CN102634146A - 一种高磨性聚偏二氟乙烯的配方 - Google Patents
一种高磨性聚偏二氟乙烯的配方 Download PDFInfo
- Publication number
- CN102634146A CN102634146A CN2012100911161A CN201210091116A CN102634146A CN 102634146 A CN102634146 A CN 102634146A CN 2012100911161 A CN2012100911161 A CN 2012100911161A CN 201210091116 A CN201210091116 A CN 201210091116A CN 102634146 A CN102634146 A CN 102634146A
- Authority
- CN
- China
- Prior art keywords
- accounts
- stearic acid
- prescription
- sodium sulfate
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明揭示了一种高磨性聚偏二氟乙烯的配方,包括减摩剂、无机引发剂、有机引发剂以及特殊材料,所述减摩剂为磷酸三苯酯,所述的无机引发剂为硫酸钠,所述的有机引发剂为稳定剂,所述的特殊材料包括硬脂酸和烷基磺酸苯酯,各成分重量配比为磷酸三苯酯占21%-73%,硫酸钠占3%-17%,稳定剂占7%-21%,硬脂酸占7%-21%,烷基磺酸苯酯占10%-20%。使制得的新型改性聚偏二氟乙烯具有更耐磨、有利于注塑成形和起到光亮作用的效果。
Description
技术领域
本发明涉及一种塑料配方,具体涉及一种高磨性聚偏二氟乙烯的配方。
背景技术
聚偏二氟乙烯是一种新颖的氟碳树脂,具有很高的机械强度与耐磨性,耐候性和热稳定性也很好,此外还具有突出的耐腐蚀性,所以是在化工行业必须要的使用原料,任何金属都无法代替的,聚偏二氟乙烯被广发采用,具有很好的压电性、耐辐射,热稳定性也很好,所以被电子行业、变压器制造广泛采用,还用在航空航天、军事领域、海水淡化、冶金、电线电缆、电器元件、机械制造等领域。
但是,要达到某些特殊领域的机械制造的零部件的要求上,还是有些不足的,众所周知,钢是制造机械的必需材料,但用在化工行业的强酸、碱、盐、极性溶剂方面是不能用的,可是,长期困扰着这方面的材料一直没有得到很好的开发,有些材料可用但加工困难,并且不能反复使用,所以在强腐蚀化工行业,每年都耗资巨大,效力、性能、使用寿命都达不到要求,当务之急必须要解决研发这方面的特殊材料,使得花工行业得到稳定长远的发展,因此,有很多企业来找我苏州特氟龙公司来研究探讨,研发高强度、搞耐腐蚀、耐开裂不变形的氟塑料高性能材料,好在特氟龙公司是国内最早研发高性能氟塑料的企业之一,在这一材料的科技领域取得了很好的发展和突破,稳定了产品的质量,又和很多企业之间有着长期的合作,并获得了它们的肯定,从而加深了更好的发展,另外,新的产品还在不断的研发和试产中。
国内第一家生产磁力驱动泵企业就是一个例子,以前长期使用没有改性过的聚偏二氟乙烯主要用在泵阀上,但其达不到要求,它在高压高温、耐腐蚀上得不到解决。客户要求强酸介质扬程100m能够使用,但没有达到,实际只能在50m徘徊,用其他材料又无法代替,后来与本公司合作后得到了充分的解决,而且还可以扬程更远,使用寿命更长,耐压提升了三倍以上,得到了很好的认可。
发明内容
本发明的目的在于提供具有更耐磨、有利于注塑成形和起到光亮作用效果的高磨性聚偏二氟乙烯的配方。
本发明的技术方案是:一种高磨性聚偏二氟乙烯的配方,包括减摩剂、无机引发剂、有机引发剂以及特殊材料,所述减摩剂为磷酸三苯酯,所述的无机引发剂为硫酸钠,所述的有机引发剂为稳定剂,所述的特殊材料包括硬脂酸和烷基磺酸苯酯,各成分重量配比为磷酸三苯酯占21%-73%,硫酸钠占3%-17%,稳定剂占7%-21%,硬脂酸占7%-21%,烷基磺酸苯酯占10%-20%。
在本发明一个较佳实施例中,所述硬脂酸包括十六碳和十八碳的饱和酸。
在本发明一个较佳实施例中,所述稳定剂包括纯的PVC树脂。
在本发明一个较佳实施例中,所述高磨性聚偏二氟乙烯的配方各成分重量配比为磷酸三苯酯占41%,硫酸钠占13%,稳定剂占17%,硬脂酸占11%,烷基磺酸苯酯占18%。
本发明的一种高磨性聚偏二氟乙烯的配方,具有更耐磨、有利于注塑成形和起到光亮作用的效果。
具体实施方式
下面结合对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
在一实施例中,一种高磨性聚偏二氟乙烯的配方,包括减摩剂、无机引发剂、有机引发剂以及特殊材料,所述减摩剂为磷酸三苯酯,所述的无机引发剂为硫酸钠,所述的有机引发剂为稳定剂,所述的特殊材料包括硬脂酸和烷基磺酸苯酯,各成分重量配比为磷酸三苯酯占21%-73%,硫酸钠占3%-17%,稳定剂占7%-21%,硬脂酸占7%-21%,烷基磺酸苯酯占10%-20%,所述硬脂酸包括十六碳和十八碳的饱和酸,所述稳定剂包括纯的PVC树脂。
进一步说明,所述高磨性聚偏二氟乙烯的配方各成分重量配比为磷酸三苯酯占41%,硫酸钠占13%,稳定剂占17%,硬脂酸占11%,烷基磺酸苯酯占18%,根据不同需求可按照不同比例进行调试,从而达到不同的使用效果,而磷酸三苯酯具有更耐磨,稳定剂和硫酸钠有利于注塑成形,硬脂酸和烷基磺酸苯酯起到光亮作用,本发明提供一种高磨性聚偏二氟乙烯的配方,具有更耐磨、有利于注塑成形和起到光亮作用的效果。
本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本领域的技术人员在本发明所揭露的技术范围内,可不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (4)
1.一种高磨性聚偏二氟乙烯的配方,其特征在于:包括减摩剂、无机引发剂、有机引发剂以及特殊材料,所述减摩剂为磷酸三苯酯,所述的无机引发剂为硫酸钠,所述的有机引发剂为稳定剂,所述的特殊材料包括硬脂酸和烷基磺酸苯酯,各成分重量配比为磷酸三苯酯占21%-73%,硫酸钠占3%-17%,稳定剂占7%-21%,硬脂酸占7%-21%,烷基磺酸苯酯占10%-20%。
2.根据权利要求1所述的高磨性聚偏二氟乙烯的配方,其特征在于:所述硬脂酸包括十六碳和十八碳的饱和酸。
3.根据权利要求1所述的高磨性聚偏二氟乙烯的配方,其特征在于:所述稳定剂包括纯的PVC树脂。
4.根据权利要求1所述的高磨性聚偏二氟乙烯的配方,其特征在于:所述高磨性聚偏二氟乙烯的配方各成分重量配比为磷酸三苯酯占41%,硫酸钠占13%,稳定剂占17%,硬脂酸占11%,烷基磺酸苯酯占18%。