CN102585662A - 一种阀门专用防腐型热固性粉末涂料 - Google Patents

一种阀门专用防腐型热固性粉末涂料 Download PDF

Info

Publication number
CN102585662A
CN102585662A CN2011104546707A CN201110454670A CN102585662A CN 102585662 A CN102585662 A CN 102585662A CN 2011104546707 A CN2011104546707 A CN 2011104546707A CN 201110454670 A CN201110454670 A CN 201110454670A CN 102585662 A CN102585662 A CN 102585662A
Authority
CN
China
Prior art keywords
parts
powder coating
epoxy resin
valve
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011104546707A
Other languages
English (en)
Inventor
刘荣兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Huahui Plastic Industry Science & Technology Co Ltd
Original Assignee
Anhui Huahui Plastic Industry Science & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Huahui Plastic Industry Science & Technology Co Ltd filed Critical Anhui Huahui Plastic Industry Science & Technology Co Ltd
Priority to CN2011104546707A priority Critical patent/CN102585662A/zh
Publication of CN102585662A publication Critical patent/CN102585662A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阀门专用防腐型热固性粉末涂料，其由下列组分组成，各组分的重量份为：环氧树脂650-850份、固化剂15～25份、钛白粉30-40份、填料200～300份、流平剂5-10份、脱漆剂5-10份、颜料50-65份、消泡剂3-5份。本发明的热固性粉末涂料具有很好的防腐效果，用本发明的涂料喷涂阀门，所得的阀门表面涂膜外观上表现出：表面流平好、光泽高、立体感强，无缩孔和针孔现象。且生产工艺简单，使用方便，从而降低了生产成本低。

Description

一种阀门专用防腐型热固性粉末涂料
技术领域
本发明涉及精细化工领域，，具体涉及一种阀门专用防腐型热固性粉末涂料。
背景技术
    金属阀门的腐蚀，通常被理解为阀门金属材料在化学的或电化学的环境作用下所受到的破坏。由于“腐蚀”现象出现于金属与周围环境自发的相互作用当中，因此，怎样将金属与周围环境相隔绝，成为人们普通关注的问题，众所周知，金属的腐蚀破坏对阀门的作用期限，可靠性和使用寿命有相当大的影响。常用的方法是在阀门的表面涂覆防腐型热固性粉末涂料，目前行业内一般阀门用热固性粉末涂料的生产工艺较复杂，生产难度高，防腐蚀性不强。 
发明内容  
    本发明提供了一种阀门专用防腐型热固性粉末涂料，本热固性粉末涂料具有防腐效果好，工艺简单，生产成本低的特点。
    本发明解决其技术问题所采用的技术方案是：
   一种阀门专用防腐型热固性粉末涂料，其由下列组分组成，各组分的重量份为： 
     环氧树脂 650-850份 
     固化剂   15～25份 
钛白粉   30-40份 
填料     200～300份
     流平剂    5-10份
脱漆剂     5-10份
颜料    50-65份
消泡剂   3-5份，
所述的环氧树脂为双酚A型环氧树脂，其软化点在100-120℃，  
所述的填料为超细碳酸钙，所述的流平疏散剂为环氧树脂专用流平剂BYK-333，所述的固化剂为滕州市瑞得丰精细化工有限公司提供的T105粉未涂料固化剂－RDF06 。
所述的阀门专用防腐型热固性粉末涂料，其由下列组分组成，各组分的重量份为： 
     环氧树脂 700-800份 
     固化剂   18-22份 
钛白粉   32-38份 
填料     240-280份
     流平剂    5-8份
脱漆剂     6-8份
颜料    55-65份
消泡剂   3.5-4.5份，
所述的环氧树脂为双酚A型环氧树脂，其软化点在100-120℃，  
所述的填料为超细碳酸钙，所述的流平疏散剂为环氧树脂专用流平剂BYK-333，所述的固化剂为滕州市瑞得丰精细化工有限公司提供的T105粉未涂料固化剂－RDF06 。
制备时将配方原材料按常规方法投入到高速搅拌机里充分搅拌即可。
    本发明的有益效果：
本发明的热固性粉末涂料，其配方中所用的环氧树脂，其软化点在100-120℃之间，其环氧树脂柔软性强，同时配方中各种主料、辅料的配比合理，因此本配方比例所得的热固性粉末涂料因此具有很好的防腐效果，且生产工艺简单，使用方便，从而降低了生产成本低。具体特点如下：
 1、本发明的热固性粉末涂料在潮湿环境和低盐度地区防腐型强 ，
2、与金属阀门的附着力强，硬度高，耐磨性好。
具体实施方式
   实施例1
一种阀门专用防腐型热固性粉末涂料， 其由下列组分组成，各组分的重量份为： 
     双酚A型环氧树脂   780份 
固化剂   18-22份       由滕州市瑞得丰精细化工有限公司提供
的T105粉未涂料固化剂－RDF06 
     钛白粉   32-38份 
填料超细碳酸钙            260份
     环氧树脂专用流平剂BYK-333  6份
脱漆剂     6份
颜料     65份
消泡剂   4份。
制备时将配方原材料按常规方法投入到高速搅拌机里充分搅拌即可。
试验测得本发明的阀门专用防腐型热固性粉末涂料涂膜（膜厚100μm）与普通阀门专用热固性粉末涂料涂膜的基本性能对比如下表1：
表1    
机械性能 普通阀门专用热固性粉末涂料 阀门专用防腐型热固性粉末涂料
冲击强度（正反） 正冲80kg.cm 反冲80kg.cm 正冲80kg.cm 反冲80kg.cm
弯曲(Φ2mm) 不通过 通过
盐雾试验（小时） 500 大于1000
外观 流平不好、光泽性差、立体感不强 表面流平好、光泽高、立体感强，无缩孔和针孔现象

Claims (2)

1.一种阀门专用防腐型热固性粉末涂料，其特征在于：其由下列组分组成，各组分的重量份为： 
环氧树脂 650-850份 
固化剂   15～25份 
钛白粉   30-40份 
填料     200～300份
流平剂    5-10份
脱漆剂     5-10份
颜料    50-65份
消泡剂   3-5份，
所述的环氧树脂为双酚A型环氧树脂，其软化点在100-120℃，  
所述的填料为超细碳酸钙，所述的流平疏散剂为环氧树脂专用流平剂BYK-333，所述的固化剂为滕州市瑞得丰精细化工有限公司提供的T105粉未涂料固化剂－RDF06 。
2.根据权利要求1所述的阀门专用防腐型热固性粉末涂料，其特征在于：其由下列组分组成，各组分的重量份为： 
环氧树脂 700-800份 
固化剂   18-22份 
钛白粉   32-38份 
填料     240-280份
流平剂    5-8份
脱漆剂     6-8份
颜料    55-65份
消泡剂   3.5-4.5份，
所述的环氧树脂为双酚A型环氧树脂，其软化点在100-120℃，  
所述的填料为超细碳酸钙，所述的流平疏散剂为环氧树脂专用流平剂BYK-333，所述的固化剂为滕州市瑞得丰精细化工有限公司提供的T105粉未涂料固化剂－RDF06。
CN2011104546707A 2011-12-30 2011-12-30 一种阀门专用防腐型热固性粉末涂料 Pending CN102585662A (zh)