CN102717569A - Manufacturing method and apparatus of high polymer sizing composite cloth - Google Patents
Manufacturing method and apparatus of high polymer sizing composite cloth Download PDFInfo
- Publication number
- CN102717569A CN102717569A CN2012101996576A CN201210199657A CN102717569A CN 102717569 A CN102717569 A CN 102717569A CN 2012101996576 A CN2012101996576 A CN 2012101996576A CN 201210199657 A CN201210199657 A CN 201210199657A CN 102717569 A CN102717569 A CN 102717569A
- Authority
- CN
- China
- Prior art keywords
- base cloth
- composite bed
- mill
- warm
- chemical fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing method of a high polymer sizing composite cloth, which comprises the following steps: respectively suspending a front and back polyvinyl chloride films and chemical fiber base cloth into a feed rack, and feeding the materials after starting the apparatus; heating and ironing the front and back polyvinyl chloride films, and transferring the front and back polyvinyl chloride films into a sizing tank; respectively heating and mixing the front and back polyvinyl chloride films with a high polymer paste resin in the sizing tank to form a surface composite layer and a bottom composite layer; preheating the surface composite layer and the bottom composite layer with heating rollers, wherein the heating rollers respectively guide the surface composite layer and the bottom composite layer to be separated, and the chemical fiber base cloth is guided by a rolling device to be separated and sent into a main press roller; compacting the surface composite layer and the bottom composite layer with the chemical fiber base cloth through the main press roller to form composite cloth; cooling the composite cloth through five cooling rollers; inspecting, and trimming; and finally, coiling and packaging the composite cloth according to the requirements. Thus, the composite cloth feels good, and is easy to produce.
Description
Technical field
The present invention relates to a kind of preparation method and making apparatus of chemical synthesis cloth, relate in particular to a kind of good hand touch, produce the preparation method and the making apparatus of simple chemical synthesis cloth.
Background technology
There is a kind of manufacture craft of chemical synthesis cloth to be called cutter sheaing technology at present; This technology is the tow sides that liquid polyvinyl chloride (PVC) slurry are applied to base cloth with uniform Qiao of some anti-scrapers; Make it be combined into integral body, a cooling forming afterwards fully through stoving process then.Be characterized in that anti-permeability, stretching resistance, antistripping ability are stronger.Because the knife scraping method product is up and down an integral body, make and peel off phenomenon and be able to stop, and the intensity that can make jointing positions through welding is greater than product itself.But its complex manufacturing technology, making apparatus are relatively more expensive, and therefore, this series products is main with import on Chinese market.The cutter sheaing front that forms through this technology is pliable and tough smooth, but the back side is coarse, and graininess is thicker and inhomogeneous, and such cloth production efficiency is low, and is very high to the base cloth requirement, and converted products is had limitation.
Summary of the invention
For overcoming the deficiency of prior art; The preparation method and the making apparatus that the purpose of this invention is to provide a kind of macromolecule starching Compound Fabric; The Compound Fabric good hand touch of this method processing is produced simply, and production efficient is high; Few and this equipment of equipment investment also can be produced other joint product, and equipment processing ability is strong, be fit to any base cloth processing, applied range.
For realizing above-mentioned purpose, the present invention realizes through following technical scheme:
A kind of preparation method of macromolecule starching Compound Fabric, it may further comprise the steps:
1) at first positive and negative two-layer pvc film and chemical fibre base cloth are hung on the discharging frame separately, carry out start and prepare, start back blowing;
2) then positive and negative two-layer pvc film heating pressing is transported in the oar groove;
3) follow positive and negative two-layer pvc film and in last stock tank, mix formation surface layer and bottom composite bed respectively with the heating of macromolecule paste resin;
4) carry out preheating with warm-up mill facings and bottom composite bed;
5) warm-up mill deflects from surface layer and bottom composite bed get off respectively simultaneously, and the chemical fibre base cloth also deflects from through tourelle and gets off to send into main pressure roller;
6) surface layer composite bed, bottom composite bed and chemical fibre base cloth compress through main pressure roller and are compounded to form Compound Fabric;
7) through five cooling running rollers Compound Fabric is cooled off;
8) the cooling back Compound Fabric processing of after cloth examination platform check, check, cutting edge;
9) as requested Compound Fabric being carried out the bundling packing at last embarks on journey.
Said 2) heating and temperature control in is at 60-80 ℃.
The temperature of the warm-up mill said 4) is controlled at 170-180 ℃.
Said 1) the positive and negative two-layer pvc behind the blowing in is the both sides that are positioned at the chemical fibre base cloth behind the blowing; Said 6) the surface layer composite bed in compresses the front that is compounded in the chemical fibre base cloth, and the bottom composite bed compresses the reverse side that is compounded in the chemical fibre base cloth, has promptly formed Compound Fabric.
Another kind of technical scheme:
A kind of making apparatus of macromolecule starching Compound Fabric, it comprise first discharging frame of placing the chemical fibre base cloth, respectively place positive and negative two-layer pvc film second discharging frame and the 3rd discharging frame, facing to positive and negative two-layer pvc film heat pressing first heater and second heater, supply positive and negative two-layer pvc film and macromolecule paste resin mixing surface layer and bottom composite bed first on the stock tank and second stock tank, facings and bottom composite bed carry out preheating first warm-up mill and second warm-up mill, the chemical fibre base cloth is deflected from the tourelle that gets off and surface layer, bottom composite bed and chemical fibre base cloth is compressed compound main pressure roller; Stock tank on the stock tank and second on second discharging frame and the 3rd discharging frame, first heater and second heater, first, and first warm-up mill and second warm-up mill all be symmetrical set with respect to main pressure roller; Stock tank, first warm-up mill and main pressure roller link together through transmission device and realize coherent transportation on second discharging frame, first heater, first, and stock tank, second warm-up mill and main pressure roller also are to link together through transmission device to realize coherent transportation on the 3rd discharging frame, second heater, second.
Compared with prior art, the invention has the beneficial effects as follows:
Through being mixed with the macromolecule paste resin, positive and negative two-layer pvc forms surface layer and bottom composite bed; Compressing compound through main pressure roller surface layer and bottom composite bed and chemical fibre base cloth; The macromolecule starching Compound Fabric good hand touch that forms like this; Produce simply, production efficient is high, can satisfy any base cloth processing, the range of work is wide.
Description of drawings
Fig. 1 is the front view of macromolecule starching Compound Fabric making apparatus of the present invention.
Fig. 2 is a macromolecule starching Compound Fabric manufacture craft flow chart of the present invention.
Among the figure: stock tank 8-the first warm-up mill 9-the second warm-up mill 10-tourelle 11-main pressure roller 12-transmission device on the stock tank 7-the second on the 1-first discharging frame 2-second discharging frame 3-the 3rd discharging frame 4-first heater 5-second heater 6-the first
The specific embodiment
Below in conjunction with accompanying drawing making apparatus and the preparation method of the present invention in concrete production described in further detail.
As shown in Figure 1; A kind of making apparatus of macromolecule starching Compound Fabric, it comprise first discharging frame 1 of placing the chemical fibre base cloth, respectively place positive and negative two-layer pvc film second discharging frame 2 and the 3rd discharging frame 3, facing to positive and negative two-layer pvc film heat pressing first heater 4 and second heater 5, supply positive and negative two-layer pvc film and macromolecule paste resin mixing surface layer and bottom composite bed first on the stock tank 6 and second stock tank 7, facings and bottom composite bed carry out preheating first warm-up mill 8 and second warm-up mill 9, the chemical fibre base cloth is deflected from the tourelle 10 that gets off and surface layer, bottom composite bed and chemical fibre base cloth is compressed compound main pressure roller 11.Main pressure roller 11 is the roller frames about its center line symmetry.Stock tank 7 on the stock tank 6 and second on second discharging frame 2 and the 3rd discharging frame 3, first heater 4 and second heater 5, first, and first warm-up mill 8 and second warm-up mill 9 all be symmetrical set with respect to the center line of main pressure roller 11, can transport surface layer and bottom composite beds to main pressure roller 11 synchronously like this.Stock tank 6, first warm-up mill 8 and main pressure roller 11 link together through transmission device 12 and realize the transportation that links up on second discharging frame 2, first heater 4, first; Stock tank 7, second warm-up mill 9 and main pressure roller 11 also are to link together through transmission device 12 to realize the transportation that links up on the 3rd discharging frame 3, second heater 5, second; Transmission device 12 can guarantee positive and negative two-layer pvc film or surface layer and bottom composite bed flexible communication, not easy fracture.The tourelle 10 that is used to deflect from the chemical fibre base cloth is tangent with the center line of main pressure roller 11, can guarantee that like this chemical fibre base cloth gets in the main pressure roller 11 accurately.First discharging frame 1 is positioned at a side and the setting in parallel of tourelle 10, can guarantee chemical fibre base cloth smooth transport like this, not easy fracture.In the present embodiment, first discharging frame 1 is arranged on second discharging frame, 2 tops.
The present invention at first is placed on the chemical fibre base cloth on first discharging frame 1, and positive and negative two-layer pvc film is placed on respectively on second discharging frame 2 and the 3rd discharging frame 3, start beginning blowing; Positive and negative two-layer pvc film is delivered to first heater 4 and second heater 5 through transmission device, and this first and second heater 4,5 heats pressing to positive and negative two-layer pvc film respectively, and temperature is controlled at 60-80 ℃; Follow positive and negative two-layer pvc and transmit respectively and be transported on first stock tank 7 on the stock tank 6 and second, on first, second, mix forming surface layer and bottom composite bed in the stock tank 6,7 with the macromolecule paste resin; Carry out preheating with first warm-up mill 8 and second warm-up mill, 9 facings and bottom composite bed respectively, temperature is controlled at 170-180 ℃, can help surface layer and bottom composite bed and chemical fibre base cloth like this and compress compound; First warm-up mill and second warm-up mill deflect from surface layer and bottom composite bed get off respectively simultaneously, and the chemical fibre base cloth also deflects from through tourelle 12 and gets off to send into main pressure roller, and this moment, surface layer and bottom composite bed were about chemical fibre base cloth symmetry; Surface layer composite bed, bottom composite bed and chemical fibre base cloth compress through main pressure roller 11 and are compounded to form Compound Fabric, and promptly the surface layer composite bed compresses the front that is compounded in the chemical fibre base cloth, and the bottom composite bed compresses the reverse side that is compounded in the chemical fibre base cloth.Through the Compound Fabric good hand touch that such equipment forms, to produce simply, production efficient is high.
The preparation method of macromolecule starching Compound Fabric of the present invention is following:
1) at first positive and negative two-layer pvc film and chemical fibre base cloth are hung on the discharging frame separately, carry out start and prepare, start back blowing;
2) then positive and negative two-layer pvc film heating pressing is transported in the oar groove;
3) follow positive and negative two-layer pvc film and in last stock tank, mix formation surface layer and bottom composite bed respectively with the heating of macromolecule paste resin;
4) carry out preheating with warm-up mill facings and bottom composite bed;
5) warm-up mill deflects from surface layer and bottom composite bed get off respectively simultaneously, and the chemical fibre base cloth also deflects from through tourelle and gets off to send into main pressure roller;
6) surface layer composite bed, bottom composite bed and chemical fibre base cloth compress through main pressure roller and are compounded to form Compound Fabric;
7) through five cooling running rollers Compound Fabric is cooled off;
8) the cooling back Compound Fabric processing of after cloth examination platform check, check, cutting edge;
9) as requested Compound Fabric being carried out the bundling packing at last embarks on journey.
Said 2) heating and temperature control in is at 60-80 ℃.
The temperature of the warm-up mill said 4) is controlled at 170-180 ℃.
Said 1) the positive and negative two-layer pvc behind the blowing in is the both sides that are positioned at the chemical fibre base cloth behind the blowing; Surface layer composite bed that deflecting from said 5) got off and bottom composite bed are symmetrical with respect to deflecting from the chemical fibre base cloth that gets off; Said 6) the surface layer composite bed in compresses the front that is compounded in the chemical fibre base cloth, and the bottom composite bed compresses the reverse side that is compounded in the chemical fibre base cloth, has promptly formed Compound Fabric.
Claims (6)
1. the preparation method of a macromolecule starching Compound Fabric is characterized in that: may further comprise the steps:
1) at first positive and negative two-layer pvc film and chemical fibre base cloth are hung on the discharging frame separately, carry out start and prepare, start back blowing;
2) then positive and negative two-layer pvc film heating pressing is transported in the oar groove;
3) follow positive and negative two-layer pvc film and in last stock tank, mix formation surface layer and bottom composite bed respectively with the heating of macromolecule paste resin;
4) carry out preheating with warm-up mill facings and bottom composite bed;
5) warm-up mill deflects from surface layer and bottom composite bed get off respectively simultaneously, and the chemical fibre base cloth also deflects from through tourelle and gets off to send into main pressure roller;
6) surface layer composite bed, bottom composite bed and chemical fibre base cloth compress through main pressure roller and are compounded to form Compound Fabric;
7) through five cooling running rollers Compound Fabric is cooled off;
8) the cooling back Compound Fabric processing of after cloth examination platform check, check, cutting edge;
9) as requested Compound Fabric being carried out the bundling packing at last embarks on journey.
2. the preparation method of macromolecule starching Compound Fabric according to claim 1 is characterized in that: the heating and temperature control said 2) is at 60-80 ℃.
3. the preparation method of macromolecule starching Compound Fabric according to claim 1 is characterized in that: the temperature of the warm-up mill said 4) is controlled at 170-180 ℃.
4. the preparation method of macromolecule starching Compound Fabric according to claim 1 is characterized in that: the positive and negative two-layer pvc behind the blowing said 1) is the both sides that are positioned at the chemical fibre base cloth behind the blowing; Said 6) the surface layer composite bed in compresses the front that is compounded in the chemical fibre base cloth, and the bottom composite bed compresses the reverse side that is compounded in the chemical fibre base cloth, has promptly formed Compound Fabric.
5. the making apparatus of a macromolecule starching Compound Fabric is characterized in that: this equipment comprise first discharging frame of placing the chemical fibre base cloth, respectively place positive and negative two-layer pvc film second discharging frame and the 3rd discharging frame, facing to positive and negative two-layer pvc film heat pressing first heater and second heater, supply positive and negative two-layer pvc film and macromolecule paste resin mixing surface layer and bottom composite bed first on the stock tank and second stock tank, facings and bottom composite bed carry out preheating first warm-up mill and second warm-up mill, the chemical fibre base cloth is deflected from the tourelle that gets off and surface layer, bottom composite bed and chemical fibre base cloth is compressed compound main pressure roller; Stock tank on the stock tank and second on second discharging frame and the 3rd discharging frame, first heater and second heater, first, and first warm-up mill and second warm-up mill all be symmetrical set with respect to the center line of main pressure roller; Stock tank, first warm-up mill and main pressure roller link together through transmission device and realize coherent transportation on second discharging frame, first heater, first, and stock tank, second warm-up mill and main pressure roller also are to link together through transmission device to realize coherent transportation on the 3rd discharging frame, second heater, second.
6. the making apparatus of macromolecule starching Compound Fabric according to claim 5 is characterized in that: the center line of said tourelle and main pressure roller is tangent, and first discharging frame is positioned at tourelle one side and setting in parallel.