CN102921760A - Machining process for metal handicraft wire with plating layer - Google Patents
Machining process for metal handicraft wire with plating layer Download PDFInfo
- Publication number
- CN102921760A CN102921760A CN2012103913065A CN201210391306A CN102921760A CN 102921760 A CN102921760 A CN 102921760A CN 2012103913065 A CN2012103913065 A CN 2012103913065A CN 201210391306 A CN201210391306 A CN 201210391306A CN 102921760 A CN102921760 A CN 102921760A
- Authority
- CN
- China
- Prior art keywords
- wire rod
- metal
- handicrafts
- metal handicrafts
- processing technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a machining process for a metal handicraft wire with a plating layer. The machining process comprises the following steps of: (A) pretreating the surface of the metal handicraft wire; (B) putting the pretreated metal handicraft wire into electroplating liquid with a plated metal, which is different from the original metal in color; and electroplating the pretreated metal handicraft wire so as to obtain the metal handicraft wire with the plating layer; and (C) turning and milling the metal handicraft wire with the plating layer, so that sunken grains with metal colors are exposed on the surface. The metal handicraft wire prepared by adopting the process disclosed by the invention has the advantages as follows: the metal color of the plating layer is obtained and the sunken grains also have metal color of the original metal handicraft wire; in particular, when being illuminated with lights, metal colors with different layers are shown, so that the artistic values of the handicraft woven by the raw materials are enhanced.
Description
Technical field
What the present invention relates to is a kind of processing technology of metal wire rod, says more specifically the processing technology of the coated metal handicrafts wire rod of a kind of tool.
Background technology
Handicraft: namely by craft or machine with the product that raw material or semi-finished product process, be the general name that is worth the art work to a group.Braiding is one of ancient handicraft of human beings, and the knitting of metal handicrafts wire rod is a kind of modern technology that adopts the metal handicrafts wire rod to weave, it can be woven into various colourful daily necessitiess, can also be woven into various adornments with art collection value or artistic decoration effect.
And the braiding raw material of the most metals craft woven product different metal handicrafts wire rod that is various cross sections, they otherwise only change the cross sectional shape of metal handicrafts wire rod, be that circular metal handicraft wire rod, cross section are that metal handicrafts wire rod or the cross section of flat is curved metal handicrafts wire rod such as the cross section; Only change the superficial layer of metal wire rod, such as its superficial layer being electroplated or its superficial layer being painted, perhaps its surface is electroplated and mirror finish; But the metal handicrafts wire rod that adopts these techniques to make, the sense organ that shows can be more single, third dimension and stereovision have been lacked, particularly under the cooperation irradiation of light, because the metal handicrafts wire rod does not have third dimension, and stereovision is more single, will reduce as the value of art appreciation of whole artifacts of material knitting one-tenth.
Summary of the invention
The invention provides the processing technology of the coated metal handicrafts wire rod of a kind of tool, it is more single that its purpose is to overcome the metal wire rod that prior art exists, and lacks without stereovision and relief deficiency and shortcoming.
The technical solution used in the present invention is as follows:
The processing technology of the coated metal handicrafts wire rod of a kind of tool, this processing technology comprises the steps:
A carries out pre-treatment with the surface of metal handicrafts wire rod;
B will put into the electroplate liquid that has with the coated metal of virgin metal true qualities different colours through the metal handicrafts wire rod after the pre-treatment and carry out electroplating processes, obtain the coated metal handicrafts wire rod of tool;
C implements turnning and milling processing to the coated metal wire rod of tool, makes the surface of metal handicrafts wire rod manifest the depression texture that sparkles with its virgin metal gloss;
Further improve as of the present invention, the material that the metal handicrafts wire rod in the described steps A adopts is that the cross section is circular zinc metal handicrafts wire rod.
Further improve as of the present invention, the material that the metal handicrafts wire rod in the described steps A adopts is that the cross section is the zinc metal handicrafts wire rod of prolate shape.
Further improve as of the present invention, the processing technology of described zinc metal handicrafts wire rod also comprises step D: above-mentioned zinc metal handicrafts wire rod with depression texture is twisted spiral processing, make this zinc metal handicrafts wire rod in the shape of a spiral.
Further improve as of the present invention, the coated metal material among the described step B is gold, perhaps copper, perhaps nickel.
Further improve as of the present invention, the thickness of coating of the metal handicrafts wire rod among the described step B is between 15 microns to 30 microns.
Further improve as of the present invention, the depression texture on the metal handicrafts wire rod among the described step C distributes in the shape of a spiral, and its helical form depression texture is spaced apart at same visual angle.
By the above-mentioned description of this invention as can be known, be compared with existing technology, the invention has the advantages that:
1, the present invention processes the metal handicrafts wire rod with coating and depression texture by after the metal handicrafts wire rod is carried out various plating and turnning and milling technique, makes its whole metal handicrafts wire rod have third dimension and stereovision.
2, the metal handicrafts wire rod of producing by technique of the present invention, not only sparkle with the metallic luster of coating, and its depression texture also sparkles with the metallic luster of virgin metal handicraft wire rod, particularly under the cooperation irradiation of light, more can show the bright gloss of metal of its different levels that have, improve the artistic value of the handicraft that weaves as raw material.
3, manufacture craft of the present invention is unique, and simple and practical, has very high marketing prospect.
Description of drawings
Fig. 1 is that its cross section of the present invention is circular structural representation.
Fig. 2 is the cross-sectional view of A-A direction among Fig. 1.
Fig. 3 is that its cross section of the present invention is the structural representation of prolate shape
The specific embodiment
Embodiment one
As shown in Figure 1 and Figure 2, the processing technology of the coated metal handicrafts wire rod of a kind of tool, this processing technology comprises the steps:
A carries out pre-treatment with its cross section for the surface of circular zinc metal handicrafts wire rod 1;
B will put into the electroplate liquid that has with the nickel metal of zinc metal true qualities different colours through the zinc metal handicrafts wire rod 1 after the pre-treatment and carry out electroplating processes, obtain having the zinc metal handicrafts wire rod 1 of nickel coating 2, the thickness of its metal-plated nickel dam 2 is between 15 microns to 30 microns;
C implements turnning and milling processing to the zinc metal handicrafts wire rod 1 with nickel coating 2, make the surface of zinc metal handicrafts wire rod 1 manifest the depression texture 3 that sparkles with its metallic luster, this depression texture 3 can be to be difform distribution at this zinc metal handicrafts wire rod 1, such as distributing in the shape of a spiral, it also can be the distribution that is around shape, or carry out turnning and milling according to the actual design effect, make it surperficial different distributions shape; And the zinc metal handicrafts wire rod 1 that depression texture 3 distributes in the shape of a spiral its depression texture 3 on same visual angle is spaced apart.
Embodiment two
As shown in Figure 3, the processing technology of the coated metal handicrafts wire rod of a kind of tool, this processing technology comprises the steps:
A is that pre-treatment is carried out on the surface of the zinc metal handicrafts wire rod 1 of prolate shape with its cross section;
B will put into the electroplate liquid that has with the nickel metal of zinc metal true qualities different colours through the zinc metal handicrafts wire rod 1 after the pre-treatment and carry out electroplating processes, obtain having the zinc metal handicrafts wire rod 1 of nickel coating 2, the thickness of its metal-plated nickel dam 2 is between 15 microns to 30 microns;
C implements turnning and milling processing to the zinc metal handicrafts wire rod 1 with nickel coating 2, make the surface of zinc metal handicrafts wire rod 1 manifest the depression texture 3 that sparkles with its silvery white metallic luster, this depression texture 3 is difform distribution at zinc metal handicrafts wire rod 1, such as distributing in the shape of a spiral, it also can be the distribution that is around shape, or carry out turnning and milling according to the actual design effect, make it surperficial different distributions shape; And the zinc metal handicrafts wire rod 1 that depression texture 3 distributes in the shape of a spiral its depression texture 3 on same visual angle is spaced apart;
D twists spiral processing to above-mentioned zinc metal handicrafts wire rod 1 with depression texture 3, makes this zinc metal handicrafts wire rod 1 in the shape of a spiral.
This metal handicrafts wire rod can comprise: the various metal handicrafts wire rods that have metallic luster and be difficult in the open getting rusty such as zinc, aluminium, kirsite, aluminium alloy, and the coated metal material of this metal handicrafts wire rod comprises: the non-ferrous metals such as gold, copper, nickel.
The handicraft that forms as raw material weaves take this metal handicrafts wire rod, particularly under the cooperation irradiation of light, not only sparkle with the gloss of coated metal, but also sparkle with the gloss of virgin metal handicraft wire rod, and the metal handicrafts wire rod more because turnning and milling is processed with the depression texture 3 of difformity texture, makes it have different stereovision and third dimension, and it is single to change in the past metal wire rod performance, the shortcoming that does not have stereovision allows whole handicraft have more value of art appreciation.
Above-mentioned only is the specific embodiment of the present invention, but design concept of the present invention is not limited to this, allly utilizes this design that the present invention is carried out the change of unsubstantiality, all should belong to the behavior of invading protection domain of the present invention.
Claims (7)
1. the processing technology of the coated metal handicrafts wire rod of tool is characterized in that comprising the steps:
A. pre-treatment is carried out on the surface of metal handicrafts wire rod;
B. will put into the plating C. liquid that has with the coated metal of virgin metal true qualities different colours through the metal handicrafts wire rod after the pre-treatment and carry out electroplating processes, obtain the coated metal handicrafts wire rod of tool;
C. the coated metal wire rod of tool is implemented turnning and milling processing, make the surface of metal handicrafts wire rod manifest the depression texture that sparkles with its virgin metal gloss.
2. the processing technology of the coated metal handicrafts wire rod of a kind of tool according to claim 1 is characterized in that: the material that the metal handicrafts wire rod in the described steps A adopts is that the cross section is circular zinc metal handicrafts wire rod.
3. the processing technology of the coated metal handicrafts wire rod of a kind of tool according to claim 1 is characterized in that: the material that the metal handicrafts wire rod in the described steps A adopts is that the cross section is the zinc metal handicrafts wire rod of prolate shape.
4. the processing technology of the coated metal handicrafts wire rod of a kind of tool according to claim 3, it is characterized in that: the processing technology of described zinc metal handicrafts wire rod also comprises step D: above-mentioned zinc metal handicrafts wire rod with depression texture is twisted spiral processing, make this zinc metal handicrafts wire rod in the shape of a spiral.
5. the processing technology of the coated metal handicrafts wire rod of a kind of tool according to claim 1 is characterized in that: the coated metal material among the described step B is gold, perhaps copper, perhaps nickel.
6. the processing technology of the coated metal handicrafts wire rod of a kind of tool according to claim 1, it is characterized in that: the thickness of coating of the metal handicrafts wire rod among the described step B is between 15 microns to 30 microns.
7. the processing technology of the coated metal handicrafts wire rod of a kind of tool according to claim 1, it is characterized in that: the depression texture on the metal handicrafts wire rod among the described step C distributes in the shape of a spiral, and its helical form depression texture is spaced apart at same visual angle.