CN102850994A - Blood adhesive for wood hot pressing - Google Patents
Blood adhesive for wood hot pressing Download PDFInfo
- Publication number
- CN102850994A CN102850994A CN2012103204285A CN201210320428A CN102850994A CN 102850994 A CN102850994 A CN 102850994A CN 2012103204285 A CN2012103204285 A CN 2012103204285A CN 201210320428 A CN201210320428 A CN 201210320428A CN 102850994 A CN102850994 A CN 102850994A
- Authority
- CN
- China
- Prior art keywords
- blood
- parts
- hot pressing
- weight parts
- weight part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a blood adhesive for wood hot pressing. The blood adhesive comprises the following components, by weight, 35-45 parts of blood powder, 15-20 parts of sodium silicate, 5-10 parts of calcium hydroxide, 1-3 parts of ammonia water, 1-3 parts of cellulose, 0.1-0.3 part of copper sulfate powder, and 60-80 parts of water. The blood adhesive of the present invention is used for wood hot pressing, and has technical effects of good adhesion effect and green environment protection.
Description
Technical field
The present invention relates to a kind of timber wood hot pressing blood sizing agent, belong to the sizing agent technical field.
Background technology
Blood glue (blood protein glue) sizing agent is the sizing agent of being made by blood.Wherein mainly to adopt the blood of ox, pig and other domestic animals be that raw material is made to blood protein glue.The shortcoming blood glue sizing agent cured glue layer of existing blood glue sizing agent is harder, and cutter easy to wear is subject to the mushroom corrosion, and color is pitch black, and off-odor is arranged.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art part, a kind of timber wood hot pressing blood sizing agent is provided.
Timber wood hot pressing of the present invention blood sizing agent comprises following composition: blood meal 35-45 weight part, water glass 15-20 weight part, calcium hydroxide 5-10 weight part, ammoniacal liquor 1-3 weight part, Mierocrystalline cellulose 1-3 weight part, sulfuric acid copper powder 0.1-0.3 weight part, water 60-80 weight part.
Described timber wood hot pressing blood sizing agent is characterised in that, comprises following composition: blood meal 40 weight parts, water glass 18 weight parts, calcium hydroxide 6 weight parts, ammoniacal liquor 2 weight parts, Mierocrystalline cellulose 2 weight parts, sulfuric acid copper powder 0.2 weight part, water 70 weight parts.
Timber wood hot pressing of the present invention has following technique effect with the blood sizing agent: be used for the hot pressing of timber, its adhesive effect is good, and environmental protection.
Embodiment
Embodiment 1
The timber wood hot pressing of the present embodiment blood sizing agent comprises following composition: comprise following composition: blood meal 40 weight parts, water glass 18 weight parts, calcium hydroxide 6 weight parts, ammoniacal liquor 2 weight parts, Mierocrystalline cellulose 2 weight parts, sulfuric acid copper powder 0.2 weight part, water 70 weight parts.
Embodiment 2
The timber wood hot pressing of the present embodiment blood sizing agent comprises following composition: blood meal 35 weight parts, water glass 20 weight parts, calcium hydroxide 5 weight parts, ammoniacal liquor 3 weight parts, Mierocrystalline cellulose 1 weight part, sulfuric acid copper powder 0.3 weight part, water 60 weight parts.
Embodiment 3
The timber wood hot pressing of the present embodiment blood sizing agent comprises following composition: blood meal 45 weight parts, water glass 20 weight parts, calcium hydroxide 10 weight parts, ammoniacal liquor 1 weight part, Mierocrystalline cellulose 3 weight parts, sulfuric acid copper powder 0.1 weight part, water 80 weight parts.
Claims (2)
1. a timber wood hot pressing blood sizing agent is characterized in that, comprises following composition: blood meal 35-45 weight part, water glass 15-20 weight part, calcium hydroxide 5-10 weight part, ammoniacal liquor 1-3 weight part, Mierocrystalline cellulose 1-3 weight part, sulfuric acid copper powder 0.1-0.3 weight part, water 60-80 weight part.
2. timber wood hot pressing according to claim 1 blood sizing agent is characterized in that, comprises following composition: blood meal 40 weight parts, water glass 18 weight parts, calcium hydroxide 6 weight parts, ammoniacal liquor 2 weight parts, Mierocrystalline cellulose 2 weight parts, sulfuric acid copper powder 0.2 weight part, water 70 weight parts.