CN102795817B - 植物纤维陶粒复合保温砌块 - Google Patents

植物纤维陶粒复合保温砌块 Download PDF

Info

Publication number
CN102795817B
CN102795817B CN201210267178.3A CN201210267178A CN102795817B CN 102795817 B CN102795817 B CN 102795817B CN 201210267178 A CN201210267178 A CN 201210267178A CN 102795817 B CN102795817 B CN 102795817B
Authority
CN
China
Prior art keywords
kilograms
vegetable fibre
haydite
cement
flyash
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210267178.3A
Other languages
English (en)
Other versions
CN102795817A (zh
Inventor
杨芳
孙林柱
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WENZHOU QINHAN CERAMSITE LIGHT WALL MATERIALS CO., LTD.
Original Assignee
Wenzhou University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wenzhou University filed Critical Wenzhou University
Priority to CN201210267178.3A priority Critical patent/CN102795817B/zh
Publication of CN102795817A publication Critical patent/CN102795817A/zh
Application granted granted Critical
Publication of CN102795817B publication Critical patent/CN102795817B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开的植物纤维陶粒复合保温砌块包括水泥、粉煤灰、陶粒、陶砂、植物纤维、水和聚氯乙烯泡沫，上述材料质量配比为水泥100-400、粉煤灰30-80、陶粒250、陶砂180或250、植物纤维5.6-34、水167-285、聚氯乙烯泡沫23.8。本发明提供的植物纤维陶粒复合保温砌块用保温材料廉价且兼顾强度和保温效果。

Description

植物纤维陶粒复合保温砌块
技术领域
 本发明涉及一种保温砌块，尤其是采用植物纤维制造的保温砌块。
背景技术
传统保温砌块一般采用水泥、陶粒、陶砂、水和聚氯乙烯泡沫等材料制成，但是这种保温材料对热量反射的能力较差，整体保温隔热效果一般，而且砌块的强度也不理想。
发明内容
本发明所要解决的技术问题是提供一种采用廉价保温材料制成，且兼顾强度和保温效果的植物纤维陶粒复合保温砌块。
为此，本发明提供的植物纤维陶粒复合保温砌块，包括水泥、粉煤灰、陶粒、陶砂、植物纤维、水和聚氯乙烯泡沫，上述材料质量配比为水泥100-400、粉煤灰30-80、陶粒250、陶砂180或250、植物纤维5.6-34、水167-285、聚氯乙烯泡沫23.8，所述植物纤维为稻壳或稻草或麦秸纤维。
 在本发明提供的植物纤维陶粒复合保温砌块中，加入了植物纤维，植物纤维具有反射热量的功效，可使砌块的保温效果大为提高，其中植物纤维一般为稻壳或稻草或麦秸纤维，其材料成本较低，进而可降低砌块的总成本，在此基础上植物纤维与其他材料混合后经压力震动成型，具有超过以往的抗压强度，经试验证明其可在保障砌块强度的基础上，大大降低其导热系数。
附图说明
图中为本发明提供的植物纤维陶粒复合保温砌块的结构剖视示意图。
具体实施方式
本发明提供的物纤维陶粒复合保温砌块包括水泥、粉煤灰、陶粒、陶砂、植物纤维、水和聚氯乙烯泡沫，上述材料质量配比为水泥100-400、粉煤灰30-80、陶粒250、陶砂180或250、植物纤维5.6-34、水167-285、聚氯乙烯泡沫22-25，其中水为混合时的用水量，本发明中的聚氯乙烯泡沫并非采用与其他材料混合的方法，而是在砌块成型后直接插入砌块的孔洞中。以上材料可以在范围内选择，其中植物纤维为稻壳或稻草或麦秸纤维，以稻壳的效果最好，主要原因在于稻壳的内外壁呈弧形，具有很好的热反射效果，而且大量稻壳加入砌块后，多层稻壳层层叠加后能够起到更好的热反射效果。在上述材料中水泥强度等级为42.5，粉煤灰为二级，陶粒粒径5-15MM，陶砂粒径小于5MM，植物纤维长度为3-12mm。
下面以实验数据列表说明本发明提供的植物纤维陶粒复合保温砌块的技术效果：
                               表格中材料质量单位为：千克
传统保温砌块的导热系数一般在0.16至0.25 W/(m·℃），而强度都是3.0 Mpa左右，上述实验列表中导热系数均低于0.16 W/(m·℃），而强度均达到3Mpa以上，因此本发明提供的保温砌块明显具有强度高于或等于传统保温砌块，但导热系数均低于传统保温砌块的性能，因此可以作为新型建筑用环保材料，可大大降低建筑物的能耗。
下面列举三个性能尤其优越的配比案例：
案例1、材料质量分别为水泥300千克、粉煤灰60千克、陶粒250千克、陶砂250千克、稻壳20千克、水285千克、聚氯乙烯泡沫23.8千克。采用上述配比混合而成的材料，经压力震动成型后，干密度达到867 kg/m3，强度3.55Mpa，导热系数为0.1569 W/(m·℃）。其中强度远高于传统砌块的3 Mpa，而导热系数低于传统砌块导热系数的最低值0.16 W/(m·℃）。
案例2、材料质量分别为水泥350千克、粉煤灰70千克、陶粒250千克、陶砂250千克、稻壳20千克、水285千克、聚氯乙烯泡沫23.8千克。采用上述配比混合而成的材料，经压力震动成型后，干密度达到867 kg/m3，强度3.49Mpa，导热系数为0.1478 W/(m·℃）。其中强度远高于传统砌块的3 Mpa，而导热系数低于传统砌块导热系数的最低值0.16 W/(m·℃）。
案例3、材料质量分别为水泥400千克、粉煤灰80千克、陶粒250千克、陶砂250千克、稻壳34千克、水285千克、聚氯乙烯泡沫23.8千克。采用上述配比混合而成的材料，经压力震动成型后，干密度达到950 kg/m3，强度4.34Mpa，导热系数为0.1311 W/(m·℃）。其中强度远高于传统砌块的3 Mpa，而导热系数低于传统砌块导热系数的最低值0.16 W/(m·℃）。本案例为本发明的最佳案例，其中砌块的性能最好。
从上述三种案例中可以观察得出稻壳加入的量增加会大大降低砌块导热系数，通过上述多种材料的混合后压力震动成型，强度并无损失，甚至有所增加，，而且采用的保温材料为稻壳，可降低材料成本，减轻环保压力。以案例3为例，其中的稻壳加入量最大，但是其强度反而是最高的4.34Mpa，导热系数为0.1311 W/(m·℃），从而可得出本发明提供的保温砌块采用了上述配比后可以得到远低于传统保温砌块的导热系数，而且强度并无损失，甚至有所增加，并且制造成本也因大量使用稻壳而降低。

Claims (6)

1.一种植物纤维陶粒复合保温砌块，其特征是：包括水泥、粉煤灰、陶粒、陶砂、植物纤维、水和聚氯乙烯泡沫，上述材料质量配比为水泥100-400、粉煤灰30-80、陶粒250、陶砂180或250、植物纤维5.6-34、水167-285、聚氯乙烯泡沫22-25，所述植物纤维为稻壳或稻草或麦秸纤维。
2.根据权利要求1所述的植物纤维陶粒复合保温砌块，其特征是：所述材料质量分别为水泥300千克、粉煤灰60千克、陶粒250千克、陶砂250千克、植物纤维20千克、水285千克、聚氯乙烯泡沫23.8千克。
3.根据权利要求1所述的植物纤维陶粒复合保温砌块，其特征是：所述材料质量分别为水泥350千克、粉煤灰70千克、陶粒250千克、陶砂250千克、植物纤维20千克、水285千克、聚氯乙烯泡沫23.8千克。
4.根据权利要求1所述的植物纤维陶粒复合保温砌块，其特征是：所述材料质量分别为水泥400千克、粉煤灰80千克、陶粒250千克、陶砂250千克、植物纤维34千克、水285千克、聚氯乙烯泡沫23.8千克。
5.根据权利要求1所述的植物纤维陶粒复合保温砌块，其特征是：所述水泥强度等级为42.5，粉煤灰为二级，陶粒粒径5-15MM，陶砂粒径小于5MM，植物纤维长度为3-12mm。
6.根据权利要求2或3或4所述的植物纤维陶粒复合保温砌块，其特征是：所述水泥强度等级为42.5，粉煤灰为二级，陶粒粒径5-15MM，陶砂粒径小于5MM，植物纤维长度为3-12mm。
CN201210267178.3A 2012-07-30 2012-07-30 植物纤维陶粒复合保温砌块 Expired - Fee Related CN102795817B (zh)