CN102828050A - 延长白银铜熔池熔炼炉使用周期的方法 - Google Patents
延长白银铜熔池熔炼炉使用周期的方法 Download PDFInfo
- Publication number
- CN102828050A CN102828050A CN2012103292835A CN201210329283A CN102828050A CN 102828050 A CN102828050 A CN 102828050A CN 2012103292835 A CN2012103292835 A CN 2012103292835A CN 201210329283 A CN201210329283 A CN 201210329283A CN 102828050 A CN102828050 A CN 102828050A
- Authority
- CN
- China
- Prior art keywords
- furnace
- furnace wall
- wall
- stones
- working layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种延长白银铜熔池熔炼炉使用周期的方法，在炉体底部按现有方法砌筑衬底，使衬底的上表面形成下凹的弧面；在衬底上砌筑反拱的次工作层，次工作层上砌筑反拱的主工作层，主工作层的拱形与次工作5的拱形相适配；在主工作层上、沿炉体内壁砌筑倾斜的炉墙，炉墙墙面与竖直平面之间的夹角为8°～12°，并且在炉墙对应火焰高温区的高度位置上、在炉墙内水平安装水套，用于冷却炉墙。本方法提高了炉墙的抗冲刷能力和稳定性，有效降低了炉料反应对炉墙的蚀损，最大程度地避免由于下部耐火材料蚀损而导致坍塌的可能，提高了白银炉炉底的耐腐蚀、耐冲刷性，使其使用周期延长到18个月。
Description
技术领域
本发明属于有色金属冶炼技术领域，涉及一种延长白银铜熔池熔炼炉使用周期的方法。
背景技术
对称全倾斜式铜熔池熔炼炉内炉墙的抗冲刷能力较弱，稳定性差，导致铜熔池熔炼炉的使用周期只有9个月，就需停产整修，不仅严重影响生产的正常进行，而且增大了维修成本。
发明内容
为了克服上述现有技术中存在的问题，本发明的目的是提供一种延长白银铜熔池熔炼炉使用周期的方法，减少停产整修次数，降低成本。
为实现上述目的，本发明所采用的技术方案是：一种延长白银铜熔池熔炼炉使用周期的方法，在炉体底部按现有方法砌筑衬底，使衬底的上表面形成下凹的弧面；在衬底上砌筑反拱的次工作层，次工作层上砌筑与次工作层的拱形相适配的反拱的主工作层；主工作层上、沿炉体内壁砌筑墙面倾斜的炉墙，炉墙墙面与竖直平面之间的夹角为8°～12°，并且在炉墙对应火焰高温区的高度位置上、在炉墙内水平安装水套，用于冷却炉墙。
次工作层采用外形尺寸为230mm的直接结合镁铬砖砌筑。
主工作层采用半再结合镁铬砖砌筑。
本发明方法对铜熔池熔炼炉的炉墙结构和材料进行优化，提高炉墙的抗冲刷能力和稳定性，有效降低炉料反应对炉墙的蚀损，最大程度地避免由于下部耐火材料蚀损而导致坍塌的可能，提高了白银炉炉底的耐腐蚀、耐冲刷性，使其使用周期延长到18个月。
附图说明
图1是采用本发明方法改造后铜熔池熔炼炉炉墙的示意图。
图中：1.炉体，2.水套，3.衬底，4.主工作层，5.次工作层，6.炉墙。
具体实施方式
下面结合附图和具体实施方式对本发明进行详细说明。
铜熔池熔炼炉的炉墙通常情况下都是沿炉体1内壁竖直砌筑，造成炉墙的抗冲刷能力较弱，稳定性差，使用周期只有9个月，就需停产整修，不仅严重影响生产的正常进行，而且增大了维修成本。为了解决上述问题，延长铜熔池熔炼炉的使用周期，减少维修次数，降低成本。本发明提供了一种能延长铜熔池熔炼炉使用周期的方法，对炉墙进行改造，同时选用优质材料砌筑炉墙，使其使用周期延长至少一倍的时间，减少熔炼炉的停产次数，降低成本。该方法具体为：在炉体1底部按现有方法砌筑衬底3，使衬底3的上表面向下凹陷，形成下凹的弧面；在衬底3上砌筑向下凹陷的弧形工作层，形成反拱的次工作层5，次工作层5采用外形尺寸为230mm的直接结合镁铬砖砌筑；次工作层5上用半再结合镁铬砖砌筑反拱的主工作层4，主工作层4的拱形与次工作层5的拱形相适配；在主工作层4上、沿炉体1内壁砌筑炉墙6，炉墙6的墙面倾斜，该墙面与竖直平面之间的夹角为8°～12°，并且在炉墙6对应火焰高温区的高度位置上、在炉墙6内水平安装水套2，用于冷却炉墙6。
炉墙6墙面与竖直平面之间的夹角为8°～12°，可最大程度地提高炉墙6的稳定性，避免由于下部耐火材料蚀损而导致坍塌的可能。与直墙式相比，可有效降低炉料反应对炉墙的蚀损。倾斜的墙面能在保持风口宽度尺寸的同时，增加熔池顶部的宽度，也增大了炉气与熔体的传热面积，有利于提高熔体的反应温度；并增大渣层面积，使炉渣在炉内过热的相对时间延长，利于降低炉渣的含铜量。
在与熔体接触的炉底反拱工作层、沉淀区渣线内衬、吹炼区水平段高温区域的炉拱、沉淀区侧的隔墙、两端墙熔池以下等易损区域选用耐腐蚀、耐冲刷性能强的优质半再结合镁铬砖；在放渣口、放铜口、风眼砖、吹风水套内衬、吹炼区侧的隔墙采用更为优质的电熔再结合镁铬砖，电熔再结合镁铬砖不仅耐腐蚀、耐冲刷性能，且耐急冷急热；其他非关键区域各处采用直接结合镁铬砖及其它适用砖型。
本发明方法在铜熔池熔炼炉炉底采用双反拱工作层，同时采用墙面倾斜的炉墙，提高了白银炉炉底的耐腐蚀、耐冲刷性，有效提高了白银炉的使用周期，使其延长了至少一倍。
Claims (3)
1.一种延长白银铜熔池熔炼炉使用周期的方法，其特征在于，该方法具体为：在炉体底部按现有方法砌筑衬底，使衬底的上表面形成下凹的弧面；在衬底上砌筑反拱的次工作层，次工作层上砌筑反拱的主工作层，主工作层的拱形与次工作层的拱形相适配；在主工作层上、沿炉体内壁砌筑墙面倾斜的炉墙，炉墙墙面与竖直平面之间的夹角为8°～12°，并且在炉墙对应火焰高温区的高度位置上、在炉墙内水平安装水套，用于冷却炉墙。
2.如权利要求1所述的延长白银铜熔池熔炼炉使用周期的方法，其特征在于，所述的次工作层采用外形尺寸为230mm的直接结合镁铬砖砌筑。
3.如权利要求1所述的延长白银铜熔池熔炼炉使用周期的方法，其特征在于，所述的主工作层采用半再结合镁铬砖砌筑。