CN102817023B - A kind of high temperature corrosion-resisting Phosphating Solution - Google Patents
A kind of high temperature corrosion-resisting Phosphating Solution Download PDFInfo
- Publication number
- CN102817023B CN102817023B CN201210263670.3A CN201210263670A CN102817023B CN 102817023 B CN102817023 B CN 102817023B CN 201210263670 A CN201210263670 A CN 201210263670A CN 102817023 B CN102817023 B CN 102817023B
- Authority
- CN
- China
- Prior art keywords
- phosphating solution
- resisting
- acid
- high temperature
- mixed solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a kind of high temperature corrosion-resisting Phosphating Solution, the mixed solution formulated by following component, in often liter of mixed solution, the weight of each component is: 80% phosphoric acid 320-330g, zinc oxide 120-125g, Sodium orthomolybdate 5-7g, citric acid 12-13g, zinc nitrate 100 ~ 150g, nitric acid 4 ~ 6g, nickelous nitrate 4-6g, chromic acid 2.0-2.5g, and surplus is water.The metal works material scope of Phosphating Solution process of the present invention is wide, and the working hour is short, and the phosphatize phosphate coat formed at workpiece surface has thick and fine and close, and adhere firmly, blackness is good, the feature that solidity to corrosion is high, stability is strong.Be widely used in using in the operations such as motor, gear and various high strength carbon steel, steel alloy, suitable applied at elevated temperature, operation is stablized.
Description
Technical field
The present invention relates to pre-treatment field, metallic surface, be specifically related to a kind of high temperature corrosion-resisting Phosphating Solution.
Background technology
Phosphatization is conventional pretreatment technology, the object of phosphatization mainly: provide protection to matrix metal, prevent metal to be corroded to a certain extent; For front bottoming of painting, improve sticking power and the anti-corrosion capability of paint film layer; Antifriction lubrication is played in metal cold complete processing.The material scope of existing Phosphating Solution process workpiece phosphatize phosphate coat sticking power that is wideless, that formed is inadequate, and erosion resistance is not strong, poor stability in high temperature environments.
Summary of the invention
The invention provides a kind of high temperature corrosion-resisting Phosphating Solution, the metal works material scope of Phosphating Solution process of the present invention is wide, and the working hour is short, and the phosphatize phosphate coat formed at workpiece surface has thick and fine and close, and adhere firmly, blackness is good, the feature that solidity to corrosion is high, stability is strong.
The technical solution used in the present invention is as follows for achieving the above object:
A kind of high temperature corrosion-resisting Phosphating Solution, is characterized in that, it is by the formulated mixed solution of following component, and in often liter of mixed solution, the weight of each component is:
80% phosphoric acid 320-330g
Zinc oxide 120-125g
Sodium orthomolybdate 5-7g
Citric acid 12-13g
Zinc nitrate 100 ~ 150g
Nitric acid 4 ~ 6g
Nickelous nitrate 4-6g
Chromic acid 2.0-2.5g
Surplus is water.
Described high temperature corrosion-resisting Phosphating Solution, is characterized in that, the mixed solution formulated by following component, and in often liter of mixed solution, the weight of each component is:
80% phosphatase 24 25g
Zinc oxide 122g
Sodium orthomolybdate 6g
Citric acid 12.5g
Zinc nitrate 120g
Nitric acid 5g
Nickelous nitrate 5g
Chromic acid 2.2g
Surplus is water.
Compound method: first diluted by phosphoric acid, place after 20-24 hour, after adding zinc oxide stirring cooling, adds all the other compositions in formula, and the 1L that adds water.
High temperature corrosion-resisting Phosphating Solution of the present invention, use temperature is 80-95 DEG C, adopts the method for soaking to carry out bonderizing to metal works, phosphorization treatment time 8-10 minute.
Beneficial effect of the present invention:
The metal works material scope of Phosphating Solution process of the present invention is wide, and the working hour is short, and sodium cellulose glycolate contributes to film forming, and the phosphatize phosphate coat formed at workpiece surface has thick and fine and close, and adhere firmly, blackness is good, the feature that solidity to corrosion is high, stability is strong.Be widely used in using in the operations such as motor, gear and various high strength carbon steel, steel alloy, suitable applied at elevated temperature, operation is stablized.
Embodiment
A kind of high temperature corrosion-resisting Phosphating Solution, the mixed solution formulated by following component, in often liter of mixed solution, the weight of each component is:
80% phosphatase 24 25g
Zinc oxide 122g
Sodium orthomolybdate 6g
Citric acid 12.5g
Zinc nitrate 120g
Nitric acid 5g
Nickelous nitrate 5g
Chromic acid 2.2g
Polyvinyl alcohol 3g
Sodium cellulose glycolate 2g
Surplus is water.
During work: above-mentioned Phosphating Solution stoste and water are mixed with working fluid with the proportioning of 1:15,
First in Phosphating Slot, Phosphating Slot useful volume 60% is filled to, the present embodiment Phosphating Solution taking requirement is poured in Phosphating Slot fully to stir and is made into working fluid, and adjustment working fluid processing range is to total acidity: 25-35 point, free acidity: 0.8-1.2 point, pH:3-4, use temperature 80-95 DEG C.
Be that the cold-reduced sheet of 120*3*4 drops in Phosphating Slot and soaks 6 minutes by specification, pull out immediately and define one deck phosphatize phosphate coat on surface, as follows to its service check:
Phosphatize phosphate coat outward appearance: perform by GB2828-88, meet the requirements.
Phosphorization film quality: measuring by GB6807-97, is 1.90-2.20g/m
2, reach phosphatization requirement completely.
Phosphatize phosphate coat solidity to corrosion: measure by GB6807-91 Appendix D, spot corrosion 3 minutes.
Shock-resistance: spray polyurethane paint by the steel plate with the process of this Phosphating Solution.Shock-resistance 550Ncm is measured by GB1732.
Snappiness: measure snappiness by GB1731 and pass through A=1mm.
Adhesion test: measure adhesion 1 grade by GB1720, and during non-phosphatization, sticking power is 2-3 level, illustrates that this phosphatize phosphate coat and paint film have good matching capacity.
Claims (1)
1. a high temperature corrosion-resisting Phosphating Solution, is characterized in that, it is by the formulated mixed solution of following component, and in often liter of mixed solution, the weight of each component is:
80% phosphoric acid 320-330g
Zinc oxide 120-125g
Sodium orthomolybdate 5-7g
Citric acid 12-13g
Zinc nitrate 100-150g
Nitric acid 4-6g
Nickelous nitrate 4-6g
Chromic acid 2.0-2.5g
Polyvinyl alcohol 3-4g
Sodium cellulose glycolate 2-3g
Surplus is water.