CN102634650A - 液压支架铰接销轴的热处理方法 - Google Patents

液压支架铰接销轴的热处理方法 Download PDF

Info

Publication number
CN102634650A
CN102634650A CN2012101223489A CN201210122348A CN102634650A CN 102634650 A CN102634650 A CN 102634650A CN 2012101223489 A CN2012101223489 A CN 2012101223489A CN 201210122348 A CN201210122348 A CN 201210122348A CN 102634650 A CN102634650 A CN 102634650A
Authority
CN
China
Prior art keywords
pin shaft
hydraulic support
heat treating
treating method
hinging pin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012101223489A
Other languages
English (en)
Inventor
王绍立
王亮忠
樊哲亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chinacoal Beijing Coal Mining Machinery Co Ltd
Original Assignee
Chinacoal Beijing Coal Mining Machinery Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chinacoal Beijing Coal Mining Machinery Co Ltd filed Critical Chinacoal Beijing Coal Mining Machinery Co Ltd
Priority to CN2012101223489A priority Critical patent/CN102634650A/zh
Publication of CN102634650A publication Critical patent/CN102634650A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种液压支架铰接销轴的热处理方法，首先对销轴进行调质处理，得到回火索氏体；然后对销轴进行表面淬火，表面淬火的温度为Ac3以上80-150℃，淬火得到细隐晶马氏体。使零件不仅表面有一定的硬度，具备耐磨和抗疲劳，而且芯部具有足够的强度和韧性。

Description

液压支架铰接销轴的热处理方法
技术领域
本发明涉及一种煤矿井下液压支架的关键部件的热处理技术，尤其涉及一种液压支架铰接销轴的热处理方法。
背景技术
液压支架用铰接销轴是连接四连杆机构的关键零件，受力较为复杂，以弯曲、剪切为主。材料以35CrMoSiA、30CrMnTi等合金结构钢为主。
以往采用的工艺方法是只对铰接销轴进行整体调质处理，设计强度满足了使用要求，经常出现外圆表面磨出沟痕现象。为解决表面硬度不足的问题，提高了调质硬度，达到HB300以上。虽然外圆表面耐磨的问题得到一定的改善，但又常常出现脆断现象。
发明内容
本发明的目的是提供一种既能使零件表面有一定的硬度，又能使芯部具有足够的强度和韧性的液压支架铰接销轴的热处理方法。
本发明的目的是通过以下技术方案实现的：
本发明的液压支架铰接销轴的热处理方法，包括：
首先，对销轴进行调质处理，得到回火索氏体；
然后，对销轴进行表面淬火，所述表面淬火的温度为Ac3以上80-150℃，淬火得到细隐晶马氏体。
由上述本发明提供的技术方案可以看出，本发明提供的液压支架铰接销轴的热处理方法，由于首先对销轴进行调质处理，得到回火索氏体；然后对销轴进行表面淬火，表面淬火的温度为Ac3以上80-150℃，淬火得到细隐晶马氏体。使零件不仅表面有一定的硬度，具备耐磨和抗疲劳，而且芯部具有足够的强度和韧性。
附图说明
图1为本发明实施例中液压支架铰接销轴的热处理后的金相结构示意图。
图中：1、细隐晶马氏体，2、回火索氏体，a、表面层厚度。
具体实施方式
下面将结合附图对本发明实施例作进一步地详细描述。
本发明的液压支架铰接销轴的热处理方法，其较佳的具体实施方式包括步骤：
首先，对销轴进行调质处理，得到回火索氏体；
然后，对销轴进行表面淬火，所述表面淬火的温度为Ac3(临界温度)以上80-150℃，淬火得到细隐晶马氏体。
所述调质处理后的硬度为HB240～HB300，所述表面淬火后的表面硬度HRC44～HRC48。
所述表面淬火的有效淬硬深度为2～10mm。
所述表面淬火采用中频感应加热或激光表面加热。
所述中频感应加热的电流频率为500～10000Hz。
所述销轴的材料为35CrMoSiA合金结构钢或30CrMnTi合金结构钢。
本发明将调质处理后的工件表面快速加热到奥氏体区，在热量尚未传到心部时立即迅速冷却，使表面得到一定深度的淬硬层，获得高硬度的表面层和有利的残余压应力分布。解决了零件不仅表面有一定的硬度，具备耐磨和抗疲劳，而且芯部具有足够的强度和韧性的使用要求。
具体实施例：
调质硬度HB240～HB300、表面硬度HRC44～HRC48。
中频感应加热：电流频率在500～10000Hz(赫)，有效淬硬深度为2～10mm(毫米)，对工件圈通以相应电流，产生磁场，在铁磁性材料中产生感生电流，由于趋肤效应，感生电流聚积于材料的表面产生热，达到相变温度，激冷达到淬火目的。它不仅改变其组织和性能，而且还提高了零件的表面硬度及耐磨性。在配合预先调质热处理的心部组织，就获得更高的疲劳强度和强韧性。
申请人发现，钢的奥氏体化在较大的过热度(Ac3以上80-150℃)下进行，晶核多、不易长大、淬火后组织为细隐晶马氏体、脆性较低；表面层淬火得到马氏体后，由于体积膨胀在工件表层造成较大的残余压应力，显著提高工件的疲劳强度；加热速度快，没有保温时间，表面氧化脱碳少。
本发明改变了销轴传统热处理方式；获得更高的疲劳强度和强韧性；生产效率高、环境污染极少。使液压支架用铰接销轴不仅表面有一定的硬度、具备耐磨，而且芯部具有足够的强度和韧性的使用要求。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书的保护范围为准。

Claims (6)

1.一种液压支架铰接销轴的热处理方法，其特征在于，包括步骤：
首先，对销轴进行调质处理，得到回火索氏体；
然后，对销轴进行表面淬火，所述表面淬火的温度为Ac3以上80-150℃，淬火得到细隐晶马氏体。
2.根据权利要求1所述的液压支架铰接销轴的热处理方法，其特征在于，所述调质处理后的硬度为HB240～HB300，所述表面淬火后的表面硬度HRC44～HRC48。
3.根据权利要求2所述的液压支架铰接销轴的热处理方法，其特征在于，所述表面淬火的有效淬硬深度为2～10mm。
4.根据权利要求1、2或3所述的液压支架铰接销轴的热处理方法，其特征在于，所述表面淬火采用中频感应加热或激光表面加热。
5.根据权利要求4所述的液压支架铰接销轴的热处理方法，其特征在于，所述中频感应加热的电流频率为500～10000Hz。
6.根据权利要求4所述的液压支架铰接销轴的热处理方法，其特征在于，所述销轴的材料为35CrMoSiA合金结构钢或30CrMnTi合金结构钢。
CN2012101223489A 2012-04-24 2012-04-24 液压支架铰接销轴的热处理方法 Pending CN102634650A (zh)