CN102621811B - A kind of developed photosensitive resin composition being applied to panel construction - Google Patents
A kind of developed photosensitive resin composition being applied to panel construction Download PDFInfo
- Publication number
- CN102621811B CN102621811B CN201110033452.6A CN201110033452A CN102621811B CN 102621811 B CN102621811 B CN 102621811B CN 201110033452 A CN201110033452 A CN 201110033452A CN 102621811 B CN102621811 B CN 102621811B
- Authority
- CN
- China
- Prior art keywords
- resin composition
- photosensitive resin
- monomer
- oxygen ethylene
- transparent substrates
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of developed photosensitive resin composition being applied to panel construction of the present invention, can develop photosensitive resin composition for one kind, it contains resin, photosensitive initiator, monomer, solvent, Chinese white and dispersant;Wherein, this Chinese white is 20 ~ 45wt% in this photosensitive resin composition, this photosensitive resin composition is made to present white appearance color, one transparent substrates wherein one surface periphery is arranged at by this photosensitive resin composition, and form the panel construction with white in finish function of frame, can be applicable in the Related products such as contact panel or flat-panel screens.
Description
Technical field
The present invention is about the composition of the photosensitive resin composition that can develop, it is desirable to provide one kind can be developed photoresist group
Become thing to can be applicable in the Related products such as contact panel or flat-panel screens, black or depth can be limited to by different conventional appearance color
The disappearance of color, uses improving product outward appearance collocation property.
Background technology
It is general that contact panel has been widely used in mobile phone mobile phone, digital camera and satellite navigator etc. at present
On consumer electronics commodity, use interface in order to improve, lift input efficiency;Generally, contact panel is transparent and is configured in
Use before the display screen of these electronic goods, user can be grasped with interacting formula input according to instruction message on display screen
Make, so greatly improve between people and machine link up interface friendliness.Typical structure of touch-control panel is by a touch-control sensor
Being arranged between a top board and a substrate of insulation, is then provided with circuit in the peripheral part of overlapping board, in order to by touch-control sensing
Touch signal on device is sent to a signal processing circuit;When earlier, the assembling mode of contact panel and display screen, mostly
Suppressed in the edge of contact panel Watch glass using a cover frame, and contact panel be fixedly arranged in front of display screen and use,
And this cover frame, in addition to the purpose in order to fixed panel, also has protection contact panel Watch glass perimeter circuit and beautification
The efficiency of mounting structure.
So this kind of known touch panel assemblage structure often can derive many disappearances, and for example, the setting of cover frame can be on surface
Glass forms rugged surface, can destroy the planarization of product-forming, and when making the plate face clean wiping of inframe, easily
So that dust dirt is snapped in the gap between cover frame and contact panel Watch glass, clean sordid hygienic issues except producing
Outside, the filling accumulation in architrave gap for the dust dirt, also it is very easy to lead to contact panel that misoperation occurs, and touch surface
The line construction of plate edge is typically more fragile, and the accumulation extruding easily side by dust and dirt wadding becomes to damage, and leads to pass
Interrogate bad phenomenon, be packed in the adhesion that the dirt in architrave gap can destroy between shell and contact panel in addition, impact is anti-
Water dust-proof effect, or even cause the damage of internal electric appliance component.
The known contact panel of another kind also can stick on a decorative layer in Watch glass, and this decorative layer is typically many non-using dark color
The frame structure that conductive material is formed, in order to hide perimeter circuit below decorations Watch glass, accomplishes the touch surface of whole plane simultaneously
Plate;Only, the manufacturing process using mode of pasting is numerous and diverse, causes the chance of error also can be lifted, and this decorative layer is most during production
For black or silver color although lifting the texture of its product, but but also its appearance color is made to be restricted and not have variability.
Content of the invention
In view of this, the present invention is intended to provide one kind can be applicable in the Related products such as contact panel or flat-panel screens,
With improving product outward appearance collocation property.
For reaching above-mentioned purpose, the photosensitive resin composition of the present invention, containing resin, photosensitive initiator, monomer, solvent,
Chinese white and dispersant;Wherein, this Chinese white is 20 ~ 45wt% in this photosensitive resin composition, makes this photonasty
Resin combination presents white appearance color.
Present invention can apply in the Related product such as contact panel or flat-panel screens, wherein, this photoresist forms
Thing may be disposed at a transparent substrates wherein surface periphery, and forms the panel construction with white in finish function of frame, and also
Bridging effect can be formed to the line layer of lower section peripheral part.
Brief description
Fig. 1 is the structural representation of panel in the present invention.
Figure number explanation:Panel construction 1;Transparent substrates 11;Lower surface 111;White frame layer 12;Circuit 13.
Specific embodiment
The photosensitive resin composition of the present invention, the resin containing 15 ~ 35wt%, the photosensitive initiator of 0.5 ~ 10wt%, 0 ~
The monomer of 20wt%, the dispersant of the solvent of 25 ~ 50wt%, the Chinese white of 20 ~ 45wt% and 1 ~ 5wt%.
Wherein:This resin can be the polymer or copolymer containing carboxylic acid group (COOH), such as can be including but not limited to pressure gram
Power resin, acryl-epoxy resin, acryl-Mei Nai ware resin, acryl-styrene resin, phenol-phenolic resin, or with
The mixing of upper resin.Because Chinese white proportion is higher, relatively tend to have the generation of precipitation, therefore molecular resin amount need to be more than 8000, resin
Molecular weight more than 8000 collocation proper proportion, can slow down white raw material settling velocity.If molecular weight is excessive but then, have
Operate the problem being difficult, therefore molecular weight requirement is preferred 100, less than 000, more preferably then in 20,000-70,000 scopes.
The function of this photosensitive initiator is photobehavior, analytic ability, its can including but not limited to oxime ester based compound,
1-Phenylethanone. based compound, benzophenone based compound or diimidazole based compound, or more photosensitive initiator mixing.
The function of this monomer is to provide preferably tack, developability, analytic ability etc., can be including but not limited to many officials
The acrylate monomer of energy, non-water soluble monomers or water-soluble monomer, this polyfunctional acrylate monomer can be trimethyl
Propane triacrylate, three propyleneglycoles double methacrylates, 1,6 hexanediol double methacrylates;And this non-water soluble monomers can
Think penta erythritol triacrylate, trimethyl ether propane triacrylate, trimethyl ether propane trimethyl acrylic ester,
Three, two-ethanol isocyanurate triacrylate, two, trihydroxymethyl propane tetraacrylate, diisoamyl tetrol five acrylate, five
Acrylate, tetraacethyl pentaerythritol, the own tetrol of six acetic acid two, six acetic acid diisoamyl tetrols, or be multiple functional radical monomer, tree
Shape/many clumps of a small bundle of straw, etc. for silkworms to spin cocoons on acrylate widow's bodies, many clumps of a small bundle of straw, etc. for silkworms to spin cocoons on polyether acrylates, aethylis carbamases;And this water-soluble monomer can be then polyoxy
Ethylene and the monomer of polyoxypropylene, it can be two-(two-oxygen ethylene oxy ethylene) ethylene propylene acid esters, 15 polyoxyethylene three
Methanol propane triacrylate, 30 oxygen ethylene two, two-bis- to phenol methane diacrylate, 30 oxygen ethylene two, two-
Double to phenol dimethylamino methane base acrylate, 20 oxygen ethylene trihydroxymethyl propane triacrylates, 15 oxygen ethylene three methanol
Propane triacrylate, 550 oxygen ethylene monomethacrylates of methyl oxygen, 200 oxygen ethylene diacrylates, four
Hundred oxygen ethylene diacrylates, 400 oxygen ethylene dimethylacrylates, 600 oxygen ethylene diacrylates, 600
Oxygen ethylene dimethylacrylate, polyoxypropylene monomethacrylates;Also or two or more monomers can be added be mixed into altogether
Monomer.
This Chinese white is including but not limited to can be titanium dioxide (titanium dioxide), ceruse (White
Lead), zinc oxide (Zinc oxide), zinc sulfide (Zinc sulphide), Griffith's zinc white. (lithopone) or stibium oxide
(Antimony oxide);Need to reach photosensitive resin composition more than 20% for reaching this Chinese white of screening effect, to reach
Screening effect, has the situation of poor visualization to produce more than 45%.And this solvent is used as adjustment viscosity, it can be propylene glycol
Monomethyl ether acetate;This photosensitive resin composition can add appropriate additive further, for example, can be interfacial agent.
Overall photosensitive resin composition is because being added with Chinese white, therefore presents white appearance color, also can be further
Add another other pigment, such as add Blue Pigment 15 and assume blueness, add Pigment Green 7 and present green
Color, or add other toners and reach the color wanted.
And the photosensitive resin composition of the present invention can be applicable in the Related products such as contact panel or flat-panel screens, its
In transparent substrates via rotary coating (spin coating) step, the photosensitive resin composition of the present invention is coated this
Transparent substrates upper surface, more sequentially via vacuum drying (vacuum dry), pre-baked (pre-baking), exposure
(exposure), the step such as development (developing), hard baking (post baking), makes this transparent substrates 11 lower surface 111 weeks
It is formed with white frame layer 12, as shown in figure 1, forming panel construction 1, this transparent substrates lower surface can be further combined with having at edge
Touch control component, and form contact panel, the white that for example this transparent substrates 11 is formed with respect to this photosensitive resin composition
Plural circuit 13 can be further provided with, as the conducting of touch signal, and this white frame layer 12 just can be complete at frame layer 12
The circuit 13 of masking peripheral part, guarantees the planarization of contact panel accordingly, and has the work(of protection contact panel perimeter circuit concurrently
Effect, and the Related product outward appearance such as the contact panel applied of the present invention or flat-panel screens, can be limited by different conventional appearance color
In the disappearance of black or dark color, product appearance collocation property can be significantly increased.
Specific embodiment is as described below, however, not limiting to the present invention with this.
Photosensitive resin composition adopts following composition, as listed by table 1 and table 2.
The composition of table 1 sensing optical activity resin combination.
The composition of table 2 photosensitive resin composition.
Method of testing is as follows.
1. precipitation is observed.
Embodiment and comparative example are carried out optical concentration (Optical Density) and measures (taking at sample upper strata 1/3), amount
Survey day for the first day after preparing and latter 7 days of preparation, period keeps sample in room temperature standing test.And shone with wavelength 380nm-780nm
Penetrate the difference that each sample compares OD value.
OD value difference=(OD value-first day OD value on the 7th)/first day OD value * 100%
2. observe screening effect (under identical thickness).
Photosensitive resin composition prepare after the first day, metallic circuit is placed in individually and scribbles the photosensitive of embodiment and comparative example
Property resin combination sheet glass under, carrying out masking observes, and observes the metal scribbling under the sheet glass of photosensitive resin composition
Whether circuit is visible, shown in the shielding test result table 3 of each embodiment and comparative example.
Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Comparative example 1 | Comparative example 2 | |
OD value difference | 0.53% | 0.62% | 0.85% | 0.71% | 3.25% | 0.58% |
Shielding | ◎ | ◎ | ◎ | ◎ | ◎ | ○ |
◎ zero is common.
Table 3 test result.
As table 3 understands, each embodiment is larger with the numerical value of comparative example 1 with the difference of OD value in comparative example, represent to use and divide
The acryl resin of son amount 5000, its deposited phenomenon is more obvious, and in comparative example 2, the content of Chinese white is less than 20 wt%,
In the comparison of shielding, relatively poor with the shielding of comparative example 2, therefore the constituent composition of comparative example 1 and comparative example 2 and ratio
Example is not suitable for the goal of the invention of the present invention, and the constituent composition of embodiment 1 ~ 4 and ratio are then the preferable enforcement of the present invention
Example.
Claims (8)
1. one kind is applied to and coats a transparent substrates wherein surface periphery and form panel construction with to lower section line layer shape
The developed photosensitive resin composition becoming bridging effect is it is characterised in that this photosensitive resin composition contains 15 ~ 35wt%
Resin, the photosensitive initiator of 0.5 ~ 10wt%, the monomer of 0 ~ 20wt%, the solvent of 25 ~ 50wt%, the Chinese white of 20 ~ 45wt%
And the dispersant of 1 ~ 5wt%;
Wherein this resin comprises acryl resin, and this molecular resin amount is in 8000-100, in the range of 000.
2. it is applied to as claimed in claim 1 and coat a transparent substrates wherein surface periphery and form panel construction with right
Lower section line layer forms the developed photosensitive resin composition of bridging effect it is characterised in that this resin contains acryl acid.
3. it is applied to as claimed in claim 1 and coat a transparent substrates wherein surface periphery and form panel construction with right
Lower section line layer forms the developed photosensitive resin composition of bridging effect it is characterised in that this photosensitive initiator comprises oxime
Ester based compound, 1-Phenylethanone. based compound, benzophenone based compound or diimidazole based compound, or more photosensitive initiator
Mixing.
4. it is applied to as claimed in claim 1 and coat a transparent substrates wherein surface periphery and form panel construction with right
Lower section line layer formed bridging effect developed photosensitive resin composition it is characterised in that this monomer comprise polyfunctional
Acrylate monomer, non-water soluble monomers or water-soluble monomer;This polyfunctional acrylate monomer is trimethyl propane 3 third
Olefin(e) acid ester, three propyleneglycoles double methacrylates or 1,6 hexanediol double methacrylates;This non-water soluble monomers is penta red algae sugar
Alcohol triacrylate, trimethyl ether propane triacrylate, trimethyl ether propane trimethyl acrylic ester, three, two-ethanol isocyanide
Acid esters triacrylate, two, trihydroxymethyl propane tetraacrylate, diisoamyl tetrol five acrylate, five acrylate, tetraacethyl
Pentaerythritol, the own tetrol of six acetic acid two, six acetic acid diisoamyl tetrols, or be multiple functional radical monomer, tree-shaped/many clump of a small bundle of straw, etc. for silkworms to spin cocoons on acrylate
Few body, many clumps of a small bundle of straw, etc. for silkworms to spin cocoons on polyether acrylates, aethylis carbamases;This water-soluble monomer is the monomer of polyoxyethylene and polyoxypropylene, its
For two-(two-oxygen ethylene oxy ethylene) ethylene propylene acid esters, 15 polyoxyethylene trihydroxymethyl propane triacrylates, 30
Oxygen ethylene two, two-bis- to phenol methane diacrylate, 30 oxygen ethylene two, two-bis- to phenol dimethylamino methane base acrylate,
20 oxygen ethylene trihydroxymethyl propane triacrylates, 15 oxygen ethylene trihydroxymethyl propane triacrylates, methyl oxygen 500
50 oxygen ethylene monomethacrylates, 200 oxygen ethylene diacrylates, 400 oxygen ethylene diacrylates, 400
Individual oxygen ethylene dimethylacrylate, 600 oxygen ethylene diacrylates, 600 oxygen ethylene dimethylacrylates or poly-
Oxypropylene monomethacrylates;Also or this monomer be comprise this polyfunctional acrylate monomer, this non-water soluble monomers
Or the two or more mixing of this water-soluble monomer.
5. it is applied to as claimed in claim 1 and coat a transparent substrates wherein surface periphery and form panel construction with right
Lower section line layer forms the developed photosensitive resin composition of bridging effect it is characterised in that this solvent is propylene glycol list first
Base ether acetate.
6. described being applied to as arbitrary in claim 1 to 5 is coated a transparent substrates wherein surface periphery and is formed panel
Structure to form the developed photosensitive resin composition of bridging effect it is characterised in that this Chinese white to lower section line layer
Comprise titanium dioxide, ceruse, zinc oxide, zinc sulfide, Griffith's zinc white. or stibium oxide.
7. it is applied to as claimed in claim 6 and coat a transparent substrates wherein surface periphery and form panel construction with right
Lower section line layer forms the developed photosensitive resin composition of bridging effect it is characterised in that this photosensitive resin composition
Add another pigment further.
8. described being applied to as arbitrary in claim 1 to 5 is coated a transparent substrates wherein surface periphery and is formed panel
Structure to form the developed photosensitive resin composition of bridging effect it is characterised in that this molecular resin to lower section line layer
Amount is in the range of 20,000-70,000.