CN102660054A - High-temperature resistant waterproof ring for air-conditioning motor - Google Patents
High-temperature resistant waterproof ring for air-conditioning motor Download PDFInfo
- Publication number
- CN102660054A CN102660054A CN2012101079168A CN201210107916A CN102660054A CN 102660054 A CN102660054 A CN 102660054A CN 2012101079168 A CN2012101079168 A CN 2012101079168A CN 201210107916 A CN201210107916 A CN 201210107916A CN 102660054 A CN102660054 A CN 102660054A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature resistant
- high temperature
- air conditioner
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a high-temperature resistant waterproof ring for an air-conditioning motor. The waterproof ring provided by the invention is prepared from the following raw materials of: by weight, 1.5-2.5 parts of sulfur powder, 64-68 parts of natural rubber, 32-34 parts of styrene-butadiene rubber, 4-6 parts of carbon black, 2-4 parts of hard kaolin, 45-55 parts of magnesium hydroxide, 35-45 parts of chlorinated paraffin, 28-32 parts of naphthenic oil, 0.4-0.6 part of microcrystalline wax, 0.4-0.6 part of Brazilian palm wax, 38-42 parts of aluminium hydroxide, 5-7 parts of zinc oxide, 0.8-1.2 parts of eleaostearic acid, 0.2-0.3 part of an anti-scorching agent, 8-12 parts of zinc borate, 8-12 parts of antimonony oxide, 7-9 parts of white factice, 0.8-1.2 parts of a promoter M, 0.3-0.7 part of a promoter DM, 0.3-0.7 part of a promoter TMTD, 0.8-1.2 parts of an antioxidant RD, 0.8-1.2 parts of an antioxidant MB and 0.1-0.2 part of an antioxidant NBC. The invention has excellent ageing resistance, high temperature resistance and flame resistance and can be used to make the waterproof ring for an air-conditioning motor. The waterproof ring saves cost and has long service life.
Description
Technical field
The present invention relates to the air conditioner motor fitting field, exactly is that a kind of air conditioner motor is used the high temperature resistant waterproof circle.
Background technology
There is the gap in traditional air conditioner motor between rotating shaft and the end cap, needs to install water proof ring; But the waterproof effect imperfection of existing air conditioner motor water proof ring is prone to wear out, and cost is higher; And the conventional waterproof circle exists high temperature trickling, the phenomenon of cold(ing)crack in the air conditioner motor operational process.
Summary of the invention
The purpose of this invention is to provide a kind of air conditioner motor anti-aging, high temperature resistant and that flame retardant properties is excellent and use the high temperature resistant waterproof circle.
Above-mentioned purpose realizes through following scheme:
A kind of air conditioner motor is used the high temperature resistant waterproof circle, it is characterized in that:
It is to be processed by the raw material of following weight parts: SULPHUR POWDER 1.5-2.5 part, tree elastomer 64-68 part, styrene-butadiene rubber(SBR) 32-34 part, carbon black 4-6 part; Hard kaoline 2-4 part, Marinco H 45-55 part, clorafin 35-45 part, NO 28-32 part; Microcrystalline wax 0.4-0.6 part, POLISHING WAX-103 0.4-0.6 part, white lake 38-42 part, zinc oxide 5-7 part; Triple Pressed Stearic Acid 0.8-1.2 part, scorch retarder 0.2-0.3 part, zinc borate 8-12 part, Antimony Trioxide: 99.5Min 8-12 part; White factice 7-9 part, captax 0.8-1.2 part, altax 0.3-0.7 part, TM monex TD 0.3-0.7 part; Anti-aging agent RD 0.8-1.2 part, antioxidant MB 0.8-1.2 part, antioxidant NBC 0.1-0.2 part.
Described a kind of air conditioner motor is used the high temperature resistant waterproof circle, it is characterized in that:
It is processed by following raw material: 2 parts of SULPHUR POWDERs, 66.7 parts of tree elastomers, 33.3 parts in styrene-butadiene rubber(SBR), 5 parts of carbon blacks, 3 parts of hard kaolines; 50 parts of Marinco Hs, 40 parts of clorafins, 30 parts of NOs, 0.5 part of microcrystalline wax, 0.5 part of POLISHING WAX-103; 40 parts in white lake, 6.25 parts in zinc oxide, 1 part of Triple Pressed Stearic Acid, 0.25 part of scorch retarder, 10 parts of zinc borates; 10 parts of Antimony Trioxide: 99.5Mins, 8 parts of white factices, 1 part of captax, 0.5 part of altax; 0.5 part of TM monex TD, 1 part of anti-aging agent RD, 1 part of antioxidant MB, 0.15 part of antioxidant NBC.
Described a kind of air conditioner motor is used the high temperature resistant waterproof circle, it is characterized in that: described SULPHUR POWDER is SULPHUR POWDER IS-60, and described carbon black is carbon black N550.
Described a kind of air conditioner motor is used the high temperature resistant waterproof circle, it is characterized in that: it adopts calendering process, sulfuration process to prepare and get.
Described a kind of air conditioner motor is used the high temperature resistant waterproof circle; It is characterized in that: preparation technology is: get by weight tree elastomer, styrene-butadiene rubber(SBR) fully mixing after; Add the abundant mixing rubber unvulcanizate postcure that obtains of other raw materials according to weight part again, the reprocessing moulding promptly gets product.
Beneficial effect of the present invention is: the present invention is anti-aging, high temperature resistant and flame retardant properties is excellent, is used to make the air conditioner motor water proof ring, practices thrift cost, long service life.
Embodiment
Described a kind of air conditioner motor is used the high temperature resistant waterproof circle,
It is processed by following raw material: 2 parts of SULPHUR POWDERs, 66.7 parts of tree elastomers, 33.3 parts in styrene-butadiene rubber(SBR), 5 parts of carbon blacks, 3 parts of hard kaolines; 50 parts of Marinco Hs, 40 parts of clorafins, 30 parts of NOs, 0.5 part of microcrystalline wax, 0.5 part of POLISHING WAX-103; 40 parts in white lake, 6.25 parts in zinc oxide, 1 part of Triple Pressed Stearic Acid, 0.25 part of scorch retarder, 10 parts of zinc borates; 10 parts of Antimony Trioxide: 99.5Mins, 8 parts of white factices, 1 part of captax, 0.5 part of altax; 0.5 part of TM monex TD, 1 part of anti-aging agent RD, 1 part of antioxidant MB, 0.15 part of antioxidant NBC.
Described SULPHUR POWDER is SULPHUR POWDER IS-60, and described carbon black is carbon black N550.
It adopts calendering process, sulfuration process to prepare and get.
Preparation technology is: get by weight tree elastomer, styrene-butadiene rubber(SBR) fully mixing after, add according to weight part again that other raw materials are fully mixing obtains the rubber unvulcanizate postcure, the reprocessing moulding promptly gets product.
Present embodiment is anti-aging, high temperature resistant and flame retardant properties is excellent, is used to make the air conditioner motor water proof ring, practices thrift cost, long service life.
The index parameter of products obtained therefrom is following:
1. aging resistance:
100 ° of C*96h heat ageing tests, HS6 ° of hardness rising-HS8 °;
2. high temperature resistant:
120 ° of C*168h, outward appearance does not have distortion, contraction, crackle, is clamminess and separates out phenomenon;
3. fire-retardant requirement:
Needle flame test, test period 30 ± 1S, residual flame＜30S, the shop fixtures layer does not ignite;
4. environmental requirement:
Rohs requires: plumbous (PB) and compound≤100PPM; Cadmium (CD) and compound≤5PPM;
Mercury (HG) and compound≤100PPM; Sexavalent chrome (CR+) and compound≤100PPM;
PBBs≤100PPM; PBDE≤100PPM;
REACH requires: meet European Union's standard.
Claims (5)
1. an air conditioner motor is used the high temperature resistant waterproof circle, it is characterized in that:
It is to be processed by the raw material of following weight parts: SULPHUR POWDER 1.5-2.5 part, tree elastomer 64-68 part, styrene-butadiene rubber(SBR) 32-34 part, carbon black 4-6 part; Hard kaoline 2-4 part, Marinco H 45-55 part, clorafin 35-45 part, NO 28-32 part; Microcrystalline wax 0.4-0.6 part, POLISHING WAX-103 0.4-0.6 part, white lake 38-42 part, zinc oxide 5-7 part; Triple Pressed Stearic Acid 0.8-1.2 part, scorch retarder 0.2-0.3 part, zinc borate 8-12 part, Antimony Trioxide: 99.5Min 8-12 part; White factice 7-9 part, captax 0.8-1.2 part, altax 0.3-0.7 part, TM monex TD 0.3-0.7 part; Anti-aging agent RD 0.8-1.2 part, antioxidant MB 0.8-1.2 part, antioxidant NBC 0.1-0.2 part.
2. a kind of air conditioner motor according to claim 1 is used the high temperature resistant waterproof circle, it is characterized in that:
It is processed by following raw material: 2 parts of SULPHUR POWDERs, 66.7 parts of tree elastomers, 33.3 parts in styrene-butadiene rubber(SBR), 5 parts of carbon blacks, 3 parts of hard kaolines; 50 parts of Marinco Hs, 40 parts of clorafins, 30 parts of NOs, 0.5 part of microcrystalline wax, 0.5 part of POLISHING WAX-103; 40 parts in white lake, 6.25 parts in zinc oxide, 1 part of Triple Pressed Stearic Acid, 0.25 part of scorch retarder, 10 parts of zinc borates; 10 parts of Antimony Trioxide: 99.5Mins, 8 parts of white factices, 1 part of captax, 0.5 part of altax; 0.5 part of TM monex TD, 1 part of anti-aging agent RD, 1 part of antioxidant MB, 0.15 part of antioxidant NBC.
3. a kind of air conditioner motor according to claim 1 is used the high temperature resistant waterproof circle, it is characterized in that: described SULPHUR POWDER is SULPHUR POWDER IS-60, and described carbon black is carbon black N550.
4. a kind of air conditioner motor according to claim 1 is used the high temperature resistant waterproof circle, it is characterized in that: it adopts calendering process, sulfuration process to prepare and get.
5. a kind of air conditioner motor according to claim 1 is used the high temperature resistant waterproof circle; It is characterized in that: preparation technology is: get by weight tree elastomer, styrene-butadiene rubber(SBR) fully mixing after; Fully the mixing rubber unvulcanizate of obtaining is behind over cure to add other raw materials according to weight part again, and the reprocessing moulding promptly gets product.