CN102700858A - GRP oil storage tank body or pipeline with anti-static property - Google Patents
GRP oil storage tank body or pipeline with anti-static property Download PDFInfo
- Publication number
- CN102700858A CN102700858A CN2012101857501A CN201210185750A CN102700858A CN 102700858 A CN102700858 A CN 102700858A CN 2012101857501 A CN2012101857501 A CN 2012101857501A CN 201210185750 A CN201210185750 A CN 201210185750A CN 102700858 A CN102700858 A CN 102700858A
- Authority
- CN
- China
- Prior art keywords
- tank body
- weight portions
- pipeline
- storage tank
- oil storage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of GRP (glass reinforced plastic) containers and particularly discloses a GRP oil storage tank body or pipeline with an anti-static property. The invention adopts the technical scheme that the GRP oil storage tank body or pipeline is formed by compounding a basis material resin and a reinforcing material glass fiber or comprises an inner tank body, an outer tank body and an interstitial substance bed arranged between the inner tank body and the outer tank body; and the inner tank body, the outer tank body and coatings are made of a resin mixture comprising the following components: 100 parts by weight of resin, 1 to 2.5 parts by weight of accelerant, 2 to 3 parts by weight of curing agent and 25 to 35 parts by weight of mica powder. The surface resistivity of the GRP oil storage tank body or pipeline with the structure is reduced to 10<4> to 10<6> Omega, so that the accumulation of a great amount of static charge especially on the surface of the oil storage tank body due to a liquid or other reasons is effectively avoided, and the volume or diameter of the GRP oil storage tank body or pipeline can be set as required without the need of considering the influence of electrostatic problems.
Description
Technical field
The invention belongs to the glass-felt plastic container technical field, relate to a kind of glass-felt plastic oil storage tank body or pipeline concretely with antistatic properties.
Background technology
Along with the high speed development of industrial economy, the supply and demand problem of oil storage tank body or pipeline becomes increasingly conspicuous.At present no matter be that the vehicle-mounted oil storage tank body that is embedded in underground large-scale oil storage tank body or pipeline, still is matched on the truck tanker all is to be processed or processed by glass-reinforced plastic material by the steel plate welding.Although it is big that the oil storage tank body that is welded into by steel plate or its volume of pipeline can be done enough, decay resistance is relatively poor because of existing, maintenance difficult is shorter its service life; Although petrol storage tank topic or the pipeline processed by glass-reinforced plastic material are because of it has lightweight, performance widespread use such as high-strength, anticorrosion, because the electrical resistivity of glass-felt plastic body is high (up to 2.5 * 10
13Ω); Poor electric conductivity; When making glass-felt plastic oil storage tank body or pipeline use, because of the flowing or very easily produce with the friction of container inner wall and accumulate the danger that a large amount of static cause its existence to blast and burn of liquid, so the volume of glass-felt plastic oil storage tank body and pipeline or diameter are restricted.
Summary of the invention
The object of the invention just provides glass-felt plastic oil storage tank body or pipeline with antistatic properties.
For realizing above-mentioned purpose, first kind of technical scheme that the present invention adopted is:
A kind of glass-felt plastic oil storage tank body or pipeline with antistatic properties is compounded to form by resin compound that constitutes basis material and the fibrous glass that constitutes reinforcing material; Wherein, described resin compound includes the resin of 100 weight portions, the accelerator of 1-2.5 weight portions, the curing agent of 2-3 weight portions and the mica powder of 25-35 weight portions.
Constitute in the above-mentioned glass-felt plastic oil storage tank body or pipeline with antistatic properties, described fibre comprises Chopped fiber, twines yarn or fabric.
For realizing above-mentioned purpose, second kind of technical scheme that the present invention adopted is:
A kind of glass-felt plastic oil storage tank body or pipeline with antistatic properties, its structure is made up of interior tank body, outer tank body and the interstitial lamella that is arranged at the two; In described the inside face of tank body with outside the outside face of tank body respectively scribble one deck electrostatic prevention resin bed, include the resin of 100 weight portions, the accelerator of 1-2.5 weight portions, the curing agent of 2-3 weight portions and the mica powder of 25-35 weight portions in this described electrostatic prevention resin bed.
For realizing above-mentioned purpose, the third technical scheme that the present invention adopted is:
A kind of glass-felt plastic oil storage tank body or pipeline with antistatic properties, its structure is made up of interior tank body, outer tank body and the metal-containing material enhancement Layer that is arranged at the two; It is characterized in that: tank body and outer tank body are to be entwined after including the resin colloid of mica powder formation of curing agent and 25-35 weight portions of accelerator, 2-3 weight portions of resin, 1-2.5 weight portions of 100 weight portions through infiltration by glass or other fibers in described.
Glass-felt plastic oil storage tank body or pipeline with antistatic properties provided by the present invention; Compared with prior art have the following advantages: promptly, make the glass fiber reinforced plastics product surface resistivity of its formation be reduced to 10 owing to contain a certain amount of mica powder in above-mentioned glass-felt plastic oil storage tank body of formation or the employed resin of pipeline
4~ 10
6The Ω order of magnitude; Satisfied the electric conductivity on glass fiber reinforced plastics product surface fully; Can effectively avoid because liquid or other reasons cause especially a large amount of accumulation of the static charge of petrol storage tank tank surface; Make the volume or the diameter of glass-felt plastic oil storage tank body and pipeline to set as required, need not to consider the influence of electrostatic problem.
Description of drawings
Fig. 1 is the cross section structure scheme drawing with glass-felt plastic oil storage tank body of antistatic properties;
Fig. 2 has the glass-felt plastic double-decker petrol storage tank of antistatic properties or the cross section structure scheme drawing of pipeline.
The specific embodiment
Below in conjunction with accompanying drawing the structure and the preparation thereof of glass-felt plastic oil storage tank body with antistatic properties provided by the present invention or pipeline are done further to specify.
As shown in Figure 1, be the cross section structure scheme drawing with glass-felt plastic petrol storage tank tank body of antistatic properties provided by the present invention.Its structure is through in the oil resistant article resin of 100 weight portions; Added the mica powder of 25-35 weight portions and the accelerator of 1-2.5 weight portions, the curing agent of 2-3 weight portions forms the resin compound colloid after mixing and stirring; Make the glass that need to twine or polyster fibre through gumming device and hang up colloid and be wrapped on the mould cylindrical shell and reach design thickness, can form glass-felt plastic petrol storage tank tank body 1 with antistatic properties.
As shown in Figure 2, have the glass-felt plastic petrol storage tank of antistatic properties or a cross section structure scheme drawing of pipeline for provided by the present invention.Its structure is by interior tank body 6, outer tank body 2 and be arranged at the two the interstitial lamella that is made up of bonding surface layer 3 and three-dimensional fiber 4; Wherein, respectively scribble the electrostatic prevention resin bed 5 of mica powder formation of curing agent and 25-35 weight portions of accelerator, 2-3 weight portions of resin that one deck includes 100 weight portions, 1-2.5 weight portions at the outside face of the inside face of above-mentioned interior tank body and outer tank body.
Certainly, constitute as the interior tank body 1 of described glass-felt plastic storage tank with antistatic properties of Fig. 2 or pipeline and outer tank body 2 also can be to be included behind the resin colloid of mica powder formation of curing agent and 25-35 weight portions of accelerator, 2-3 weight portions of resin, 1-2.5 weight portions of 100 weight portions injection through infiltration or be entwined by glass or other fibers.
Performance requriements according to tank body or pipeline in above-mentioned Fig. 1, the glass-felt plastic tank body with antistatic properties shown in Figure 2 or the employed resin compound of pipeline can also contain other such as compositions such as anti-wear agents; Wherein resin choice can be as required such as can also be bisphenol type resin (3301 resin), to benzene resin (D490 base ester, SW963 base ester), vinyl ester resin epoxy vinyl ester resins such as (DOW470 are the epoxy vinyl ester of modification, epoxy vinyl ester, the W901 base ester 3201 basic esters that DOW411 is modification), also can select vinyl ester resin, phenol resin etc.;
Accelerator more options cobalt naphthenate in the above-mentioned resin solidification system, curing agent can be selected MEKP (methyl ethyl ketone peroxide), can certainly select other accelerators, curing agent as required.
The preparation of resin compound: what get 100 weight portions is that mica powder that base-material adds accelerator and 25-35 weight portions of 1-2.5 weight portions is placed in the container and stirs at a slow speed with propeller agitator to benzene resin or other resins; In mixture container, add the curing agent of 2-3 weight portions again and fully stir, then itself and fibre (comprise Chopped fiber, twine yarn, fabric etc.) are carried out composite injection, winding or coating and get final product.
Wherein, the mica powder that is added is the best with the conductive mica powder of the Kang Te board on the market.
Claims (4)
1. a glass-felt plastic oil storage tank body or the pipeline with antistatic properties is compounded to form by resin compound that constitutes basis material and the fibrous glass that constitutes reinforcing material; It is characterized in that: described resin compound includes the resin of 100 weight portions, the accelerator of 1-2.5 weight portions, the curing agent of 2-3 weight portions and the mica powder of 25-35 weight portions.
2. a kind of glass-felt plastic oil storage tank body or pipeline with antistatic properties as claimed in claim 1 is characterized in that: described fibre comprises Chopped fiber, twines yarn or fabric.
3. a glass-felt plastic oil storage tank body or pipeline with antistatic properties, its structure is made up of interior tank body, outer tank body and the interstitial lamella that is arranged at the two; It is characterized in that: in described the inside face of tank body with outside the surface of tank body respectively scribble one deck electrostatic prevention resin bed, include the resin of 100 weight portions, the accelerator of 1-2.5 weight portions, the curing agent of 2-3 weight portions and the mica powder of 25-35 weight portions in this described electrostatic prevention resin bed.
4. a glass-felt plastic oil storage tank body or pipeline with antistatic properties, its structure is made up of interior tank body, outer tank body and the interstitial lamella that is arranged at the two; It is characterized in that: tank body and outer tank body are to be included behind the resin colloid that the mica powder of curing agent and 25-35 weight portions of accelerator, 2-3 weight portions of resin, 1-2.5 weight portions of 100 weight portions constitutes injection through infiltration or be entwined by glass or other fibers in described.