CN102850161B - Olefin deoxygenation agent, its preparation method, and olefin deoxygenation method using the same - Google Patents
Olefin deoxygenation agent, its preparation method, and olefin deoxygenation method using the same Download PDFInfo
- Publication number
- CN102850161B CN102850161B CN201110184565.6A CN201110184565A CN102850161B CN 102850161 B CN102850161 B CN 102850161B CN 201110184565 A CN201110184565 A CN 201110184565A CN 102850161 B CN102850161 B CN 102850161B
- Authority
- CN
- China
- Prior art keywords
- alkene
- reductor
- manganese
- compound
- tio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses an olefin deoxygenation agent, its preparation method, and olefin deoxygenation method using the same. The preparation method includes (by weight parts) (1) mixing manganese source (as Mn3O4) 100 and titania nanoparticle 58-100 to obtain a mixture; (2) kneading the mixture and a silver compound (as Ag2O) aqueous solution 8-35, and forming; (3) aging and drying; and (4) calcining. The inventive olefin deoxygenation agent has high room-temperature deoxygenation capacity up to 25.5 mL/g, deoxygenation depth smaller than 0.01 ppm, low reduction temperature, and wide applicability in industrial production. The agent realizes high-efficiency deoxygenation at room temperature.
Description
Technical field
The alkene reductor that the present invention relates to a kind of preparation method of alkene reductor and made by this preparation method and the application of this alkene reductor and alkene method of deoxidation.
Background technology
Alkene is important basic organic chemical raw material.Wherein ethene and propylene are produced the main raw material of macromolecule polymeric material especially.Along with developing rapidly of polyethylene and polypropylene technology, the sequential use such as various new and effective polyethylene, polypropylene catalyst and metallocene catalyst are in industrial production.In order to avoid, the efficient polyolefin catalyst of this class is poisoning, inactivation and improving the quality of products, and the foreign matter content of the ethene for polymerization and propylene feedstocks is had to strict restriction.According to ethene and propylene feedstocks national standard, in qualified polymer grade ethylene, propylene, oxygen level is≤5ppm (5 × 10
-6v/V, below identical), can not meet the requirement of novel polymeric technique, need in polymerization process, further remove micro amount of oxygen in ethene and propylene, oxygen level is purified to≤0.1ppm.Therefore, to be applied to the deep purifying high efficiency deoxidiser of ethene and propylene gas-phase polymerization process be necessary in research and development.
The micro amount of oxygen of applying in Patents document and industrial production purifies adopt more and is unworthy of hydrogen deoxidization technique.Being unworthy of hydrogen deoxidation is to utilize the micro amount of oxygen in medium that the reductor of reduction-state is oxidized, and generation high oxide reaches the decontamination effect improving of deoxidation.Such reductor, because deoxidation finite capacity, for preventing frequent reducing/regenerating, affects normal production, is mainly applicable to oxygen level in gas and is less than 50ppm, is particularly less than the deoxidization technique of 10ppm.
CN1246383A discloses one and has been unworthy of hydrogen reductor, and wherein Mn content is 24～44 % by weight, and support carrier is high-alumina cement, diatomite or Al
2o
3.Deoxidation capacity when this reductor is used for ethene deoxidation is only 5.3ml/g.
CN1110249A discloses a kind of loading type reductor, utilizes pickling process at Al
2o
3load Mn (NO on carrier
3)
2, Ni (NO
3)
2with in alkaline-earth metal one or more oxide compound and prepare and be unworthy of hydrogen reductor.This reductor is for nitrogen deoxidation, and the deoxidation capacity under room temperature is 16.2ml/g.
CN1342516A discloses the reductor that a kind of bimetallic oxide MnO and CuO are active constituent, and adds Al
2o
3carrier machine-shaping, this reductor is for ethene deoxidation, and under room temperature, deoxidation capacity is 10ml/g.
CN1955150A discloses a kind of with Mn
3o
4for active ingredient, add the reductor of accelerative activator alkaline earth metal oxide and aluminum oxide, for the purification of the alkene such as ethene and propylene micro amount of oxygen, under room temperature, deoxidation capacity is 7.6ml/g.
CN101165030A discloses a kind of Mn-Ag double activated component reductor, reduction temperature can be reduced.But, the mixture carrier of the calcium aluminate using or calcium aluminate and ca aluminosilicate need to be at 1200 DEG C～1650 DEG C temperature lower calcination 3～8h, then pulverize, sieve, the production cost of reductor is higher, and the specific surface area of carrier is low, this reductor is for ethene deoxidation, and under room temperature, deoxidation capacity is 10.9ml/g.
As can be seen here, under alkene reductor room temperature prepared by prior art, deoxidation capacity is on the low side, work-ing life is short, and in order to improve deoxygenation temperature the work-ing life that extends alkene reductor, result brings polyolefine plant energy consumption to increase.
Summary of the invention
The object of the invention is, in order to overcome the defect that under existing alkene reductor room temperature (25 DEG C), deoxidation capacity is low, work-ing life is short, provides a kind of new alkene reductor and its preparation method and application and alkene method of deoxidation.
The present inventor surprisingly finds under study for action, adopts nano level TiO
2prepare alkene reductor as support material, can greatly improve the deoxidation capacity under alkene reductor room temperature, and increase the service life, and can reach the darker deoxidation degree of depth.
Therefore, to achieve these goals, on the one hand, the invention provides a kind of preparation method of alkene reductor, said method comprising the steps of:
(1) by manganese source and nano level TiO
2mix and obtain mixture, respectively with Mn
3o
4with nano level TiO
2meter, the manganese source based on 100 weight parts, nano level TiO
2consumption be 58-100 weight part, described manganese source is Mn
3o
4and/or can obtain Mn after roasting
3o
4the compound of manganese;
(2) aqueous solution incipient impregnation of mixture step (1) being obtained and silver-colored compound, then kneading, moulding, respectively with Mn
3o
4and Ag
2o meter, the manganese source based on 100 weight parts, the aqueous solution of the compound of silver is 8-35 weight part, the compound of described silver is can decompose and obtain Ag after roasting
2the compound of the water miscible silver of O;
(3) product of step (2) moulding is carried out to burin-in process, then the solid after burin-in process is dried;
(4) the dried product of step (3) is carried out to roasting.
On the other hand, the invention provides a kind of alkene reductor, described alkene reductor is made up of method as above.
The third aspect, the invention provides the application of a kind of alkene reductor as above in alkene deoxidation.
Fourth aspect, the invention provides a kind of alkene method of deoxidation, described method comprises uses the reducing gas that contains hydrogen to reduce to above-mentioned alkene reductor, then, under alkene deoxygenation conditions, alkene is carried out to gas phase deoxidation by the alkene reductor after reducing.
Deoxidation capacity under alkene reductor room temperature of the present invention is high, can reach 25.5ml/g, much larger than the deoxidation capacity under existing alkene reductor room temperature, therefore under identical deoxygenation conditions, be also correspondingly longer than the work-ing life of existing alkene reductor the work-ing life of alkene reductor of the present invention; The deoxidation degree of depth is less than 0.01ppm, is less than 0.05ppm has reduced by five times than prior art level; Reduction temperature is low, reducible at 150～160 DEG C of temperature, and the reductor reduction temperature that can provide with existing polyolefin device is consistent, and therefore not needing to carry out plant modification can directly use.Alkene reductor provided by the invention has successfully been realized efficient deoxidation under room temperature, calculate according to contriver, produce per year 300,000 tons of polyethylene devices room temperature not under heating condition deoxidation can save every year units up to a million than deoxidation at 100 DEG C, saved the energy, reduced the discharge of greenhouse gases.Alkene reductor of the present invention can be widely used in industrial production.
Other features and advantages of the present invention are described in detail the embodiment part subsequently.
Embodiment
Below the specific embodiment of the present invention is elaborated.Should be understood that, embodiment described herein only, for description and interpretation the present invention, is not limited to the present invention.
On the one hand, the invention provides a kind of preparation method of alkene reductor, said method comprising the steps of:
(1) by manganese source and nano level TiO
2mix and obtain mixture, respectively with Mn
3o
4with nano level TiO
2meter, the manganese source based on 100 weight parts, nano level TiO
2consumption be 58-100 weight part, described manganese source is Mn
3o
4and/or can obtain Mn after roasting
3o
4the compound of manganese;
(2) aqueous solution incipient impregnation of mixture step (1) being obtained and silver-colored compound, then kneading, moulding, respectively with Mn
3o
4and Ag
2o meter, the manganese source based on 100 weight parts, the aqueous solution of the compound of silver is 8-35 weight part, the compound of described silver is can decompose and obtain Ag after roasting
2the compound of the water miscible silver of O;
(3) product of step (2) moulding is carried out to burin-in process, then the solid after burin-in process is dried;
(4) the dried product of step (3) is carried out to roasting.
Room temperature in the present invention refers to 25 DEG C.Ppm refers to volumetric concentration.
Nano level TiO
2type have Detitanium-ore-type, rutile-type and brookite type three types, preferably adopt nano level Detitanium-ore-type and/or nm-class rutile-type TiO
2prepare alkene reductor as support material, further preferably adopt nano level Detitanium-ore-type TiO
2prepare alkene reductor as support material.Nano level TiO in the present invention
2refer to average particle size range does not reach micron number magnitude TiO in nanometer scale
2, i.e. the TiO of median size below 1 μ m
2; Non-nano level TiO
2refer to average particle size range not in nanometer scale, the TiO more than nanometer scale
2.
Median size in the present invention refers to volume average particle size, adopts transmission electron microscope to record.
According to the present invention, although adopt nano level TiO
2prepare alkene reductor as the carrier of alkene reductor, and the consumption in manganese source, TiO
2consumption and concentration and the consumption of the aqueous solution of the compound of silver make with Mn
3o
4, nano level TiO
2and Ag
2o meter, the manganese source based on 100 weight parts, nano level TiO
2consumption be 58-100 weight part, the aqueous solution of compound of silver is 8-35 weight part, can reach object of the present invention, but under preferable case, nano level TiO
2median size be 5-50nm, can further improve the deoxidation capacity under the alkene reductor room temperature that the inventive method makes, further extend the work-ing life under alkene reductor room temperature; Under further preferable case, nano level TiO
2median size be 5-20nm, can further improve the deoxidation capacity under the alkene reductor room temperature that the inventive method makes, further extend the work-ing life under alkene reductor room temperature.
Nano level TiO
2specific surface area be preferably 30-200m
2/ g, more preferably 100-200m
2/ g.
As long as the compound of manganese can obtain Mn after meeting roasting
3o
4; it can be the compound of the thinkable various manganese of those skilled in the art; be preferably selected from least one in the group being formed by manganous carbonate, manganese acetate, formic acid manganese, manganous oxalate, manganese acetylacetonate, manganous phosphate, Manganous chloride tetrahydrate, manganous nitrate, Manganse Dioxide, manganous sulfate and manganous hydroxide; more preferably select at least one in the group of free manganous carbonate, manganous oxalate, manganese acetate and formic acid manganese composition, more preferably manganous carbonate.
The compound of silver is as long as for decomposing and obtain Ag after roasting
2the compound of the water miscible silver of O, can, by the compound of the thinkable various silver of those skilled in the art, be preferably Silver Nitrate.
The consumption of preparation method's Raw of alkene reductor provided by the invention, i.e. manganese source and nano level TiO
2consumption and concentration and the consumption of the aqueous solution of the compound of silver make respectively with Mn
3o
4, nano level TiO
2and Ag
2o meter, the manganese source based on 100 weight parts, nano level TiO
2for 58-100 weight part, the aqueous solution of the compound of silver is 8-35 weight part, is preferably the manganese source based on 100 weight parts, nano level TiO
2consumption be 58-85 weight part, the aqueous solution of compound of silver is 15-35 weight part, the more preferably manganese source based on 100 weight parts, nano level TiO
2for 58-70 weight part, the aqueous solution of the compound of silver is 20-35 weight part.
By manganese source and nano level TiO
2mix and obtain mixture, the method mixing, without particular requirement, can adopt the conventional the whole bag of tricks in this area, for example can be by manganese source and nano level TiO
2putting into cone-type mixer mixes.
The aqueous solution incipient impregnation of the mixture that step (1) is obtained and silver-colored compound, then mediates, moulding, so that manganese source, nano level TiO
2even with the aqueous solution of silver-colored compound.For the shape after the method for incipient impregnation and kneading, moulding and kneading, moulding without particular requirement, for example can in the mixture that step (1) obtains, add the aqueous solution of silver-colored compound to carry out incipient impregnation, then be prepared into strip segment with banded extruder, the mixture that also step (1) can be obtained joins in coater, the aqueous solution that sprays into silver-colored compound carries out incipient impregnation, is then rolled onto spherical.
In the present invention, the product of step (2) moulding being carried out to burin-in process is preferably the airtight placement of product of step (2) moulding, airtight being placed under room temperature normal pressure, the time of airtight placement is preferably 12-72h, more preferably 24-60h.Without particular requirement, can adopt the conventional the whole bag of tricks adopting in this area to be dried for dry, dry condition optimization is dry 5-12h at 80-150 DEG C, more preferably dry 8-12h at 100-140 DEG C.
Without particular requirement, can adopt the conventional the whole bag of tricks adopting in this area to carry out roasting for roasting, the condition optimization of roasting is roasting 2-10h at 400-550 DEG C, more preferably roasting 2-10h at 450-500 DEG C.
On the other hand, the invention provides a kind of alkene reductor of being prepared by aforesaid method.The mean pore size of alkene reductor is preferably 10-50nm, and specific surface area is preferably 50-250m
2/ g.
The alkene reductor of being prepared by the inventive method, through XRD analysis, includes stronger Mn
3o
4characteristic diffraction peak, TiO
2characteristic peak and weak Ag
2o characteristic peak.
Active constituent before alkene reductor prepared by the inventive method uses in reductor product is Ag
2o and Mn
3o
4, it should be appreciated by those skilled in the art that while use and need scene that this active ingredient is reduced into active constituent Ag and the MnO with deoxidizing capacity.Equally, when the alkene reductor after reduction is after deoxidation is after a while used, the Ag of lower valency and MnO can be oxidized to the Ag of high valence state
2o and Mn
3o
4.In the time that after alkene reductor complete deactivation or deoxidation, oxygen level is greater than requirement index, need reducing/regenerating reductor again, reductor of the present invention can on-the-spot reducing/regenerating, reuses.The active ingredient under room temperature with deoxy activity is mainly the Ag of high dispersing.
The concrete reductive condition of alkene reductor is preferably: logical temperature is hydrogen or hydrogen and the N of 130-160 DEG C
2the on-the-spot reduction of mixed gas, hydrogen or hydrogen and N
2the volume space velocity 50-2000h of mixed gas
-1, the recovery time is 5-24h; More preferably: logical temperature is hydrogen and the N that the hydrogeneous volume fraction of 150～160 DEG C is 0.5-10%
2the on-the-spot reduction of mixed gas, hydrogen and N
2the volume space velocity of mixed gas be 50-1000h
-1, the recovery time is 10-15h.
The third aspect, the invention provides the application of above-mentioned alkene reductor in alkene deoxidation.Having no special requirements for concrete application, can be the application mode of this area routine, does not repeat them here.
Fourth aspect, the invention provides a kind of alkene method of deoxidation, described method comprises uses the reducing gas that contains hydrogen to reduce to above-mentioned alkene reductor, then, under alkene deoxygenation conditions, alkene is carried out to gas phase deoxidation by the alkene reductor after reducing.
Have no special requirements for concrete alkene method of deoxidation, can adopt the conventional the whole bag of tricks adopting in this area, for example can be in fixed-bed reactor by the alkene that contains 2-5 carbon atom by carrying out gas phase deoxidation through the alkene reductor of reduction, in alkene, oxygen level is 1-100ppm, and alkene volume space velocity is 100-3000h
-1, the service temperature of fixed-bed reactor is 20-100 DEG C, pressure is 0.1-10MPa.More preferably in fixed-bed reactor by the alkene that contains 2-4 carbon atom by through reduction alkene reductor carry out gas phase deoxidation, in alkene, oxygen level is 1-5ppm, alkene volume space velocity is 500-2000h
-1, the service temperature of fixed-bed reactor is 20-30 DEG C, pressure is 0.1-5MPa.Carry out more preferably ethene or the propylene of alkene of deoxidation.
More than describe the preferred embodiment of the present invention in detail; but the present invention is not limited to the detail in above-mentioned embodiment, within the scope of technical conceive of the present invention; can carry out multiple simple variant to technical scheme of the present invention, these simple variant all belong to protection scope of the present invention.
It should be noted that in addition, each concrete technical characterictic described in above-mentioned embodiment, in reconcilable situation, can combine by any suitable mode, for fear of unnecessary repetition, the present invention is to the explanation no longer separately of various possible array modes.
In addition, also can carry out arbitrary combination between various embodiment of the present invention, as long as it is without prejudice to thought of the present invention, it should be considered as content disclosed in this invention equally.
Embodiment
The present invention is further illustrated for following embodiment, but therefore do not limit the present invention.
In following embodiment and comparative example, the measuring method of alkene reductor deoxidation capacity and the deoxidation degree of depth is as follows: get 50ml alkene reductor and pack in the stainless steel reactor of Φ 25mm, at 150 DEG C, pass into hydrogen volume mark and be 1% nitrogen, at volume space velocity 200h
-1under condition, reduce after 12h and stop passing into.After cooling, at pressure 0.4MPa, at 25 DEG C of temperature, pass into ethene, volume of ethylene air speed is 1500h
-1, entrance oxygen level 1000ppm.After system brings into operation, the concentration of residual oxygen after observation deoxidation in ethene, the concentration of residual oxygen after discovery deoxidation in ethene is less than 0.01ppm all the time, stops experiment in the time that the concentration of residual oxygen in ethene after deoxidation is greater than 0.01ppm.The deoxidation degree of depth under alkene reductor room temperature is defined as after deoxidation concentration of residual oxygen (ppm) in alkene by the present invention; The oxygen volume (the milliliter number of correspondence under standard state) that deoxidation capacity definition is removed in the time that the deoxidation degree of depth is less than 0.01ppm, divided by the quality of reductor, measure unit is ml/g.
In following embodiment and comparative example, TiO
2be purchased from Xuancheng Jingrui New Material Co., Ltd..
Embodiment 1
This embodiment is used for illustrating the preparation method of alkene reductor provided by the invention.
By MnCO
3with median size be that 9.8nm, specific surface area are 160m
2the Detitanium-ore-type TiO of/g
2mix.MnCO
3and TiO
2consumption make respectively with Mn
3o
4and TiO
2meter, based on the MnCO of 1000g
3, TiO
2for 650g, in the blend composition after mixing, add AgNO
3solution carries out incipient impregnation, AgNO
3concentration and the consumption of solution make with Mn
3o
4and Ag
2o meter, based on the MnCO of 1000g
3, AgNO
3solution is 300g, fully mediates, and is prepared into the strip segment of the long 5mm of diameter of phi 3mm with banded extruder, then airtight placement 48h, and then dry 8h at 120 DEG C, then roasting 5h at 480 DEG C, is prepared into alkene reductor.Record the deoxidation capacity of the alkene reductor making and the deoxidation degree of depth in table 1.
Embodiment 2
This embodiment is used for illustrating the preparation method of alkene reductor provided by the invention.
By MnCO
3with median size be that 5nm, specific surface area are 200m
2the Detitanium-ore-type TiO of/g
2mix.MnCO
3and TiO
2consumption make respectively with Mn
3o
4and TiO
2meter, based on the MnCO of 1000g
3, TiO
2for 580g, the blend composition after mixing is joined in coater, spray into AgNO
3solution carries out incipient impregnation, AgNO
3concentration and the consumption of solution make with Mn
3o
4and Ag
2o meter, based on the MnCO of 1000g
3, AgNO
3solution is 350g, is rolled onto the spherical of Φ 3mm, then airtight placement 60h, and then dry 5h at 140 DEG C, then roasting 2h at 500 DEG C, is prepared into alkene reductor.Record the deoxidation capacity of the alkene reductor making and the deoxidation degree of depth in table 1.
Embodiment 3
This embodiment is used for illustrating the preparation method of alkene reductor provided by the invention.
By MnCO
3with median size be that 20nm, specific surface area are 100m
2the Detitanium-ore-type TiO of/g
2mix.MnCO
3and TiO
2consumption make respectively with Mn
3o
4and TiO
2meter, based on the MnCO of 1000g
3, TiO
2for 700g, in the blend composition after mixing, add AgNO
3solution carries out incipient impregnation, AgNO
3concentration and the consumption of solution make with Mn
3o
4and Ag
2o meter, based on the MnCO of 1000g
3, AgNO
3solution is 200g, fully mediates, and is prepared into the strip segment of the long 5mm of diameter of phi 3mm with banded extruder, then airtight placement 24h, and then dry 12h at 100 DEG C, then roasting 10h at 450 DEG C, is prepared into alkene reductor.Record the deoxidation capacity of the alkene reductor making and the deoxidation degree of depth in table 1.
Embodiment 4
Prepare alkene reductor according to the method for embodiment 1, different, Detitanium-ore-type TiO
2median size be 40nm, record the deoxidation capacity of the alkene reductor making and the deoxidation degree of depth in table 1.
Embodiment 5
Prepare alkene reductor according to the method for embodiment 1, different, Detitanium-ore-type TiO
2specific surface area be 40m
2/ g, records the deoxidation capacity of the alkene reductor making and the deoxidation degree of depth in table 1.
Embodiment 6
Prepare alkene reductor according to the method for embodiment 1, different, AgNO
3concentration and the consumption of solution make with Mn
3o
4and Ag
2o meter, based on the MnCO of 1000g
3, AgNO
3solution is 100g, records the deoxidation capacity of the alkene reductor making and the deoxidation degree of depth in table 1.
Embodiment 7
Prepare alkene reductor according to the method for embodiment 1, different, with Mn
3o
4, TiO
2and Ag
2o meter, MnCO
3consumption be 900g, TiO
2consumption and AgNO
3concentration and the consumption of solution are constant, record the deoxidation capacity of the alkene reductor making and the deoxidation degree of depth in table 1.
Embodiment 8
Prepare alkene reductor according to the method for embodiment 1, different, TiO
2for rutile TiO
2, median size is that 10nm, specific surface area are 165m
2/ g, records the deoxidation capacity of the alkene reductor making and the deoxidation degree of depth in table 1.
Comparative example 1
Prepare alkene reductor according to the method for embodiment 1, different, TiO
2for Detitanium-ore-type non-nano level TiO
2, median size is 2 μ m, specific surface area is 150m
2/ g, records the deoxidation capacity of the alkene reductor making and the deoxidation degree of depth in table 1.
Comparative example 2
Prepare alkene reductor according to the method for embodiment 1, different, be that 20 μ m, specific surface area are 300m by median size
2γ-Al of/g
2o
3alternative median size is that 9.8nm, specific surface area are 160m
2the Detitanium-ore-type TiO of/g
2, record the deoxidation capacity of the alkene reductor making and the deoxidation degree of depth in table 1.
Table 1 embodiment and comparative example experimental result
| Embodiment | Deoxidation capacity (ml/g) | The deoxidation degree of depth (ppm) |
| 1 | 24.5 | 0.008 |
| 2 | 25.5 | 0.007 |
| 3 | 22.5 | 0.008 |
| 4 | 21.1 | 0.009 |
| 5 | 20.0 | 0.009 |
| 6 | 19.5 | 0.009 |
| 7 | 22.9 | 0.009 |
| 8 | 20.5 | 0.009 |
| Comparative example 1 | 14.1 | 0.035 |
| Comparative example 2 | 10.1 | 0.049 |
Embodiment 1 and comparative example 1 are compared and can be found out, non-nano level TiO
2, the deoxidation capacity of the alkene reductor of making obviously reduces; Embodiment 1 and comparative example 2 are compared and can be found out, adopt Al
2o
3the alkene reductor of making alkene reductor carrier is nothing like employing TiO
2the deoxidation effect of alkene reductor of making alkene reductor carrier is good.
Embodiment 1 and embodiment 4 compare and can find out, nano level Detitanium-ore-type TiO
2median size less, the deoxidation capacity of the alkene reductor of making is higher, theoretical derivation may be the TiO little due to median size
2can be with the band-gap energy between conduction band high, its hole and electronics have very strong redox ability; Embodiment 1 and embodiment 5 compare and can find out, nano level Detitanium-ore-type TiO
2specific surface area larger, the deoxidation capacity of the alkene reductor of making is higher; Embodiment 1 and embodiment 6 compare and can find out, Ag in the alkene reductor making
2the content of O is higher, and the deoxidation capacity of alkene reductor is higher, and Ag
2the content of O has considerable influence to the deoxidation capacity of alkene reductor, visible Ag
2o is the main active ingredient in alkene reductor; Embodiment 1 and embodiment 7 compare and can find out, Mn in the alkene reductor making
3o
4content higher, the deoxidation capacity of the alkene reductor of making is higher, but Mn
3o
4content little to the deoxidation capacity impact of alkene reductor, visible Mn
3o
4for the less important activeconstituents in alkene reductor, theoretical derivation may be because high dispersing is at TiO
2than MnO at room temperature there is oxidizing reaction in the micro amount of oxygen more easily and in raw material to Ag on carrier; Embodiment 1 and embodiment 8 are compared and can be found out, rutile TiO
2the alkene reductor making is not as Detitanium-ore-type TiO
2the deoxidation effect of the alkene reductor making is good.
Deoxidation capacity under alkene reductor room temperature of the present invention is high, can reach 25.5ml/g, much larger than the deoxidation capacity under existing alkene reductor room temperature, therefore under identical deoxygenation conditions, be also correspondingly longer than the work-ing life of existing alkene reductor the work-ing life of alkene reductor of the present invention; The deoxidation degree of depth is less than 0.01ppm, is less than 0.05ppm has reduced by five times than prior art level; Reduction temperature is low, reducible at 150～160 DEG C of temperature, and the reductor reduction temperature that can provide with existing polyolefin device is consistent, and therefore not needing to carry out plant modification can directly use.Alkene reductor provided by the invention has successfully been realized efficient deoxidation under room temperature, has saved the energy, has reduced the discharge of greenhouse gases, can be widely used in industrial production.
Claims (13)
1. a preparation method for alkene reductor, said method comprising the steps of:
(1) by manganese source and nano level TiO
2mix and obtain mixture, respectively with Mn
3o
4with nano level TiO
2meter, the manganese source based on 100 weight parts, nano level TiO
2consumption be 58-100 weight part, described manganese source is Mn
3o
4and/or can obtain Mn after roasting
3o
4the compound of manganese;
(2) aqueous solution incipient impregnation of mixture step (1) being obtained and silver-colored compound, then kneading, moulding, respectively with Mn
3o
4and Ag
2o meter, the manganese source based on 100 weight parts, the aqueous solution of the compound of silver is 8-35 weight part, the compound of described silver is can decompose and obtain Ag after roasting
2the compound of the water miscible silver of O;
(3) product of step (2) moulding is carried out to burin-in process, then the solid after burin-in process is dried;
(4) the dried product of step (3) is carried out to roasting;
Wherein, the burin-in process in described step (3) is for to carry out airtight placement by the product of step (2) moulding; Described nano level TiO
2median size be 5-50nm, described nano level TiO
2specific surface area be 30-200m
2/ g.
2. method according to claim 1, wherein, described nano level TiO
2median size be 5-20nm.
3. alkene reductor according to claim 1, wherein, described nano level TiO
2specific surface area be 100-200m
2/ g.
4. alkene reductor according to claim 1, wherein, described nano level TiO
2for nano level Detitanium-ore-type TiO
2.
5. method according to claim 1, wherein, the compound of described manganese is at least one that select in the group of free manganous carbonate, manganese acetate, formic acid manganese, manganous oxalate, manganese acetylacetonate, manganous phosphate, Manganous chloride tetrahydrate, manganous nitrate, Manganse Dioxide, manganous sulfate and manganous hydroxide composition.
6. method according to claim 5, wherein, the compound of described manganese is at least one that select in the group of free manganous carbonate, manganous oxalate, manganese acetate and formic acid manganese composition.
7. method according to claim 6, wherein, the compound of described manganese is manganous carbonate.
8. method according to claim 1, wherein, the compound of described silver is Silver Nitrate.
9. an alkene reductor, is characterized in that, described alkene reductor is made up of the method described in any one in claim 1-8.
10. alkene reductor according to claim 9, wherein, the mean pore size of described alkene reductor is 10-50nm.
11. alkene reductors according to claim 9, wherein, the specific surface area of described alkene reductor is 50-250m
2/ g.
The application in alkene deoxidation of 12. 1 kinds of alkene reductors as described in any one in claim 9-11.
13. 1 kinds of alkene method of deoxidations, described method comprises uses the reducing gas that contains hydrogen to reduce to the alkene reductor described in any one in claim 9-11, then under alkene deoxygenation conditions, alkene is carried out to gas phase deoxidation by the alkene reductor after reducing.