CN102863768A - 聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料 - Google Patents
聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料 Download PDFInfo
- Publication number
- CN102863768A CN102863768A CN2012103536223A CN201210353622A CN102863768A CN 102863768 A CN102863768 A CN 102863768A CN 2012103536223 A CN2012103536223 A CN 2012103536223A CN 201210353622 A CN201210353622 A CN 201210353622A CN 102863768 A CN102863768 A CN 102863768A
- Authority
- CN
- China
- Prior art keywords
- parts
- alloy material
- polymethylmethacrylate
- polycarbonate alloy
- polycarbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料，属于高分子材料技术领域。其是由以下组份的原料组成：聚碳酸酯树脂 150~170 份；聚甲基丙烯酸甲酯 37.5 ～ 42.5 份；苯乙烯 - 丙烯腈共聚物 9~13 份；乙烯 - 丙烯酸甲酯共聚物 5.5~7.2 份；抗氧剂 0.4~0.9 份；润滑剂 1.2~2.4 份。具有透明性好、质量轻、综合性能优异等特点。拉伸强度 55~60MPa ，断裂伸长率 39~51% ，冲击强度 33~41KJ/m 2,弯曲强度 86~95MPa 。
Description
技术领域
本发明属于高分子材料技术领域，具体涉及一种聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料。
背景技术
聚碳酸酯具有优异的力学性能，其热变形温度高达120～143℃，成型收缩率小，在汽车、电子、电器等领域得到广泛应用。聚甲基丙烯酸甲酯具有透光率高、比重轻、耐候好等特点。若将聚甲基丙烯酸甲酯与聚碳酸酯材料共混，生产一种外观透明性好、质量轻的合金材料，可以极大的扩展聚碳酸酯的用途，本发明在下面将要介绍的技术方案便是在这种背景下产生的。
发明内容
本发明的任务是提供一种聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料，该材料具有透明性好、质量轻和综合性能优异的特点。
本发明的任务是这样来完成的，一种聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料，其是由以下组份的原料组成：
在本发明的一个具体的实施例中，所述的聚碳酸酯树脂为双酚A型聚碳酸酯。
在本发明的另一个具体的实施例中，所述的聚甲基丙烯酸甲酯为通用型聚甲基丙烯酸甲酯树脂。
在本发明的又一个具体的实施例中，所述的苯乙烯-丙烯腈共聚物为苯乙烯与丙烯腈共聚树脂经过马来酸酐接枝处理的并且接枝率0.5%的苯乙烯-丙烯腈共聚物。
在本发明的再一个具体的实施例中，所述的乙烯-丙烯酸甲酯共聚物为乙烯与丙烯酸甲酯共聚树脂经马来酸酐接枝处理的并且接枝率0.5%的乙烯-丙烯酸甲酯共聚物。
在本发明的还有一个具体的实施例中，所述的抗氧剂为2,6-二叔丁基对甲基苯酚。
在本发明的更而一个具体的实施例中，所述的润滑剂为硬脂酸酰胺。
由本发明提供的聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料具有透明性好、质量轻、综合性能优异等特点。拉伸强度55~60MPa,断裂伸长率39~51%， 冲击强度33~41KJ/m2, 弯曲强度 86~95 MPa。
具体实施方式
实施例1：
双酚A型聚碳酸酯150份；
通用型聚甲基丙烯酸甲酯树脂42.5份；
苯乙烯与丙烯腈共聚树脂经过马来酸酐接枝处理的并且接枝率0.5%的苯乙烯-丙烯腈共聚物 10份；
马来酸酐接枝处理的并且接枝率0.5%的乙烯-丙烯酸甲酯共聚物7.2份；
2,6-二叔丁基对甲基苯酚0.4份；
硬脂酸酰胺1.2份。
实施例2：
双酚A型聚碳酸酯155份；
通用型聚甲基丙烯酸甲酯树脂37.5份；
苯乙烯与丙烯腈共聚树脂经过马来酸酐接枝处理的并且接枝率0.5%的苯乙烯-丙烯腈共聚物 9份；
马来酸酐接枝处理的并且接枝率0.5%的乙烯-丙烯酸甲酯共聚物5.5份；
2,6-二叔丁基对甲基苯酚0.9份；
硬脂酸酰胺1.4份。
实施例3：
双酚A型聚碳酸酯170份；
通用型聚甲基丙烯酸甲酯树脂39份；
苯乙烯与丙烯腈共聚树脂经过马来酸酐接枝处理的并且接枝率0.5%的苯乙烯-丙烯腈共聚物 13份；
马来酸酐接枝处理的并且接枝率0.5%的乙烯-丙烯酸甲酯共聚物7份；
2,6-二叔丁基对甲基苯酚0.6份；
硬脂酸酰胺1.8份。
实施例4：
双酚A型聚碳酸酯165份；
通用型聚甲基丙烯酸甲酯树脂41份；
苯乙烯与丙烯腈共聚树脂经过马来酸酐接枝处理的并且接枝率0.5%的苯乙烯-丙烯腈共聚物 11份；
马来酸酐接枝处理的并且接枝率0.5%的乙烯-丙烯酸甲酯共聚物6份；
2,6-二叔丁基对甲基苯酚0.7份；
硬脂酸酰胺2.4份。
由上述实施例1至4所得的聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料经测试具有下表所示的技术效果：
| 测试项目 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
| 拉伸强度MPa | 55.3 | 57.2 | 58.5 | 59.2 |
| 断裂伸长率% | 39 | 43 | 47 | 51 |
| 冲击强度KJ/m2 | 34.2 | 36.5 | 39.3 | 40.7 |
| 弯曲强度MPa | 86 | 89 | 92 | 95 |
Claims (7)
1.一种聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料，其特征在于其是由以下组份的原料组成：
聚碳酸酯树脂 150~170份；
聚甲基丙烯酸甲酯 37.5～42.5份；
苯乙烯-丙烯腈共聚物 9~13份；
乙烯-丙烯酸甲酯共聚物 5.5~7.2份；
抗氧剂 0.4~0.9份；
润滑剂 1.2~2.4份。
2.根据权利要求1所述的聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料，其特征在于所述的聚碳酸酯树脂为双酚A型聚碳酸酯。
3.根据权利要求1所述的聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料，其特征在于所述的聚甲基丙烯酸甲酯为通用型聚甲基丙烯酸甲酯树脂。
4.根据权利要求1所述的聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料，其特征在于所述的苯乙烯-丙烯腈共聚物为苯乙烯与丙烯腈共聚树脂经过马来酸酐接枝处理的并且接枝率0.5%的苯乙烯-丙烯腈共聚物。
5.根据权利要求1所述的聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料，其特征在于所述的乙烯-丙烯酸甲酯共聚物为乙烯与丙烯酸甲酯共聚树脂经马来酸酐接枝处理的并且接枝率0.5%的乙烯-丙烯酸甲酯共聚物。
6.根据权利要求1所述的聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料，其特征在于所述的抗氧剂为2,6-二叔丁基对甲基苯酚。
7.根据权利要求1所述的聚甲基丙烯酸甲酯改性的聚碳酸酯合金材料，其特征在于所述的润滑剂为硬脂酸酰胺。