CN102898845B - Anti-corrosion anti-rust wax composition for surface of automobile engine - Google Patents
Anti-corrosion anti-rust wax composition for surface of automobile engine Download PDFInfo
- Publication number
- CN102898845B CN102898845B CN201210339656.7A CN201210339656A CN102898845B CN 102898845 B CN102898845 B CN 102898845B CN 201210339656 A CN201210339656 A CN 201210339656A CN 102898845 B CN102898845 B CN 102898845B
- Authority
- CN
- China
- Prior art keywords
- wax composition
- kerosene
- automobile engine
- solvent oil
- rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses an anti-corrosion anti-rust wax composition for the surface of an automobile engine. The anti-corrosion anti-rust wax composition comprises, by mass, 5 to 6% of fully refining No. 70 paraffin, 2% of gum rosin, 1 to 2% of C9 petroleum resin, 4 to 3% of polyethylene, 2 to 3% of ethyl cellulose, 2 to 2.5% of ethene-vinyl acetate copolymer, 2% of silica bentonite, 5 to 7% of kerosene, 1 to 2% of aluminum powder and 0.5 to 1% of 2,6-di-tert-butyl-4-methylphenol, with the balance being No. 200 white solvent naphtha. The liquid anti-corrosion anti-rust wax composition for the surface of an automobile engine has stable performance and good high temperature resistance, does not influence the performance and the service life of a non-steel protective member of an automobile engine and guarantees high efficiency working of the engine.
Description
Technical field
The present invention relates to a kind of motor car engine surface anticorrosion rust-proofing wax composition.
Background technology:
Motor car engine surface anticorrosion rust-proofing wax requires the stable performance of wax liquid, particularly has good resistance to elevated temperatures, and on protection rubber parts, plastic component and the nonferrous materials of motor car engine without impact, be difficult for adhering to.
Motor car engine surface spray coating process is conventionally arranged in the antiseptic and rustproof wax of car body surface and completes in same post, and post conditional request and car body surface antirust, anti-corrosive wax phase are same.
Summary of the invention
The technical problem to be solved in the present invention be to provide a kind of there is good resistance to elevated temperatures and on protection rubber parts, plastic component and the nonferrous materials on motor car engine surface without impact, the motor car engine surface anticorrosion rust-proofing wax composition be difficult for adhering to.
The present invention solves the problems of the technologies described above with following technical scheme:
Component and the mass percent of motor car engine surface anticorrosion rust-proofing wax composition are:
| Component | Content (mass percent) |
| Complete refining No. 70 paraffin | 5%-6% |
| Gum resin | 2% |
| C 9 petroleum resin | 1%-2% |
| Polyethylene | 4%-3% |
| Ethyl cellulose | 2%-3% |
| Vinyl-vinyl acetate copolymer | 2%-2.5% |
| Silicon-dioxide wilkinite | 2% |
| Kerosene | 5%-7% |
| Aluminium powder | 1%-2% |
| 2.6-ditertbutylparacresol | 0.5%-1% |
| 200# white solvent oil | Surplus |
The preparation method of motor car engine surface anticorrosion rust-proofing wax composition of the present invention is: will account for white solvent oil and the wax fusing of total mass 1/3rd, and be heated to 100-110 ℃, and under 30r-50r/min, constantly stir; Then the additive except kerosene is all added, and is heated to 120-125 ℃, with the same speed be constantly stirred to completely dispersed till; The white solvent oil that adds again surplus, constantly stirs and is cooled to room temperature, finally adds kerosene to stir 1h, static 24h.
Motor car engine surface anticorrosion rust-proofing wax composition of the present invention; by application Fuzzy AHP, select raw material and determine formula; the product wax liquid stable performance of preparing; resistance to elevated temperatures is good; do not affect performance and the life-span of the non-steel guard member of motor car engine, guaranteed the efficiency operation of engine.
Embodiment:
Embodiment 1:
Motor car engine surface anticorrosion rust-proofing wax composition is in harmonious proportion and is formed by following component and mass percent:
| Component | Content (mass percent) |
| Complete refining No. 70 paraffin | 5% |
| Gum resin | 2% |
| C 9 petroleum resin | 1% |
| Polyethylene | 3% |
| Ethyl cellulose | 2% |
| Vinyl-vinyl acetate copolymer | 2% |
| Silicon-dioxide wilkinite | 2% |
| Kerosene | 5% |
| Aluminium powder | 1% |
| 2.6-ditertbutylparacresol | 0.5% |
| 200# white solvent oil | 76.5% |
Embodiment 2:
Motor car engine surface anticorrosion rust-proofing wax composition is in harmonious proportion and is formed by following component and mass percent:
| Component | Content (mass percent) |
| Complete refining No. 70 paraffin | 5.5% |
| Gum resin | 2% |
| C 9 petroleum resin | 1.5% |
| Polyethylene | 3.5% |
| Ethyl cellulose | 2.5% |
| Vinyl-vinyl acetate copolymer | 2.3% |
| Silicon-dioxide wilkinite | 2% |
| Kerosene | 6% |
| Aluminium powder | 1.5% |
| 2.6-ditertbutylparacresol | 0.7% |
| 200# white solvent oil | 72.5% |
Embodiment 3:
Motor car engine surface anticorrosion rust-proofing wax composition is in harmonious proportion and is formed by following component and mass percent:
| Component | Content (mass percent) |
| Complete refining No. 70 paraffin | 6% |
| Gum resin | 2% |
| C 9 petroleum resin | 2% |
| Polyethylene | 4% |
| Ethyl cellulose | 3% |
| Vinyl-vinyl acetate copolymer | 2.5% |
| Silicon-dioxide wilkinite | 2% |
| Kerosene | 7% |
| Aluminium powder | 2% |
| 2.6-ditertbutylparacresol | 1% |
| 200# white solvent oil | 68.5% |
Through relevant department's check, the technical target of the product of embodiment 3 is as follows:
Claims (1)
1. a motor car engine surface anticorrosion rust-proofing wax composition, is characterized in that being comprised of following component and mass percent:
Its preparation process is:
200# white solvent oil and the wax fusing that will account for total mass 1/3rd, be heated to 100-110 ℃, under 30r-50r/min, constantly stirs; Then the additive except kerosene is all added, and is heated to 120-125 ℃, be constantly stirred to completely dispersed till; The 200# white solvent oil that adds again surplus, constantly stirs and is cooled to room temperature, finally adds kerosene to stir 1h, static 24h.