CN102827592A - 一种耐高温稠化时间长的水泥浆 - Google Patents
一种耐高温稠化时间长的水泥浆 Download PDFInfo
- Publication number
- CN102827592A CN102827592A CN2012103209880A CN201210320988A CN102827592A CN 102827592 A CN102827592 A CN 102827592A CN 2012103209880 A CN2012103209880 A CN 2012103209880A CN 201210320988 A CN201210320988 A CN 201210320988A CN 102827592 A CN102827592 A CN 102827592A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement slurry
- thickening
- temperature
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐高温稠化时间长的水泥浆,它是由下列各组份(重量份)的原料构成:钻井水:47~48;消泡剂:0.3~0.5;分散剂:1~2;降失水剂:4~5;高温缓凝剂:5~6;中低温缓凝剂:0.4~0.6;硅粉:30~40;水泥:95~105。本发明使用后,解决了超深井钻杆少量精确注水泥的难题,根据钻杆下入时间要求,需研制稠化时间达到30小时的耐高温水泥浆体系,在保证耐高温180℃和水泥浆凝固强度30MPa的基础上,通过调节高温缓凝剂使稠化时间达到30小时,可以在超深井中通过钻杆将水泥浆输送到位并确保水泥浆流动性,实现精确注水泥。
Description
技术领域
本发明涉及一种水泥浆,具体是指一种耐高温稠化时间长的水泥浆。
背景技术
在石油天然气开采过程中,经常涉及到水泥浆固井作业。常规的固井作业注入量比较大,可通过管柱按量泵入定量的水泥浆,这类固井作业泵注和循环的时间较短,水泥浆的稠化时间较短,技术成熟,应用很广。但在部分生产井中,需要泵注少量水泥浆封堵相应层段,同时又不影响生产层段,此时就要求在封堵层段严格控制水泥浆注入量。
为了实现少量精确注水泥,一般情况下会选用电缆或连续油管送水泥浆至相应层段后,通过加电或加压的方法将水泥浆倒出。采用电缆或连续油管的方式送入,一般起下时间不超过15小时,对水泥浆稠化时间要求较低,但电缆和连续油管的作业能力有限,对于超深井的精确注水泥技术存在很大的风险,因此一般选用钻杆进行作业,由于钻杆下入时间长,对于常规的水泥浆体系稠化时间太短,完全满足不了钻杆送入的要求。
现有水泥浆技术也能满足高温180℃,水泥浆凝固强度30MPa的要求。钻井固井中一般采用循环方式泵送定量水泥浆到位,稠化时间较短;对于少量精确注水泥,一般采用电缆或连续油管输送方式送入定量水泥浆,稠化时间最长15小时。
发明内容
为了克服上述之不足,本发明目的在于提供一种耐高温稠化时间长的水泥浆。该水泥浆解决了超深井钻杆少量精确注水泥的难题,根据钻杆下入时间要求,需研制稠化时间达到30小时的耐高温水泥浆体系,以满足钻杆将水泥浆送入后依然具有可流动性,同时在高温条件下凝固后水泥强度满足要求。
为了实现上述目的,本发明采用的技术方案如下:
一种耐高温稠化时间长的水泥浆,它是由下列各组份(重量份)的原料构成:钻井水:47~48; 消泡剂:0.3~0.5; 分散剂:1~2;降失水剂:4~5 ;高温缓凝剂:5~6;中低温缓凝剂:0.4~0.6; 硅粉: 30~40;水泥:95~105。
上述各原料的最佳重量百分比为:钻井水:47.498; 消泡剂:0.4; 分散剂:1.5;降失水剂:4.5 ;高温缓凝剂:5.5;中低温缓凝剂:0.5; 硅粉: 35;水泥:100。
本发明的有益效果:由于采用上述的配方所制的水泥浆,在保证耐高温180℃和水泥浆凝固强度30MPa的基础上,通过调节高温缓凝剂使稠化时间达到30小时,可以在超深井中通过钻杆将水泥浆输送到位并确保水泥浆流动性,实现精确注水泥。
具体实施方式
实施例一:一种耐高温稠化时间长的水泥浆,它是由下列各组份(重量份)的原料构成:钻井水(F/W):47; 消泡剂(PC-X60L):0.3; 分散剂(PC-F41L):1;降失水剂(PC-G80L):4;高温缓凝剂(PC-H40L):5;中低温缓凝剂(PC-H21L):0.4; 硅粉(SSA-1): 30;G级水泥:95。
实施例二:一种耐高温稠化时间长的水泥浆,它是由下列各组份(重量份)的原料构成:钻井水(F/W):47.498; 消泡剂(PC-X60L):0.4; 分散剂(PC-F41L):1.5;降失水剂(PC-G80L):4.5 ;高温缓凝剂(PC-H40L):5.5;中低温缓凝剂(PC-H21L):0.5; 硅粉(SSA-1): 35;G级水泥:100。
实施例三:一种耐高温稠化时间长的水泥浆,它是由下列各组份(重量份)的原料构成:钻井水(F/W):48; 消泡剂(PC-X60L):0.5; 分散剂(PC-F41L):2;降失水剂(PC-G80L):5 ;高温缓凝剂(PC-H40L):6;中低温缓凝剂(PC-H21L):0.6; 硅粉(SSA-1): 40;G级水泥:105。
上述三个实施例中,实施例二是本发明的最佳实施方式。
利用本发明在施工的过程中,经过15分钟温度从20℃迅速升至60℃,经过20小时从60℃逐步升温至180℃,再经过恒温180℃养护10小时后,即模拟钻杆下入30小时,在高温180℃条件下水泥配方仍然具有流动性,再继续恒温180℃养护48小时候凝,水泥浆强度达到30MPa以上。
以上所述是本发明的优选实施方式而已,当然不能以此来限定本发明之权利范围。应当指出,对于本技术领域的普通技术人员来说,对本发明的技术方案进行修改或者等同替换,都不脱离本发明的保护范围。
Claims (2)
1.一种耐高温稠化时间长的水泥浆,其特征在于:它是由下列各组份(重量份)的原料构成:钻井水:47~48; 消泡剂:0.3~0.5; 分散剂:1~2;降失水剂:4~5 ;高温缓凝剂:5~6;中低温缓凝剂:0.4~0.6; 硅粉: 30~40;水泥:95~105。
2.根据权利要求1所述的耐高温稠化时间长的水泥浆,其特征在于:上述各原料的最佳重量百分比为:钻井水:47.498; 消泡剂:0.4; 分散剂:1.5;降失水剂:4.5 ;高温缓凝剂:5.5;中低温缓凝剂:0.5; 硅粉: 35;水泥:100。