CN102839564A - 一种纳米银防霉壁纸涂层及其制备方法 - Google Patents
一种纳米银防霉壁纸涂层及其制备方法 Download PDFInfo
- Publication number
- CN102839564A CN102839564A CN2012102713714A CN201210271371A CN102839564A CN 102839564 A CN102839564 A CN 102839564A CN 2012102713714 A CN2012102713714 A CN 2012102713714A CN 201210271371 A CN201210271371 A CN 201210271371A CN 102839564 A CN102839564 A CN 102839564A
- Authority
- CN
- China
- Prior art keywords
- nano
- silver
- parts
- wallpaper
- mildew
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于壁纸辅料领域,具体涉及一种纳米银防霉壁纸涂层,由下述重量份的原料搅拌混合制得:聚氯乙烯糊状树脂100份,邻苯二甲酸二辛脂50~70份,钛白粉10~15份,降粘剂2~8份,发泡剂6~10份,碳酸钙50~75份,稳定剂3~5份,纳米银2~3份。本发明还提供了所述纳米银防霉壁纸涂层的制备方法。本发明解决以往装修过程中,粘贴壁纸后出现的发霉、生菌,影响壁纸使用者身体健康和墙纸美观度霉变问题。
Description
技术领域
本发明属于壁纸行业领域,具体涉及一种纳米银防霉壁纸涂层及其制备方法。
背景技术
壁纸使用过程中,墙体易返潮,壁纸胶黏剂长时间不干,或者施工涂胶过厚,胶液不易干燥,易滋生霉菌,导致壁纸在使用过程发霉生菌危害居住者身体健康。现在普通壁纸生产主要是在原纸上进行涂布及印刷等工序,这些生产过程无法保证后期壁纸使用不受环境影响,原纸受潮后就变成细菌滋生的“温床”,细菌会不断生长,直接影响居住者的健康。
发明内容
本发明主要解决以往装修过程中,粘贴壁纸后出现的发霉、生菌,影响壁纸使用者身体健康和墙纸美观度霉变问题。旨在提供一种纳米银防霉壁纸涂层,以使得到的纳米银壁纸,具有广谱、强效、持久、快速的杀菌效果,实现健康环保的目的。
具体说来,发明人提供如下的技术方案:
一种纳米银防霉壁纸涂层,由下述重量份的原料搅拌混合制得:
聚氯乙烯糊状树脂 100份,
邻苯二甲酸二辛脂 (简称DOP) 50~70份,
钛白粉 10~15份,
降粘剂 2~8份,
发泡剂 6~10份,
碳酸钙 50~75份,
稳定剂 3~5份,
纳米银 2~3份。
发明人通过长期研究,精心筛选原料,通过在壁纸生产的过程中,在壁纸浆料中添加纳米银材料,利用无机杀菌剂—纳米银广谱、强效、持久、快速的杀菌功效为壁纸使用者提供安全有效居家防护。实验研究发现,在壁纸涂层中加入纳米银作为防霉剂,配以合适的比例,可以起到防霉变和杀菌的作用,同时还能保持壁纸涂层良好的涂覆性能。本发明通过将无机杀菌材料的导入,并且应用纳米银循环杀菌原理,可以有效将各类细菌杀灭在最初的萌芽阶段,从而有效保障居住者的居家安全。
作为优选,根据本发明所述的一种纳米银防霉壁纸涂层,其中,所述的聚氯乙烯糊状树脂选用PVC聚氯乙烯糊状树脂,型号P450。
作为优选,根据本发明所述的一种纳米银防霉壁纸涂层,其中,所述的降粘剂选用降粘剂D80。
作为优选,根据本发明所述的一种纳米银防霉壁纸涂层,其中,所述的发泡剂选用发泡剂AC410。
作为优选,根据本发明所述的一种纳米银防霉壁纸涂层,其中,所述的稳定剂选用钾锌稳定剂 ,型号9004-4。
作为优选,根据本发明所述的一种纳米银防霉壁纸涂层,其中,所述的纳米银选用纳米银颗粒,型号AGS-WB3000。
本发明还提供了上述的一种纳米银防霉壁纸涂层的制备方法,包括:
将聚氯乙烯糊状树脂和邻苯二甲酸二辛脂加入到分散桶内,搅拌(低速搅拌)均匀后依次加入发泡剂、降粘剂,再慢慢加入钛白粉、碳酸钙和稳定剂,搅拌(低速搅拌),分散均匀后加入纳米银,加速搅拌,分散均匀后,研磨过滤,得到纳米银防霉壁纸涂层产品。
本发明纳米银防霉壁纸涂层应用:主要应用于壁纸生产的涂布,延长壁纸使用寿命。
与现有技术相比,本发明具有以下优点:
解决以往装修过程中,粘贴壁纸后出现的发霉、生菌,影响壁纸使用者身体健康和墙纸美观度霉变问题。
本发明的纳米银防霉壁纸涂层产品,突破以往壁纸生产过程中浆料只能现配现用的模式,有效解决浆料涂层存贮时存在的变质风险并提高生产效率。本发明的纳米银防霉壁纸涂层的存贮:常温7天,产品外观及使用性能无改变。
本发明的制备方法具有工艺简单、生产成本低的特点,产品贮存稳定、质量好。
具体实施方式
下面结合实施例,更具体地说明本发明的内容。应当理解,本发明的实施并不局限于下面的实施例,对本发明所做的任何形式上的变通和/或改变都将落入本发明保护范围。
在本发明中,若非特指,所有的份、百分比均为重量单位,所有的设备和原料等均可从市场购得或是本行业常用的。下述实施例中的方法,如无特别说明,均为本领域的常规方法。
主要原料、试剂说明:
聚氯乙烯糊状树脂:PVC聚氯乙烯糊状树脂,型号P450,上海氯碱化工股份有限公司生产,
降粘剂:降粘剂D80,山东齐鲁石化生产,
发泡剂:发泡剂AC410,上海向阳化工厂生产,
稳定剂:钾锌稳定剂,型号9004-4,德清东来化学有限公司,
纳米银:纳米银颗粒,型号AGS-WB3000,上海沪正纳米科技有限公司。
实施例1:
一种纳米银防霉壁纸涂层,原料配方:聚氯乙烯糊状树脂 100kg,邻苯二甲酸二辛脂 50kg,钛白粉 10kg,降粘剂 2 kg,发泡剂 6 kg,碳酸钙 50 kg,稳定剂 3 kg,纳米银 2 kg,按下述方法制备:
将聚氯乙烯糊状树脂和邻苯二甲酸二辛脂加入到分散桶内,低速搅拌均匀后依次加入发泡剂、降粘剂,再慢慢加入钛白粉、碳酸钙和稳定剂,低速搅拌20分钟,分散均匀后加入纳米银,加速搅拌30分钟,分散均匀后,研磨过滤,得到纳米银防霉壁纸涂层产品。得到的产品用于涂布及后处理加工。
本实施例得到的产品,经检测使用情况:常温存放48h,没有出现霉菌菌落,浆料可正常使用,没有出现产品沉淀结块等异常情况。
实施例2
一种纳米银防霉壁纸涂层,原料配方:聚氯乙烯糊状树脂 100kg,邻苯二甲酸二辛脂 70kg,钛白粉 15 kg,降粘剂 8 kg,发泡剂10 kg,碳酸钙 75 kg,稳定剂 5 kg,纳米银 3 kg,按下述方法制备:
将聚氯乙烯糊状树脂和邻苯二甲酸二辛脂加入到分散桶内,低速搅拌均匀后依次加入发泡剂、降粘剂,再慢慢加入钛白粉、碳酸钙和稳定剂,低速搅拌,20分钟后分散均匀后加入纳米银,加速搅拌,分散均匀后,30分钟后研磨过滤,得到纳米银防霉壁纸涂层产品。得到的产品用于涂布及后处理加工。
本实施例得到的产品,经检测使用情况:常温存放60h,没有出现霉菌菌落,浆料可正常使用,没有出现产品沉淀结块等异常情况。
实施例3
一种纳米银防霉壁纸涂层,原料配方:聚氯乙烯糊状树脂 100kg,邻苯二甲酸二辛脂 55kg,钛白粉 12kg,降粘剂 5kg,发泡剂 7kg,碳酸钙 60kg,稳定剂 4kg,纳米银 3kg,按下述方法制备:
将聚氯乙烯糊状树脂和邻苯二甲酸二辛脂加入到分散桶内,低速搅拌均匀后依次加入发泡剂、降粘剂,再慢慢加入钛白粉、碳酸钙和稳定剂,低速搅拌,20分钟后分散均匀后加入纳米银,加速搅拌,分散均匀后,30分钟后研磨过滤,得到纳米银防霉壁纸涂层产品。得到的产品用于涂布及后处理加工。
本实施例得到的产品,经检测使用情况:常温存放60h,没有出现霉菌菌落,浆料可正常使用,没有出现产品沉淀结块等异常情况。
经检测,纳米银防霉剂对日常生活中最主要的四种霉菌的MIC值如下:
Ⅰ 对常现青霉的MIC值
对常现青霉而言,培养5天后,防霉剂纳米银浓度为5ppm的平板上霉菌开始生长,继续培养至第9天,防霉剂浓度为10ppm的平板霉菌亦开始生长,而其余浓度的平皿没有萌动。此后,继续培养至第14天,防霉剂浓度大于等于20ppm的平板中霉菌均未见生长。得知纳米银防霉剂对常现青霉的MIC值为20ppm。
Ⅱ 对绳状青霉的MIC值
在接种过绳状青霉的平皿培养期间,每天观察平板上霉菌的萌发和生长情况,试验发现,纳米银防霉剂对绳状青霉的抑制作用较强。培养14天后纳米银防霉剂浓度为5ppm的平皿仅培养皿壁上有少量霉菌生长,而培养基上未见霉菌生长.也就是说纳米银防霉剂对绳状青霉的MIC值仅为5ppm。
Ⅲ 对产黄青霉的MIC值
在接种过产黄青霉的平皿培养期间,每天观察平板上霉菌的萌发和生长情况,对产黄青霉而言,在培养7天后,5ppm的平板霉菌开始生长,此后,继续培养至第14天,纳米银防霉剂浓度等于10ppm的平板中霉菌仅在培养皿壁上生长,但未长到培养基上,而其它平皿均未萌动。所以纳米银防霉剂对产黄青霉的MIC值为10ppm。
Ⅳ纳米银防霉剂对土曲霉的MIC值
在接种过土曲霉的平皿培养期间,每天观察平板上霉菌的萌发和生长情况,试验发现,对土曲霉而言,在培养5天后,含防霉剂5ppm的平板霉菌开始生长,继续培养至第14天,防霉剂浓度大于或等于l0ppm的平板中霉菌均未见生长。所以纳米银防霉剂对土曲霉的MIC值为10ppm。
纳米银防霉剂对四种霉菌的MIC值分别为20ppm,5ppm,10ppm,10ppm,大于等于这些浓度时,培养14天,平板上均未见霉菌生长或霉菌仅在培养皿壁上生长。所以,纳米银是一种高效广谱,长效杀菌、无毒环保、稳定性高、适用范围宽、能直接应用于墙纸工业的纳米银抗菌材料。
应用例
本发明得到的纳米银防霉壁纸涂层产品,粘贴于靠近有水源的卫生间外的壁纸,在300天内未见黑斑、红斑等细菌滋生的情况。而采用以往未添加纳米银颗粒生产的壁纸浆料的壁纸在14天已经出现发红的霉菌滋生现象。此外,本发明的纳米银防霉壁纸涂层产品常温下存贮7天,产品外观及使用性能无改变,打破了以往壁纸生产过程中浆料只能现配现用的模式,有效解决了浆料涂层存贮时存在的变质风险问题,提高了生产效率。
上述优选实施例只是用于说明和解释本发明的内容,并不构成对本发明内容的限制。尽管发明人已经对本发明做了较为详细地列举,但是,本领域的技术人员根据发明内容部分和实施例所揭示的内容,能对所描述的具体实施例做各种各样的修改或/和补充或采用类似的方式来替代是显然的,并能实现本发明的技术效果,因此,此处不再一一赘述。本发明中出现的术语用于对本发明技术方案的阐述和理解,并不构成对本发明的限制。
Claims (7)
1.一种纳米银防霉壁纸涂层,其特征在于由下述重量份的原料搅拌混合制得:
聚氯乙烯糊状树脂 100份,
邻苯二甲酸二辛脂 50~70份,
钛白粉 10~15份,
降粘剂 2~8份,
发泡剂 6~10份,
碳酸钙 50~75份,
稳定剂 3~5份,
纳米银 2~3份。
2.如权利要求1所述的一种纳米银防霉壁纸涂层,其特征在于,所述的聚氯乙烯糊状树脂选用PVC聚氯乙烯糊状树脂,型号P450。
3.如权利要求1所述的一种纳米银防霉壁纸涂层,其特征在于,所述的降粘剂选用降粘剂D80。
4.如权利要求1所述的一种纳米银防霉壁纸涂层,其特征在于,所述的发泡剂选用发泡剂AC410。
5.如权利要求1所述的一种纳米银防霉壁纸涂层,其特征在于,所述的稳定剂选用钾锌稳定剂,型号9004-4。
6.如权利要求1所述的一种纳米银防霉壁纸涂层,其特征在于,所述的纳米银选用纳米银颗粒,型号AGS-WB3000。
7.如权利要求1-6之一所述的一种纳米银防霉壁纸涂层的制备方法,其特征在于包括:
将聚氯乙烯糊状树脂和邻苯二甲酸二辛脂加入到分散桶内,搅拌均匀后依次加入发泡剂、降粘剂,再加入钛白粉、碳酸钙和稳定剂,搅拌,分散均匀后加入纳米银,加速搅拌,分散均匀后,研磨过滤,得到纳米银防霉壁纸涂层产品。