CN102653462A - Binding material coal ash-cement and production method thereof - Google Patents
Binding material coal ash-cement and production method thereof Download PDFInfo
- Publication number
- CN102653462A CN102653462A CN2011100552268A CN201110055226A CN102653462A CN 102653462 A CN102653462 A CN 102653462A CN 2011100552268 A CN2011100552268 A CN 2011100552268A CN 201110055226 A CN201110055226 A CN 201110055226A CN 102653462 A CN102653462 A CN 102653462A
- Authority
- CN
- China
- Prior art keywords
- cement
- flyash
- coal ash
- binding material
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a binding material coal ash-cement and a production method thereof. The binding material coal ash-cement is prepared from 0-95 percent by weight of coal ash binding material, 0-95 percent by weight of active admixture, 0-5 percent by weight of alkaline exciting agent, 0-10 percent by weight of lime, 0-1 percent by weight of water reducing agent and 0-1 percent by weight of early strength agent. The production method comprises the steps of: weighing all raw materials according to a preset proportion, then uniformly mixing the raw materials, and packaging to obtain the binding material coal ash-cement. Grade 12.5, grade 17.5, grade 22.5, grade 32.5 and grade 42.5 of binding material coal ash-cement are obtained according to different proportions of the components, and can be used for constructing plaster cement, cement plaster, thermal mortar, underground engineering and the like.
Description
Technical field
The present invention relates to a kind of high-strength environmental protection gelling material, specifically, relate to a kind of as the flyash-cement of building the cement of wiping one's face, sand-cement slurry, thermal insulation mortar by laying bricks or stones.
Technical background
Flyash is as large industrial residue, and its processing and comprehensive utilization have been accompanied and paid close attention to by countries in the world.In China's method commonly used is blended material and concrete adulterant, brick, the building block that original state flyash or fine-ground fly-ash are made cement.Flyash is as the blended material and the concrete adulterant of cement, and China standardizes, and has formulated the corresponding techniques standard.But use the dried row's top grade ash, the one-level that are preferably sorting grey at present, the utilization ratio of a large amount of wet ash discharges and inferior grade ash is also lower.Exciting with the method for Study of Activation of flyash is more, mainly is that mechanical grinding method, lime alkali excite method, steam-cured method.At present, use more complex excitation, promptly lime, gypsum, sodium sulfate mix dry grinding with flyash; Though early strength increases, activity is not high, and volume is low; Be not higher than 30%, effect is undesirable, poor stability; Often to join miserable slag etc., add lime alkali high temperature and excite with steam-cured and excite, fail to be used widely because cost is high, investment is big, complex process.
Summary of the invention
The object of the present invention is to provide a kind of production energy consumption low, cost is low, the gelling material flyash-cement of water-tolerant.
The objective of the invention is to realize through following proposal: it is processed by fly ash gel material, active admixture, alkali-activator, lime, water reducer and hardening accelerator; The weight proportion of each component is: fly ash gel material 0%~95%; Activity is closed material 0%~95%, alkali-activator 0%~5%, lime 0%~10% disastrously; Water reducer 0%~1%, hardening accelerator 0%~1%;
Said fly ash gel material is flyash, gypsum and cement three's mixing, and three's weight proportion is a flyash: (gypsum+cement)=0%~100%: 100%~0%;
Described flyash is one-level, the second class powered coal ash of power plant, or the wet ash discharge of levigated and low waits greyly, and gypsum is natural dihydrate gypsum or desulfurated plaster or anhydrite, and powder size 60 orders~500 orders, cement are cement clinker or various label cement;
Said active admixture is one or more mixtures in levigate blast furnace slag, ground steel slag, the levigate Fluorspar Powder;
Said alkali-activator is for being selected from Na
2SO
4, K
2SO
4, NaHSO
4, KHSO
4, CuSO
4, FeSO
4, Al
2(SO
4)
3, ZnSO
4, KAL (SO
4)
2, K
2Cr
2O
7, one or more the mixture among the NaOH, granularity order number is greater than 80 orders;
Working method: each raw material by the preset blending ratio metering, is mixed all raw material dryings then, packing.
Embodiment
Embodiment 1:
Embodiment 2:
Embodiment 3:
Embodiment 4:
Embodiment 5:
Embodiment 6:
Embodiment 7:
Embodiment 8:
Claims (6)
1. a gelling material flyash-cement is characterized in that, it is processed by fly ash gel material, active admixture, alkali-activator, lime, water reducer and hardening accelerator; The weight proportion of each component is: fragrant coal ash gelling material 0%~95%; Activity is closed material 0%~95%, alkali-activator 0%~5%, lime 0%~10% disastrously; Water reducer 0%~1%, hardening accelerator 0%~1%.
2. be flyash, gypsum and cement three's mixing according to the said fly ash gel material of claim 1, three's weight proportion is a flyash: (gypsum+cement)=0%~100%: 100%~0%.
3. one-level, second class powered coal ash that flyash according to claim 1 is power plant; Or the wet ash discharge of levigated reaches ashes such as low; Gypsum is natural dihydrate gypsum or desulfurated plaster or anhydrite, and powder size 60 orders~500 orders, cement are cement clinker or various label cement.
4. be one or more mixtures in levigate blast furnace slag, ground steel slag, the levigate Fluorspar Powder according to the said active admixture of claim 1.
According to the said alkali-activator of claim 1 for being selected from Na
2SO
4, K
2SO
4, NaHSO
4, KHSO
4, CuSO
4, FeSO
4, Al
2(SO
4)
3, ZnSO
4, KAL (SO
4)
2, K
2Cr
2O
7, one or more the mixture among the NaOH, granularity order number is greater than 80 orders.
6. according to the described gelling material flyash of claim 1~5-Cement Production method, it is characterized in that, each raw material by the preset blending ratio metering, is mixed all raw material dryings then, packing.