CN102585613B - 一种抗渗黄乳胶漆 - Google Patents
一种抗渗黄乳胶漆 Download PDFInfo
- Publication number
- CN102585613B CN102585613B CN201210026787.XA CN201210026787A CN102585613B CN 102585613 B CN102585613 B CN 102585613B CN 201210026787 A CN201210026787 A CN 201210026787A CN 102585613 B CN102585613 B CN 102585613B
- Authority
- CN
- China
- Prior art keywords
- emulsion paint
- yellow
- impervious
- alcohol ester
- namigai
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种涉及化工涂料领域的抗渗黄乳胶漆,所述的乳胶漆由去离子水、聚合物胶粉、五合一钠米钙、钛白粉BA101-01、成膜助剂醇脂12、润湿分散剂4100、VAE乳液707、乙二醇、消泡剂F-111、防腐剂C115和消黄粉组成;所述的乳胶漆不但质地细腻,手感入稠,低价环保,耐水冲洗,而且能够避免在涂刷后发生渗黄现象。
Description
【技术领域】
本发明涉及化工涂料领域,尤其是涉及一种用于涂刷内墙的抗渗黄乳胶漆。
【背景技术】
公知的,目前市场上常用的乳胶漆多为常规型涂料,当对烟熏过的酒店、宾馆、餐厅和厨房的内墙涂刷翻新时,这些乳胶漆在涂刷后大多会在墙面渗出一层象云彩块似的黄色渗出物;由于这些黄色渗出物直接影响到翻新后内墙的整体美观,因此,乳胶漆的这种渗黄现象是一个让涂料施工人员十分头疼的问题。
【发明内容】
为了克服背景技术中的不足,本发明提供了一种抗渗黄乳胶漆,所述的乳胶漆不但质地细腻,手感入稠,低价环保,耐水冲洗,而且能够避免在涂刷后发生渗黄现象。
为实现上述发明目的,本发明采用如下技术方案:
一种抗渗黄乳胶漆,所述的乳胶漆由如下组份按重量百分比组成:
去离子水 30—40%
聚合物胶粉 1.2%—1.5%
五合一钠米钙 40%—50%
钛白粉BA101-01 5%—10%
成膜助剂醇脂12 0.5%—0.7%
润湿分散剂4100 0.1%—0.15%
VAE乳液707 8%—15%
乙二醇 0.07%—0.1%
消泡剂F-111 0.02%—0.03%
防腐剂C115 0.1%—0.2%
消黄粉 0.2%—0.3%
上述各组份的百分比总和为100%。
所述的抗渗黄乳胶漆,所述的乳胶漆由如下组份按重量百分比组成:
去离子水 32.42%
聚合物胶粉 1.2%
五合一钠米钙 42%
钛白粉BA101-01 8%
成膜助剂醇脂12 0.6%
润湿分散剂4100 0.15%
VAE乳液707 15%
乙二醇 0.1%
消泡剂F-111 0.03%
防腐剂C115 0.2%
消黄粉 0.3%
上述各组份的百分比总和为100%。
将上述各组份按重量百分比混合后搅拌均匀,并研磨至25微米后过滤包装即制成所述的抗渗黄乳胶漆。
所述的抗渗黄乳胶漆,所述的聚合物胶粉由纤维素、纤维素醚和助溶剂按5:3:2比例混合组成。
所述的抗渗黄乳胶漆,所述的五合一纳米钙由洛阳市阳光涂料研究所生产。
所述的抗渗黄乳胶漆,所述的去离子水、聚合物胶粉、五合一纳米钙、钛白粉BA101-01和VAE乳液707为主料,所述的成膜助剂醇脂12、润湿分散剂4100、乙二醇、消泡剂F-111、防腐剂C115和消黄粉为辅料。
由于采用如上所述的技术方案,本发明具有如下有益效果:
本发明所述的抗渗黄乳胶漆不但质地细腻,手感入稠,低价环保,耐水冲洗,而且能够有效避免在涂刷后发生渗黄现象;此外,所述的乳胶漆不但符合GB/T9756—2001,即合成树脂内墙涂料标准,同时也符合GB/T18582—2008,即装修装饰内墙涂料有害物质限量的环保标准。
【具体实施方式】
通过下面的实施例可以更详细的解释本发明,公开本发明的目的旨在保护本发明范围内的一切变化和改进,本发明并不局限于下面的实施例;
按重量百分比称取:
去离子水 32.42%
聚合物胶粉 1.2%
五合一钠米钙 42%
钛白粉BA101-01 8%
成膜助剂醇脂12 0.6%
润湿分散剂4100 0.15%
VAE乳液707 15%
乙二醇 0.1%
消泡剂F-111 0.03%
防腐剂C115 0.2%
消黄粉 0.3%
将上述各组份混合后搅拌均匀,并研磨至25微米后过滤包装即制成所述的抗渗黄乳胶漆;其中,所述的聚合物胶粉由纤维素、纤维素醚和助溶剂按5:3:2比例混合组成;所述的五合一纳米钙是洛阳市阳光涂料研究所生产的产品;此外,所述的抗渗黄乳胶漆中,所述的去离子水、聚合物胶粉、五合一纳米钙、钛白粉BA101-01和VAE乳液707为主料,所述的成膜助剂醇脂12、润湿分散剂4100、乙二醇、消泡剂F-111、防腐剂C115和消黄粉为辅料。
经检测证实,所述的抗渗黄乳胶漆不仅符合合成树脂内墙涂料标准GB/T9756—2001的标准,而且还符合装修装饰内墙涂料有害物质限量GB/T18582—2008的环保标准。
Claims (5)
1.一种抗渗黄乳胶漆,其特征是:所述的乳胶漆由如下组份按重量百分比组成:
去离子水 30—40%
聚合物胶粉 1.2%—1.5%
五合一纳米钙 40%—50%
钛白粉BA101-01 5%—10%
成膜助剂醇酯十二 0.5%—0.7%
润湿分散剂4100 0.1%—0.15%
VAE乳液707 8%—15%
乙二醇 0.07%—0.1%
消泡剂F-111 0.02%—0.03%
防腐剂C115 0.1%—0.2%
消黄粉 0.2%—0.3%
上述各组份的百分比总和为100%;所述的聚合物胶粉由纤维素、纤维素醚和助溶剂按5:3:2比例混合组成。
2.根据权利要求1所述的抗渗黄乳胶漆,其特征是:所述的乳胶漆由如下组份按重量百分比组成:
去离子水 32.42%
聚合物胶粉 1.2%
五合一纳米钙 42%
钛白粉BA101-01 8%
成膜助剂醇酯十二 0.6%
润湿分散剂4100 0.15%
VAE乳液707 15%
乙二醇 0.1%
消泡剂F-111 0.03%
防腐剂C115 0.2%
消黄粉 0.3%
上述各组份的百分比总和为100%。
3.根据权利要求1或2所述的抗渗黄乳胶漆,其特征是:将所述的各组份按重量百分比混合后搅拌均匀,并研磨至25微米后过滤包装即制成所述的抗渗黄乳胶漆。
4.根据权利要求1或2所述的抗渗黄乳胶漆,其特征是:所述的五合一纳米钙由洛阳市阳光涂料研究所生产。
5.根据权利要求1或2所述的抗渗黄乳胶漆,其特征是:所述的去离子水、聚合物胶粉、五合一纳米钙、钛白粉BA101-01和VAE乳液707为主料,所述的成膜助剂醇酯十二、润湿分散剂4100、乙二醇、消泡剂F-111、防腐剂C115和消黄粉为辅料。