CN102602086A - Flame-retardant sci-tech veneer and preparation method thereof - Google Patents
Flame-retardant sci-tech veneer and preparation method thereof Download PDFInfo
- Publication number
- CN102602086A CN102602086A CN2012100499720A CN201210049972A CN102602086A CN 102602086 A CN102602086 A CN 102602086A CN 2012100499720 A CN2012100499720 A CN 2012100499720A CN 201210049972 A CN201210049972 A CN 201210049972A CN 102602086 A CN102602086 A CN 102602086A
- Authority
- CN
- China
- Prior art keywords
- retardant
- wooden skin
- fire
- flame
- science
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flame-retardant sci-tech veneer and a preparation method thereof. A piece of aluminum foil sandwich paper is adopted as a flame-retardant base material, or a piece of aluminum foil paper with one side surface being provided with fiber paper is adopted as the flame-retardant base material, and the sci-tech veneer with a flame-retardant function is adhered onto the surface of the fiber paper of the flame-retardant base material and processed at a high temperature and high pressure to prepare the flame-retardant sci-tech veneer. The traditional sci-tech veneer is adhered onto the aluminum foil sandwich paper having the physical flame-retardant function after being subjected to the flame-retardant processing, and the flame-retardant function is integrated with a decorative function of the sci-tech veneer into a whole, so that a decorative material is developed in the direction of multiple functions and multiple usages, and requirements of a consumption market can be met.
Description
Technical field
The present invention relates to the fire-retardant decorative field of materials, be specifically related to have the scientific and technological wooden skin of anti-flaming function.
Background technology
In recent years, because people's environmental consciousness is more and more stronger, natural finiss wood skin is more and more rare.Ornament materials market at home and abroad, scientific and technological wooden skin replaces natural wooden skin to become the main flow of ornament materials just in a large number.The Along with people's growth in the living standard not only requires environmental protection to ornament materials, and requires its function that possesses fire protection flame retarding, does not possess the scientific and technological wooden skin of fire protection flame retarding function, can not adapt to the requirement of development.Research and development have the scientific and technological wooden skin of fire-proof function, and the decoration functions of fire protection flame retarding function and scientific and technological wooden skin is ideally combined together, and have become the target of this area pursuit.But at present, also do not see on the market not only have imitative natural aesthetic feeling and texture, but also scientific and technological wooden skin with fire protection flame retarding function.
Summary of the invention
The technical problem that the present invention will solve provides wooden skin of a kind of fire-retardant science and technology and preparation method thereof, satisfies the demand of consumption market, when beautifying the environment, makes safe, relieved that people live.
The present invention realizes through following technical scheme:
The wooden skin of a kind of fire-retardant science and technology, adopting the sandwich paper of aluminium foil is ignition resistant substrate, or adopts aluminium-foil paper one side surface to be provided with the ignition resistant substrate that is of fibrous paper, pastes the scientific and technological wooden skin of tool anti-flaming function again in the fibrous paper surface of said ignition resistant substrate, processes through HTHP.
The further improvement project of the present invention is, the wooden skin of said science and technology floods through fire retardant, the scientific and technological wooden skin behind the dipping, and fire retardant accounts for the 3-5% of its weight.
The present invention further improvement project is that said fire retardant is one or both mixing in ten water Boratexes, the diammonium hydrogen phosphate.Both can mix with arbitrary proportion.No matter be to use any in two kinds of fire retardants, or use both mixtures, all needing water that it is blent into solid content is that 15-20% uses.
The present invention further improvement project is, ignition resistant substrate thickness is 0.1 ~ 0.3mm, and scientific and technological wooden skin thickness is 0.15 ~ 0.5mm.
The present invention's preparation comprises the following steps:
(1) at room temperature the wooden skin of science and technology was put into the fire retardant dipping 1.5-2.5 hour, then
Take out oven dry, bake out temperature is 80 ~ 95 ℃, and the scientific and technological wooden skin water content after the oven dry is 10-14%;
(2) the scientific and technological wooden skin that step (1) is obtained is attached to the fibrous paper surface of ignition resistant substrate again, adopts the thermoset phenolic resin with anti-flaming function as adhesive, cloth glue amount 70-90g/m
2, be 115 ~ 130 ℃ in temperature, pressure is 80 ~ 100 * 10
5Hot pressing 5-10min under the Pa.
The present invention compared with prior art has following obvious advantage:
One, the present invention carries out the scientific and technological wooden skin of tradition to be attached on the sandwich paper of aluminium foil of physics anti-flaming function after the flame treatment again; The decoration functions of anti-flaming function and scientific and technological wooden skin is combined as a whole; Ornament materials is developed to multi-functional, multipurpose direction, satisfy the demand of consumption market.
Two, the present invention has flame retardant effect preferably, can effectively delay the burning of material of main parts such as furniture at the fire early period of origination, for fire fighting and rescue gains time.
Description of drawings
Fig. 1 is a schematic perspective view of the present invention.
Fig. 2 is preparation flow figure of the present invention.
The specific embodiment
As shown in Figure 1, it is ignition resistant substrate that the present invention adopts the sandwich paper of aluminium foil, pastes scientific and technological wooden skin 2 again on fibrous paper 11 surfaces of a side of said ignition resistant substrate.Still as shown in Figure 1, the intermediate layer of the sandwich paper of said aluminium foil is an aluminium-foil paper 1, and outer 11 is fibrous paper, and said fibrous paper is pasted on the both side surface (pasting fibrous paper on the aluminium-foil paper surface is prior art) of aluminium-foil paper.In the present embodiment, aluminium-foil paper adopts 20 grammes per square metres, and the fibrous paper of both side surface adopts the blank sheet of paper of 40 grammes per square metres respectively, and the thickness of the sandwich paper of processing of aluminium foil is 0.2 mm.
In the present embodiment, it is 2540mm (length) * 660mm (wide) that the truewood skin adopts book size, and thickness is the wooden truewood skin of 0.3mm brazilic acid branch science and technology, and moisture content is 12%, and thickness is 0.3 mm.
Fire retardant is selected diammonium hydrogen phosphate for use, and adding water, to blend into solid content be that 20% solution uses.
Preparation comprises the following steps:
(1) at room temperature the wooden skin of science and technology was put into above-mentioned retardant solution dipping 2 hours, take out oven dry then, bake out temperature is 80 ~ 95 ℃, and the scientific and technological wooden skin water content after the oven dry is 10-14%, and the fire retardant that carries accounts for 4% of its weight;
(2) the scientific and technological wooden skin that step (1) is obtained is attached to sandwich paper one side surface of aluminium foil again, adopts the thermoset phenolic resin with anti-flaming function as adhesive, and cloth glue amount is 80g/m
2, be 120 ℃ in temperature, pressure is 90 * 10
5Hot pressing 5min under the Pa.
The performance of the wooden skin of processing of fire-retardant science and technology:
Wood grain and color and luster with brazilic acid branch timber, decorate properties reach truewood leather jacket plaque high-class product grade; Fire resistance is excellent.
Fire retardant is selected ten water Boratexes and diammonium hydrogen phosphate mixture (both mixed proportions are 1:1) for use, and it is 15% that water blends into solid content with both mixtures.All the other are implemented like embodiment 1.
Embodiment 3
Fire retardant is selected ten water Boratexes for use, and it is 18% that water blends into solid content with fire retardant.All the other are implemented like embodiment 1.
Claims (5)
1. the wooden skin of fire-retardant science and technology; It is characterized in that: adopting the sandwich paper of aluminium foil is ignition resistant substrate; Or adopt aluminium-foil paper one side surface to be provided with the ignition resistant substrate that is of fibrous paper, and paste the scientific and technological wooden skin of tool anti-flaming function again in the fibrous paper surface of said ignition resistant substrate, process through HTHP.
2. based on the wooden skin of the described a kind of fire-retardant science and technology of claim 1, it is characterized in that: the wooden skin of said science and technology floods through fire retardant, the scientific and technological wooden skin behind the dipping, and fire retardant accounts for the 3-5% of its weight.
3. the wooden skin of a kind of fire-retardant science and technology according to claim 2 is characterized in that: said fire retardant is one or both mixing in ten water Boratexes, the diammonium hydrogen phosphate.
4. the wooden skin of a kind of fire-retardant science and technology according to claim 1 and 2, it is characterized in that: ignition resistant substrate thickness is 0.1 ~ 0.3mm, scientific and technological wooden skin thickness is 0.15 ~ 0.5mm.
5. the wooden skin of a kind of fire-retardant science and technology according to claim 2 is characterized in that preparation comprises the following steps:
(1) at room temperature the wooden skin of science and technology was put into the fire retardant dipping 1.5-2.5 hour, then
Take out oven dry, bake out temperature is 80 ~ 95 ℃, and the scientific and technological wooden skin water content after the oven dry is 10-14%;
(2) the scientific and technological wooden skin that step (1) is obtained is attached to the fibrous paper surface of ignition resistant substrate again, adopts the thermoset phenolic resin with anti-flaming function as adhesive, cloth glue amount 70-90g/m
2, be that 115 ~ 130 ℃, pressure are 80 ~ 100 * 10 in temperature
5Hot pressing 5-10min under the Pa.