CN102702599A - Stiffening agent for polyethylene corrugated pipe - Google Patents
Stiffening agent for polyethylene corrugated pipe Download PDFInfo
- Publication number
- CN102702599A CN102702599A CN2012101626988A CN201210162698A CN102702599A CN 102702599 A CN102702599 A CN 102702599A CN 2012101626988 A CN2012101626988 A CN 2012101626988A CN 201210162698 A CN201210162698 A CN 201210162698A CN 102702599 A CN102702599 A CN 102702599A
- Authority
- CN
- China
- Prior art keywords
- stiffening agent
- corrugated pipe
- agent
- polyethylene
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a stiffening agent for a polyethylene corrugated pipe, wherein the stiffening agent comprises following components in part by weight: 15-20 parts of high-density and low-pressure polyethylene, 70-75 parts of calcium carbonate superfine powder, 0.3-0.5 part of aluminate coupling agent and 3-5 parts of chlorinated polyethylene. The preparation process of the stiffening agent comprises the steps of preparing the components, stirring and mixing the materials, warming and pelleting, cooling, discharging and packaging. The invention has a rational idea and a norm process, and is simple in operation, low in price and pollution-free. When being used for processing the polyethylene corrugated pipe, the stiffening agent can improve product performance and reduce product cost. The stiffening agent can form industrial batch production, and can be widely applied in processing field of the polyethylene corrugated pipe.
Description
Technical field
The present invention relates to a kind of firm agent of increasing of plastics that is used for, particularly relate to a kind of firm agent of increasing of polytene corrugated tube road that is used for.
Background technology
Up to now, traditional to be used for the firm agent of increasing of polytene corrugated tube road unreasonable because of the auxiliary material and the proportioning thereof of adding, therefore, the polytene corrugated tube road poor-performing of producing, cost is higher, is difficult to satisfy the demands of consumers, and limits it and applies.
Summary of the invention
The objective of the invention is to research and develop a kind of new auxiliary agent as auxiliary material,, reduce production costs, and a kind of firm agent of increasing of polytene corrugated tube road that is used for is provided in order to improve the performance in polytene corrugated tube road in order to overcome the deficiency of above-mentioned background technology.
To achieve these goals, the technical scheme that increases firm agent that is used for the polytene corrugated tube road that the present invention is alleged is such:
Of the present inventionly increase firm agent and comprise following component and weight part: Vilaterm 15 ~ 20; Calcium carbonate superfine powder 70 ~ 75; Aluminate coupling agent 0.3 ~ 0.5; Chlorinatedpolyethylene 3 ~ 5.
Of the present inventionly increase firm agent and comprise following component and weight part: Vilaterm 18; Calcium carbonate superfine powder 72; Aluminate coupling agent 0.4; Chlorinatedpolyethylene 4.
The order number of calcium carbonate superfine powder of the present invention is 1500 ~ 2200 orders.
The order number of calcium carbonate superfine powder of the present invention is 2000 orders.
The firm agent of increasing of polytene corrugated tube road that is used for that the present invention is alleged has following beneficial effect: reasonable idea, technological specification, simple to operate, cheap, pollution-free; Be used for the firm agent of increasing of polytene corrugated tube road, can improve performance of products, promote the quality of product, reduce production cost of products.The present invention can form industrialized mass production, can be widely used in the manufacture field in polytene corrugated tube road.
Embodiment
Below in conjunction with embodiment the present invention is made further detailed description, but this embodiment should not be construed as limitation of the present invention.
Embodiment 1
Of the present inventionly increase firm agent and join by following processing sequence system:
1, the preparation of each component and weight part
Get high-density low pressure polyethylene 15,1500 order calcium carbonate superfine powders 70, aluminate coupling agent 0.3, chlorinatedpolyethylene 3, subsequent use;
2, batch mixing: above-mentioned each ingredients weight parts for preparing is mixed, drop into mixing and stirring in the kneader together, heating to 135 ℃ ~ 140 ℃ to stop to heat subsequent use;
3, granulation: the mixing for standby use material is dropped into granulation in the tablets press;
4, discharging packing: will can discharging pack behind the above-mentioned granulate cooling that processes to the normal temperature, i.e. finished product---describedly increase firm agent.
Embodiment 2
Present embodiment and embodiment 1 are basic identical, and its difference is:
1, the preparation of each component and weight part
Get high-density low pressure polyethylene 18,2000 order calcium carbonate superfine powders 72, aluminate coupling agent 0.4, chlorinatedpolyethylene 4, subsequent use;
Embodiment 3
Present embodiment and embodiment 1 are basic identical, and its difference is:
1, the preparation of each component and weight part
Get high-density low pressure polyethylene 20,2200 order calcium carbonate superfine powders 75, aluminate coupling agent 0.5, chlorinatedpolyethylene 5, subsequent use;
Obviously, those skilled in the art can carry out various changes and modification to the present invention and not break away from the spirit and scope of the present invention.Like this, belong within the scope of claim of the present invention and equivalent technologies thereof if of the present invention these are revised with modification, then the present invention also is intended to comprise these changes and modification interior.
The content of not doing in this specification sheets to describe in detail belongs to this area professional and technical personnel's known prior art.
Claims (4)
1. one kind is used for the firm agent of increasing of polytene corrugated tube road, it is characterized in that: describedly increase firm agent and comprise following component and weight part:
Vilaterm 15 ~ 20; Calcium carbonate superfine powder 70 ~ 75; Aluminate coupling agent 0.3 ~ 0.5; Chlorinatedpolyethylene 3 ~ 5.
2. according to claim 1ly be used for the firm agent of increasing of polytene corrugated tube road, it is characterized in that: describedly increase firm agent and comprise following component and weight part:
Vilaterm 18; Calcium carbonate superfine powder 72; Aluminate coupling agent 0.4; Chlorinatedpolyethylene 4.
3. be used for the firm agent of increasing of polytene corrugated tube road according to arbitrary claim in the claim 1 to 2 is described, it is characterized in that: the order number of described calcium carbonate superfine powder is 1500 ~ 2200 orders.
4. according to claim 3ly be used for the firm agent of increasing of polytene corrugated tube road, it is characterized in that: the order number of described calcium carbonate superfine powder is 2000 orders.