CN102875989A - High-hardness inflaming retarding propylene carbonate and acrylonitrile butadiene styrene (PC/ABS) alloy material - Google Patents
High-hardness inflaming retarding propylene carbonate and acrylonitrile butadiene styrene (PC/ABS) alloy material Download PDFInfo
- Publication number
- CN102875989A CN102875989A CN 201210316522 CN201210316522A CN102875989A CN 102875989 A CN102875989 A CN 102875989A CN 201210316522 CN201210316522 CN 201210316522 CN 201210316522 A CN201210316522 A CN 201210316522A CN 102875989 A CN102875989 A CN 102875989A
- Authority
- CN
- China
- Prior art keywords
- abs
- alloy material
- coupling agent
- high rigidity
- abs alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-hardness inflaming retarding propylene carbonate and acrylonitrile butadiene styrene (PC/ABS) alloy material, which is characterized by comprising the following raw material components in part by weight: 65 to 70 parts of PC/ABS, 25 to 30 parts of polymethyl methacrylate, 5 to 8 parts of compatilizer, 8 to 10 parts of flexibilizer, 10 to 12 parts of inflaming retarding agent, 15 to 18 parts of coupling agent, 1 to 1.5 parts of antioxidant, 5 to 8 parts of modified powder and 0.5 to 1.5 parts of dispersing agent. According to the PC/ABS alloy material, the PC/ABS material is adopted, so that the surface hardness and fire resistance are enhanced, and the PC/ABS alloy is widely applied.
Description
Technical field
The present invention relates to a kind of PC/ABS plastic alloy material, belong to technical field of polymer materials.
Background technology
The PC/ABS resin is preferably engineering materials of a kind of over-all properties of growing up of the mid-1960s, and it had both had thermotolerance, physical strength and the dimensional stability of PC, has again workability and the advantage such as inexpensive of ABS resin, and Application Areas is very extensive.
Because the PC/ABS alloy is widely used in the panel of electric equipment products, in order to keep permanent aesthetic appearance and fire safety performance, effects on surface hardness and flame retardant resistance have proposed Secretary.All be to adopt the method for surface lacquer to improve surface hardness, but surface lacquer had both increased cost and environment protection is caused certain pressure, for this reason, the fire retardation PC of research and development high rigidity/ABS alloy has seemed very important in the past.
Summary of the invention
Technical problem to be solved by this invention is: a kind of PC/ABS modified alloy is provided, and this alloy changes little basis in its mechanical property and has improved surface hardness and flame retardant properties.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A kind of high rigidity fire retardation PC/ABS alloy material comprises the feed composition of following parts by weight proportioning:
PC/ABS,65-70;
Polymethylmethacrylate, 25-30;
Compatilizer, 5-8;
Toughner, 8-10;
Fire retardant, 10-12;
Coupling agent, 15-18;
Oxidation inhibitor, 1-1.5;
Modified powder, 5-8;
Dispersion agent, 0.5-1.5.
In above-mentioned high rigidity fire retardation PC/ABS alloy material, toughner is a kind of in methacrylic vinegar one propylene vinegar multipolymer, the cured styrene-acrylonitrile copolymer vinegar of the propylene multipolymer.
Described coupling agent is a kind of in titanate coupling agent, KH-550 type silane coupling agent, KH-560 type silane coupling agent, the KH-570 type silane coupling agent.
Described oxidation inhibitor is antioxidant 1076 or oxidation inhibitor 29210.
Described dispersion agent is a kind of among dispersion agent TAS-3A, the dispersion agent TAF.
Described modified powder is a kind of in sharp iron ore type nanometer titanium dioxide iron, nano-calcium carbonate, nano oxidized cutting edge of a knife or a sword, zeolite, the montmorillonite, and the particle diameter of modified powder is 500nm-3000nm.
The invention has the beneficial effects as follows: PC/ABS material of the present invention has improved surface hardness and flame retardant resistance, thereby it is more extensive that the PC/ABS Alloyapplication is got.
Embodiment
Embodiment 1
A kind of high rigidity fire retardation PC/ABS alloy material comprises the feed composition of following parts by weight proportioning:
PC/ABS,65;
Polymethylmethacrylate, 25;
Compatilizer, 5;
Toughner, 8;
Fire retardant, 10;
Coupling agent, 15;
Oxidation inhibitor, 1;
Modified powder, 5;
Dispersion agent, 0.5.
In above-mentioned high rigidity fire retardation PC/ABS alloy material, toughner is methacrylic vinegar one propylene vinegar multipolymer.
Described coupling agent is titanate coupling agent.
Described oxidation inhibitor is antioxidant 1076.
Described dispersion agent is dispersion agent TAS-3A.
Described modified powder is that the particle diameter of sharp iron ore type nanometer titanium dioxide iron, modified powder is 500nm.
Embodiment 2
A kind of high rigidity fire retardation PC/ABS alloy material comprises the feed composition of following parts by weight proportioning:
PC/ABS,70;
Polymethylmethacrylate, 30;
Compatilizer, 8;
Toughner, 10;
Fire retardant, 12;
Coupling agent, 18;
Oxidation inhibitor, 1.5;
Modified powder, 8;
Dispersion agent, 1.5.
In above-mentioned high rigidity fire retardation PC/ABS alloy material, toughner is the cured styrene-acrylonitrile copolymer vinegar of propylene multipolymer.
Described coupling agent is KH-570 type silane coupling agent.
Described oxidation inhibitor is oxidation inhibitor 29210.
Described dispersion agent is among the dispersion agent TAF.
Described modified powder is montmorillonite, and the particle diameter of modified powder is 3000nm.
Embodiment 3
A kind of high rigidity fire retardation PC/ABS alloy material comprises the feed composition of following parts by weight proportioning:
PC/ABS,68;
Polymethylmethacrylate, 26;
Compatilizer, 7;
Toughner, 9;
Fire retardant, 11;
Coupling agent, 16;
Oxidation inhibitor, 1.3;
Modified powder, 7;
Dispersion agent, 0.8.
In above-mentioned high rigidity fire retardation PC/ABS alloy material, toughner is methacrylic vinegar one propylene vinegar multipolymer.
Described coupling agent is KH-550 type silane coupling agent.
Described oxidation inhibitor is oxidation inhibitor 29210.
Described dispersion agent is dispersion agent TAS-3A.
Described modified powder is nano oxidized cutting edge of a knife or a sword, and the particle diameter of modified powder is 1500nm.
Claims (6)
1. high rigidity fire retardation PC/ABS alloy material is characterized in that, comprises the feed composition of following parts by weight proportioning:
PC/ABS,65-70;
Polymethylmethacrylate, 25-30;
Compatilizer, 5-8;
Toughner, 8-10;
Fire retardant, 10-12;
Coupling agent, 15-18;
Oxidation inhibitor, 1-1.5;
Modified powder, 5-8;
Dispersion agent, 0.5-1.5.
2. high rigidity fire retardation PC according to claim 1/ABS alloy material is characterized in that: described toughner is a kind of in methacrylic vinegar one propylene vinegar multipolymer, the cured styrene-acrylonitrile copolymer vinegar of the propylene multipolymer.
3. high rigidity fire retardation PC according to claim 1/ABS alloy material is characterized in that: described coupling agent is a kind of in titanate coupling agent, KH-550 type silane coupling agent, KH-560 type silane coupling agent, the KH-570 type silane coupling agent.
4. high rigidity fire retardation PC according to claim 1/ABS alloy material, it is characterized in that: described oxidation inhibitor is antioxidant 1076 or oxidation inhibitor 29210.
5. high rigidity fire retardation PC according to claim 1/ABS alloy material is characterized in that: described dispersion agent is a kind of among dispersion agent TAS-3A, the dispersion agent TAF.
6. high rigidity fire retardation PC according to claim 1/ABS alloy material, it is characterized in that: described modified powder is a kind of in sharp iron ore type nanometer titanium dioxide iron, nano-calcium carbonate, nano oxidized cutting edge of a knife or a sword, zeolite, the montmorillonite, and the particle diameter of modified powder is 500nm-3000nm.