CN102922166A - 高熔敷效率金属粉芯药芯焊丝 - Google Patents
高熔敷效率金属粉芯药芯焊丝 Download PDFInfo
- Publication number
- CN102922166A CN102922166A CN2012104208495A CN201210420849A CN102922166A CN 102922166 A CN102922166 A CN 102922166A CN 2012104208495 A CN2012104208495 A CN 2012104208495A CN 201210420849 A CN201210420849 A CN 201210420849A CN 102922166 A CN102922166 A CN 102922166A
- Authority
- CN
- China
- Prior art keywords
- flux
- cored
- cored wire
- metal powder
- deposition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种药芯焊丝,具体涉及一种高熔敷效率金属粉芯药芯焊丝。本发明所述的高熔敷效率金属粉芯药芯焊丝,包括药芯,其药芯组分全部由金属粉构成,以质量百分比计,药芯配料组成为:钛铁1.0-3.0%、电解锰2.0-6.0%、75#硅铁1.0-5.0%、中碳锰铁3.0-8.0%、硅锆铁2.0-5.0%,余量为还原铁粉。本发明提供的高熔敷效率金属粉芯药芯焊丝,配合富氩气体保护,其熔敷效率可达98%以上,并且电弧稳定、飞溅极小、焊缝成型美观,熔敷金属扩散氢含量低于4ml/100g,力学性能优良。其焊接工艺好,可大幅提高生产效率,缩短生产周期。该焊丝适于船舶,桥梁等领域的结构钢及低合金钢的平焊及平角焊。
Description
技术领域
本发明涉及一种药芯焊丝,具体涉及一种高熔敷效率金属粉芯药芯焊丝。
背景技术
药芯焊丝是一种新型焊接材料,是由钢带包覆药芯,经过轧制,拔制成产品。现有的药芯焊丝为了保证焊接工艺性能及焊缝成型美观,或多或少在药芯中加入矿物粉及化工产品稳弧剂,在焊接时,容易生成焊渣,降低了药芯焊丝的熔敷效率。
发明内容
本发明的目的在于提供一种高熔敷效率金属粉芯药芯焊丝,其熔敷效率可达98%以上,并且电弧稳定、飞溅极小、焊缝成型美观,力学性能优良。
本发明所述的高熔敷效率金属粉芯药芯焊丝,包括药芯,其药芯组分全部由金属粉构成,以质量百分比计,药芯配料组成为:钛铁1.0-3.0%、电解锰2.0-6.0%、75#硅铁1.0-5.0%、中碳锰铁3.0-8.0%、硅锆铁2.0-5.0%,余量为还原铁粉。
所述的药芯占药芯焊丝总质量的24.0-30.0%。
所述的药芯各组分粒度为60目全通过,小于60目的不大于5wt.%,大于180目的不大于15wt.%。
本发明是富氩气体保护的金属粉芯药芯焊丝,使用药芯焊丝专用低碳钢带即可。例如可以使用首钢生产的牌号为HS1冷轧钢。
药芯各组分成分如下:
(1)钛铁:Ti含量为38-42wt.%、C含量为<0.2wt.%;
(2)电解锰:Mn含量为>99wt.%、C含量为<0.1wt.%;
(3)75#硅铁:Si含量为73-77wt.%、C含量为<0.3wt.%;
(4)中碳锰铁:Mn含量为>80wt.%、C含量为<1.0wt.%;
(5)硅锆铁:Si含量为45-50wt.%、Zr含量为35-40wt.%、C含量为<0.1wt.%;
(6)还原铁粉:Fe含量为>98%、C含量为<0.04wt.%。
本发明药芯焊丝焊接时所用富氩保护气为氩气与二氧化碳的混合气体,以体积百分比计,氩气为80-85%,二氧化碳为15-20%,氩气纯度,Ar≥99.9wt.%;二氧化碳中:CO2≥99.5wt.%,H2O<0.3wt.%。
与现有技术相比,本发明的有益效果如下:
本发明提供的高熔敷效率金属粉芯药芯焊丝,配合富氩气体保护,其熔敷效率可达98%以上,并且电弧稳定、飞溅极小、焊缝成型美观,熔敷金属扩散氢含量低于4.0ml/100g,力学性能优良。其焊接工艺好,可大幅提高生产效率,缩短生产周期。该焊丝适于船舶,桥梁等领域的结构钢及低合金钢的平焊及平角焊。
具体实施方式
以下结合实施例对本发明作进一步描述。
实施例1
本发明所述的高熔敷效率金属粉芯药芯焊丝,包括药芯,其药芯组分全部由金属粉构成,以质量百分比计,药芯配料组成为:钛铁1.0%、电解锰5.8%、75#硅铁4.8%、中碳锰铁3.6%、硅锆铁3.8%,余量为还原铁粉;药芯占药芯焊丝总质量的30.0%;药芯各组分粒度60目全通过,粒度小于60目的为5wt.%,大于180目为6wt.%。焊丝直径1.2mm,在焊接电压30V,焊接电流230A条件下施焊的熔敷效率为98.2%,熔敷金属扩散氢含量为3.0ml/100g。
实施例2
本发明所述的高熔敷效率金属粉芯药芯焊丝,包括药芯,其药芯组分全部由金属粉构成,以质量百分比计,药芯配料组成为:钛铁3.0%、电解锰2.4%、75#硅铁1.5%、中碳锰铁7.0%、硅锆铁2.4%,余量为还原铁粉;药芯占药芯焊丝总质量的25.5%;药芯各组分粒度60目全通过,粒度小于60目的为5wt.%,大于180目为8wt.%。焊丝直径1.2mm,在焊接电压30V,焊接电流230A条件下施焊的熔敷效率为98.4%,熔敷金属扩散氢含量为3.5ml/100g。
实施例3
本发明所述的高熔敷效率金属粉芯药芯焊丝,包括药芯,其药芯组分全部由金属粉构成,以质量百分比计,药芯配料组成为:钛铁2.4%、电解锰3.2%、75#硅铁2.4%、中碳锰铁6.0%、硅锆铁4.2%,余量为还原铁粉;药芯占药芯焊丝总质量的26.0%;药芯各组分粒度60目全通过,粒度小于60目的为4wt.%,大于180目为8wt.%。焊丝直径1.6mm,在焊接电压32V,焊接电流240A条件下施焊的熔敷效率为98.4%,熔敷金属扩散氢含量为3.6ml/100g。
实施例4
本发明所述的高熔敷效率金属粉芯药芯焊丝,包括药芯,其药芯组分全部由金属粉构成,以质量百分比计,药芯配料组成为:钛铁1.8%、电解锰4.8%、75#硅铁3.1%、中碳锰铁4.6%、硅锆铁3.0%,余量为还原铁粉;药芯占药芯焊丝总质量的24.2%;药芯各组分粒度60目全通过,粒度小于60目的为3wt.%,大于180目为6wt.%。焊丝直径1.2mm,在焊接电压30V,焊接电流230A条件下施焊的熔敷效率为98.6%,熔敷金属扩散氢含量为3.3ml/100g。
实施例5
本发明所述的高熔敷效率金属粉芯药芯焊丝,包括药芯,其药芯组分全部由金属粉构成,以质量百分比计,药芯配料组成为:钛铁1.4%、电解锰2.0%、75#硅铁5.0%、中碳锰铁7.8%、硅锆铁5.0%,余量为还原铁粉;药芯占药芯焊丝总质量的27.8%;药芯各组分粒度60目全通过,粒度小于60目的为3wt.%,大于180目为10wt.%。焊丝直径1.6mm,在焊接电压30V,焊接电流230A条件下施焊的熔敷效率为98.3%,熔敷金属扩散氢含量为3.2ml/100g。
实施例1-5中所有物质均为市售产品,优选如下厂家的产品,具体如下:
钛铁:牌号FeTi40-A,Ti含量为40wt.%、C含量为0.08wt.%,锦州运海金属粉末加工有限公司产品。
电解锰:Mn含量为99.2wt.%、C含量为0.06wt.%,锦州运海金属粉末加工有限公司产品。
75#硅铁:Si含量为76.2wt.%、C含量为0.26wt.%;锦州运海金属粉末加工有限公司产品。
中碳锰铁:Mn含量为80.5wt.%、C含量为0.8wt.%;锦州运海金属粉末加工有限公司产品。
硅锆铁:Si含量为46.2wt.%、Zr含量为38.3wt.%、C含量为0.06wt.%;南京国鼎有色金属有限公司产品。
还原铁粉:Fe含量为98.3%、C含量为0.02wt.%;武钢集团粉末冶金公司产品。
Claims (3)
1.一种高熔敷效率金属粉芯药芯焊丝,包括药芯,其特征在于:药芯组分全部由金属粉构成,以质量百分比计,药芯配料组成为:钛铁1.0-3.0%、电解锰2.0-6.0%、75#硅铁1.0-5.0%、中碳锰铁3.0-8.0%、硅锆铁2.0-5.0%,余量为还原铁粉。
2.根据权利要求1所述的高熔敷效率金属粉芯药芯焊丝,其特征在于:所述的药芯占药芯焊丝总质量的24.0-30.0%。
3.根据权利要求1或2所述的高熔敷效率金属粉芯药芯焊丝,其特征在于:所述的药芯各组分粒度为60目全通过,小于60目的不大于5wt.%,大于180目的不大于15wt.%。