CN102731157A - Lead-containing assistant of frit used for preparation of ceramics - Google Patents
Lead-containing assistant of frit used for preparation of ceramics Download PDFInfo
- Publication number
- CN102731157A CN102731157A CN2012101953227A CN201210195322A CN102731157A CN 102731157 A CN102731157 A CN 102731157A CN 2012101953227 A CN2012101953227 A CN 2012101953227A CN 201210195322 A CN201210195322 A CN 201210195322A CN 102731157 A CN102731157 A CN 102731157A
- Authority
- CN
- China
- Prior art keywords
- parts
- frit
- preparation
- leaded
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a lead-containing assistant of a frit used for preparation of ceramics. The assistant is prepared from the following raw materials by weight: 20-40 parts of SiO2, 5-15 parts of Al2O3, 5-15 parts of an alkali metal, 10-20 parts of PbO, 3-8 parts of acetophenone, and 3-5 parts of a defoaming agent. The lead-containing assistant of the frit used for preparation of ceramics provided by the invention has scientific and reasonable component proportioning, can promote frit fusion, lower fusion temperature, and prevent high temperature volatilization of materials. And the prepared glaze slip has good performance and can be used in a wide range.
Description
?
Technical field
The present invention relates to a kind of frit for preparing ceramic usefulness, be specifically related to a kind of leaded auxiliary agent for preparing pottery with frit.
Background technology
Frit is the important source material of preparation pottery, can water-soluble raw material be processed water-fast raw material, can deleterious raw material be processed nontoxic raw material; But the frit meltbility that present potting is used is relatively poor, and the temperature of burning paper as sacrificial offerings height is when temperature is high; Can make the volatilization of part material material, product performance are reduced, therefore necessary on the basis of prior art; The research and development design is a kind of to promote the frit fusion, reduces the leaded auxiliary agent of the preparation pottery of fusion firing temperature with frit.
Summary of the invention
Goal of the invention: technical problem to be solved by this invention is the deficiency that overcomes prior art, provides a kind of and can promote the frit fusion, reduction fusion firing temperature, the leaded auxiliary agent that the glaze slip performance is good.
Technical scheme: for solving above technical problem, the present invention takes following technical scheme:
A kind of leaded auxiliary agent for preparing pottery with frit, it is processed by the raw material of following parts by weight:
SiO
220 ~ 40 parts, Al
2O
35 ~ 15 parts, 5 ~ 15 parts in basic metal, PbO10 ~ 20 part, 3 ~ 8 parts of methyl phenyl ketones, 3 ~ 5 parts of skimmers.
As preferred version, above-described preparation pottery is with the leaded auxiliary agent of frit, and it is processed by the raw material of following parts by weight:
SiO
220 ~ 30 parts, Al
2O
35 ~ 10 parts, 5 ~ 10 parts in basic metal, PbO10 ~ 15 part, 3 ~ 5 parts of methyl phenyl ketones, 3 ~ 5 parts of skimmers.
As preferred version, above-described preparation pottery is with the leaded auxiliary agent of frit, and it is processed by the raw material of following parts by weight:
SiO
230 parts, Al
2O
310 parts, 10 parts in basic metal, PbO15 part, 5 parts of methyl phenyl ketones, 5 parts of skimmers.
As preferred version, above-described preparation pottery is with the leaded auxiliary agent of frit, and described basic metal is K
2O or Na
2O.
The present invention is directed to the deficiency of the higher grade of frit melt temperature in the prior art; Confirm that through a large amount of experiments the preparation pottery is with the composition of the leaded auxiliary agent of frit and the ratio of each component; Test experience result shows that the each component proportioning is scientific and reasonable, and leaded auxiliary agent provided by the invention can promote the fusion of frit; Reduce melt temperature, prevent the material vaporization at high temperature.
Beneficial effect: preparation pottery provided by the invention is compared with prior art with the leaded auxiliary agent of frit has following advantage:
Preparation pottery provided by the invention is formed according to the best of the preferred frit of a large amount of experiments with the leaded auxiliary agent of frit, and the each component proportioning is scientific and reasonable; The Ceramic glaze slickness that frit prepares is good, enamel is good; Milky white color and luster is even, the glaze slip performance is good, and firing property is good, and sintering technology is simple; Preparation cost is low, and the scope of application is extensive.
Embodiment
Below in conjunction with specific embodiment; Further illustrate the present invention; Should understand these embodiment only be used to the present invention is described and be not used in the restriction scope of the present invention; After having read the present invention, those skilled in the art all fall within the application's accompanying claims institute restricted portion to the modification of the various equivalent form of values of the present invention.
Embodiment 1
A kind of leaded auxiliary agent for preparing pottery with frit, it is processed by the raw material of following parts by weight:
SiO
240 parts, Al
2O
315 parts, 15 parts in basic metal, PbO20 part, 8 parts of methyl phenyl ketones, 5 parts of skimmers.
Embodiment 2
A kind of leaded auxiliary agent for preparing pottery with frit, it is processed by the raw material of following parts by weight:
SiO
220 parts, Al
2O
35 parts, 5 parts in basic metal, PbO10 part, 3 parts of methyl phenyl ketones, 3 parts of skimmers.
Embodiment 3
A kind of leaded auxiliary agent for preparing pottery with frit, it is processed by the raw material of following parts by weight:
SiO
230 parts, Al
2O
310 parts, 10 parts in basic metal, PbO15 part, 5 parts of methyl phenyl ketones, 5 parts of skimmers.
The above only is a preferred implementation of the present invention; Should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the principle of the invention; Can also make some improvement and retouching, these improvement and retouching also should be regarded as protection scope of the present invention.
Claims (4)
1. one kind prepares pottery with the leaded auxiliary agent of frit, it is characterized in that it is processed by the raw material of following parts by weight:
SiO
220 ~ 40 parts, Al
2O
35 ~ 15 parts, 5 ~ 15 parts in basic metal, PbO10 ~ 20 part, 3 ~ 8 parts of methyl phenyl ketones, 3 ~ 5 parts of skimmers.
2. preparation pottery according to claim 1 is characterized in that with the leaded auxiliary agent of frit it is processed by the raw material of following parts by weight:
SiO
220 ~ 30 parts, Al
2O
35 ~ 10 parts, 5 ~ 10 parts in basic metal, PbO10 ~ 15 part, 3 ~ 5 parts of methyl phenyl ketones, 3 ~ 5 parts of skimmers.
3. preparation pottery according to claim 1 is characterized in that with the leaded auxiliary agent of frit it is processed by the raw material of following parts by weight:
SiO
230 parts, Al
2O
310 parts, 10 parts in basic metal, PbO15 part, 5 parts of methyl phenyl ketones, 5 parts of skimmers.
4. according to the leaded auxiliary agent of each described preparation pottery of claim 1 to 3, it is characterized in that described basic metal is K with frit
2O or Na
2O.