CN102898730A - Rubber material for high temperature-resistant conveyer belt and manufacturing method thereof - Google Patents
Rubber material for high temperature-resistant conveyer belt and manufacturing method thereof Download PDFInfo
- Publication number
- CN102898730A CN102898730A CN2012103354494A CN201210335449A CN102898730A CN 102898730 A CN102898730 A CN 102898730A CN 2012103354494 A CN2012103354494 A CN 2012103354494A CN 201210335449 A CN201210335449 A CN 201210335449A CN 102898730 A CN102898730 A CN 102898730A
- Authority
- CN
- China
- Prior art keywords
- antioxidant
- high temperature
- conveyer belt
- conveyor belt
- elastomeric material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a conveyer belt and especially to a rubber material for a high temperature-resistant conveyer belt and a manufacturing method thereof. The invention aims to provide the rubber material for the high temperature-resistant conveyer belt to allow rubber of the conveyer belt not to be melted at a temperature of 180 DEG C and the conveyer belt to normally work at the temperature and the manufacturing method for the rubber material. The rubber material comprises ethylene propylene diene monomer, carbon black, nanometer zinc oxide, stearic acid, dicumyl peroxide, a co-crosslinking agent, a crosslinking agent, a promoter CZ, a promoter MDB, an antioxidant MB, an antioxidant 264,an antioxidant RD, an antioxidant 4020, polybutene, a tackifying resin PN-110, tackifier reaction type methacrylate, magnesium oxide, a dispersant and special paraffin hydrocarbon oil. According to the invention, the co-crosslinking agent, the crosslinking agent, the promoter MDB and the special paraffin hydrocarbon oil are added to the high temperature-resistant conveyer belt on the basis of an original conveyer belt, so the conveyer belt manufactured in the invention has better high temperature resistance.
Description
Technical field
The present invention relates to conveying belt, it is arranged is a kind of elastomeric material and manufacture method thereof of high temperature-resistance conveyor belt.
Background technology
Conveying belt is as the term suggests be a kind of special tool for transmitting article.The kind of conveying belt is a lot, and it has different functions according to required Working environment, such as high temperature-resistance conveyor belt.
Employed conveying belt in steel mill, cement mill or coke-oven plant, owing to it is worked under the environment of the high temperature of being everlasting, so conveying belt must have resistant to elevated temperatures characteristic.Present conveying belt is mainly due to employed elastomeric material non-refractory, thereby the resistant to elevated temperatures effect of the conveying belt of producing and using on the market is relatively poor, can not be up to state standards 175 degrees centigrade requirement, therefore, during this type of conveying belt uses, life-span is shorter, because in steel mill, cement mill or coke-oven plant, very frequent of the use of conveying belt, therefore, in case ruptured belt or other problems occurs then can bring very large impact to the production of enterprise directly causes the financial loss of enterprise.
Summary of the invention
The objective of the invention is to provide for the deficiency that solves above-mentioned technology a kind of in the time of 180 ℃ the rubber of conveying belt do not melt and elastomeric material and the manufacture method thereof of a kind of high temperature-resistance conveyor belt that can work.
In order to achieve the above object, the elastomeric material of a kind of high temperature-resistance conveyor belt that the present invention is designed, it comprises 100-150 part terpolymer EP rubber, 40-80 part carbon black, 2-5 part nano zine oxide, 1-3 part stearic acid, 1-5 part dicumyl peroxide, 1-3 part co-crosslinker, 0.1-1.5 part linking agent, 2-6 part promotor, 4-12 part anti-aging agent, 5-10 part polybutene, 2-12 part tackifying resin, the reactive methacrylic acid salt of 5-15 part tackifier, 5-10 part magnesium oxide, 2-8 part dispersion agent and the special-purpose paraffin hydrocarbon ils of 3-15 part, and above-described umber by weight ratio.
As preferably, described promotor is comprised of accelerant CZ and captax DB.
Described anti-aging agent is comprised of antioxidant MB, antioxidant 264, anti-aging agent RD and antioxidant 4020.
As preferably, described antioxidant MB is that 1-3 part, antioxidant 264 are that 1-3 part, anti-aging agent RD are that 1-3 part, antioxidant 4020 are 1-3 part.
As preferably, described tackifying resin is tackifying resin PN-110.
A kind of manufacture method of elastomeric material of high temperature-resistance conveyor belt: the first step, terpolymer EP rubber and dispersion agent were reacted 60 seconds under 50 ℃; Second step adds nano zine oxide, stearic acid, accelerant CZ, antioxidant MB, antioxidant 264, anti-aging agent RD, antioxidant 4020, the reactive methacrylic acid salt of tackifier, tackifying resin PN-110 and magnesium oxide again 60-80 ℃ of lower reaction 60 seconds; In the 3rd step, add again carbon black, polybutene and special-purpose paraffin hydrocarbon ils 80-100 ℃ of lower reaction 140 seconds; In the 4th step, add again dicumyl peroxide, co-crosslinker, linking agent and captax DB and can obtain desired product in 130 seconds 60-85 ℃ of lower reaction.
The elastomeric material of the resulting a kind of high temperature-resistance conveyor belt of the present invention and manufacture method thereof, co-crosslinker, linking agent, captax DB and special-purpose paraffin hydrocarbon ils have been added on original basis, so that the conveying belt that manufactures with this elastomeric material has better high thermal resistance.
Embodiment
The present invention is further described by the following embodiment.
Embodiment 1:
The manufacture method of the elastomeric material of a kind of high temperature-resistance conveyor belt that present embodiment is described, the first step is reacted 100 parts of terpolymer EP rubbers and 2 parts of dispersion agents 60 seconds under 50 ℃; Second step adds 2 parts of nano zine oxides, 1 part of stearic acid, 1 part of accelerant CZ, 1 part of antioxidant MB, 1 part of antioxidant 264,1 part of anti-aging agent RD, 1 part of antioxidant 4020,5 parts of tackifier response type methacrylic acid salts, 2 parts of tackifying resin PN-110 and 5 parts of magnesium oxide again 60-80 ℃ of lower reaction 60 seconds; In the 3rd step, add again 40 parts of carbon blacks, 5 parts of polybutene and 3 parts of special-purpose paraffin hydrocarbon ils 80-100 ℃ of lower reaction 140 seconds; The 4th step added 1 part of dicumyl peroxide, 1 part of co-crosslinker, 0.1 part of linking agent and 1 part of captax DB again and can obtain desired product in 130 seconds 60-85 ℃ of lower reaction, and above-described umber by weight ratio.The temperature of this high temperature-resistance conveyor belt is 185 ℃ of normal operations after testing.
Embodiment 2:
The manufacture method of the elastomeric material of a kind of high temperature-resistance conveyor belt that present embodiment is described, the first step is reacted 150 parts of terpolymer EP rubbers and 8 parts of dispersion agents 60 seconds under 50 ℃; Second step adds 5 parts of nano zine oxides, 3 parts of stearic acid, 3 parts of accelerant CZs, 3 parts of antioxidant MBs, 3 parts of antioxidant 264s, 3 parts of anti-aging agent RDs, 3 parts of antioxidant 4020s, 12 parts of tackifying resin PN-110,15 parts of tackifier response type methacrylic acid salts and 10 parts of magnesium oxide again 60-80 ℃ of lower reaction 60 seconds; In the 3rd step, add again 80 parts of carbon blacks, 10 parts of polybutene and 15 parts of special-purpose paraffin hydrocarbon ils 80-100 ℃ of lower reaction 140 seconds; The 4th step added 5 parts of dicumyl peroxides, 3 parts of co-crosslinkers, 1.5 parts of linking agents and 3 parts of captax DB again and can obtain desired product in 130 seconds 60-85 ℃ of lower reaction, and above-described umber by weight ratio.The temperature of this high temperature-resistance conveyor belt is 182 ℃ of normal operations after testing.
Claims (6)
1. the elastomeric material of a high temperature-resistance conveyor belt, it is characterized in that: it comprises 100-150 part terpolymer EP rubber, 40-80 part carbon black, 2-5 part nano zine oxide, 1-3 part stearic acid, 1-5 part dicumyl peroxide, 1-3 part co-crosslinker, 0.1-1.5 part linking agent, 2-6 part promotor, 4-12 part anti-aging agent, 5-10 part polybutene, 2-12 part tackifying resin, the reactive methacrylic acid salt of 5-15 part tackifier, 5-10 part magnesium oxide, 2-8 part dispersion agent, the special-purpose paraffin hydrocarbon ils of 3-15 part forms, and above-described umber by weight ratio.
2. the elastomeric material of high temperature-resistance conveyor belt according to claim 1, it is characterized in that: described promotor is comprised of accelerant CZ and captax DB.
3. the elastomeric material of high temperature-resistance conveyor belt according to claim 1 and 2, it is characterized in that: described anti-aging agent is comprised of antioxidant MB, antioxidant 264, anti-aging agent RD and antioxidant 4020.
4. the elastomeric material of high temperature-resistance conveyor belt according to claim 1 and 2, it is characterized in that: described antioxidant MB is that 1-3 part, antioxidant 264 are that 1-3 part, anti-aging agent RD are that 1-3 part, antioxidant 4020 are 1-3 part.
5. the elastomeric material of high temperature-resistance conveyor belt according to claim 1, it is characterized in that: described tackifying resin is tackifying resin PN-110.
6. the manufacture method of the elastomeric material of a high temperature-resistance conveyor belt is characterized in that: the first step, with terpolymer EP rubber and dispersion agent 50 ℃ of lower reactions 60 seconds; Second step adds nano zine oxide, stearic acid, accelerant CZ, antioxidant MB, antioxidant 264, anti-aging agent RD, antioxidant 4020, the reactive methacrylic acid salt of tackifier, tackifying resin PN-110 and magnesium oxide again 60-80 ℃ of lower reaction 60 seconds; In the 3rd step, add again carbon black, polybutene and special-purpose paraffin hydrocarbon ils 80-100 ℃ of lower reaction 140 seconds; In the 4th step, add again dicumyl peroxide, co-crosslinker, linking agent and captax DB and can obtain desired product in 130 seconds 60-85 ℃ of lower reaction.