CN102628235A - Dyeing and finishing process of mixed fabric of bamboo fiber and real silk - Google Patents
Dyeing and finishing process of mixed fabric of bamboo fiber and real silk Download PDFInfo
- Publication number
- CN102628235A CN102628235A CN2012100947252A CN201210094725A CN102628235A CN 102628235 A CN102628235 A CN 102628235A CN 2012100947252 A CN2012100947252 A CN 2012100947252A CN 201210094725 A CN201210094725 A CN 201210094725A CN 102628235 A CN102628235 A CN 102628235A
- Authority
- CN
- China
- Prior art keywords
- dyeing
- fabric
- bamboo fiber
- temperature
- bamboo fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dyeing and finishing process of mixed fabric of bamboo fiber and real silk, which includes the following steps: greige cloth sewing, pre-setting, pretreatment, dyeing, dehydration and after finishing. A dyeing process includes the following steps: first, 70% alcohol liquid is adopted for soaking for 30-40 minutes, then bamboo fiber is dyed with low-temperature disperse dyes, dyeing temperature is below 120-130 DEG C, potential of hydrogen (pH) value of dye bath is 5-6, reduction clearing of the dyed bamboo fiber is performed, and real silk is dyed after reduction clearing. The pre-setting of the dyeing and finishing process ensures high smoothness of appearance, sense of touch and color. The pretreatment process not only plays the roles of desizing and scouring, but also ensures that strong force of bamboo fiber does not suffer great damage. The dyeing process ensures good dyeing effect and dyeing fastness. By using alcohol for sterilization, circumstances of bamboo fiber mildewing and the like can be prevented. Clove oil is capable of enabling fabric to be soft and smooth.
Description
Background technology
The present invention relates to field of textiles, specifically is the dyeing and finishing technology of a kind of bamboo fibre and silk interlaced fabric.
Background technology
Real silk is the dress material that people like, in state-owned several thousand history; Bamboo fibre is a kind of string; Have nice and cool, environmental protection is special, is particularly suitable for the cloth textile in summer, on fabric, using constantly increases; But still not with bamboo fibre and silk blend, the present invention explores in the dyeing and finishing of bamboo fibre and silk blend fabric in the existing fabric technology.
Summary of the invention
The invention provides the dyeing and finishing technology of a kind of bamboo fibre and silk interlaced fabric, have good dye uptake, in conjunction with the advantage of real silk and bamboo fibre, nice and cool, good hand touch.
Technical scheme of the present invention is:
The dyeing and finishing technology of a kind of bamboo fibre and silk interlaced fabric; Include following steps: grey cloth margin to seam, pre-setting, pre-treatment, dyeing, dehydration, postfinishing process; It is characterized in that: the temperature of described presetting technology is 110-120 ℃, and the time is 30-35 minute; Described pre-treatment process contains NaOH, the hydrogen peroxide solution of 3-7g/L, the 1-2g/L amylase of 1-2g/L for the fabric behind the pre-setting is carried out destarch in the desizing liquid, the desizing liquid temperature is below 70 ℃; Described dyeing is to adopt 70% alcohol liquid to soak earlier 30-40 minute; Adopt the low form DISPERSE DYES to dye to bamboo fibre again, dyeing temperature is below 120-130 ℃, and the pH value of dye bath is 5~6; Bamboo fibre after the dyeing carries out reduction cleaning, carries out dyeing silk after the reduction cleaning again; In the reduction cleaning liquid: sodium hydrosulfite 0.5-1.5g/L, anionic detergent 1.5-2.5g/L, sodium acid carbonate 0.5-1.5g/L transfers Ph6-6.5 with acetic acid, and cleaning temperature is 58-63 ℃, and the time is 15-20 minute; The hydrophilic amino silicone softener that described postfinishing process is put into 6-8 g/L for the fabric after will dyeing pads, and the fabric after padding is in 80-90 ℃ of oven dry and stentering forming.
Add the clove oil of 0.2-0.3% percentage by weight, the Bamboo vinegar solution of 2-3% in the described 70% alcohol liquid.
Bamboo fibre of the present invention has following advantage:
Pre-setting of the present invention has guaranteed good surface appearance planarization, feel and color and luster; The effect of destarch kiering had both been played in described pre-treatment, had guaranteed that again the brute force of bamboo fibre does not receive greater loss; Described dyeing has guaranteed good Color and dyefastness, has reduced the dyeing cost again; Described postfinishing process has guaranteed the brute force of yarn.Adopt alcohol to carry out sterilization, can play situation such as the prevention bamboo fibre goes mouldy, clove oil can be so that fabric be more soft, smooth.
The specific embodiment
Example 1:
The dyeing and finishing technology of bamboo fibre and silk interlaced fabric includes following steps:
Carry out grey cloth margin to seam, pre-setting, pre-treatment, dyeing, dehydration, postfinishing process successively, the temperature of presetting technology is 110-120 ℃, and the time is 30-35 minute; Described pre-treatment process contains NaOH, the hydrogen peroxide solution of 3-7g/L, the 1-2g/L amylase of 1-2g/L for the fabric behind the pre-setting is carried out destarch in the desizing liquid, the desizing liquid temperature is below 70 ℃; Described dyeing is to adopt 70% alcohol liquid to soak earlier 30-40 minute; Adopt the low form DISPERSE DYES to dye to bamboo fibre again, dyeing temperature is below 120-130 ℃, and the pH value of dye bath is 5~6; Bamboo fibre after the dyeing carries out reduction cleaning, carries out dyeing silk after the reduction cleaning again; In the reduction cleaning liquid: sodium hydrosulfite 0.5-1.5g/L, anionic detergent 1.5-2.5g/L, sodium acid carbonate 0.5-1.5g/L transfers Ph6-6.5 with acetic acid, and cleaning temperature is 58-63 ℃, and the time is 15-20 minute; The hydrophilic amino silicone softener that described postfinishing process is put into 6-8 g/L for the fabric after will dyeing pads, and the fabric after padding is in 80-90 ℃ of oven dry and stentering forming.
Example 2:
The dyeing and finishing technology of bamboo fibre and silk interlaced fabric includes following steps:
Carry out grey cloth margin to seam, pre-setting, pre-treatment, dyeing, dehydration, postfinishing process successively, the temperature of presetting technology is 110-120 ℃, and the time is 30-35 minute; Described pre-treatment process contains NaOH, the hydrogen peroxide solution of 3-7g/L, the 1-2g/L amylase of 1-2g/L for the fabric behind the pre-setting is carried out destarch in the desizing liquid, the desizing liquid temperature is below 70 ℃; Described dyeing is to adopt 70% alcohol liquid to soak earlier 30-40 minute; Add the clove oil of 0.2-0.3% percentage by weight, the Bamboo vinegar solution of 2-3% in the 70% alcohol liquid; Adopt the low form DISPERSE DYES to dye to bamboo fibre again, dyeing temperature is below 120-130 ℃, and the pH value of dye bath is 5~6; Bamboo fibre after the dyeing carries out reduction cleaning, carries out dyeing silk after the reduction cleaning again; In the reduction cleaning liquid: sodium hydrosulfite 0.5-1.5g/L, anionic detergent 1.5-2.5g/L, sodium acid carbonate 0.5-1.5g/L transfers Ph6-6.5 with acetic acid, and cleaning temperature is 58-63 ℃, and the time is 15-20 minute; The hydrophilic amino silicone softener that described postfinishing process is put into 6-8 g/L for the fabric after will dyeing pads, and the fabric after padding is in 80-90 ℃ of oven dry and stentering forming.The fabric COLOR FASTNESS that obtains is good, soft, smooth.
Claims (2)
1. the dyeing and finishing technology of a bamboo fibre and silk interlaced fabric; Include following steps: grey cloth margin to seam, pre-setting, pre-treatment, dyeing, dehydration, postfinishing process; It is characterized in that: the temperature of described presetting technology is 130-150 ℃, and the time is 3-5 minute; Described pre-treatment process contains NaOH, the hydrogen peroxide solution of 3-7g/L, the 1-2g/L amylase of 2-4g/L for the fabric behind the pre-setting is carried out destarch in the desizing liquid, the desizing liquid temperature is below 70 ℃; Described dyeing is to adopt 70% alcohol liquid to soak earlier 30-40 minute; Adopt the low form DISPERSE DYES to dye to bamboo fibre again, dyeing temperature is below 110 ℃, and the pH value of dye bath is 5~6; Bamboo fibre after the dyeing carries out reduction cleaning, carries out dyeing silk after the reduction cleaning again; In the reduction cleaning liquid: sodium hydrosulfite 0.5-1.5g/L, anionic detergent 1.5-2.5g/L, sodium acid carbonate 0.5-1.5g/L, cleaning temperature are 58-63 ℃, the time is 15-20 minute; The hydrophilic amino silicone softener that described postfinishing process is put into 6-8 g/L for the fabric after will dyeing pads, and the fabric after padding is in 80-90 ℃ of oven dry and stentering forming.
2. the dyeing and finishing technology of bamboo fibre according to claim 1 and silk interlaced fabric is characterized in that adding in the described 70% alcohol liquid clove oil of 0.2-0.3% percentage by weight, the Bamboo vinegar solution of 2-3%.