CN102766921A - Process for chinlon 6 DTY high elastic yarn - Google Patents
Process for chinlon 6 DTY high elastic yarn Download PDFInfo
- Publication number
- CN102766921A CN102766921A CN201210212295XA CN201210212295A CN102766921A CN 102766921 A CN102766921 A CN 102766921A CN 201210212295X A CN201210212295X A CN 201210212295XA CN 201210212295 A CN201210212295 A CN 201210212295A CN 102766921 A CN102766921 A CN 102766921A
- Authority
- CN
- China
- Prior art keywords
- dty
- false
- poy
- consumption
- technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a process for a chinlon 6 DTY high elastic yarn. The chinlon 6 DTY high elastic yarn is prepared from raw materials comprising polyamide 6 chips, a tulip powder capsule, an antioxidant, a metal salt catalyst and a dispersant by a POY-DTY process. The prepared DTY high elastic yarn has fresh and long-lasting fragrance and good stability, and can meet different requirements of post-weaving finishing.
Description
Technical field
The invention belongs to the spinning material field, be specifically related to a kind of the section and produce the spinning technique of polyamide fiber.
Background technology
Take synthetic fiber at present terylene (polyester), polyamide fibre (polyamide), polypropylene fibre (polypropylene), spandex (polyurethane), acrylic fibers (polyacrylonitrile) etc. are generally arranged.These fibers have different qualities, thereby different purposes is also arranged.But at present general wearing fabric, because its fiber is thicker, feel is coarse, flexibility is poor, gas permeability is poor, water imbibition is poor, be easy to pilling.The Along with people's growth in the living standard, also increasingly high for the dress requirement of textiles.
Polyamide fiber is the synthetic fiber kind that drops into suitability for industrialized production in the world the earliest; It is to be raw material by aliphatic dibasic acid and diamine or aliphatic amino acid through the synthetic polyamide of polycondensation reaction, again through the general name of the prepared one type of synthetic fiber of melt spinning.Owing to all contain amido link therein, so be referred to as polyamide fiber.It belongs to a kind of of heterochain class synthetic fiber.Wherein the output with polycaprolactone nylon (Nylon6, polyamide fibre 6, polyamide 6) and poly fibre (Nylon66, polyamide fibre 66, polyamide 66) is maximum, uses the widest.Polyamide fibre is not only industrialized the earliest synthetic fiber kind; And it also has multiple good characteristic; It has higher intensity, elasticity, and wear-resisting weather resisteant is good, thereby the consumers in general's that experience welcome; But along with improving constantly of living standards of the people, people to the diversity of clothes, comfortableness, functional requirement also more and more widely.Fiber finer dawnization, functionalization are important directions of fibre in differentiation development, also are the main development trends of polyamide fiber spinning.Compare with conventional polyamide fibre, differential nylon fibre has more excellent performance: gas permeability, compliance, comfortableness, dyeability, functional etc., exploitation variety classes, just like a raging fire the carrying out of research novel, the functional polyalkylene nylon.
Summary of the invention
In order to satisfy diversity, comfortableness, the functional requirement of people to clothes, continually develop out novel functional nylon-6 fiber, the objective of the invention is to develop a kind of nylon-6 fiber with aromatic function.
In order to solve the above-mentioned technical problem that exists in the prior art, reach the described purpose of invention, the present invention has adopted following technical scheme:
A kind of polyamide fibre 6 DTY fiber false-twist textured yarn technologies; It is meant with chinlon 6 section, tulip powder capsule, anti-oxidant, metal salt catalyst and dispersant is that raw material adopts the manufacturing of POY-DTY technology; It is characterized in that: the weight with chinlon 6 section is benchmark, and the consumption of tulip powder capsule is 0.15-0.48wt%, and the consumption of anti-oxidant is: 0.12-0.35wt%; Catalyst consumption is 0.75-1.25wt%, and the consumption of dispersant is 0.50-1.20wt%.
Wherein, in said POY-DTY technology, the process route of POY is: screw extruder → prefilter → static mixer → measuring pump → filament spinning component → spray silk → lateral blowing oils → path → POY undrawn yarn; Wherein: spinning temperature: 270-278 ℃; The lateral blowing condition: wind speed is 0.2-0.5 m/s, wind-warm syndrome 25-30 ℃, relative humidity 60-75%; The rate of oiling is 0.70-1.50%; Spinning speed is 3500-4500 m/min; Wherein, the DTY production process route is: the hot case → coldplate of thread guide → feeding roller → first → false twister → delivery roller → oiling device → DTY undrawn yarn; Wherein, first heater temperature is 140-175 ℃, and D/Y ratio is 1. 2-1.8, and drafting multiple is 1.20-1.30.
Wherein, described tulip powder capsule can be in urethane raw, to disperse the formed polyurethane microcapsule of root tuber of aromatic turmeric face powder, also can other be dispersed with the microcapsules of root tuber of aromatic turmeric face powder.
Wherein, described anti-oxidant is phosphite antioxidant DP-613.
Wherein, described metal salt catalyst is a zinc sulfate.
Wherein, described dispersant is a Tissuemat E.
Wherein, also containing particle diameter in the described raw material is the titanium dioxide fine particles below 3 microns, with preparation FD fiber.
Compared with prior art; The present invention has following beneficial technical effects: used to 1. the invention property tulip powder capsule raw material; Add specific metal salt catalyst simultaneously and change the nylon melt structure, prepared the DTY false-twist textured yarn with delicate fragrance fragrance, the fragrance durability is long; And good stability, weave the different demands of arrangement processing after can satisfying.2. through adjustment related process parameter, the polyamide fibre 6 DTY false-twist textured yarns that technology of the present invention is applicable to preparation 20D-70D add delustering agent simultaneously and can prepare corresponding full-dull false-twist textured yarn.
The specific embodiment
Below in conjunction with embodiment, content of the present invention is described more specifically.Should be appreciated that enforcement of the present invention is not limited to following embodiment, all will fall into protection domain of the present invention any pro forma modification and/or the change that the present invention made.
Chinlon 6 section: relative viscosity 2.47 ± 0.02, density 1.14g/cm
3, fusing point is 215-222 ℃, moisture content is less than 600ppm.
Embodiment 1
With chinlon 6 section, tulip powder capsule, anti-oxidant, metal salt catalyst and dispersant is raw material; Adopt the said DTY false-twist textured yarn of POY-DTY prepared; Wherein in said POY-DTY technology, the process route of POY is: screw extruder → prefilter → static mixer → measuring pump → filament spinning component → spray silk → lateral blowing oils → path → POY undrawn yarn; Wherein: spinning temperature: 270-278 ℃; The lateral blowing condition: wind speed is 0.2-0.5 m/s, wind-warm syndrome 25-30 ℃, relative humidity 60-75%; The rate of oiling is 0.70-1.50%; Spinning speed is 3500-4500 m/min; Wherein, the DTY production process route is: the hot case → coldplate of thread guide → feeding roller → first → false twister → delivery roller → oiling device → DTY undrawn yarn; Wherein, first heater temperature is 140-175 ℃, and D/Y ratio is 1. 2-1.8, and drafting multiple is 1.20-1.30.Said raw material is a benchmark with the weight of chinlon 6 section, and the consumption of tulip powder capsule is 0.15wt%, and the consumption of phosphite antioxidant DP-613 is: 0.12wt%, the consumption of zinc sulfate are 0.8wt%, and the consumption of Tissuemat E is 0.50wt%; The consumption of titanium dioxide fine particles is 2.0 wt%.
Embodiment 2
With chinlon 6 section, tulip powder capsule, anti-oxidant, metal salt catalyst and dispersant is raw material; Adopt the said DTY false-twist textured yarn of POY-DTY prepared; Wherein in said POY-DTY technology, the process route of POY is: screw extruder → prefilter → static mixer → measuring pump → filament spinning component → spray silk → lateral blowing oils → path → POY undrawn yarn; Wherein: spinning temperature: 270-278 ℃; The lateral blowing condition: wind speed is 0.2-0.5 m/s, wind-warm syndrome 25-30 ℃, relative humidity 60-75%; The rate of oiling is 0.70-1.50%; Spinning speed is 3500-4500 m/min; Wherein, the DTY production process route is: the hot case → coldplate of thread guide → feeding roller → first → false twister → delivery roller → oiling device → DTY undrawn yarn; Wherein, first heater temperature is 140-175 ℃, and D/Y ratio is 1. 2-1.8, and drafting multiple is 1.20-1.30.Wherein, said raw material is a benchmark with the weight of chinlon 6 section, and the consumption of tulip powder capsule is 0.48wt%, and the consumption of phosphite antioxidant DP-613 is: 0.25wt%, the consumption of zinc acetate are 1.2wt%, and the consumption of Tissuemat E is 1.20wt%; The consumption of titanium dioxide fine particles is 2.0wt%.
Embodiment 3
With chinlon 6 section, tulip powder capsule, anti-oxidant, metal salt catalyst and dispersant is raw material; Adopt the said DTY false-twist textured yarn of POY-DTY prepared; Wherein in said POY-DTY technology, the process route of POY is: screw extruder → prefilter → static mixer → measuring pump → filament spinning component → spray silk → lateral blowing oils → path → POY undrawn yarn; Wherein: spinning temperature: 270-278 ℃; The lateral blowing condition: wind speed is 0.2-0.5 m/s, wind-warm syndrome 25-30 ℃, relative humidity 60-75%; The rate of oiling is 0.70-1.50%; Spinning speed is 3500-4500 m/min; Wherein, the DTY production process route is: the hot case → coldplate of thread guide → feeding roller → first → false twister → delivery roller → oiling device → DTY undrawn yarn; Wherein, first heater temperature is 140-175 ℃, and D/Y ratio is 1. 2-1.8, and drafting multiple is 1.20-1.30.Wherein, said raw material is a benchmark with the weight of chinlon 6 section, and the consumption of tulip powder capsule is 0.36wt%, and the consumption of phosphite antioxidant DP-613 is: 0.35wt%; The consumption of zinc sulfate is 1.0wt%, and the consumption of Tissuemat E is 1. 0wt%; The consumption of titanium dioxide fine particles is 2. 0wt%.
Although the inventor has done comparatively detailed elaboration to technical scheme of the present invention and has enumerated; Be to be understood that; For one of ordinary skill in the art, according to disclosed content, the foregoing description is made modification and/or changed or adopt the replacement scheme that is equal to is conspicuous; It all can not break away from the present invention and require the scope protected, and the protection domain among the present invention is as the criterion with the claim that is limited in claims.
Claims (6)
1. polyamide fibre 6 DTY fiber false-twist textured yarn technologies; It is meant with chinlon 6 section, tulip powder capsule, anti-oxidant, metal salt catalyst and dispersant is that raw material adopts the manufacturing of POY-DTY technology; It is characterized in that: the weight with chinlon 6 section is benchmark, and the consumption of tulip powder capsule is 0.15-0.48wt%, and the consumption of anti-oxidant is: 0.12-0.35wt%; Catalyst consumption is 0.75-1.25wt%, and the consumption of dispersant is 0.50-1.20wt%.
2. the described DTY fiber of claim 1 false-twist textured yarn technology; It is characterized in that the process route of POY is in said POY-DTY technology: screw extruder → prefilter → static mixer → measuring pump → filament spinning component → spray silk → lateral blowing oils → path → POY undrawn yarn; Wherein: spinning temperature: 270-278 ℃; The lateral blowing condition: wind speed is 0.2-0.5 m/s, wind-warm syndrome 25-30 ℃, relative humidity 60-75%; The rate of oiling is 0.70-1.50%; Spinning speed is 3500-4500 m/min; Wherein, the DTY production process route is: the hot case → coldplate of thread guide → feeding roller → first → false twister → delivery roller → oiling device → DTY undrawn yarn; Wherein, first heater temperature is 140-175 ℃, and D/Y ratio is 1. 2-1.8, and drafting multiple is 1.20-1.30.
3. the described DTY fiber of claim 1 false-twist textured yarn technology is characterized in that described tulip powder capsule can be in urethane raw, to disperse the formed polyurethane microcapsule of root tuber of aromatic turmeric face powder.
4. the described DTY fiber of claim 1 false-twist textured yarn technology is characterized in that described anti-oxidant is phosphite antioxidant DP-613.
5. the described DTY fiber of claim 1 false-twist textured yarn technology is characterized in that described metal salt catalyst is a zinc sulfate.
6. the described DTY fiber of claim 1 false-twist textured yarn technology is characterized in that described dispersant is a Tissuemat E.