CN102766931A - Process for antistatic and antibacterial nylon 6FDY filament - Google Patents
Process for antistatic and antibacterial nylon 6FDY filament Download PDFInfo
- Publication number
- CN102766931A CN102766931A CN2012102152349A CN201210215234A CN102766931A CN 102766931 A CN102766931 A CN 102766931A CN 2012102152349 A CN2012102152349 A CN 2012102152349A CN 201210215234 A CN201210215234 A CN 201210215234A CN 102766931 A CN102766931 A CN 102766931A
- Authority
- CN
- China
- Prior art keywords
- nylon
- godet roller
- speed
- long filament
- antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a process for an antistatic and antibacterial nylon 6FDY filament. The 6FDY filament is prepared from raw materials containing nylon chips and additives on a high-speed spinning device by a process route comprising a screw extruder, a pre-filter, a static mixer, a metering pump, a spinning assembly, flow, side blowing, oil application, a spinning shaft, a first godet, a second godet, a third godet and winding. The prepared FDY filament has antistatic and antibacterial function, and good stability, and can meet different requirements of post-weaving finishing.
Description
Technical field
The invention belongs to the spinning material field, be specifically related to a kind of section and produce nylon 6 FDY long filament technologies.
Background technology
Take synthetic fiber at present terylene (polyester), polyamide fibre (polyamide), polypropylene fibre (polypropylene), spandex (polyurethane), acrylic fibers (polyacrylonitrile) etc. are generally arranged.These fibers have different qualities, thereby different purposes is also arranged.But at present general wearing fabric, because its fiber is thicker, feel is coarse, flexibility is poor, gas permeability is poor, water imbibition is poor, be easy to pilling.The Along with people's growth in the living standard, also increasingly high for the dress requirement of textiles.
Polyamide fiber is the synthetic fiber kind that drops into suitability for industrialized production in the world the earliest; It is to be raw material by aliphatic dibasic acid and diamine or aliphatic amino acid through the synthetic polyamide of polycondensation reaction, again through the general name of the prepared one type of synthetic fiber of melt spinning.Owing to all contain amido link therein, so be referred to as polyamide fiber.It belongs to a kind of of heterochain class synthetic fiber.Wherein the output with polycaprolactone nylon (Nylon6, polyamide fibre 6, nylon 6) and poly fibre (Nylon66, polyamide fibre 66, nylon 66) is maximum, uses the widest.Polyamide fibre is not only industrialized the earliest synthetic fiber kind; And it also has multiple good characteristic; It has higher intensity, elasticity, and wear-resisting weather resisteant is good, thereby the consumers in general's that experience welcome; But along with improving constantly of living standards of the people, people to the diversity of clothes, comfortableness, functional requirement also more and more widely.Fiber finer dawnization, functionalization are important directions of fibre in differentiation development, also are the main development trends of polyamide fiber spinning.Compare with conventional polyamide fibre, differential nylon fibre has more excellent performance: gas permeability, compliance, comfortableness, dyeability, functional etc., exploitation variety classes, just like a raging fire the carrying out of research novel, the functional polyalkylene nylon.
Summary of the invention
In order to satisfy diversity, comfortableness, the functional requirement of people to clothes, continually develop out novel functional polyalkylene nylon, the objective of the invention is to develop a kind of have antistatic and polyamide fiber antibacterial functions.
In order to solve the above-mentioned technical problem that exists in the prior art, reach the described purpose of invention, the present invention has adopted following technical scheme:
A kind of nylon 6 FDY long filament technologies of antistatic, antibacterial functions; It is meant on high-speed spinning equipment with nylon 6 slice and additive is raw material; The process route of employing screw extruder-prefilter-static mixer-measuring pump-filament spinning component-thread-lateral blowing-oil-path-first godet roller-second godet roller-the 3rd godet roller-coiling; It is characterized in that: the weight with described nylon 6 slice is benchmark; Described additive comprises the methacrylic acid hydroxyethyl ester of 0.45-0.90wt%, the lithium iodide of 0.25-0.30wt%, the barium sulfate of 0.4-0.8wt%; The zeolite with carrying silver of 0.20-0.25wt%, the catalyst of 1.2-1.8wt% and the dispersant of 0.50-1.20wt%.
Wherein, described catalyst is a sodium metasilicate.
Wherein, described dispersant is a PLA.
Wherein, also containing particle diameter in the described raw material is the titanium dioxide fine particles below 3 microns, with preparation FD/SD fiber.
Wherein, Spinning temperature is 273-275 ℃, and the lateral blowing mode is adopted in cooling, and the blowing wind-warm syndrome is 25-30 ℃; The cooling wind speed is 0.1-0.5 ℃; The speed of first godet roller is 4000-4500 m/min, and the speed of second godet roller is 5000-5500 m/min, and the speed of the 3rd godet roller is 5000-5500 m/min.
Compared with prior art, the present invention has the following advantages: process of the present invention is simple, but and the nylon 6 for preparing not only has and common nylon 6 akin mechanical properties and textile performance, also have good antibiotic and antistatic property.The polyamide filaments that technology of the present invention is applicable to preparation 20D-70D adds delustering agent simultaneously and can prepare corresponding full-dull or half delustring product.
The specific embodiment
Below in conjunction with embodiment, technical scheme of the present invention is done further to set forth.Should be appreciated that scope of the present invention is not limited to following embodiment, all will fall into protection domain of the present invention any pro forma modification and/or the change that the present invention made.
Nylon 6 slice: relative viscosity 2.48 ± 0.02, density 1.14g/cm3, fusing point is 214-223 ℃, moisture content is less than 600ppm.
Embodiment 1
A kind of nylon 6 FDY long filament technologies of antistatic, antibacterial functions; It is meant on high-speed spinning equipment with nylon 6 slice and additive is raw material; Adopting the process route of screw extruder-prefilter-static mixer-measuring pump-filament spinning component-thread-lateral blowing-oil-path-first godet roller-second godet roller-the 3rd godet roller-coiling, wherein, is benchmark with the weight of described nylon 6 slice; Described additive comprises the methacrylic acid hydroxyethyl ester of 0.45-0.90wt%; The lithium iodide of 0.25wt%, the barium sulfate of 0.4wt%, the zeolite with carrying silver of 0.20wt%; The sodium metasilicate of 1.2wt% and the PLA of 0.50wt%, the consumption of titanium dioxide fine particles are 0.75wt%.The temperature of screw extruder is 180-200 ℃; Spinning temperature is 273-275 ℃, and the lateral blowing mode is adopted in cooling, and the blowing wind-warm syndrome is 25-30 ℃; The cooling wind speed is 0.1-0.5 ℃; The speed of first godet roller is 4000 m/min, and the speed of second godet roller is 5000 m/min, and the speed of the 3rd godet roller is 5000 m/min.
Embodiment 2
A kind of nylon 6 FDY long filament technologies of antistatic, antibacterial functions; It is meant on high-speed spinning equipment with nylon 6 slice and additive is raw material; Adopting the process route of screw extruder-prefilter-static mixer-measuring pump-filament spinning component-thread-lateral blowing-oil-path-first godet roller-second godet roller-the 3rd godet roller-coiling, wherein, is benchmark with the weight of described nylon 6 slice; Described additive comprises the methacrylic acid hydroxyethyl ester of 0.90wt%; The lithium iodide of 0.30wt%, the barium sulfate of 0.8wt%, the zeolite with carrying silver of 0.25wt%; The sodium metasilicate of 1.8wt% and the PLA of 1.20wt%, the consumption of titanium dioxide fine particles are 2.0wt%.The temperature of screw extruder is 180-200 ℃; Spinning temperature is 273-275 ℃, and the lateral blowing mode is adopted in cooling, and the blowing wind-warm syndrome is 25-30 ℃; The cooling wind speed is 0.1-0.5 ℃; The speed of first godet roller is 4000 m/min, and the speed of second godet roller is 5000 m/min, and the speed of the 3rd godet roller is 5000 m/min.
Embodiment 3
On high-speed spinning equipment, be raw material with nylon 6 slice and additive; Adopting the process route of screw extruder-prefilter-static mixer-measuring pump-filament spinning component-thread-lateral blowing-oil-path-first godet roller-second godet roller-the 3rd godet roller-coiling, wherein, is benchmark with the weight of described nylon 6 slice; Described additive comprises the methacrylic acid hydroxyethyl ester of 0.6wt%; The lithium iodide of 0.27wt%, the barium sulfate of 0.6wt%, the zeolite with carrying silver of 0.23wt%; The sodium metasilicate of 1.5wt% and the PLA of 0.8wt%, the consumption of titanium dioxide fine particles are 1.5wt%.The temperature of screw extruder is 180-200 ℃; Spinning temperature is 273-275 ℃, and the lateral blowing mode is adopted in cooling, and the blowing wind-warm syndrome is 25-30 ℃; The cooling wind speed is 0.1-0.5 ℃; The speed of first godet roller is 4000 m/min, and the speed of second godet roller is 5000 m/min, and the speed of the 3rd godet roller is 5000 m/min.
Although the inventor has done comparatively detailed elaboration to technical scheme of the present invention and has enumerated; Be to be understood that; For one of ordinary skill in the art, according to disclosed content, the foregoing description is made modification and/or changed or adopt the replacement scheme that is equal to is conspicuous; It all can not break away from the present invention and require the scope protected, and the protection domain among the present invention is as the criterion with the claim that is limited in claims.
Claims (5)
1. the nylon 6 FDY long filament technologies of antistatic a, antibacterial functions; It is meant on high-speed spinning equipment with nylon 6 slice and additive is raw material; The process route of employing screw extruder-prefilter-static mixer-measuring pump-filament spinning component-thread-lateral blowing-oil-path-first godet roller-second godet roller-the 3rd godet roller-coiling; It is characterized in that: the weight with described nylon 6 slice is benchmark; Described additive comprises the methacrylic acid hydroxyethyl ester of 0.35-0.72wt%, the lithium iodide of 0.12-0.25wt%, the barium sulfate of 0.4-0.8wt%; The zeolite with carrying silver of 0.20-0.25wt%, the catalyst of 1.2-1.8wt% and the dispersant of 0.50-1.20wt%.
2. the described nylon 6 FDY long filament technologies of claim 1 is characterized in that described catalyst is a sodium metasilicate.
3. the described nylon 6 FDY long filament technologies of claim 1 is characterized in that described dispersant is a PLA.
4. described nylon 6 FDY long filament technologies of claim 1, it is characterized in that also containing in the described raw material particle diameter is the titanium dioxide fine particles below 3 microns, with preparation FD/SD fiber.
5. described nylon 6 FDY long filament technologies of claim 1; It is characterized in that spinning temperature is 273-275 ℃, the lateral blowing mode is adopted in cooling, and the blowing wind-warm syndrome is 25-30 ℃; The cooling wind speed is 0.1-0.5 ℃; The speed of first godet roller is 4000-4500 m/min, and the speed of second godet roller is 5000-5500 m/min, and the speed of the 3rd godet roller is 5000-5500 m/min.