CN102863880A - Flame retardant and anti-corrosion paint - Google Patents

Flame retardant and anti-corrosion paint Download PDF

Info

Publication number
CN102863880A
CN102863880A CN 201210309538 CN201210309538A CN102863880A CN 102863880 A CN102863880 A CN 102863880A CN 201210309538 CN201210309538 CN 201210309538 CN 201210309538 A CN201210309538 A CN 201210309538A CN 102863880 A CN102863880 A CN 102863880A
Authority
CN
China
Prior art keywords
parts
paint
powder
fire retardant
flame retardant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201210309538
Other languages
Chinese (zh)
Inventor
田敬强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Baolikang New Material Co Ltd
Original Assignee
Qingdao Baolikang New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Baolikang New Material Co Ltd filed Critical Qingdao Baolikang New Material Co Ltd
Priority to CN 201210309538 priority Critical patent/CN102863880A/en
Publication of CN102863880A publication Critical patent/CN102863880A/en
Pending legal-status Critical Current

Abstract

The invention relates to flame retardant and anti-corrosion paint, which comprises the following components in part by weight: 20 to 25 parts of low molecule epoxy resin, 5 to 10 parts of unsaturated polyester, 5 to 10 parts of leveling agent, 10 to 20 parts of mica powder, 10 to 15 parts of zeolite powder, 5 to 10 parts of toluene, 10 to 15 parts of cyclohexane, 10 to 15 parts of titanium dioxide, 5 to 8 parts of talcum powder, 3 to 8 parts of ammonium polyphosphate, 1 to 2 parts of coloring agent and 2 to 4 parts of metal tungsten powder. The leveling agent is a polyether modified polysiloxane copolymer. According to the flame retardant and anti-corrosion paint, the low molecule epoxy resin and the unsaturated polyester are adopted to form an organic substance with strong affinity; and the substance can produce very strong adhesive force to the surface of inorganic substances. The ammonium polyphosphate is added into the paint, so that the paint has a good flame retardant function and can slow fire behavior down. The strength and anti-corrosion performance of the product can be improved by adding the zeolite powder and the metal tungsten powder.

Description

A kind of fire retardant, anticorrosive erosion paint
Technical field
The present invention relates to a kind of paint, especially have the paint of anti-corrosion function.
Background technology
Paint is a kind ofly can firmly cover body surface; play the chemical mixture of protection, decoration, sign and other special purposes; belong to organic chemical industry's macromolecular material, modern paint is progressively becoming the polyfunctional engineering materials of a class, is an important industry in the chemical industry.Paint is as application of paints is very extensive repeatedly; present paint on the market is of a great variety; but along with the increase of people to the functional requirement of paint, existing paint can not satisfy people's this needs, and paint no longer has been only to have realized protection, decoration functions just.Generally all be to be prepared from according to a certain percentage by macromolecule epoxy resin, phenylformic acid two phosphatide toughner, organic silicone oil flow agent, titanium dioxide packing agent solvent, the paint brushing that said components is prepared from is at body surface, after solidifying, form corrosion protection coating.Although this paint has played seemingly effect, when because sticking power is relatively poor, long easy fall in flakes of time one, so the life-span is shorter.
Summary of the invention
The technical problem to be solved in the present invention provides a kind of fire retardant, anticorrosive paint of strong adhesion.
For solving the problems of the technologies described above, fire retardant, anticorrosive erosion paint of the present invention comprises following integral part
Low molecule based epoxy resin 20-25 part
Unsaturated polyester 5-10 part
Flow agent 5-10 part
Mica powder 10-20 part
Zeolite powder 10-15 part
Toluene 5-10 part
Cyclohexanone 10-15 part
Titanium dioxide 10-15 part
Talcum powder 5-8 part
Ammonium polyphosphate 3-8 part
Tinting material 1-2 part
Preferably, the metal tungsten powder that also comprises 2-4 part in the paint.
Preferably, flow agent is the Siloxane-Oxyalkylene Copolymers multipolymer.
Preferred embodiment of the present invention paints each constituent mass number and is: 20 parts of low molecule based epoxy resins, 8 parts of unsaturated polyesters, 7 parts of Siloxane-Oxyalkylene Copolymers multipolymers, 15 parts of mica powders, 15 parts of zeolite powders, 5 parts of toluene, 12 parts of cyclohexanones, 12 parts of titanium dioxides, 7 parts of talcum powder, 5 parts of ammonium polyphosphates, 1 part of tinting material, 3 parts of metal tungsten powders.
Fire retardant, anticorrosive erosion paint of the present invention adopts low-molecular-weight epoxy resin and unsaturated polyester, has formed the organic substance with very strong avidity, and these materials produce extremely strong sticking power to the inorganics surface energy.Add ammonium polyphosphate in the paint of the present invention, preferably anti-flaming function has been arranged, can slow down the intensity of a fire.Adding zeolite powder and tungsten metal powder can improve intensity and the non-corrosibility of product.
Embodiment
The present invention is described in further detail below in conjunction with embodiment:
Embodiment 1
Fire retardant, anticorrosive erosion paint of the present invention comprises the integral part of following weight percent: 20 parts of low molecule based epoxy resins, 8 parts of unsaturated polyesters, 7 parts of Siloxane-Oxyalkylene Copolymers multipolymers, 15 parts of mica powders, 15 parts of zeolite powders, 5 parts of toluene, 12 parts of cyclohexanones, 12 parts of titanium dioxides, 7 parts of talcum powder, 5 parts of ammonium polyphosphates, 1 part of tinting material, 3 parts of metal tungsten powders.
Embodiment 2
Fire retardant, anticorrosive erosion paint of the present invention comprises the integral part of following weight percent: 25 parts of low molecule based epoxy resins, 5 parts of unsaturated polyesters, 5 parts of Siloxane-Oxyalkylene Copolymers multipolymers, 11 parts of mica powders, 12 parts of zeolite powders, 6 parts of toluene, 15 parts of cyclohexanones, 10 parts of titanium dioxides, 5 parts of talcum powder, 3 parts of ammonium polyphosphates, 1 part of tinting material, 2 parts of metal tungsten powders.
Embodiment 3
Fire retardant, anticorrosive erosion paint of the present invention comprises the integral part of following weight percent: 20 parts of low molecule based epoxy resins, 5 parts of unsaturated polyesters, 0 part of Siloxane-Oxyalkylene Copolymers copolymer 1,10 parts of mica powders, 10 parts of zeolite powders, 10 parts of toluene, 15 parts of cyclohexanones, 10 parts of titanium dioxides, 5 parts of talcum powder, 8 parts of ammonium polyphosphates, 2 parts of tinting materials, 4 parts of metal tungsten powders.
The above only is to preferred embodiment of the present invention, is not that the present invention is done other forms of restriction, and any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the equivalent embodiment of equal variation.Every the present invention program's content that do not break away from, all drops in protection scope of the present invention any simple modification, equivalent variations and remodeling that above embodiment does according to technical spirit of the present invention.

Claims (3)

1. a fire retardant, anticorrosive erosion is painted, and it is characterized in that: it comprises following integral part
Low molecule based epoxy resin 20-25 part
Unsaturated polyester 5-10 part
Flow agent 5-10 part
Mica powder 10-20 part
Zeolite powder 10-15 part
Toluene 5-10 part
Cyclohexanone 10-15 part
Titanium dioxide 10-15 part
Talcum powder 5-8 part
Ammonium polyphosphate 3-8 part
Tinting material 1-2 part
According to fire retardant, anticorrosive erosion paint claimed in claim 1, it is characterized in that: the metal tungsten powder that also comprises 2-4 part in the described paint.
2. according to fire retardant, anticorrosive erosion paint claimed in claim 2, it is characterized in that: described flow agent is the Siloxane-Oxyalkylene Copolymers multipolymer.
3. according to fire retardant, anticorrosive erosion paint claimed in claim 3, it is characterized in that: each constituent mass number of described paint is: 20 parts of low molecule based epoxy resins, 8 parts of unsaturated polyesters, 7 parts of Siloxane-Oxyalkylene Copolymers multipolymers, 15 parts of mica powders, 15 parts of zeolite powders, 5 parts of toluene, 12 parts of cyclohexanones, 12 parts of titanium dioxides, 7 parts of talcum powder, 5 parts of ammonium polyphosphates, 1 part of tinting material, 3 parts of metal tungsten powders.
CN 201210309538 2012-08-28 2012-08-28 Flame retardant and anti-corrosion paint Pending CN102863880A (en)