CN102876172A - Water-based fireproof paint - Google Patents
Water-based fireproof paint Download PDFInfo
- Publication number
- CN102876172A CN102876172A CN2012104188769A CN201210418876A CN102876172A CN 102876172 A CN102876172 A CN 102876172A CN 2012104188769 A CN2012104188769 A CN 2012104188769A CN 201210418876 A CN201210418876 A CN 201210418876A CN 102876172 A CN102876172 A CN 102876172A
- Authority
- CN
- China
- Prior art keywords
- parts
- silane
- paint
- ball
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a water-based fireproof paint, belonging to the technical field of paints. The paint is prepared from the following raw materials in parts by weight: 20-40 parts of silicone modified styrene-acrylic emulsion, 5-15 parts of vinyl acetate-ethylene copolymer emulsion, 10-22 parts of water-based epoxy resin emulsion, 2-5 parts of 2,4,6-hydroxyhydroquinone, 6-15 parts of hydroxyethyl cellulose, 6-14 parts of triethanolamine, 3-6 parts of ammonium polyphosphate, 2-5 parts of zinc borate, 6-15 parts of aluminium hydroxide, 2-8 parts of titanium dioxide, 1-4 parts of expanded graphite, 1-6 parts of maleic anhydride, 2-4 parts of paraformaldehyde, 10-20 parts of aluminium sol, 1-2 parts of potassium tripolyphosphate, 2-4 parts of surfactant, 1-3 parts of polyol amine, 1-4 parts of light calcium carbonate, 3-8 parts of silane and 80-160 parts of deionized water. The paint has the following beneficial effects that the paint has good fireproof and flame retardant properties and excellent antiseptic property; the formed film is beautiful, glossy and resistant to wear and scratch; and the paint has simple production process, is convenient to use, is safe, nontoxic and environment-friendly and has low cost.
Description
Technical field
The present invention relates to a kind of frie retardant coating, particularly a kind of outdoor use steel structure fireproofing, waterproof, preserved aqueous coating belong to technical field of coatings.
Background technology
Along with outward appearance and the improving constantly of function of people to building, steel construction because intensity height, good toughness, from heavy and light, antivibration pinking and good impact resistance, and be easy to make and the characteristics such as use, extensively should be in modern architecture already.Steel construction mainly is metallic substance, and therefore good heat conductivity exists poor, the corrosion-prone shortcoming of resistivity against fire.When temperature surpassed 250 ℃, larger variation occured in material, and intensity progressively reduces.When temperature reached 500 ℃, steel enter plastic state can not continue carrying, causes caving in of buildings and causes casualties and financial loss.Therefore, the fire retardant anticorrosion of steel construction is significant.
Summary of the invention
For above-mentioned total amount, the object of the present invention is to provide a kind of fire resistance excellent, waterproof, antiseptic property are given prominence to the outdoor steel structure water-borne coatings of non-toxic and safe environmental protection.Adopt following technical scheme:
A kind of aqueous fire-proof coating, made by the following raw material according to weight ratio: 20 ~ 40 parts of organic-silicon-modified benzene emulsions, 5 ~ 15 parts of vinyl-acetic ester-ethylene copolymerization emulsions, 10 ~ 22 parts of aqueous epoxy resin emulsions, 2,2 ~ 5 parts of 4,6-benzenetriols, 6 ~ 15 parts of Natvosols, 6 ~ 14 parts of trolamines, 3 ~ 6 parts of ammonium polyphosphates, 2 ~ 5 parts of zinc borates, 6 ~ 15 parts in aluminium hydroxide, 2 ~ 8 parts of titanium dioxide, 1 ~ 4 part of expanded graphite, along 1 ~ 6 part of divinyl dicarboxylic anhydride, 2 ~ 4 parts of Paraformaldehyde 96s, 10 ~ 20 parts of aluminium colloidal sols, 1 ~ 2 part of Potassium tripolyphosphate, 2 ~ 4 parts in tensio-active agent, 1 ~ 3 part of polyvalent alcohol amine, 1 ~ 4 part of light calcium carbonate, 3 ~ 8 parts in silane, 80 ~ 160 parts of deionized waters.
The concentration of described aluminium colloidal sol is 10%.
Described silane is methyltrimethoxy silane, Union carbide A-162, n-octyl Trimethoxy silane, N-propyl-triethoxysilicane, γ-glycidyl ether oxygen propyl trimethoxy silicane, triethoxy (3,3,4,4,5,5,6,6,7,7,8,8,8-, ten trifluoro octyl groups) a kind of in the silane.
The preparation method is:
S1 is with organic-silicon-modified benzene emulsion, vinyl-acetic ester-ethylene copolymerization emulsions, aqueous epoxy resin emulsion, 2,4,6-benzenetriol, Natvosol, trolamine, ammonium polyphosphate, zinc borate, aluminium hydroxide, titanium dioxide, expanded graphite, suitable divinyl dicarboxylic anhydride, Paraformaldehyde 96, tensio-active agent and part deionized water join in the stirring tank, under the stirring velocity of 200r/min, each component is stirred.
The slurry that S2 obtains S1 is packed in the ball grinder, carries out ball milling take alumina ball as ball-milling medium, Ball-milling Time 2 ~ 4 hours.
S3 joins aluminium colloidal sol, Potassium tripolyphosphate, polyvalent alcohol amine, light calcium carbonate, silane and remaining deionized water in the slurry behind the ball milling, with high-speed shearing emulsion machine under the rotating speed of 1000 ~ 3000r/min, stir 10 ~ 30min, filter and namely get desired product.
Beneficial effect
Water-borne coatings fire retardant performance of the present invention is good, has outstanding waterproof, antiseptic property, and film forming is attractive in appearance glossy, wear-resisting scraping, and production technique is simple, and is easy to use, and the safety non-toxic environmental protection is helped cheap.
Embodiment
The weight proportion of table 1 embodiment 1~embodiment 3
The concentration of above-mentioned aluminium colloidal sol is 10%.
Above-mentioned silane adopts Union carbide A-162.
The preparation method of each embodiment is:
S1 is with organic-silicon-modified benzene emulsion, vinyl-acetic ester-ethylene copolymerization emulsions, aqueous epoxy resin emulsion, 2,4,6-benzenetriol, Natvosol, trolamine, ammonium polyphosphate, zinc borate, aluminium hydroxide, titanium dioxide, expanded graphite, suitable divinyl dicarboxylic anhydride, Paraformaldehyde 96, tensio-active agent and part deionized water join in the stirring tank, under the stirring velocity of 200r/min, each component is stirred.
The slurry that S2 obtains S1 is packed in the ball grinder, carries out ball milling take alumina ball as ball-milling medium, Ball-milling Time 2 ~ 4 hours.
S3 joins aluminium colloidal sol, Potassium tripolyphosphate, polyvalent alcohol amine, light calcium carbonate, silane and remaining deionized water in the slurry behind the ball milling, with high-speed shearing emulsion machine under the rotating speed of 1000 ~ 3000r/min, stir 10 ~ 30min, filter and namely get desired product.
Performance test
In order to contrast the performance of this frie retardant coating, disclosed frie retardant coating is routine in contrast among the employing patent CN201010197742.X.With the frie retardant coating of preparation according to the requirement of standard GB/T/T 14907-2002 " steel structure fire-proof paint " apply, sample preparation, and carry out performance test.The performance test results is as shown in table 2.
The performance comparison of table 2 case study on implementation 1-3 and reference examples
The performance test project | Enforcement case 1 | Enforcement case 2 | Enforcement case 3 | Reference examples |
Time of drying/h | 2.5 | 2.5 | 2.3 | 2.8 |
The initial dry cracking resistance energy | Flawless | Flawless | Flawless | Flawless |
Cohesive strength/MPa | 0.66 | 0.58 | 0.63 | 0.41 |
Humidity resistance/h | >504 | >504 | >504 | 250 |
Acid resistance/h | >360 | >360 | >360 | 220 |
Expansion multiplying power | 24 | 28 | 25 | 18 |
Coat-thickness/mm | 2.10 | 1.98 | 2.03 | 2.08 |
Fire endurance/min | 99 | 104 | 108 | 90 |
Claims (3)
1. aqueous fire-proof coating, made by the following raw material according to weight ratio: 20 ~ 40 parts of organic-silicon-modified benzene emulsions, 5 ~ 15 parts of vinyl-acetic ester-ethylene copolymerization emulsions, 10 ~ 22 parts of aqueous epoxy resin emulsions, 2,2 ~ 5 parts of 4,6-benzenetriols, 6 ~ 15 parts of Natvosols, 6 ~ 14 parts of trolamines, 3 ~ 6 parts of ammonium polyphosphates, 2 ~ 5 parts of zinc borates, 6 ~ 15 parts in aluminium hydroxide, 2 ~ 8 parts of titanium dioxide, 1 ~ 4 part of expanded graphite, along 1 ~ 6 part of divinyl dicarboxylic anhydride, 2 ~ 4 parts of Paraformaldehyde 96s, 10 ~ 20 parts of aluminium colloidal sols, 1 ~ 2 part of Potassium tripolyphosphate, 2 ~ 4 parts in tensio-active agent, 1 ~ 3 part of polyvalent alcohol amine, 1 ~ 4 part of light calcium carbonate, 3 ~ 8 parts in silane, 80 ~ 160 parts of deionized waters; Its preparation method is:
S1 is with organic-silicon-modified benzene emulsion, vinyl-acetic ester-ethylene copolymerization emulsions, aqueous epoxy resin emulsion, 2,4,6-benzenetriol, Natvosol, trolamine, ammonium polyphosphate, zinc borate, aluminium hydroxide, titanium dioxide, expanded graphite, suitable divinyl dicarboxylic anhydride, Paraformaldehyde 96, tensio-active agent and part deionized water join in the stirring tank, under the stirring velocity of 200r/min, each component is stirred.
The slurry that S2 obtains S1 is packed in the ball grinder, carries out ball milling take alumina ball as ball-milling medium, Ball-milling Time 2 ~ 4 hours.
S3 joins aluminium colloidal sol, Potassium tripolyphosphate, polyvalent alcohol amine, light calcium carbonate, silane and remaining deionized water in the slurry behind the ball milling, under the rotating speed of 1000 ~ 3000r/min, stirs 10 ~ 30min with the emulsification pretreatment machine, filters and namely gets desired product.
2. aqueous fire-proof coating according to claim 1, it is characterized in that: the concentration of described aluminium colloidal sol is 10%.
3. aqueous fire-proof coating according to claim 1, it is characterized in that: described silane is methyltrimethoxy silane, Union carbide A-162, n-octyl Trimethoxy silane, N-propyl-triethoxysilicane, γ-glycidyl ether oxygen propyl trimethoxy silicane, triethoxy (3,3,4,4,5,5,6,6,7,7,8,8,8-, ten trifluoro octyl groups) a kind of in the silane.