CN102604718A - Environmentally-friendly water-soluble non-oil metal rust-inhibiting lubricant - Google Patents
Environmentally-friendly water-soluble non-oil metal rust-inhibiting lubricant Download PDFInfo
- Publication number
- CN102604718A CN102604718A CN2012100301207A CN201210030120A CN102604718A CN 102604718 A CN102604718 A CN 102604718A CN 2012100301207 A CN2012100301207 A CN 2012100301207A CN 201210030120 A CN201210030120 A CN 201210030120A CN 102604718 A CN102604718 A CN 102604718A
- Authority
- CN
- China
- Prior art keywords
- minutes
- reaction kettle
- rust
- lubricant
- friendly water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an environmentally-friendly water-soluble non-oil metal rust-inhibiting lubricant which is characterized by comprising the following materials in percent by weight: 30% of amine borate, 5% of sodium gluconate, 2% of sodium molybdate, 20% of monoethanolamine, 13% of polyethylene glycol, 5% of ethanol, 15% of glycerol and the balance of deionized water. An organic metal corrosion inhibitor and an inorganic metal corrosion inhibitor are compounded and blended into the rust-inhibiting lubricant, thus the modern civilization production requirements for low energy consumption, low pollution, low emission and high environment friendliness are met. The lubricant has the four functions of inhibiting rust, removing rust, lubricating and washing and is a high-efficiency maintaining agent which is used for the production, storage, maintenance and repair of a variety of mechanical equipment, precision instruments and parts and component and can be used for keeping the metal product in the optimum work state so that the service life of the metal product is prolonged. The detection of the Shenyang Disease Control Center shows that the LD50 (lethal dose, 50%) is more than 10,000mg/kg, and the fishes and shrimps can live and propagate normally in 1 per mill aqueous solution.
Description
Technical field
The invention belongs to a kind of technology rust-inhibiting lubricant that is used for black, non-ferrous metal, the non-oily metal rust preventing lubricant of particularly a kind of environment-friendly water-soluble.
Background technology
Centuries, the home and abroad mainly is an oil at the metallic antirust material of usefulness always, promptly so-called " slushing oil ".Scientific development with facts have proved, oil unsatisfactory as rush-resisting material, shortcoming is: 1, labor high energy; 2, oil is prone to oxygenolysis, and rust-proof life is short, and damage a large amount of iron and steel because of corrosion every year; 3, follow-up oil removing difficulty; 4, the waste liquid after the oil removing is extremely hard to manage, and seriously polluted.
Summary of the invention
The invention solves the drawback of traditional slushing oil, purpose provides a kind of high-efficiency environment friendly, energy-conservation, the reduction of discharging characteristics that has, and is used for the non-oily metal rust preventing lubricant of a kind of environment-friendly water-soluble of ferrous metal, non-ferrous metal processing industry and equipment protection.
The non-oily metal rust preventing lubricant content Description of environment-friendly water-soluble of the present invention:
The non-oily metal rust preventing lubricant of environment-friendly water-soluble of the present invention is characterized in that: be made up of by mass percentage following substances: amine borate 30%, glucono-receive 5%, Sodium orthomolybdate 2%, Monoethanolamine MEA BASF 20%, polyoxyethylene glycol 13%, ethanol 5%, USP Kosher 15%, deionized water surplus.
The non-oily metal rust preventing lubricant of preparation environment-friendly water-soluble is pressed following process step:
(1), the capping still adds Monoethanolamine MEA BASF in the reaction kettle, stop to heat up behind the heat temperature raising to 65 ℃;
(2), in reaction kettle, add amine borate capping still, stirred 10 minutes, stir;
(3), with stirring 20～30 minutes in polyoxyethylene glycol, the USP Kosher adding reaction kettle;
(4), with glucono-receive, Sodium orthomolybdate fully dissolves the back with deionized water and adds in the reaction kettle and stirred 15 minutes;
(5), in reaction kettle, add ethanol and stir after 15 minutes static 20 minutes;
(6), blowing packing.
The non-oily metal rust preventing lubricant of environment-friendly water-soluble of the present invention; The organo-metallic inhibiter is incorporated in the rust-inhibiting lubricant through composite with the inorganic metal inhibiter; Overcome the defective that traditional rust-preventive agent exists, realized the requirement that the modern civilization of less energy-consumption, low pollution, low emission, high environmental protection is produced.Four large effects such as that the present invention has is antirust, separate rust, lubricated, cleaning; It is a kind of efficient maintaining agent that all kinds of mechanical means, precision instrument, component can both be suitable in links such as production, storage, maintenance, repairings; Can let metal products keep excellent working order for a long time, increase the service life.The non-oily metal rust preventing lubricant of while environment-friendly water-soluble, CDC is detected through Shenyang: LD
50>10000 milligrams of/㎏, but the procreation of 1 ‰ aqueous solution fishes and shrimps normal existences.
Embodiment
Do below the non-oily metal rust preventing lubricant of environment-friendly water-soluble of the present invention is achieved in that and specify.
Preparation environment-friendly water-soluble non-oily metal rust preventing lubricant, get: amine borate 30 ㎏, glucono-are received 5 ㎏, Sodium orthomolybdate 2 ㎏, Monoethanolamine MEA BASF 20 ㎏, polyoxyethylene glycol 13 ㎏, ethanol 5 ㎏, USP Kosher 15 ㎏, deionized water surplus.
At first the capping still adds Monoethanolamine MEA BASF 20 ㎏ in the reaction kettle, stops to heat up behind the heat temperature raising to 65 ℃; In reaction kettle, add amine borate 30 ㎏ capping stills, stirred 10 minutes, stir; With stirring 20～30 minutes in polyoxyethylene glycol 13 ㎏, the USP Kosher 15 ㎏ adding reaction kettle; Glucono-is received 5 ㎏, Sodium orthomolybdate 2 ㎏ fully to be dissolved the back with proper amount of deionized water and adds in the reaction kettle and stirred 15 minutes; In reaction kettle, add ethanol 5 ㎏ and stir after 15 minutes, static 20 minutes, the blowing packing.
The non-oily metal rust preventing lubricant of environment-friendly water-soluble of the present invention is a kind of smokeless, tasteless, nontoxic, harmless product, LD
50>10000 milligrams of/㎏, but the procreation of 1 ‰ aqueous solution fishes and shrimps normal existences.Prove through the industrialness production test: the present invention have antirust, separate four large effects such as rust, lubricated, cleaning; It is a kind of efficient maintaining agent that all kinds of mechanical means, precision instrument, component can both be suitable in links such as production, storage, maintenance, repairings; Can let metal products keep excellent working order for a long time, increase the service life.The non-oily metal rust preventing lubricant of while environment-friendly water-soluble, CDC is detected through Shenyang: LD
50>10000 milligrams of/㎏, but the procreation of 1 ‰ aqueous solution fishes and shrimps normal existences.
Claims (3)
1. non-oily metal rust preventing lubricant of environment-friendly water-soluble is characterized in that: be made up of by mass percentage following substances: amine borate 30%, glucono-receive 5%, Sodium orthomolybdate 2%, Monoethanolamine MEA BASF 20%, polyoxyethylene glycol 13%, ethanol 5%, USP Kosher 15%, deionized water surplus.
2. prepare the non-oily metal rust preventing lubricant of environment-friendly water-soluble as claimed in claim 1, it is characterized in that: press following process step:
(1), the capping still adds Monoethanolamine MEA BASF in the reaction kettle, stop to heat up behind the heat temperature raising to 65 ℃;
(2), in reaction kettle, add amine borate capping still, stirred 10 minutes, stir;
(3), with stirring 20～30 minutes in polyoxyethylene glycol, the USP Kosher adding reaction kettle;
(4), with glucono-receive, Sodium orthomolybdate fully dissolves the back with deionized water and adds in the reaction kettle and stirred 15 minutes;
(5), in reaction kettle, add ethanol and stir after 15 minutes static 20 minutes;
(6), blowing packing.
3. the non-oily metal rust preventing lubricant of environment-friendly water-soluble according to claim 1 is characterized in that: get: amine borate 30 ㎏, glucono-are received 5 ㎏, Sodium orthomolybdate 2 ㎏, Monoethanolamine MEA BASF 20 ㎏, polyoxyethylene glycol 13 ㎏, ethanol 5 ㎏, USP Kosher 15 ㎏, deionized water surplus; At first the capping still adds Monoethanolamine MEA BASF 20 ㎏ in the reaction kettle, stops to heat up behind the heat temperature raising to 65 ℃; In reaction kettle, add amine borate 30 ㎏ capping stills, stirred 10 minutes, stir; With stirring 20～30 minutes in polyoxyethylene glycol 13 ㎏, the USP Kosher 15 ㎏ adding reaction kettle; Glucono-is received 5 ㎏, Sodium orthomolybdate 2 ㎏ fully to be dissolved the back with proper amount of deionized water and adds in the reaction kettle and stirred 15 minutes; In reaction kettle, add ethanol 5 ㎏ and stir after 15 minutes, static 20 minutes, the blowing packing.