CN102807705A - Sulfur antibacterial masterbatch and manufacturing method thereof - Google Patents
Sulfur antibacterial masterbatch and manufacturing method thereof Download PDFInfo
- Publication number
- CN102807705A CN102807705A CN2012100904859A CN201210090485A CN102807705A CN 102807705 A CN102807705 A CN 102807705A CN 2012100904859 A CN2012100904859 A CN 2012100904859A CN 201210090485 A CN201210090485 A CN 201210090485A CN 102807705 A CN102807705 A CN 102807705A
- Authority
- CN
- China
- Prior art keywords
- sulphur
- plastics material
- composite plastics
- antibacterial matrices
- sulfur
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of polymer compound processing, and specifically relates to a masterbatch and a manufacturing method. The sulfur antimicrobial masterbatch comprises a masterbatch matrix manufactured by a composite plastic material containing a sulfur material. The manufacturing method of the sulfur antimicrobial masterbatch comprises the following steps of: 1) mixing of the composite plastic material: the composite plastic material containing the sulfur material is put in a stirrer for stirring at a low temperature of less than 80 DEG C to obtain a mixed material; and 2) the extrusion granulation of the mixed material: the mixed material is added to a twin-screw extruder to be subjected to extrusion and granulation by low-temperature die head heat cutting to obtain the sulfur antimicrobial masterbatch. With the technical scheme, the masterbatch prepared by the invention has the advantages of low cost, small addition amount of an antimicrobial material, obvious antimicrobial effect, low-temperature preparation and the like.
Description
Technical field
The present invention relates to the macromolecular compound manufacture field, be specifically related to a kind of master batch and method of manufacture.
Background technology
The preparation of anti-biotic material, particularly antibiotic plastic, film and non-woven fabrics normally adopt and add the antiseptic-germicide realization.The antibacterial efficacy of antiseptic-germicide and goods usefulness are directly related.Antiseptic-germicide in the market mainly is divided into three major types: inorganic antiseptic, organic antibacterial agent and natural antibacterial agent.
1) inorganic antiseptic: the antibacterial ability that utilizes metals such as silver, copper, zinc; Through methods such as physical adsorption IXs; Antiseptic-germicide is processed on the surface that metals such as silver, copper, zinc (or its ion) is fixed on porous materials such as fluorite, silica gel, then it is joined the material that promptly obtains to have antibacterial ability in the corresponding articles.Metals such as mercury, cadmium, lead also have antibacterial ability, but harmful; Copper, nickel, brill plasma have color, and with influencing the attractive in appearance of product, zinc has certain bacterinertness, but its antibacterial strength is merely 1/1000 of silver ions.
Silver ion antimicrobial agent occupies dominant position in inorganic antiseptic.Silver ions class antiseptic-germicide is the most frequently used antiseptic-germicide, the fine powdered that is white in color, and heat resisting temperature can reach more than 1300 ℃.The carrier of silver ions class antiseptic-germicide has zirconium phosphate, zeolite, pottery, gac etc.Sometimes in order to improve synergy, add some cupric ions, zine ion again.But the cost of silver ion antimicrobial agent is higher.
Inorganic antiseptics such as zinc oxide, cupric oxide, primary ammonium phosphate, Quilonum Retard are arranged in addition.
2) organic antibacterial agent: the principal item of organic antibacterial agent has Vanillin or vanillal compounds, is usually used in the polyethylene kind food packaging film, plays anti-microbial effect.Also have anilid class, imidazoles, thiazoles, isothiazolones verivate, quaternary ammonium salt, two croak class, phenols etc. in addition.The security of organic antibacterial agent at present still under study for action.In general the organic antibacterial agent poor heat resistance is a little, hydrolysis easily, and validity period is short.
3) natural antibacterial agent: natural antibacterial agent is mainly from the extraction of natural phant, quantity seldom, the application in being unfavorable for producing in enormous quantities.
Summary of the invention
The objective of the invention is to, a kind of sulphur antibacterial matrices is provided, solve the problems of the technologies described above.
The present invention also aims to, a kind of method of manufacture of sulphur antibacterial matrices is provided, solve the problems of the technologies described above.
The technical problem that the present invention solved can adopt following technical scheme to realize:
The sulphur antibacterial matrices comprises a master batch matrix, it is characterized in that, and the master batch matrix of said master batch matrix for adopting composite plastics material to process, said composite plastics material includes sulfur material.
It is anti-biotic material that the present invention adopts sulfur material, is prepared into the high-performance antibiosis master batch.Can be widely applied to packing, defend in the material plastics.Sulfur material with low cost, its cost be well below many silver-ion antibiotic materials of usefulness in the market, and still keeping the preferred of good anti-bacterial effect.In addition, when the preparation master batch,, can adopt the method for low temperature preparation to prepare master batch owing to added sulfur material.Preparation difficulty and preparation cost have been effectively reduced.
Said sulphur accounts for the 60%-80% of said composite plastics material total amount.The present invention adopts sulfur material as anti-biotic material, and the master batch of processing is used for the preparation of anti-biotic material, can the long period keep good antibacterial effect.
Said sulphur preferably adopts medical sulphur.Medical sulphur does not have injury than industrial sulphur safety to human body basically.After the master batch that contains medical sulphur was used to manufacture a product, product also had no side effect safely.
Said composite plastics material also comprises vector resin, lubricant, dispersion agent, coupling agent.
Said composite plastics material preferably includes the material of following parts by weight and processes: sulphur 60-80 part, vector resin 5-15 part, lubricant 1-3 part, 0.5～3 part of dispersion agent, 0.5～2 part of coupling agent.The sulphur that relates among the present invention, with low cost with respect to other anti-biotic materials, can significantly reduce the material cost of antibacterial matrices.
Said vector resin is at least a among PP, EVA or the PE.
The method of manufacture of sulphur antibacterial matrices is characterized in that, comprises the steps:
1) mixing of composite plastics material: the composite plastics material that will contain sulfur material is put into stirrer and is stirred, and adopts the low temperature preparation, and preparation temperature is no more than 80 ℃, processes compound;
2) extruding pelletization of compound: compound joined in the twin screw extruder extrude, the fervent pelletizing of low temperature die head, promptly get the sulphur antibacterial matrices.
In the step 1), said sulphur accounts for the 60%-80% of said composite plastics material total amount.
In the step 1), said sulphur preferably adopts medical sulphur.
In the step 1), said composite plastics material also comprises vector resin, lubricant, dispersion agent, coupling agent.
Said composite plastics material preferably includes the material of following parts by weight and processes: sulphur 60-80 part, vector resin 5-15 part, lubricant 1-3 part, 0.5～3 part of dispersion agent, 0.5～2 part of coupling agent.
Said vector resin is at least a among PP, EVA or the PE.
Beneficial effect: owing to adopt technique scheme, the master batch that the present invention processes has with low cost, advantages such as the anti-biotic material addition is little, antibacterial effect obvious, low temperature preparation.
Description of drawings
Fig. 1 is the schematic flow sheet of method of manufacture of the present invention.
Embodiment
For technique means, creation characteristic that the present invention is realized, reach purpose and effect and be easy to understand and understand, further set forth the present invention below in conjunction with concrete diagram.
The sulphur antibacterial matrices comprises a master batch matrix, the master batch matrix that master batch matrix adopting composite plastics material is processed, and composite plastics material includes sulfur material.Sulphur accounts for the 60%-80% of composite plastics material total amount.The present invention adopts sulfur material as anti-biotic material, and the master batch of processing is used for the preparation of anti-biotic material, can the long period keep good antibacterial effect.Sulphur preferably adopts medical sulphur.Medical sulphur does not have injury than industrial sulphur safety to human body basically.After the master batch that contains medical sulphur was used to manufacture a product, product also had no side effect safely.
It is anti-biotic material that the present invention adopts sulfur material, is prepared into the high-performance antibiosis master batch.Can be widely applied to packing, defend in the material plastics.Sulfur material with low cost, its cost be well below many silver-ion antibiotic materials of usefulness in the market, and still keeping the preferred of good anti-bacterial effect.In addition, when the preparation master batch,, can adopt the method for low temperature preparation to prepare master batch owing to added sulfur material.Preparation difficulty and preparation cost have been effectively reduced.
Composite plastics material also comprises vector resin, lubricant, dispersion agent, coupling agent.Composite plastics material preferably includes the material of following parts by weight and processes: sulphur 60-80 part, vector resin 5-15 part, lubricant 1-3 part, 0.5～3 part of dispersion agent, 0.5～2 part of coupling agent.
Vector resin is at least a among PP, EVA or the PE.
With reference to Fig. 1, the method for manufacture of sulphur antibacterial matrices comprises the steps:
The first step, the mixing of composite plastics material: the composite plastics material that will contain sulfur material is put into stirrer and is stirred, and adopts the low temperature preparation, and preparation temperature is no more than 80 ℃, processes compound.
Second step, the extruding pelletization of compound: compound joined in the twin screw extruder extrude, the fervent pelletizing of low temperature die head, promptly get the sulphur antibacterial matrices.
In the step 1), sulphur accounts for the 60%-80% of composite plastics material total amount.Sulphur preferably adopts medical sulphur.Composite plastics material also comprises vector resin, lubricant, dispersion agent, coupling agent.Composite plastics material preferably includes the material of following parts by weight and processes: sulphur 60-80 part, vector resin 5-15 part, lubricant 1-3 part, 0.5～3 part of dispersion agent, 0.5～2 part of coupling agent.The carrier free resin is at least a among PP, EVA or the PE.
Lubricant of the present invention, dispersion agent, coupling agent all can adopt disclosed lubricant, dispersion agent, coupling agent in the prior art.
Embodiment one: the composite plastics material that will contain 60% sulphur is put into stirrer and is stirred, and temperature to 70 ℃ is processed compound; Compound joined in the twin screw extruder extrude, the fervent pelletizing of low temperature die head, promptly get the sulphur antibacterial matrices.
Embodiment two: the composite plastics material that will contain 70% sulphur is put into stirrer and is stirred, and temperature to 75 ℃ is processed compound; Compound joined in the twin screw extruder extrude, the fervent pelletizing of low temperature die head, promptly get the sulphur antibacterial matrices.
Embodiment three: the composite plastics material that will contain 80% sulphur is put into stirrer and is stirred, and temperature to 80 ℃ is processed compound; Compound joined in the twin screw extruder extrude, the fervent pelletizing of low temperature die head, promptly get the sulphur antibacterial matrices.
Embodiment four: the composite plastics material of 65 parts in sulphur, 10 parts of vector resins, 2 parts of lubricants, 2 parts of dispersion agents, 1 part of coupling agent is put into stirrer stir, temperature to 80 ℃ is processed compound; Compound joined in the twin screw extruder extrude, the fervent pelletizing of low temperature die head, promptly get the sulphur antibacterial matrices.
Embodiment five: the composite plastics material of 75 parts in sulphur, 15 parts of vector resins, 3 parts of lubricants, 3 parts of dispersion agents, 2 parts of coupling agents is put into stirrer stir, temperature to 75 ℃ is processed compound; Compound joined in the twin screw extruder extrude, the fervent pelletizing of low temperature die head, promptly get the sulphur antibacterial matrices.
Embodiment six: the composite plastics material of 60 parts in sulphur, 5 parts of vector resins, 1 part of lubricant, 1 part of dispersion agent, 1.5 parts of coupling agents is put into stirrer stir, temperature to 70 ℃ is processed compound; Compound joined in the twin screw extruder extrude, the fervent pelletizing of low temperature die head, promptly get the sulphur antibacterial matrices.
Embodiment seven: the composite plastics material of 80 parts in sulphur, 8 parts of vector resins, 1.5 parts of lubricants, 1.5 parts of dispersion agents, 0.5 part of coupling agent is put into stirrer stir, temperature to 75 ℃ is processed compound; Compound joined in the twin screw extruder extrude, the fervent pelletizing of low temperature die head, promptly get the sulphur antibacterial matrices.
More than show and described ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; The present invention is not restricted to the described embodiments; That describes in the foregoing description and the specification sheets just explains principle of the present invention; Under the prerequisite that does not break away from spirit and scope of the invention, the present invention also has various changes and modifications, and these variations and improvement all fall in the scope of the invention that requires protection.The present invention requires protection domain to be defined by appending claims and equivalent thereof.
Claims (10)
1. the sulphur antibacterial matrices comprises a master batch matrix, it is characterized in that, and the master batch matrix of said master batch matrix for adopting composite plastics material to process, said composite plastics material includes sulfur material.
2. sulphur antibacterial matrices according to claim 1 is characterized in that: said sulphur accounts for the 60%-80% of said composite plastics material total amount.
3. sulphur antibacterial matrices according to claim 1 is characterized in that: said sulphur adopts medical sulphur.
4. according to claim 1,2 or 3 described sulphur antibacterial matrices, it is characterized in that: said composite plastics material also comprises vector resin, lubricant, dispersion agent, coupling agent.
5. sulphur antibacterial matrices according to claim 4 is characterized in that: said composite plastics material comprises that the material of following parts by weight processes: sulphur 60-80 part, vector resin 5-15 part, lubricant 1-3 part, 0.5～3 part of dispersion agent, 0.5～2 part of coupling agent.
6. sulphur antibacterial matrices according to claim 5 is characterized in that: vector resin is at least a among PP, EVA or the PE.
7. the method for manufacture of sulphur antibacterial matrices is characterized in that, comprises the steps:
1) mixing of composite plastics material: the composite plastics material that will contain sulfur material is put into stirrer and is stirred, and adopts the low temperature preparation, and preparation temperature is no more than 80 ℃, processes compound;
2) extruding pelletization of compound: compound joined in the twin screw extruder extrude, the fervent pelletizing of low temperature die head, promptly get the sulphur antibacterial matrices.
8. the method for manufacture of sulphur antibacterial matrices according to claim 7 is characterized in that: in the step 1), said sulphur accounts for the 60%-80% of said composite plastics material total amount.
9. according to the method for manufacture of claim 7 or 8 described sulphur antibacterial matrices, it is characterized in that: said sulphur adopts medical sulphur.
10. the method for manufacture of sulphur antibacterial matrices according to claim 7 is characterized in that: in the step 1), said composite plastics material also comprises vector resin, lubricant, dispersion agent, coupling agent; Said composite plastics material comprises that the material of following parts by weight processes: sulphur 60-80 part, vector resin 5-15 part, lubricant 1-3 part, 0.5～3 part of dispersion agent, 0.5～2 part of coupling agent.