CN102672098A - Evanescent mould coating and preparation method thereof - Google Patents
Evanescent mould coating and preparation method thereof Download PDFInfo
- Publication number
- CN102672098A CN102672098A CN2012101793980A CN201210179398A CN102672098A CN 102672098 A CN102672098 A CN 102672098A CN 2012101793980 A CN2012101793980 A CN 2012101793980A CN 201210179398 A CN201210179398 A CN 201210179398A CN 102672098 A CN102672098 A CN 102672098A
- Authority
- CN
- China
- Prior art keywords
- parts
- graphite powder
- water
- rosin
- lost foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Provided are evanescent mould coating and a preparation method thereof. The preparation method of the evanescent mould coating comprises the following steps of step one, mixing 40 parts of scaly graphite powder, 60 parts of earthy graphite powder, 5 parts of activated bentonite, 10 parts of high-temperature refractory clay and 23-35 parts of water, grinding the mixture for 4 hours to obtain paste; step two, mixing 30 parts of acetic acid resin and 4 parts of rosin with 50-100 parts of water to obtain solution; and step three, putting 138-150 parts of paste and 84-134 parts of solution into a coating blender to obtain prepared evanescent mould coating. The preparation method of the evanescent mould coating has the advantage that the evanescent mould coating is prepared by the paste containing 40 parts of the scaly graphite powder, 60 parts of the earthy graphite powder, 5 parts of the activated bentonite, 10 parts of the high-temperature refractory clay and 23-35 parts of the water and the solution containing 30 parts of the acetic acid resin, 4 parts of the rosin and 50-100 parts of the water, so that the evanescent mould coating has good air permeability, good refractoriness and high cold and hot strength.
Description
Technical field
The present invention relates to a kind of lost foam paint and preparation method thereof, relate in particular to lost foam paint of a kind of die casting production field that disappears and preparation method thereof.
Background technology
When the die casting that disappears was produced, foam can produce a large amount of gas.If the gas permeability of coating is bad, will make the foundry goods of producing produce a large amount of pores, foundry goods is scrapped.If there is not good refractoriness, will makes foundry goods produce scab, thereby cause the metalworking difficulty even scrap.If there is not good cold strength, will make the coating on the disappearance mould take place to ftracture or peel off, thereby generation scab or coating interlayer make foundry goods scrap.
Existing nowadays, the lost foam paint of selling on the market, price is comparatively expensive and can't satisfy the production of large-scale disappearance die casting, performances such as the gas permeability of lost foam paint, refractoriness and cold strength still fail to reach requirement.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of good permeability, refractoriness is good and cold strength is high lost foam paint and preparation method thereof.
A kind of lost foam paint, form by the component of following portions by weight:
Flaky graphite powder 38-42 part;
Amorphous graphite powder 58-62 part;
Active bentonite 4-6 part;
High-temperature flame-proof mud 9-11 part;
Water 70-135 part;
Rosin 3-5 part;
White glue with vinyl 28-32 part.
Preferably, form by the component of following portions by weight:
40 parts in flaky graphite powder;
60 parts in amorphous graphite powder;
5 parts of active bentonites;
10 parts in high-temperature flame-proof mud;
Water 70-135 part;
4 parts of rosin;
30 parts of white glue with vinyl.
A kind of preparation method of lost foam paint comprises following sequential steps:
(1) flaky graphite powder, amorphous graphite powder, active bentonite and high-temperature flame-proof mud are mixed, are made into paste after adding suitable quantity of water, place grinding mill to carry out 4 hours milling then after, take out sealed storage;
(2) with white glue with vinyl and rosin dilute with water, soaked 24 hours, stir white glue with vinyl and rosin be dissolved in the water, make solution;
(3) paste of step (1) gained and the solution of step (2) gained are put into mould wash mixer by following parts by weight, stirred 2 hours, make lost foam paint:
Paste 138-150 part;
Solution 84-134 part.
Preferably, the paste in the step (1) is for being that 40 parts flaky graphite powder, 60 parts amorphous graphite powder, 5 parts active bentonite, 10 parts high-temperature flame-proof mud and the water hybrid modulation of 23-35 part form with parts by weight.
Preferably, the solution in the step (2) is for being that 30 parts white glue with vinyl and 4 parts rosin and the water hybrid modulation of 50-100 part form with parts by weight.
Beneficial effect of the present invention is: with parts by weight is that 40 parts flaky graphite powder, 60 parts amorphous graphite powder, 5 parts active bentonite, 10 parts high-temperature flame-proof mud and the water hybrid modulation of 23-35 part become paste; The white glue with vinyl that with parts by weight is 30 parts becomes solution with 4 parts rosin and the water hybrid modulation of 50-100 part; Paste of 138-150 part and the solution of 84-134 part are put into mould wash mixer; Stirred 2 hours, and made lost foam paint, the rosin that wherein adds 4 parts makes the gas permeability of lost foam paint better; Add 40 parts flaky graphite powder, 60 parts amorphous graphite powder; Make the refractoriness of lost foam paint better, add 30 parts white glue with vinyl, make the cold strength of lost foam paint better.
The specific embodiment
Below in conjunction with embodiment invention is described further, but protection scope of the present invention is not limited to this.
Embodiment 1
A kind of lost foam paint, form by the component of following portions by weight:
Flaky graphite powder 38-42 part;
Amorphous graphite powder 58-62 part;
Active bentonite 4-6 part;
High-temperature flame-proof mud 9-11 part;
Water 70-135 part;
Rosin 3-5 part;
White glue with vinyl 28-32 part.
A kind of preparation method of lost foam paint comprises following sequential steps:
(1) flaky graphite powder, amorphous graphite powder, active bentonite and high-temperature flame-proof mud are mixed, are made into paste after adding suitable quantity of water, place grinding mill to carry out 4 hours milling then after, take out sealed storage;
(2) with white glue with vinyl and rosin dilute with water, soaked 24 hours, stir white glue with vinyl and rosin be dissolved in the water, make solution;
(3) paste of step (1) gained and the solution of step (2) gained are put into mould wash mixer by following parts by weight, stirred 2 hours, make lost foam paint:
Paste 138-150 part;
Solution 84-134 part.
Paste in the step (1) is for being that 40 parts flaky graphite powder, 60 parts amorphous graphite powder, 5 parts active bentonite, 10 parts high-temperature flame-proof mud and the water hybrid modulation of 23-35 part form with parts by weight.
Solution in the step (2) is for being that 30 parts white glue with vinyl and 4 parts rosin and the water hybrid modulation of 50-100 part form with parts by weight.
Embodiment 2
A kind of lost foam paint, form by the component of following portions by weight:
40 parts in flaky graphite powder;
60 parts in amorphous graphite powder;
5 parts of active bentonites;
10 parts in high-temperature flame-proof mud;
Water 70-135 part;
4 parts of rosin;
30 parts of white glue with vinyl.
A kind of preparation method of lost foam paint comprises following sequential steps:
(1) flaky graphite powder, amorphous graphite powder, active bentonite and high-temperature flame-proof mud are mixed, are made into paste after adding suitable quantity of water, place grinding mill to carry out 4 hours milling then after, take out sealed storage;
(2) with white glue with vinyl and rosin dilute with water, soaked 24 hours, stir white glue with vinyl and rosin be dissolved in the water, make solution;
(3) paste of step (1) gained and the solution of step (2) gained are put into mould wash mixer by following parts by weight, stirred 2 hours, make lost foam paint:
Paste 138-150 part;
Solution 84-134 part.
Paste in the step (1) is for being that 40 parts flaky graphite powder, 60 parts amorphous graphite powder, 5 parts active bentonite, 10 parts high-temperature flame-proof mud and the water hybrid modulation of 23-35 part form with parts by weight.
Solution in the step (2) is for being that 30 parts white glue with vinyl and 4 parts rosin and the water hybrid modulation of 50-100 part form with parts by weight.
Above-mentioned compositions in weight portion is that lost foam paint adopts above-mentioned compositions in weight portion through repeatedly drawing best component proportioning value after the proportioning, and performances such as its gas permeability, refractoriness, cold strength are best.
Claims (5)
1. lost foam paint, it is characterized in that: described lost foam paint is processed by following materials based on weight:
Flaky graphite powder 38-42 part;
Amorphous graphite powder 58-62 part;
Active bentonite 4-6 part;
High-temperature flame-proof mud 9-11 part;
Water 70-135 part;
Rosin 3-5 part;
White glue with vinyl 28-32 part.
2. lost foam paint according to claim 1 is characterized in that: processed by following materials based on weight:
40 parts in flaky graphite powder;
60 parts in amorphous graphite powder;
5 parts of active bentonites;
10 parts in high-temperature flame-proof mud;
Water 70-135 part;
4 parts of rosin;
30 parts of white glue with vinyl.
3. preparation method of lost foam paint according to claim 1 or claim 2, it is characterized in that: described preparation method comprises following sequential steps:
Flaky graphite powder, amorphous graphite powder, active bentonite and high-temperature flame-proof mud are mixed, are made into paste after adding suitable quantity of water, place grinding mill to carry out 4 hours milling then after, take out sealed storage;
With white glue with vinyl and rosin dilute with water, soaked 24 hours, stir white glue with vinyl and rosin be dissolved in the water, make solution;
The paste of step (1) gained and the solution of step (2) gained are put into mould wash mixer by following parts by weight, stirred 2 hours, make lost foam paint:
Paste 138-150 part;
Solution 84-134 part.
4. according to the preparation method of the said lost foam paint of claim 3, it is characterized in that: the paste in the step (1) is for being that 40 parts flaky graphite powder, 60 parts amorphous graphite powder, 5 parts active bentonite, 10 parts high-temperature flame-proof mud and the water hybrid modulation of 23-35 part form with parts by weight.
5. according to the preparation method of the said lost foam paint of claim 3, it is characterized in that: the solution in the step (2) is for being that 30 parts white glue with vinyl and 4 parts rosin and the water hybrid modulation of 50-100 part form with parts by weight.