CN102586680A - 一种低屈强比的高层建筑结构用钢板及其正火工艺 - Google Patents

一种低屈强比的高层建筑结构用钢板及其正火工艺 Download PDF

Info

Publication number
CN102586680A
CN102586680A CN2012100765998A CN201210076599A CN102586680A CN 102586680 A CN102586680 A CN 102586680A CN 2012100765998 A CN2012100765998 A CN 2012100765998A CN 201210076599 A CN201210076599 A CN 201210076599A CN 102586680 A CN102586680 A CN 102586680A
Authority
CN
China
Prior art keywords
steel plate
percent
temperature
yield
equal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100765998A
Other languages
English (en)
Inventor
高志国
董瑞峰
程德富
史文义
杨雄
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Baotou Iron and Steel Group Co Ltd
Inner Mongolia Baotou Steel Union Co Ltd
Original Assignee
Baotou Iron and Steel Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baotou Iron and Steel Group Co Ltd filed Critical Baotou Iron and Steel Group Co Ltd
Priority to CN2012100765998A priority Critical patent/CN102586680A/zh
Publication of CN102586680A publication Critical patent/CN102586680A/zh
Pending legal-status Critical Current

Abstract

一种低屈强比的高层建筑结构用钢板及其正火工艺，属于冶金技术领域，涉及热处理工艺技术，其特征在于板坯的(重量百分比)化学成分为：C0.10％-0.18％，Si 0.25％-0.45％，Mn 1.3％-1.6％，P≤0.015％，S≤0.008％，Nb+V+Ti0.05％-0.24％，Ni 0.1％-0.4％，余量为Fe和不可避免的杂质。其正火工艺为：加热温度为860-920℃，板坯到温入炉，保温时间10-100分钟，然后出炉空冷。由此工艺生产的产品具有优良的力学性能，抗拉强度550-570MPa，屈服强度达430-450MPa，延伸率28-31％，屈强比≤0.80，-40℃冲击值≥100J，Z向性能满足Z35要求。

Description

一种低屈强比的高层建筑结构用钢板及其正火工艺
技术领域
本发明属于冶金技术领域，特别涉及钢板正火热处理工艺。
背景技术
建筑行业是我国消费钢材量最大的行业，但是与发达国家相比，我国建筑用钢产业消费结构仍处于中低档水平，建筑用钢生产和应用技术相对落后，资源浪费巨大，在抗震、耐候、耐火、特殊规格等高端建筑用钢产品研发方面尚不能满足国家发展战略的需求。在建筑结构钢设计上，不断提高钢材强度等级、减少钢材用量、减轻自重等成为必然趋势，在节能环保方面也日益提高其要求，大量采用低碳产品，一方面减少焊接环节的复杂作业、另一方面获得韧性更优良的材料特性。
目前国内各大钢厂均在开发高等级高层建筑结构钢方面投入很大，采用热轧、TMCP、热处理等手段开发了大量优质产品，应用到国内的各种标志性建筑物建设当中，部分品种已经达到国际领先水平，但对于低屈强比建筑结构用钢方面的研发相对较少。本发明公开一种低屈强比的高层建筑结构钢板及其正火工艺，为我国高抗震性建筑结构用钢的开发和应用奠定基础。
发明内容
本发明的目的是公开一种低屈强比的高层建筑结构用钢板及其正火工艺，其板坯的(重量百分比)化学成分含量应符合：C 0.10％-0.18％，Si 0.25％-0.45％，Mn 1.3％-1.6％，P≤0.015％，S≤0.008％，Nb+V+Ti 0.05％-0.24％，Ni 0.1％-0.4％，余量为Fe和不可避免的杂质。
板坯的加热温度为850-920℃，样品到温入炉，保温时间10-100分钟，然后出炉空冷。由此工艺生产的产品具有优良的力学性能，抗拉强度550-570MPa，屈服强度达430-450MPa，延伸率28-31％，屈强比≤0.80，冲击值≥100J，Z向性能满足Z35要求。
本发明突出优点是热轧钢板不仅具有高强度和高塑性，而且屈强比低于0.80，抗震性能优异。
附图说明
图1为实施例1对应的典型金相组织照片；
图2为实施例2对应的典型金相组织照片。
具体实施方式
以下结合实施例对本发明作进一步详细的说明。
实施例1：
将拟正火处理的板坯放入加热炉，板坯的(重量百分比)化学成分为：C0.15，Si 0.36％，Mn 1.51％，P 0.009％，S 0.002％，Nb 0.042％，V 0.05％，Ti0.012，Ni 0.2％，余量为Fe和不可避免的杂质。板坯的加热温度为860℃，样品到温入炉，保温时间20分钟，然后出炉空冷。由此工艺生产的产品具有优良的力学性能，其拉伸性能检测值见表1，冲击功见表2，力学性能均符合国标GB/T19879-2008的要求，屈强比为0.77，Z向性能满足Z35要求。典型钢板金相组织如图1所示，平均晶粒度评定为12.5级。
表1拉伸性能检测值
Figure BSA00000688076900021
表2冲击功测试值
Figure BSA00000688076900022
实施例2：
将拟正火处理的板坯放入加热炉，板坯的(重量百分比)化学成分为：C0.15，Si 0.36％，Mn 1.51％，P 0.009％，S 0.002％，Nb 0.042％，V 0.05％，Ti0.012，Ni 0.2％，余量为Fe和不可避免的杂质。板坯的加热温度为860℃，到温入炉，保温时间40分钟，然后出炉空冷。由此工艺生产的产品具有优良的力学性能，其拉伸性能检测值见表3，冲击功见表4，力学性能均符合国标GB/T19879-2008的要求，屈强比为0.76，Z向性能满足Z35要求。典型钢板金相组织如图2所示，平均晶粒度评定为12级。
表3拉伸性能检测值
Figure BSA00000688076900031
表4冲击功测试值
Figure BSA00000688076900032

Claims (2)

1.一种低屈强比的高层建筑结构用钢板，其特征在于以重量百分比计化学成分为：C 0.10％-0.18％，Si 0.25％-0.45％，Mn 1.3％-1.6％，P≤0.015％，S≤0.008％，Nb+V+Ti 0.05％-0.24％，Ni 0.1％-0.4％，余量为Fe和不可避免的杂质。
2.如权利要求1所述特征的一种低屈强比的高层建筑结构用钢板的正火工艺，其特征在于正火加热温度为860-920℃，板坯到温入炉，保温时间10-100分钟，然后出炉空冷。
CN2012100765998A 2012-03-22 2012-03-22 一种低屈强比的高层建筑结构用钢板及其正火工艺 Pending CN102586680A (zh)