CN102699981A - Preparing method of dry floor heating construction gypsum plate - Google Patents
Preparing method of dry floor heating construction gypsum plate Download PDFInfo
- Publication number
- CN102699981A CN102699981A CN201210094128XA CN201210094128A CN102699981A CN 102699981 A CN102699981 A CN 102699981A CN 201210094128X A CN201210094128X A CN 201210094128XA CN 201210094128 A CN201210094128 A CN 201210094128A CN 102699981 A CN102699981 A CN 102699981A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- plasterboard
- solution
- floor heating
- gypsum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparing method of a dry floor heating construction gypsum plate. The method comprises the following steps of: 1) making a mold: taking 3.5 kg of silica gel by a container, and continuously stirring for 10 min along the same direction; pouring 0.105 kg of curing agent into the silica gel, continuously stirring for 15 min, pouring the stirred silica gel solution in a glass mold, and pouring 0.721 kg of release agent in the glass mold, so as to strip; 2) making the gypsum plate: putting 10 kg of water and 9 kg of alpha high-intensity gypsum powder in a container, quickly and continuously stirring for 5 min, putting two cotton screens with the same size in the made mold, pouring the alpha high-intensity gypsum powder solution in the mold when the solution is stirred and becomes into a floccule, taking the alpha high-intensity gypsum powder solution out after the powder solution flows per se to be a plane and is solidified, and naturally air-drying or stoving to finish the preparation of the gypsum plate. The preparing method is simple in operation steps; the alpha high-intensity gypsum powder is mainly used as the main material of the gypsum plate; the construction speed is quick; the transverse heat conduction speed of the processed gypsum plate is high; and the processed gypsum plate is suitable for wide popularization and application.
Description
Technical field
The present invention relates to a kind of preparation method of dry floor heating construction plasterboard.
Background technology
In the market dry floor heating construction sheet material material adopts plastics, foam or aluminium sheet to process more, and this construction plate is frangible, inflammable when concrete construction, be prone to come unglued, and long-term the covering shunk easily and melted, and be not durable.Can't be from solving long-term use problem with this, existing simultaneously dry floor heating construction plate preparation method is complicated, and inefficiency has brought great inconvenience to the user.
Summary of the invention
For solving the problems of the technologies described above, the present invention provides a kind of preparation method of dry floor heating construction plasterboard, and speed of application is fast, and laterally heat conduction is fast, sturdy and durable.
The preparation method of dry floor heating construction plasterboard of the present invention may further comprise the steps:
1) makes mould: get 3.5 kilograms silica gel through container, equidirectional continuous stirring 10 minutes; In silica gel, pour 0.105 kilogram curing agent into, continuous stirring 15 minutes is poured the silica gel solution that stirs in the glass mold into, after curing a period of time, 0.721 kilogram releasing agent is poured in the glass mold, and then molding, Mold Making is accomplished;
2) make plasterboard: get 10 kilograms water and 9 kilograms α high strength gypsum powder and put into container, rapid Continuous stirred 5 minutes, in the mould of making, put into two webs of identical size then; When treating that solution stirring is cotton-shaped; α high strength gypsum powder solution is poured in the mould, treat that it flows automatically into the plane after, placed 30 minutes; Treat that it solidifies the back and takes out, the making of plasterboard is promptly accomplished in natural air drying or oven dry.
In the preparation method's of above-mentioned dry floor heating construction plasterboard step 1), the hardening time of said silica gel solution in glass mold is 3 hours.
Step 2 in the preparation method of above-mentioned dry floor heating construction plasterboard) in, the α high strength gypsum powder solution after solidifying is placed on natural air drying or oven dry in the above environment of 5 degree.
Beneficial effect compared with prior art of the present invention is: preparation method's operating procedure of dry floor heating construction plasterboard of the present invention is simple, high efficiency, and plasterboard is a main material with α high strength gypsum powder mainly; Add related raw material, speed of application is fast, and the horizontal heat conduction of the plasterboard that is processed into is fast; Sturdy and durable, occupy little space environmental protection; Good looking appearance can recycle and meets national industrial policies, suitablely applies on a large scale.
The specific embodiment
Below in conjunction with embodiment, specific embodiments of the invention describes in further detail.Following examples are used to explain the present invention, but are not used for limiting scope of the present invention.
A kind of preparation method of dry floor heating construction plasterboard may further comprise the steps:
1) makes mould: get 3.5 kilograms silica gel through container, equidirectional continuous stirring 10 minutes; In silica gel, pour 0.105 kilogram curing agent into, continuous stirring 15 minutes is poured the silica gel solution that stirs in the glass mold into, after curing a period of time, 0.721 kilogram releasing agent is poured in the glass mold, and then molding, Mold Making is accomplished;
2) make plasterboard: get 10 kilograms water and 9 kilograms α high strength gypsum powder and put into container, rapid Continuous stirred 5 minutes, in the mould of making, put into two webs of identical size then; When treating that solution stirring is cotton-shaped; α high strength gypsum powder solution is poured in the mould, treat that it flows automatically into the plane after, placed 30 minutes; Treat that it solidifies the back and takes out, the making of plasterboard is promptly accomplished in natural air drying or oven dry.
In the preparation method's of above-mentioned dry floor heating construction plasterboard step 1), the hardening time of said silica gel solution in glass mold is 3 hours.
Step 2 in the preparation method of above-mentioned dry floor heating construction plasterboard) in, the α high strength gypsum powder solution after solidifying is placed on natural air drying or oven dry in the above environment of 5 degree.
Preparation method's operating procedure of dry floor heating construction plasterboard of the present invention is simple, high efficiency, and plasterboard is a main material with α high strength gypsum powder mainly; Add related raw material, speed of application is fast, and the horizontal heat conduction of the plasterboard that is processed into is fast; Sturdy and durable, occupy little space environmental protection; Good looking appearance can recycle and meets national industrial policies, suitablely applies on a large scale.
The above only is a preferred implementation of the present invention; Should be pointed out that for those skilled in the art, under the prerequisite that does not break away from know-why of the present invention; Can also make some improvement and modification, these improve and modification also should be regarded as protection scope of the present invention.
Claims (3)
1. the preparation method of a dry floor heating construction plasterboard is characterized in that, may further comprise the steps:
1) makes mould: get 3.5 kilograms silica gel through container, equidirectional continuous stirring 10 minutes; In silica gel, pour 0.105 kilogram curing agent into, continuous stirring 15 minutes is poured the silica gel solution that stirs in the glass mold into, after curing a period of time, 0.721 kilogram releasing agent is poured in the glass mold, and then molding, Mold Making is accomplished;
2) make plasterboard: get 10 kilograms water and 9 kilograms α high strength gypsum powder and put into container, rapid Continuous stirred 5 minutes, in the mould of making, put into two webs of identical size then; When treating that solution stirring is cotton-shaped; α high strength gypsum powder solution is poured in the mould, treat that it flows automatically into the plane after, placed 30 minutes; Treat that it solidifies the back and takes out, the making of plasterboard is promptly accomplished in natural air drying or oven dry.
2. the preparation method of dry floor heating according to claim 1 construction plasterboard is characterized in that: in step 1), the hardening time of said silica gel solution in glass mold is 3 hours.
3. the preparation method of dry floor heating construction plasterboard according to claim 1 is characterized in that: in step 2) in, the α high strength gypsum powder solution after solidifying is placed on natural air drying or oven dry in the above environment of 5 degree.