Wherein, reflective coating special glass powder is the mixture of plumbous oxide, silicon-dioxide and titanium dioxide.
With a preparation method for the nerf bar coating of reflective and fantasy coloured effect, comprise the following steps:
(1) chameleon nacrolacquer, reflective coating special glass powder, dimethylbenzene and wetting agent are added in container successively, stir into pasty state, prepare the first component;
(2) resin, cellulose acetate butyrate and N-BUTYL ACETATE are added in the first component successively, under the stirring velocity of 1500 revs/min, stir and obtain product.
Embodiment 3
With a nerf bar coating that is reflective and fantasy coloured effect, this coating is made up of the raw material of following weight percent: chameleon nacrolacquer 8, reflective coating special glass powder 10, dimethylbenzene 11, wetting agent (BYK161) 1, acrylic resin (nuplex1385) 10, the cellulose acetate butyrate mixture of 1: 1 (CAB381-0.5 and the CAB381-1 by weight) 50, N-BUTYL ACETATE 10.
With a preparation method for the nerf bar coating of reflective and fantasy coloured effect, comprise the following steps:
(1) chameleon nacrolacquer, reflective coating special glass powder, dimethylbenzene and wetting agent are added in container successively, stir into pasty state, prepare the first component,
(2) resin, cellulose acetate butyrate and N-BUTYL ACETATE are added in the first component successively, under the stirring velocity of 2000 revs/min, stir and obtain product.
Embodiment 4
With a nerf bar coating that is reflective and fantasy coloured effect, this coating is made up of the raw material of following weight percent: chameleon nacrolacquer 2, reflective coating special glass powder 10, dimethylbenzene 20, wetting agent (BYK161) 0.1, acrylic resin (nuplex1385) 20, cellulose acetate butyrate (CAB381-1) 33, N-BUTYL ACETATE 14.9.Wherein, reflective coating special glass powder is the mixture of plumbous oxide, silicon-dioxide and titanium dioxide.
With a preparation method for the nerf bar coating of reflective and fantasy coloured effect, comprise the following steps:
(1) chameleon nacrolacquer, reflective coating special glass powder, dimethylbenzene and wetting agent are added in container successively, stir into pasty state, prepare the first component;
(2) resin, cellulose acetate butyrate and N-BUTYL ACETATE are added in the first component successively, under the stirring velocity of 1800 revs/min, stir and obtain product.
Claims (5)
1., with a nerf bar coating that is reflective and fantasy coloured effect, it is characterized in that, this coating is made up of the raw material of following weight percent:
Described resin is acrylic resin;
Described reflective coating special glass powder is the mixture of plumbous oxide, silicon-dioxide and titanium dioxide.
2. according to claim 1 a kind of with nerf bar coating that is reflective and fantasy coloured effect, it is characterized in that, this coating is made up of the raw material of following weight percent:
3. according to claim 1 and 2 a kind of with nerf bar coating that is reflective and fantasy coloured effect, it is characterized in that, described wetting agent is selected from commercially available BYK110 or BYK161.
4. according to claim 1 and 2 a kind of with nerf bar coating that is reflective and fantasy coloured effect, it is characterized in that, described cellulose acetate butyrate is selected from commercially available CAB381-0.5.
5., as a preparation method for the nerf bar coating with reflective and fantasy coloured effect according to claim 1 and 2, it is characterized in that, this preparation method comprises the following steps:
(1) chameleon nacrolacquer, reflective coating special glass powder, dimethylbenzene and wetting agent are added in container successively, stir into pasty state, prepare the first component;
(2) resin, cellulose acetate butyrate and N-BUTYL ACETATE are added in the first component successively, under the stirring velocity of 1000-2000 rev/min, stir and obtain product.