CN102627894A - 一种墙体保温涂料及其制备方法 - Google Patents
一种墙体保温涂料及其制备方法 Download PDFInfo
- Publication number
- CN102627894A CN102627894A CN2012100860742A CN201210086074A CN102627894A CN 102627894 A CN102627894 A CN 102627894A CN 2012100860742 A CN2012100860742 A CN 2012100860742A CN 201210086074 A CN201210086074 A CN 201210086074A CN 102627894 A CN102627894 A CN 102627894A
- Authority
- CN
- China
- Prior art keywords
- urethane foam
- thermal insulation
- insulating coating
- insulation coatings
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种墙体保温涂料,它由以下重量百分比的组分组成:聚氨酯泡体10-15%、丙烯酸树脂15-20%、石英颗粒15-20%、成膜助剂1-2%、余量的其他助剂和水。所述的保温涂料能够实现施工简便,减少工序,减少工时,防火不易燃,使用年限加长等技术效果,为住宅环保节能做保障产品。
Description
技术领域
本发明涉及一种保温涂料,具体涉及一种墙体保温涂料,及其制备方法。
背景技术
现有技术中的墙体保温材料及其主要局限性如下:
1.胶粉聚苯颗粒外墙外保温系统:所需保温层太厚,并且外面需要挂网,抹抗裂砂浆,施工工序繁复。(JG 158-2004胶粉聚苯颗粒外墙外保温系统);
2.膨胀聚苯板薄抹灰外墙外保温系统:需要打钉挂板,挂网,再抹抗裂砂浆,施工工序繁复,并且如果有水渗入墙面和聚苯板之间,易产生膨胀开裂,失去保温效果。(JG 149-2003膨胀聚苯板薄抹灰外墙外保温系统);
3.喷涂聚氨酯硬泡体保温材料:主要用作屋顶和平面保温,对立面墙体保温则不适合。(JC/T 998-2006喷涂聚氨酯硬泡体保温材料)。
发明内容
现用的保温系统工序复杂,需要工时多,使用年限短,有些易燃,完工几年后易出问题。为了解决以上问题,本发明提出一种墙体聚氨酯泡体保温涂料,能够实现施工简便,减少工序,减少工时,防火不易燃,使用年限加长等技术效果,为住宅环保节能做保障产品。
本发明的上述目的是通过以下技术方案实现的:
提供一种墙体保温涂料,它由以下重量百分比的组分组成:聚氨酯泡体10-15%、丙烯酸树脂15-20%、石英颗粒15-20%、成膜助剂1-2%、余量的其他助剂和水。
所述的聚氨酯泡体可以选自市售的各种聚氨酯泡体,优选每单位体积内含有3~10个气泡的聚氨酯泡体。
本发明优选的聚氨酯泡体可以通过以下方法制备得到:
由等比例的MDI(异氰酸酯)和聚醚多元醇双组份在20-30℃温度和常压下合成发泡为聚氨酯固体,再经过挤出研磨达至28~46目,然后经过常规表面处理后得到本发明优选的聚氨酯泡体。
所述的丙烯酸树脂和成膜助剂都是常规的市售产品;所述的成膜助剂优选伊士曼C-12成膜助剂。
所述的石英颗粒的粒径没有限制。
所述的其他助剂可以根据不同需要选自阻燃剂、防腐剂、紫外线吸收剂或颜料中的一种或两种以上的混合物。
所述的阻燃剂优选甲基磷酸二甲酯(DMMP)。
本发明优选的墙体保温涂料由以下重量百分比的组分组成:聚氨酯泡体10-15%、丙烯酸树脂15-20%、石英颗粒15-20%、成膜助剂1-2%、4.5~5%的阻燃剂和余量的水。
本发明所述的墙体保温涂料的制备方法是将所述组分按比例混合至均匀分散即得。
所述的均匀分散可以通过可兼顾高低剪切速率的乳化设备快速高效地完成,优选低剪切速率可达100-300转/分钟、高剪切速率可达600-800转/分钟的乳化设备。
本发明优选的制备方法中,还可以先对聚氨酯泡体的表面进一步添加阻燃剂,然后再与其他组分按所述比例混合。这样可以使本发明的保温涂料具有阻燃效果,使保温涂料的整体防火等级额达到不燃。
本发明的施工工艺如下:
a、在旧墙面上,经过简单处理后,可以取本发明所述的涂料直接进行喷涂,达到一定厚度后,可以有效填平墙面凹凸和填补墙缝;
b、在新建水泥墙面上,可以用本发明所述的涂料替代腻子直接进行刮涂,使墙面找平、填缝、抗碱封闭一次完成,并且具有显著的保温效果。
本发明的墙体保温涂料与现有技术相比,具有以下有益效果:
a、由于本发明所述的涂料具有粘度高,粒径均匀的特点,因此可以通过直接喷涂的方式完成施工,而不需要像现有技术中的涂料那样需要预先挂板、挂网等工序。本发明的涂料在平面装饰和异面装饰中都可以通过喷涂一次完成。
b、本发明的涂料兼具耐候、隔音、保温和阻燃等多方面优点。
本发明的涂料中,聚氨酯泡体内部有多个小泡,内含空气,泡体的隔绝作用不仅可以达到良好的保温效果,而且能使音波产生漫反射,相互抵消,有效地达到吸音效果;丙烯酸树脂能起到粘合作用,增强涂料的粘结强度;石英颗粒能起到巩固涂层结构的作用;成膜助剂能起到外层成膜保护作用,使得本发明的涂料更加坚固耐用,使用寿命更长。
c、通过调色和泡体染色可以使色彩更加丰富多彩,达到更多风格的装饰功能。通过喷涂施工方法,可以达到仿真石漆效果。
具体实施方式
实施例1.
一种墙体保温涂料,它含有以下重量百分比的组分:
10%的聚氨酯泡体、20%的丙烯酸树脂、15%的石英颗粒、2%的成膜助剂伊士曼C-12、4.5%的阻燃剂DMMP和余量的水。
所述的聚氨酯泡体是市售的产品,每单位体积内含有3~10个气泡。
所述的涂料的制备方法是:按照所述比例取原料后,先在所述的聚氨酯泡体表面添加所述比例的阻燃剂,然后再与其余原料混合至均匀分散即可。
实施例2.
一种墙体保温涂料,它含有以下重量百分比的组分:
10%的聚氨酯泡体、15%的丙烯酸树脂、20%的石英颗粒、1%的成膜助剂伊士曼C-12、4.5%的阻燃剂DMMP和余量的水。
所述的聚氨酯泡体是市售的产品,每单位体积内含有3~10个气泡。
所述的涂料的制备方法是:按照所述比例取原料后,先在所述的聚氨酯泡体表面添加所述比例的阻燃剂,然后再与其余原料混合至均匀分散即可。
实施例3.
一种墙体保温涂料,它含有以下重量百分比的组分:
15%的聚氨酯泡体、20%的丙烯酸树脂、20%的石英颗粒、2%的成膜助剂伊士曼C-12和余量的水。
所述的聚氨酯泡体是市售的产品,每单位体积内含有5~10个气泡,并按照以下方法制备得到:
由等比例的MDI(异氰酸酯)和聚醚多元醇双组份在20℃温度和常压下合成发泡为聚氨酯固体,再经过挤出研磨达至28~30目,然后经过常规表面处理即得。
所述的涂料的制备方法是:按照所述比例取原料后混合至均匀分散即可。
实施例4.
一种墙体保温涂料,它含有以下重量百分比的组分:
10%的聚氨酯泡体、15%的丙烯酸树脂、15%的石英颗粒、1%的成膜助剂伊士曼C-12、4.5%的阻燃剂DMMP和余量的水。
所述的聚氨酯泡体是市售的产品,每单位体积内含有5~10个气泡,并按照以下方法制备得到:
由等比例的MDI(异氰酸酯)和聚醚多元醇双组份在30℃温度和常压下合成发泡为聚氨酯固体,再经过挤出研磨达至36~46目,然后经过常规表面处理即得。
所述的涂料的制备方法是:按照所述比例取原料后,先在所述的聚氨酯泡体表面添加所述比例的阻燃剂,然后再与其他的原料一起混合后,用低剪切速率可达100-300转/分钟、高剪切速率可达600-800转/分钟的乳化设备进行分散,直至分散均匀即可。
Claims (10)
1.一种墙体保温涂料,其特征在于,它由以下重量百分比的组分组成:聚氨酯泡体10-15%、丙烯酸树脂15-20%、石英颗粒15-20%、成膜助剂1-2%、余量的其他助剂和水。
2.权利要求1所述的保温涂料,其特征在于:所述的聚氨酯泡体每单位体积内含有3~10个气泡的聚氨酯泡体。
3.权利要求2所述的保温涂料,其特征在于,所述的聚氨酯泡体通过以下方法制备得到:由等比例的异氰酸酯和聚醚多元醇双组份在20-30℃温度和常压下合成发泡为聚氨酯固体,再经过挤出研磨至28~46目,然后经过常规表面处理后得到所述的聚氨酯泡体。
4.权利要求1所述的保温涂料,其特征在于:所述的成膜助剂是伊士曼C-12成膜助剂。
5.权利要求1所述的保温涂料,其特征在于:所述的其他助剂选自阻燃剂、防腐剂、紫外线吸收剂或颜料中的一种或两种以上的混合物。
6.权利要求5所述的保温涂料,其特征在于:所述的阻燃剂是甲基磷酸二甲酯。
7.权利要求1所述的保温涂料,其特征在于:所述的墙体保温涂料由以下重量百分比的组分组成:聚氨酯泡体10-15%、丙烯酸树脂15-20%、石英颗粒15-20%、成膜助剂1-2%、4.5~5%的阻燃剂和余量的水。
8.权利要求1所述的保温涂料的制备方法,是将所述组分按比例混合至均匀分散即得。
9.权利要求8所述的制备方法,其特征在于:所述的均匀分散通过低剪切速率可达100-300转/分钟、高剪切速率可达600-800转/分钟的乳化设备完成。
10.权利要求8所述的制备方法,其特征在于:先对聚氨酯泡体的表面进一步添加阻燃剂,然后再与其他组分按所述比例混合。